Fuel injection properties,including the injection rate(temporal aspects)and spray behavior(spatial aspects),play a crucial role in the combustion efficiency and emissions of diesel engines.This study investigates the ...Fuel injection properties,including the injection rate(temporal aspects)and spray behavior(spatial aspects),play a crucial role in the combustion efficiency and emissions of diesel engines.This study investigates the effects of different ethanol-biodiesel-diesel(EBD)blends on the injection performance in diesel engines.Experimental tests are conducted to examine key injection parameters,such as spray penetration distance,spray cone angle,and droplet size,alongside an analysis of coupling leakage.The main findings are as follows:(1)The injection behavior of ethanol and diesel differs significantly.The addition of ethanol reduces the density,viscosity,and modulus of elasticity of the fuel mixture.While the injection advance angle,penetration distance,and Sauter mean diameter show minimal changes,the spray cone angle and coupling leakage increase notably.These alterations may disrupt the“fuelair-chamber”matching characteristics of the original engine,potentially affecting performance.(2)In contrast,the injection performance of biodiesel ismore similar to that of diesel.As biodiesel content increases,the density,viscosity,and modulus of elasticity of the blended fuel also grow.Though changes in injection timing,penetration distance,and spray cone angle remain minimal,the Sauter mean diameter experiences a slight increase.The“air-fuel chamber”compatibility of the original engine is largely unaffected,though fuel atomization slightly deteriorates.Blending up to 20%biodiesel and 30%ethanol with diesel effectively compensates for the shortcomings of using single fuels,maintaining favorable injection dynamics while enhancing lubrication and sealing performance of engine components.展开更多
The effect of maleic anhydride grafted styrene-ethylene- buty-lene-styrene block copolymer （SEBS-g-MAH） and in-situ grafting MAH on mechanical, dynamic mechanical properties of wood flour/recycled plastic blends com...The effect of maleic anhydride grafted styrene-ethylene- buty-lene-styrene block copolymer （SEBS-g-MAH） and in-situ grafting MAH on mechanical, dynamic mechanical properties of wood flour/recycled plastic blends composites was investigated. Recycled plastic polypro-pylene （PP）, high-density polyethylene （HDPE） and polystyrene （PS）, were mixed with wood flour in a high speed blender and then extruded by a twin/single screw tandem extruder system to form wood flour/recycled plastic blends composites. Results show that the impact properties of the composites were improved more significantly by using SEBS-g-MAH compatibilizer than by using the mixtures of MAH and DCP via reactive blending in situ. However, contrary results were ob-served on the tensile and flexural properties of the corresponding com-posites. In General, the mechanical properties of composites made from recycled plastic blends were inferior to those made from virgin plastic blends, especially in elongation break. The morphological study verified that the interfacial adhesion or the compatibility of plastic blends with wood flour was improved by adding SEBS-g-MAH or in-situ grafting MAH. A better interfacial bonding between PP, HDPE, PS and wood flour was obtained by in-situ grafting MAH than the addition of SEBS-g-MAH. In-situ grafting MAH can be considered as a potential way of increasing the interfacial compatibility between plastic blends and wood flour. The storage modulus and damping factor of composites were also characterized through dynamic mechanical analysis （DMA）.展开更多
Poly（vinylidene fluoride） （PVDF） and poly（butylene succinate-co-24 mol% hexamethylene succinate） （PBHS）, both crystalline polymers, formed melt-miscible crystalline/crystalline polymer blends. Both the charact...Poly（vinylidene fluoride） （PVDF） and poly（butylene succinate-co-24 mol% hexamethylene succinate） （PBHS）, both crystalline polymers, formed melt-miscible crystalline/crystalline polymer blends. Both the characteristic diffraction peaks and nonisothermal melt crystallization peak of each component were found in the blends, indicating that PVDF and PBHS crystallized separately. The crystalline morphology and crystallization kinetics of each component were studied under different crystallization conditions for the PVDF/PBHS blends. Both the spherulitic growth rates and overall isothermal melt crystallization rates of blended PVDF decreased with increasing the PBHS composition and were lower than those of neat PVDF, when the crystallization temperature was above the melting point of PBHS component. The crystallization mechanism of neat and blended PVDF remained unchanged, despite changes of blend composition and crystallization temperature. The crystallization kinetics and crystalline morphology of neat and blended PBHS were further studied, when the crystallization temperature was below the melting point of PBHS component. Relative to neat PBHS, the overall crystallization rates of the blended PBHS first increased and then decreased with increasing the PVDF content in the blends, indicating that the preexisting PVDF crystals may show different effects on the nucleation and crystal growth of PBHS component in the crystalline/crystalline polymer blends.展开更多
In order to improve the flexibility of poly（propylene carbonate） （PPC）, poly（1,2-propylene succinate） （PPSu） was used to plasticize PPC in a batch mixer. The effects of PPSu on the miscibility, thermal stabili...In order to improve the flexibility of poly（propylene carbonate） （PPC）, poly（1,2-propylene succinate） （PPSu） was used to plasticize PPC in a batch mixer. The effects of PPSu on the miscibility, thermal stability, mechanical and theological properties of the blends were investigated. PPC was partially miscible with PPSu. It was demonstrated that PPSu decreased the glass transition temperature and melt viscosity of PPC, as shown in the DSC and rheological curves. With the increase in PPSu content, the PPC/PPSu blends showed decreased tensile strength, however, the elongation at break was increased to 1100% for the 70/30 PPC/PPSu blend. The introduction of PPSu provided an efficient and novel plasticization method to extend the application area of PPC.展开更多
Aim To investigate the melting behavior of polyamide 6 in polyamide 6/polyethy lene blends crystallized from amorphous state. Methods DSC was used to test effects of annealing temperature, annealing time, DS...Aim To investigate the melting behavior of polyamide 6 in polyamide 6/polyethy lene blends crystallized from amorphous state. Methods DSC was used to test effects of annealing temperature, annealing time, DSC scan rate, and the step wise annealing on the melting peaks of the ice water quenched specimens. Results and Conclusion Varied melting peaks of PA6 component were obtained. The degree of perfection and the crystallization degree of PA6 crystals decreased in the blends, and the crystallization degree of PA6 increased with the increasing of the annealing time. The height of the upper melting peak of reference PA6 is higher than that in blends.展开更多
