To develop a smelting process for the comprehensive utilization of high-chromium vanadium-titanium magnetite(HCVTM),the micro-sinter test was applied to investigate the influence of basicity and temperature on the HCV...To develop a smelting process for the comprehensive utilization of high-chromium vanadium-titanium magnetite(HCVTM),the micro-sinter test was applied to investigate the influence of basicity and temperature on the HCVTM sinters.The bonding phase strength(BS) was tested via an electronic universal testing machine.The phase transformations of the HCVTM sinters were detected via X-ray diffraction(XRD),whereas the structure and mineralogy of the HCVTM sinters under different temperatures and basicities were detected via scanning electron microscopy in combination with energy-dispersive spectroscopy(SEM–EDS).Our results demonstrate that the BS of the HCVTM sinters exhibits a slightly increasing tendency with an increase in temperature when the basicity is 2.4 and within the range of 2.8–4.0.Many cracks,small size crystals,and dependent phase structures are generated by increasing the sinter basicity.The BS is lower than 4000 N when the basicity is 2.2 and 2.8.When the temperature is in the range of 1280–1300?C,the BS exceeds 4000 N with the basicity of 2.0,2.4,and 3.4–4.0.The pore size of the HCVTM sinters increases with the increase of the temperature.The perovskite decreases,whereas the silicate phase increases with basicity higher than 3.2.This study provides theoretical and technical foundations for the effective production of HCVTM sinters.展开更多
With the use of Ti/Ni/Cu/Ni multiple foils as interlayer,carbon/carbon（C/C） composite was bonded to Nibased superalloy GH3044 by partial transient liquid-phase bonding technique.The effect of bonding temperature on ...With the use of Ti/Ni/Cu/Ni multiple foils as interlayer,carbon/carbon（C/C） composite was bonded to Nibased superalloy GH3044 by partial transient liquid-phase bonding technique.The effect of bonding temperature on the microstructures and strengths of the joints was investigated.The results showed that gradient structural multiple interlayers composed of ‘‘C–Ti reaction layer/Ti–Ni intermetallic compound layer/Ni–Cu sosoloid/residual Cu layer/Ni-GH3044 diffusion layer＇＇ were formed between C/C composite and GH3044.The shear strength of the C/C composite/GH3044 joint reached the highest value of 26.1 MPa when the bonding temperature was 1,030 °C.In addition,the fracture morphology showed that the fracture mode changed with the increase of bonding temperature.展开更多
Partial transient liquid-phase bonding （PTLP bonding） of Si3N4 ceramic with Ti/Cu/Ti multi-interlayer is performed with changing the thickness of Ti foil. The influence of Ti foil thickness on interface structure an...Partial transient liquid-phase bonding （PTLP bonding） of Si3N4 ceramic with Ti/Cu/Ti multi-interlayer is performed with changing the thickness of Ti foil. The influence of Ti foil thickness on interface structure and joint strength was discussed. The joint interface structures are investigated by scanning electron microscope （SEM） and energy dispersion spectroscopy（EDS）. The results show that the maximum joint strength of 210 MPa is obtained at room temperature in the experiments. When joining temperature and time are not changed and the process of isothermal solidification is sufficient , interface structure, reaction layer thickness and isothermal solidification thickness change with the thickness of Ti foil.展开更多
基金financially supported by the National Basic Research Program of China (No.2013CB632603)the National Key Technology R&D Program of China (No.2015BAB19B02)the National Natural Science Foundation of China (Nos.51674084,51174051,and 51574082)
文摘To develop a smelting process for the comprehensive utilization of high-chromium vanadium-titanium magnetite(HCVTM),the micro-sinter test was applied to investigate the influence of basicity and temperature on the HCVTM sinters.The bonding phase strength(BS) was tested via an electronic universal testing machine.The phase transformations of the HCVTM sinters were detected via X-ray diffraction(XRD),whereas the structure and mineralogy of the HCVTM sinters under different temperatures and basicities were detected via scanning electron microscopy in combination with energy-dispersive spectroscopy(SEM–EDS).Our results demonstrate that the BS of the HCVTM sinters exhibits a slightly increasing tendency with an increase in temperature when the basicity is 2.4 and within the range of 2.8–4.0.Many cracks,small size crystals,and dependent phase structures are generated by increasing the sinter basicity.The BS is lower than 4000 N when the basicity is 2.2 and 2.8.When the temperature is in the range of 1280–1300?C,the BS exceeds 4000 N with the basicity of 2.0,2.4,and 3.4–4.0.The pore size of the HCVTM sinters increases with the increase of the temperature.The perovskite decreases,whereas the silicate phase increases with basicity higher than 3.2.This study provides theoretical and technical foundations for the effective production of HCVTM sinters.
基金financially supported by the National Natural Science Foundation of China(Nos.51202193 and 51221001)the Fundamental Research Foundation of Northwestern Polytechnical University(No.GBKY1021)the‘‘111’’Project(No.08040)
文摘With the use of Ti/Ni/Cu/Ni multiple foils as interlayer,carbon/carbon（C/C） composite was bonded to Nibased superalloy GH3044 by partial transient liquid-phase bonding technique.The effect of bonding temperature on the microstructures and strengths of the joints was investigated.The results showed that gradient structural multiple interlayers composed of ‘‘C–Ti reaction layer/Ti–Ni intermetallic compound layer/Ni–Cu sosoloid/residual Cu layer/Ni-GH3044 diffusion layer＇＇ were formed between C/C composite and GH3044.The shear strength of the C/C composite/GH3044 joint reached the highest value of 26.1 MPa when the bonding temperature was 1,030 °C.In addition,the fracture morphology showed that the fracture mode changed with the increase of bonding temperature.
文摘Partial transient liquid-phase bonding （PTLP bonding） of Si3N4 ceramic with Ti/Cu/Ti multi-interlayer is performed with changing the thickness of Ti foil. The influence of Ti foil thickness on interface structure and joint strength was discussed. The joint interface structures are investigated by scanning electron microscope （SEM） and energy dispersion spectroscopy（EDS）. The results show that the maximum joint strength of 210 MPa is obtained at room temperature in the experiments. When joining temperature and time are not changed and the process of isothermal solidification is sufficient , interface structure, reaction layer thickness and isothermal solidification thickness change with the thickness of Ti foil.