Aim To investigate the multiple melting behavior of polyamide 6(PA 6) in polyamide 6/linear low density polyethylene blends crystallized from the crystal amorphous state. Methods\ The effects of annealing tempera...Aim To investigate the multiple melting behavior of polyamide 6(PA 6) in polyamide 6/linear low density polyethylene blends crystallized from the crystal amorphous state. Methods\ The effects of annealing temperature, annealing time, heating rate, and the step wise annealing were measured by DSC. Results and Conclusion\ There exists a critical heating rate affecting the middle temperature melting peak. When annealed at the temperature close to the melting peak, the main melting peak of PA 6 shifted to a higher temperature. Within a short time, annealing time has much effect on neat PA 6 but little effect on PA 6 in the blends. Addition of PE results in a decreasing in the height of melting peak. These phenomenon show that the melting behavior of PA 6 was affected by PE, compatibilizer, as well as thermal treatment.展开更多
Hybrid organic-inorganic perovskites have been the subject of recent intense interest due to advances in photovoltaic and other optoelectronic applications. However, their poor stability limits commercial market appli...Hybrid organic-inorganic perovskites have been the subject of recent intense interest due to advances in photovoltaic and other optoelectronic applications. However, their poor stability limits commercial market application We enhance water stability by post treatment preparation of hybrid metal halide perovskite nanocrystal-embedded polymethylmethacrylate （PM- MA） blend films. Through blending process without any cleaning of nanocrystals, crystalline hybrid organic-inorganic perovs-kite nanocrystals were incorporated into PMMA matrix with well-dispersion Passivation of PMMA on the surface of the per-ovskite nanocrystals results in decreased traps and a long photoluminescence （PL） lifetime despite the bromine vacancies in the crystal lattice. Moreover, such color purity and inherent high transmittance for fluorescence emission of perovskite nanocrystals will endow the films with promising potentials in diverse practice photonic applications.展开更多
To explore the best preparation process for terminal blend(TB)composite-modified asphalt and to filter its formulation with excellent performance,this study evaluates the performance of TB composite modified asphalt b...To explore the best preparation process for terminal blend(TB)composite-modified asphalt and to filter its formulation with excellent performance,this study evaluates the performance of TB composite modified asphalt by physical property index,microscopic morphology,rheological testing,and infrared spectroscopy on multiple scales.The results show that the best preparation process for TB-modified asphalt is stirring at 260℃ for 4 h at 400 rpm,which significantly reduces the modification time of the asphalt.From a physical property viewpoint,the TB composite-modified asphalt sample with 5% styrene-butadiene-styrene(SBS)+1% aromatics+0.1% sulfur exhibits high-comprehensive,high-and low-temperature properties.More-over,its crosslinked mesh structure comprises black rubber particles uniformly interwoven in the middle,which further enhances the performance of the asphalt and results in an excellent performance formulation.In addition,the sample with 5%SBS content has a higher G*value and smaller δ value than that with 3%SBS content,indicating that its high-temperature resistance is improved.The effect of adding 3%SBS content on the viscoelastic ratio is,to some extent,less than that caused by 20% rubber powder.展开更多
In this paper, experimental investigations are presented to assess the performance variations in a single cylinder spark ignited engine when run with three different gasoline-alcohol blends： （88% gasoline-12% methan...In this paper, experimental investigations are presented to assess the performance variations in a single cylinder spark ignited engine when run with three different gasoline-alcohol blends： （88% gasoline-12% methanol, 88% gasoline-12% ethanol and 88% gasoline-6% methanol-6% ethanol）. Additional tests are carried out with the basic gasoline fuel for comparison analysis and performance assessment. Engine performance is investigated under a variety of engine operating conditions. The results are presented in the domain of engine speed. In particular, the brake power of the engine is shown to be slightly increased. The brake thermal efficiency showed an increase compared with the basic gasoline engine. Similarly, it is shown that brake specific fuel consumption is enhanced compared with basic gasoline engine. The exhaust gas temperature showed a decrease compared with gasoline fuel which is preferable to reduce emissions. The alcohol additives are strongly recommended to enhance performance, increasing the mileage and reducing the emissions.展开更多
The miscibility and crystallization of solution casting biodegradable poly（3-hydroxybuty- rate）/poly（ethylene succinate） （PHB/PES） blends was investigated by differential scanning calorimetry, rheology, and opti...The miscibility and crystallization of solution casting biodegradable poly（3-hydroxybuty- rate）/poly（ethylene succinate） （PHB/PES） blends was investigated by differential scanning calorimetry, rheology, and optical microscopy. The blends showed two glass transition temperatures and a depression of melting temperature of PHB with compositions in phase diagram, which indicated that the blend was partially miscible. The morphology observation supported this result. It was found that the PHB and PES can crystallize simultaneously or upon stepwise depending on the crystallization temperatures and compositions. The spherulite growth rate of PHB increased with increasing of PES content. The influence of compositions on the spherulitic growth rate for the partially miscible polymer blends was discussed.展开更多
Shape memory polymer （SMP） blends based on polyurethane （PU） and polyaniline （PANI） were prepared via chemical in situ polymerization process. The thermal, mechanical, electrical and shape memory properties were...Shape memory polymer （SMP） blends based on polyurethane （PU） and polyaniline （PANI） were prepared via chemical in situ polymerization process. The thermal, mechanical, electrical and shape memory properties were investigated. The structural characterization and morphology of the polymer blends were inspected by Fourier transform infrared （FTIR） and scanning electron microscopy （SEM）, respectively. The 1 wt% of PANI loading enhanced the thermal stability of the system up to 339 ~C. According to differential scanning calorimetry （DSC）, the glass transition temperature （Tg） and melting temperature （Tm） of PU/PANI blends increased with the polyaniline loading （0.1 wt%-l wt%）. Improved mechanical properties such as tensile strength and Young＇s modulus of PU matrix were also observed with PANI. Moreover, the electrical conductivity of PU/PANI blends was also found to be a function of PANI loading. Remarkable recoverability of thermally triggered shape memory （SM） behavior to the extent of 96% was achieved for 1 wt% PANI blend.展开更多
The molecular weight of a polymer is of prime importance and greatly influences the processing and mechanical properties of the polymer.Trans-1,4-poly(butadiene-co-isoprene)multi-block copolymer rubbers(TBIR)exhibit o...The molecular weight of a polymer is of prime importance and greatly influences the processing and mechanical properties of the polymer.Trans-1,4-poly(butadiene-co-isoprene)multi-block copolymer rubbers(TBIR)exhibit outstanding fatigue resistance,low heat build-up and good abrasion resistance,and are expected to be desirable candidate for high performance tire.Study on the influence of TBIR with different molecular weights on the structure and properties of TBIR and natural rubber(NR)/TBIR blends is essential to understand its contribution to the greatly improved dynamic properties of the rubber vulcanizates.TBIR with different molecular weights characterized by 1H-NMR,13C-NMR,GPC,and DSC were highly trans-1,4-copolymers with similar chain sequence distribution and crystalline trans-1,4-polyisoprene(TPI)blocks.The green strength and modulus of TBIR increased with the increasing molecular weight.The NR/TBIR compounds filled with 40 phr carbon black were chemically cured by sulfur for the preparation of NR/TBIR vulcanizates.The compatibility between NR and TBIR,filler distribution,crosslinking bond and density,and properties of NR/TBIR vulcanizates were studied.The NR/TBIR vulcanizates showed increasing tensile strength,hardness,modulus,rebound,abrasion resistance,and flexural fatigue properties with increasing molecular weight of TBIR.Furthermore,they presented significant improvement in flexural fatigue resistance when compared with that of NR vulcanizate.The contribution mechanism of TBIR on the NR/TBIR blends was discussed.The TBIR with a wide range of molecular weight are ideal rubbers for high performance tires.展开更多
Sustainable blends of poly(propylene carbonate)(PPC)and stereocomplex polylactide(sc-PLA)were prepared by melt blending equimolar poly(L-lactic acid)(PLLA)and poly(D-lactide acid)(PDLA)with PPC to form sc-PLA crystals...Sustainable blends of poly(propylene carbonate)(PPC)and stereocomplex polylactide(sc-PLA)were prepared by melt blending equimolar poly(L-lactic acid)(PLLA)and poly(D-lactide acid)(PDLA)with PPC to form sc-PLA crystals in situ in the melt blending process.Differential seanning calorimetry analysis revealed that only sc-PLA,no homo-crystallization of PLLA or PDLA,formed in the PPC matrix as the sc-PLA con tent was more than 10 wt%.Very in triguingly,scan ning electronic microscopy observati on showed that sc-PLA was evenly dispersed in the PPC phase as spherical particles and the sizes of sc-PLA particles did not obviously increase with in creasing sc-PLA con tent.As a con seque nee,the rheological properties of PPC were greatly improved by incorporation of sc-PLA.When the sc-PLA con tent was 20 wt%,a percolati on n etwork structure was formed,and the blends showed solid-like behavior.The sc-PLA particles could reinforce the PPC matrix,especially at a temperature above the glass transition temperature of PPC.Moreover,the Vicat softening temperature of PPC/sc-PLA blends could be increased compared with that of neat PPC.展开更多
Regulated and unregulated emissions from four passenger cars fueled with methanol/gasoline blends at different mixing ratios （M15,M20,M30,M50,M85 and M100） were tested over the New European Driving Cycle （NEDC）.Vo...Regulated and unregulated emissions from four passenger cars fueled with methanol/gasoline blends at different mixing ratios （M15,M20,M30,M50,M85 and M100） were tested over the New European Driving Cycle （NEDC）.Volatile organic compounds （VOCs） were sampled by Tenax TA and analyzed by thermal desorption-gas chromatograph/mass spectrometer （TD-GC/MS）.Carbonyls were trapped on dinitrophenylhydrazine （DNPH） cartridges and analyzed by high performance liquid chromatography （HPLC）.The results showed that total emissions of VOCs and BTEX （benzene,toluene,ethylbenzene,p,m,o-xylene） from all vehicles fueled with methanol/gasoline blends were lower than those from vehicles fueled with only gasoline.Compared to the baseline,the use of M85 decreased BTEX emissions by 97.4%,while the use of M15 decreased it by 19.7%.At low-to-middle mixing ratios （M15,M20,M30 and M50）,formaldehyde emissions showed a slight increase while those of high mixing ratios （M85 and M100） were three times compared with the baseline gasoline only.When the vehicles were retrofitted with new three-way catalytic converters （TWC）,emissions of carbon monoxide （CO）,total hydrocarbon （THC）,and nitrogen oxides （NOx） were decreased by 24%–50%,10%–35%,and 24%–58% respectively,compared with the cars using the original equipment manufacture （OEM） TWC.Using the new TWC,emissions of formaldehyde and BTEX were decreased,while those of other carbonyl increased.It is necessary that vehicles fueled with methanol/gasoline blends be retrofitted with a new TWC.In addition,the specific reactivity of emissions of vehicles fueled with M15 and retrofitted with the new TWC was reduced from 4.51 to 4.08 compared to the baseline vehicle.This indicates that the use of methanol/gasoline blend at a low mixing ratio may have lower effect on environment than gasoline.展开更多
Poly（propylene carbonate） （PPC） was melt blended in a batch mixer with poly（butylene carbonate） （PBC） in an effort to improve the toughness of the PPC without compromising its biodegradability and biocompatibi...Poly（propylene carbonate） （PPC） was melt blended in a batch mixer with poly（butylene carbonate） （PBC） in an effort to improve the toughness of the PPC without compromising its biodegradability and biocompatibility. DMA results showed that the PPC/PBC blends were an immiscible two-phase system. With the increase in PBC content, the PPC/PBC blends showed decreased tensile strength, however, the elongation at break was increased to 230% for the 50/50 PPC/PBC blend. From the tensile strength experiments, the Pukanszky model gave credit to the modest interfacial adhesion between PPC and PBC, although PPC/PBC was immscible. The impact strength increased significantly which indicated the toughening effects of the PBC on PPC. SEM examination showed that cavitation and shear yielding were the major toughening mechanisms in the blends subjected the impact tests. TGA measurements showed that the thermal stability of PPC decreased with the incorporation of PBC. Rheological investigation demonstrated that the addition of PBC reduced the value of storage modulus, loss modulus and complex viscosity of the PPC/PBC blends to some extent. Moreover, the addition of PBC was found to increase the processability of PPC in extrusion. The introduction of PBC provided an efficient and novel toughened method to extend the application area of PPC.展开更多
A simultaneous increase of both stiffness and extensibility ofpoly（ethylene glycol-co-cyclohexane-1,4-dimethanol terephthalate） （PETG）/polycarbonate （PC） blends prepared through the slit die extrusion-uniaxial c...A simultaneous increase of both stiffness and extensibility ofpoly（ethylene glycol-co-cyclohexane-1,4-dimethanol terephthalate） （PETG）/polycarbonate （PC） blends prepared through the slit die extrusion-uniaxial cold stretching process was observed. The stretched sheets have a unique mechanical character that an increased tensile modulus is accompanied by an increased extensibility with increasing the draw ratio. Especially, a sharp increasing of the extensibility is observed for PETG/PC （70/30 wt%） blends at draw ratios between 8.2 and 20.0, where a nine times increase of extensibility is achieved. The mechanism of stretching-induced superior extensibility is investigated via micrograph observation, rheometry and calorimetric analysis. The observed superior extensibility could be tentatively explained by the bridging effect of the PC microfibrils on the crack development during tensile failure.展开更多
Metallocene-catalyzed linear low-density polyethylene/polypropylene （mLLDPE/PP） blends were prepared by ultrasonic extrusion in this work. Their extrusion processing behaviors were estimated by online measured data,...Metallocene-catalyzed linear low-density polyethylene/polypropylene （mLLDPE/PP） blends were prepared by ultrasonic extrusion in this work. Their extrusion processing behaviors were estimated by online measured data, such as the die pressure and flow rate. Crystallization and mechanical properties of the blends were also investigated. The results show that the addition of PP improves the processing behaviors of mLLDPE, but has little effect on its mechanical properties. On the other hand, the addition of mLLDPE improves the impact strength of PP, but has little effect on its processing behavior. The processing behaviors and mechanical properties of mLLDPE/PP blends get further improved due to the presence of ultrasonic oscillation during extrusion. Compared with PP-rich blends, the apparent viscosity drop of mLLDPE-rich blends is more sensitive to ultrasonic oscillation. The ultrasonic oscillation affects the crystal nucleation, while barely the other crystalline behaviors of the blends.展开更多
Phase separation was studied by the optical microscopy in blends of nylon 6 (PA6) with sodium salt of ethylene/methacrylic acid copolymer (PEMA).The image collecting technology was used to keep track of the developme...Phase separation was studied by the optical microscopy in blends of nylon 6 (PA6) with sodium salt of ethylene/methacrylic acid copolymer (PEMA).The image collecting technology was used to keep track of the development of blends at a certain temperature.The fractal dimension of phase separation was calculated by the image solving technology according to the fractal theory and the self similarity behavior of the process was proved.The relationship of the fractal behavior with composition and experimental temperature was discussed.The fractal behavior of the crystallization development of the crystal phase of PA6 in blends was also discussed and the fractal behavior calculated.展开更多
Polyamide/acrylonitrile-butadiene-styrene copolymer(PA/ABS) blends have drawn considerable attention from both academia and industry for their important applications in automotive and electronic areas. Due to poor mis...Polyamide/acrylonitrile-butadiene-styrene copolymer(PA/ABS) blends have drawn considerable attention from both academia and industry for their important applications in automotive and electronic areas. Due to poor miscibility of PA and ABS, developing an effective compatibilization strategy has been an urgent challenge to achieve prominent mechanical properties. In this study, we create a set of mechanically enhanced PA6/ABS blends using two multi-monomer melt-grafted compatibilizers, SEBSg-(MAH-co-St) and ABS-g-(MAH-co-St). The dispersed domain size is significantly decreased and meanwhile the unique "soft shell-encapsulating-hard core" structures form in the presence of compatibilizers. The optimum mechanical performances manifest an increase of 36% in tensile strength and an increase of 1300% in impact strength, compared with the neat PA6/ABS binary blend.展开更多
The effect of PBS on the morphological features of PVDF has been investigated by optical and atomic force microscopies under various conditions. It was found that neat PVDF forms large γform spherulites with extraord...The effect of PBS on the morphological features of PVDF has been investigated by optical and atomic force microscopies under various conditions. It was found that neat PVDF forms large γform spherulites with extraordinarily weak birefringence at 170℃. Adding 30% PBS makes PVDF exhibit intrigued flower-like spherulitic morphology. The growth mechanism was explained by the decrease of the supercooling and the materials dissipation. Increasing the PBS content to 70% favors the formation of ring banded spherulites. Temperature dependent experiments verify the α→γ phase transition occurs from the junction sites of the ot and y crystals, while starts from the centers of α spherulites in the blends. Ring banded structures could be observed in neat PVDF, 70/30 blend and 30/70 blend when crystallized at 155℃, without γ crystals. The band period of PVDF α spherulites increases with crystallization temperature as well as the amount of PBS content. At 140℃, spherulites in neat PVDF lose their ring banded feature, while coarse spherulites consisting of evident lamellar bundles could be found in 30/70 blend.展开更多
基金supported by Innovation Research Project for the training of high-level scientific and technological talents(Technical expert talents)of the Armed Police Force ZZKY20222415“13th Five-Year Plan”military key colleges and key disciplines-Equipment Engineering(Power)-17.
文摘Fuel injection properties,including the injection rate(temporal aspects)and spray behavior(spatial aspects),play a crucial role in the combustion efficiency and emissions of diesel engines.This study investigates the effects of different ethanol-biodiesel-diesel(EBD)blends on the injection performance in diesel engines.Experimental tests are conducted to examine key injection parameters,such as spray penetration distance,spray cone angle,and droplet size,alongside an analysis of coupling leakage.The main findings are as follows:(1)The injection behavior of ethanol and diesel differs significantly.The addition of ethanol reduces the density,viscosity,and modulus of elasticity of the fuel mixture.While the injection advance angle,penetration distance,and Sauter mean diameter show minimal changes,the spray cone angle and coupling leakage increase notably.These alterations may disrupt the“fuelair-chamber”matching characteristics of the original engine,potentially affecting performance.(2)In contrast,the injection performance of biodiesel ismore similar to that of diesel.As biodiesel content increases,the density,viscosity,and modulus of elasticity of the blended fuel also grow.Though changes in injection timing,penetration distance,and spray cone angle remain minimal,the Sauter mean diameter experiences a slight increase.The“air-fuel chamber”compatibility of the original engine is largely unaffected,though fuel atomization slightly deteriorates.Blending up to 20%biodiesel and 30%ethanol with diesel effectively compensates for the shortcomings of using single fuels,maintaining favorable injection dynamics while enhancing lubrication and sealing performance of engine components.
基金supported by the National High Technology Research and Development Program of China(2010AA101703)the Natural Science Foundation of Heilongjiang Province of China (C200950)the Fundamental Research Fundsfor the Central Universities (DL09BB38)
文摘The effect of maleic anhydride grafted styrene-ethylene- buty-lene-styrene block copolymer （SEBS-g-MAH） and in-situ grafting MAH on mechanical, dynamic mechanical properties of wood flour/recycled plastic blends composites was investigated. Recycled plastic polypro-pylene （PP）, high-density polyethylene （HDPE） and polystyrene （PS）, were mixed with wood flour in a high speed blender and then extruded by a twin/single screw tandem extruder system to form wood flour/recycled plastic blends composites. Results show that the impact properties of the composites were improved more significantly by using SEBS-g-MAH compatibilizer than by using the mixtures of MAH and DCP via reactive blending in situ. However, contrary results were ob-served on the tensile and flexural properties of the corresponding com-posites. In General, the mechanical properties of composites made from recycled plastic blends were inferior to those made from virgin plastic blends, especially in elongation break. The morphological study verified that the interfacial adhesion or the compatibility of plastic blends with wood flour was improved by adding SEBS-g-MAH or in-situ grafting MAH. A better interfacial bonding between PP, HDPE, PS and wood flour was obtained by in-situ grafting MAH than the addition of SEBS-g-MAH. In-situ grafting MAH can be considered as a potential way of increasing the interfacial compatibility between plastic blends and wood flour. The storage modulus and damping factor of composites were also characterized through dynamic mechanical analysis （DMA）.
基金financially supported by the National Natural Science Foundation of China(No.51221002)
文摘Poly（vinylidene fluoride） （PVDF） and poly（butylene succinate-co-24 mol% hexamethylene succinate） （PBHS）, both crystalline polymers, formed melt-miscible crystalline/crystalline polymer blends. Both the characteristic diffraction peaks and nonisothermal melt crystallization peak of each component were found in the blends, indicating that PVDF and PBHS crystallized separately. The crystalline morphology and crystallization kinetics of each component were studied under different crystallization conditions for the PVDF/PBHS blends. Both the spherulitic growth rates and overall isothermal melt crystallization rates of blended PVDF decreased with increasing the PBHS composition and were lower than those of neat PVDF, when the crystallization temperature was above the melting point of PBHS component. The crystallization mechanism of neat and blended PVDF remained unchanged, despite changes of blend composition and crystallization temperature. The crystallization kinetics and crystalline morphology of neat and blended PBHS were further studied, when the crystallization temperature was below the melting point of PBHS component. Relative to neat PBHS, the overall crystallization rates of the blended PBHS first increased and then decreased with increasing the PVDF content in the blends, indicating that the preexisting PVDF crystals may show different effects on the nucleation and crystal growth of PBHS component in the crystalline/crystalline polymer blends.
基金financially supported by the Science&Technology Bureau of Jilin Province of China(No.20126023)the National High Technology Research and Development Program of China(863 Program)(No.2012AA062904)the National Natural Science Foundation of China(No.51021003)
文摘In order to improve the flexibility of poly（propylene carbonate） （PPC）, poly（1,2-propylene succinate） （PPSu） was used to plasticize PPC in a batch mixer. The effects of PPSu on the miscibility, thermal stability, mechanical and theological properties of the blends were investigated. PPC was partially miscible with PPSu. It was demonstrated that PPSu decreased the glass transition temperature and melt viscosity of PPC, as shown in the DSC and rheological curves. With the increase in PPSu content, the PPC/PPSu blends showed decreased tensile strength, however, the elongation at break was increased to 1100% for the 70/30 PPC/PPSu blend. The introduction of PPSu provided an efficient and novel plasticization method to extend the application area of PPC.
文摘Aim To investigate the melting behavior of polyamide 6 in polyamide 6/polyethy lene blends crystallized from amorphous state. Methods DSC was used to test effects of annealing temperature, annealing time, DSC scan rate, and the step wise annealing on the melting peaks of the ice water quenched specimens. Results and Conclusion Varied melting peaks of PA6 component were obtained. The degree of perfection and the crystallization degree of PA6 crystals decreased in the blends, and the crystallization degree of PA6 increased with the increasing of the annealing time. The height of the upper melting peak of reference PA6 is higher than that in blends.
文摘Aim To investigate the multiple melting behavior of polyamide 6(PA 6) in polyamide 6/linear low density polyethylene blends crystallized from the crystal amorphous state. Methods\ The effects of annealing temperature, annealing time, heating rate, and the step wise annealing were measured by DSC. Results and Conclusion\ There exists a critical heating rate affecting the middle temperature melting peak. When annealed at the temperature close to the melting peak, the main melting peak of PA 6 shifted to a higher temperature. Within a short time, annealing time has much effect on neat PA 6 but little effect on PA 6 in the blends. Addition of PE results in a decreasing in the height of melting peak. These phenomenon show that the melting behavior of PA 6 was affected by PE, compatibilizer, as well as thermal treatment.
文摘Hybrid organic-inorganic perovskites have been the subject of recent intense interest due to advances in photovoltaic and other optoelectronic applications. However, their poor stability limits commercial market application We enhance water stability by post treatment preparation of hybrid metal halide perovskite nanocrystal-embedded polymethylmethacrylate （PM- MA） blend films. Through blending process without any cleaning of nanocrystals, crystalline hybrid organic-inorganic perovs-kite nanocrystals were incorporated into PMMA matrix with well-dispersion Passivation of PMMA on the surface of the per-ovskite nanocrystals results in decreased traps and a long photoluminescence （PL） lifetime despite the bromine vacancies in the crystal lattice. Moreover, such color purity and inherent high transmittance for fluorescence emission of perovskite nanocrystals will endow the films with promising potentials in diverse practice photonic applications.
基金Funded by the National Natural Science Foundation of China(No.52278446)。
文摘To explore the best preparation process for terminal blend(TB)composite-modified asphalt and to filter its formulation with excellent performance,this study evaluates the performance of TB composite modified asphalt by physical property index,microscopic morphology,rheological testing,and infrared spectroscopy on multiple scales.The results show that the best preparation process for TB-modified asphalt is stirring at 260℃ for 4 h at 400 rpm,which significantly reduces the modification time of the asphalt.From a physical property viewpoint,the TB composite-modified asphalt sample with 5% styrene-butadiene-styrene(SBS)+1% aromatics+0.1% sulfur exhibits high-comprehensive,high-and low-temperature properties.More-over,its crosslinked mesh structure comprises black rubber particles uniformly interwoven in the middle,which further enhances the performance of the asphalt and results in an excellent performance formulation.In addition,the sample with 5%SBS content has a higher G*value and smaller δ value than that with 3%SBS content,indicating that its high-temperature resistance is improved.The effect of adding 3%SBS content on the viscoelastic ratio is,to some extent,less than that caused by 20% rubber powder.
文摘In this paper, experimental investigations are presented to assess the performance variations in a single cylinder spark ignited engine when run with three different gasoline-alcohol blends： （88% gasoline-12% methanol, 88% gasoline-12% ethanol and 88% gasoline-6% methanol-6% ethanol）. Additional tests are carried out with the basic gasoline fuel for comparison analysis and performance assessment. Engine performance is investigated under a variety of engine operating conditions. The results are presented in the domain of engine speed. In particular, the brake power of the engine is shown to be slightly increased. The brake thermal efficiency showed an increase compared with the basic gasoline engine. Similarly, it is shown that brake specific fuel consumption is enhanced compared with basic gasoline engine. The exhaust gas temperature showed a decrease compared with gasoline fuel which is preferable to reduce emissions. The alcohol additives are strongly recommended to enhance performance, increasing the mileage and reducing the emissions.
基金ACKNOWLEDGMENT This work was supported by the Key Science Foundation of Education Ministry of China and the Anhui Science Foundation.
文摘The miscibility and crystallization of solution casting biodegradable poly（3-hydroxybuty- rate）/poly（ethylene succinate） （PHB/PES） blends was investigated by differential scanning calorimetry, rheology, and optical microscopy. The blends showed two glass transition temperatures and a depression of melting temperature of PHB with compositions in phase diagram, which indicated that the blend was partially miscible. The morphology observation supported this result. It was found that the PHB and PES can crystallize simultaneously or upon stepwise depending on the crystallization temperatures and compositions. The spherulite growth rate of PHB increased with increasing of PES content. The influence of compositions on the spherulitic growth rate for the partially miscible polymer blends was discussed.
基金financially supported by the Higher Education Commission(HEC),Islamabad,Pakistan under the indigenous Ph D fellowship scheme and IRSIP program
文摘Shape memory polymer （SMP） blends based on polyurethane （PU） and polyaniline （PANI） were prepared via chemical in situ polymerization process. The thermal, mechanical, electrical and shape memory properties were investigated. The structural characterization and morphology of the polymer blends were inspected by Fourier transform infrared （FTIR） and scanning electron microscopy （SEM）, respectively. The 1 wt% of PANI loading enhanced the thermal stability of the system up to 339 ~C. According to differential scanning calorimetry （DSC）, the glass transition temperature （Tg） and melting temperature （Tm） of PU/PANI blends increased with the polyaniline loading （0.1 wt%-l wt%）. Improved mechanical properties such as tensile strength and Young＇s modulus of PU matrix were also observed with PANI. Moreover, the electrical conductivity of PU/PANI blends was also found to be a function of PANI loading. Remarkable recoverability of thermally triggered shape memory （SM） behavior to the extent of 96% was achieved for 1 wt% PANI blend.
基金financially supported by the National Basic Research Program of China(No.2015CB654700(2015CB 654706))Major Program of Shandong Province Natural Science Foundation(No.ZR2017ZA0304)Taishan Scholar Program
文摘The molecular weight of a polymer is of prime importance and greatly influences the processing and mechanical properties of the polymer.Trans-1,4-poly(butadiene-co-isoprene)multi-block copolymer rubbers(TBIR)exhibit outstanding fatigue resistance,low heat build-up and good abrasion resistance,and are expected to be desirable candidate for high performance tire.Study on the influence of TBIR with different molecular weights on the structure and properties of TBIR and natural rubber(NR)/TBIR blends is essential to understand its contribution to the greatly improved dynamic properties of the rubber vulcanizates.TBIR with different molecular weights characterized by 1H-NMR,13C-NMR,GPC,and DSC were highly trans-1,4-copolymers with similar chain sequence distribution and crystalline trans-1,4-polyisoprene(TPI)blocks.The green strength and modulus of TBIR increased with the increasing molecular weight.The NR/TBIR compounds filled with 40 phr carbon black were chemically cured by sulfur for the preparation of NR/TBIR vulcanizates.The compatibility between NR and TBIR,filler distribution,crosslinking bond and density,and properties of NR/TBIR vulcanizates were studied.The NR/TBIR vulcanizates showed increasing tensile strength,hardness,modulus,rebound,abrasion resistance,and flexural fatigue properties with increasing molecular weight of TBIR.Furthermore,they presented significant improvement in flexural fatigue resistance when compared with that of NR vulcanizate.The contribution mechanism of TBIR on the NR/TBIR blends was discussed.The TBIR with a wide range of molecular weight are ideal rubbers for high performance tires.
基金the Chinese Academy of scienee and technology service network planning(No.KFJSTS-QYZD-140)a program of Cooperation of Hubei Province and Chinese Academy of Sciences,Innovation team project of Beijing Institute of Science and Technology(No.IG201703N)"13^th five-year"Science and Technology Research Program of the Education Department of Jilin Provinee(No.JJKH20190862KJ).
文摘Sustainable blends of poly(propylene carbonate)(PPC)and stereocomplex polylactide(sc-PLA)were prepared by melt blending equimolar poly(L-lactic acid)(PLLA)and poly(D-lactide acid)(PDLA)with PPC to form sc-PLA crystals in situ in the melt blending process.Differential seanning calorimetry analysis revealed that only sc-PLA,no homo-crystallization of PLLA or PDLA,formed in the PPC matrix as the sc-PLA con tent was more than 10 wt%.Very in triguingly,scan ning electronic microscopy observati on showed that sc-PLA was evenly dispersed in the PPC phase as spherical particles and the sizes of sc-PLA particles did not obviously increase with in creasing sc-PLA con tent.As a con seque nee,the rheological properties of PPC were greatly improved by incorporation of sc-PLA.When the sc-PLA con tent was 20 wt%,a percolati on n etwork structure was formed,and the blends showed solid-like behavior.The sc-PLA particles could reinforce the PPC matrix,especially at a temperature above the glass transition temperature of PPC.Moreover,the Vicat softening temperature of PPC/sc-PLA blends could be increased compared with that of neat PPC.
基金supported by the National Natural Science Foundation of China(No.50876013)
文摘Regulated and unregulated emissions from four passenger cars fueled with methanol/gasoline blends at different mixing ratios （M15,M20,M30,M50,M85 and M100） were tested over the New European Driving Cycle （NEDC）.Volatile organic compounds （VOCs） were sampled by Tenax TA and analyzed by thermal desorption-gas chromatograph/mass spectrometer （TD-GC/MS）.Carbonyls were trapped on dinitrophenylhydrazine （DNPH） cartridges and analyzed by high performance liquid chromatography （HPLC）.The results showed that total emissions of VOCs and BTEX （benzene,toluene,ethylbenzene,p,m,o-xylene） from all vehicles fueled with methanol/gasoline blends were lower than those from vehicles fueled with only gasoline.Compared to the baseline,the use of M85 decreased BTEX emissions by 97.4%,while the use of M15 decreased it by 19.7%.At low-to-middle mixing ratios （M15,M20,M30 and M50）,formaldehyde emissions showed a slight increase while those of high mixing ratios （M85 and M100） were three times compared with the baseline gasoline only.When the vehicles were retrofitted with new three-way catalytic converters （TWC）,emissions of carbon monoxide （CO）,total hydrocarbon （THC）,and nitrogen oxides （NOx） were decreased by 24%–50%,10%–35%,and 24%–58% respectively,compared with the cars using the original equipment manufacture （OEM） TWC.Using the new TWC,emissions of formaldehyde and BTEX were decreased,while those of other carbonyl increased.It is necessary that vehicles fueled with methanol/gasoline blends be retrofitted with a new TWC.In addition,the specific reactivity of emissions of vehicles fueled with M15 and retrofitted with the new TWC was reduced from 4.51 to 4.08 compared to the baseline vehicle.This indicates that the use of methanol/gasoline blend at a low mixing ratio may have lower effect on environment than gasoline.
基金financially supported by the fund of Science&Technology Bureau of Jilin Province of China(No.20126023)the National High Technology Research and Development Program of China(863 Program)(No.2012AA062904)the National Natural Science Foundation of China(No.51021003)
文摘Poly（propylene carbonate） （PPC） was melt blended in a batch mixer with poly（butylene carbonate） （PBC） in an effort to improve the toughness of the PPC without compromising its biodegradability and biocompatibility. DMA results showed that the PPC/PBC blends were an immiscible two-phase system. With the increase in PBC content, the PPC/PBC blends showed decreased tensile strength, however, the elongation at break was increased to 230% for the 50/50 PPC/PBC blend. From the tensile strength experiments, the Pukanszky model gave credit to the modest interfacial adhesion between PPC and PBC, although PPC/PBC was immscible. The impact strength increased significantly which indicated the toughening effects of the PBC on PPC. SEM examination showed that cavitation and shear yielding were the major toughening mechanisms in the blends subjected the impact tests. TGA measurements showed that the thermal stability of PPC decreased with the incorporation of PBC. Rheological investigation demonstrated that the addition of PBC reduced the value of storage modulus, loss modulus and complex viscosity of the PPC/PBC blends to some extent. Moreover, the addition of PBC was found to increase the processability of PPC in extrusion. The introduction of PBC provided an efficient and novel toughened method to extend the application area of PPC.
基金supported by the National Natural Science Foundation of China(Nos.50533050,20874064 and 50873063)
文摘A simultaneous increase of both stiffness and extensibility ofpoly（ethylene glycol-co-cyclohexane-1,4-dimethanol terephthalate） （PETG）/polycarbonate （PC） blends prepared through the slit die extrusion-uniaxial cold stretching process was observed. The stretched sheets have a unique mechanical character that an increased tensile modulus is accompanied by an increased extensibility with increasing the draw ratio. Especially, a sharp increasing of the extensibility is observed for PETG/PC （70/30 wt%） blends at draw ratios between 8.2 and 20.0, where a nine times increase of extensibility is achieved. The mechanism of stretching-induced superior extensibility is investigated via micrograph observation, rheometry and calorimetric analysis. The observed superior extensibility could be tentatively explained by the bridging effect of the PC microfibrils on the crack development during tensile failure.
基金This work was financially supported by the Special Funds for Major State Basic Research Projects of China (No.2005CB623800)the National Natural Science Foundation of China (No. 20374037)the Open Foundation of Key Laboratory of Rubber-plastics (QUST),Ministry of Education, China and the Foundation for Youth of Sichuan University
文摘Metallocene-catalyzed linear low-density polyethylene/polypropylene （mLLDPE/PP） blends were prepared by ultrasonic extrusion in this work. Their extrusion processing behaviors were estimated by online measured data, such as the die pressure and flow rate. Crystallization and mechanical properties of the blends were also investigated. The results show that the addition of PP improves the processing behaviors of mLLDPE, but has little effect on its mechanical properties. On the other hand, the addition of mLLDPE improves the impact strength of PP, but has little effect on its processing behavior. The processing behaviors and mechanical properties of mLLDPE/PP blends get further improved due to the presence of ultrasonic oscillation during extrusion. Compared with PP-rich blends, the apparent viscosity drop of mLLDPE-rich blends is more sensitive to ultrasonic oscillation. The ultrasonic oscillation affects the crystal nucleation, while barely the other crystalline behaviors of the blends.
文摘Phase separation was studied by the optical microscopy in blends of nylon 6 (PA6) with sodium salt of ethylene/methacrylic acid copolymer (PEMA).The image collecting technology was used to keep track of the development of blends at a certain temperature.The fractal dimension of phase separation was calculated by the image solving technology according to the fractal theory and the self similarity behavior of the process was proved.The relationship of the fractal behavior with composition and experimental temperature was discussed.The fractal behavior of the crystallization development of the crystal phase of PA6 in blends was also discussed and the fractal behavior calculated.
基金the National Natural Science Foundation of China (No. 51633003) for the financial support
文摘Polyamide/acrylonitrile-butadiene-styrene copolymer(PA/ABS) blends have drawn considerable attention from both academia and industry for their important applications in automotive and electronic areas. Due to poor miscibility of PA and ABS, developing an effective compatibilization strategy has been an urgent challenge to achieve prominent mechanical properties. In this study, we create a set of mechanically enhanced PA6/ABS blends using two multi-monomer melt-grafted compatibilizers, SEBSg-(MAH-co-St) and ABS-g-(MAH-co-St). The dispersed domain size is significantly decreased and meanwhile the unique "soft shell-encapsulating-hard core" structures form in the presence of compatibilizers. The optimum mechanical performances manifest an increase of 36% in tensile strength and an increase of 1300% in impact strength, compared with the neat PA6/ABS binary blend.
基金financially supported by the National Natural Science Foundations of China(No.20974011)the program of Introducing Talents of Discipline to Universities(No.B08003)
文摘The effect of PBS on the morphological features of PVDF has been investigated by optical and atomic force microscopies under various conditions. It was found that neat PVDF forms large γform spherulites with extraordinarily weak birefringence at 170℃. Adding 30% PBS makes PVDF exhibit intrigued flower-like spherulitic morphology. The growth mechanism was explained by the decrease of the supercooling and the materials dissipation. Increasing the PBS content to 70% favors the formation of ring banded spherulites. Temperature dependent experiments verify the α→γ phase transition occurs from the junction sites of the ot and y crystals, while starts from the centers of α spherulites in the blends. Ring banded structures could be observed in neat PVDF, 70/30 blend and 30/70 blend when crystallized at 155℃, without γ crystals. The band period of PVDF α spherulites increases with crystallization temperature as well as the amount of PBS content. At 140℃, spherulites in neat PVDF lose their ring banded feature, while coarse spherulites consisting of evident lamellar bundles could be found in 30/70 blend.