The effect of growth rates (V=2-50 μm·s-1) on microstructure and microhardness of directionally solidified Ti-44Al-5Nb-1.5Cr-1.5Zr-1Mo-0.1B (at.%) alloy at a constant temperature gradient (G=18 K·mm-1) was ...The effect of growth rates (V=2-50 μm·s-1) on microstructure and microhardness of directionally solidified Ti-44Al-5Nb-1.5Cr-1.5Zr-1Mo-0.1B (at.%) alloy at a constant temperature gradient (G=18 K·mm-1) was investigated. Results indicated that β phase was the primary phase of the directionally solidified Ti-44Al-5Nb-1.5Cr-1.5Zr-1Mo-0.1B alloy. As the growth rate increases, the solid/liquid interface turns from cellular growth to dendric growth. The interlamellar spacing (λs) decreases with the increase of growth rate according to the relationship of λs=3.39V -0.31. The solidification segregation occurs due to the enrichment of β-stabilizing element Nb, Cr in primary β phase during solidification;moreover, the degree of the segregation increases with the growth rate, resulting in the emergence of B2 phase in lamellar colonies at high growth rates. The microhardness (Hv) grows with the growth rate based on the equation of HV=328.69V 0.072, which mainly attributes to the microstructure refinement.展开更多
基金This research was financially supported by the National Key Research and Development Program of China(Grant No.2016YFB0301201)National Natural Science Foundation of China(Grant Nos.51671073,51425402)+2 种基金Fundamental Research and Development Program of China(Grant No.JCKY2017205B032)Yunnan Rare Metal Materials Genetic Engineering Project(Grant No.2018ZE013)Major Special Science and Technology Project ofYunnan Province(Grant No.2019ZE001).
文摘The effect of growth rates (V=2-50 μm·s-1) on microstructure and microhardness of directionally solidified Ti-44Al-5Nb-1.5Cr-1.5Zr-1Mo-0.1B (at.%) alloy at a constant temperature gradient (G=18 K·mm-1) was investigated. Results indicated that β phase was the primary phase of the directionally solidified Ti-44Al-5Nb-1.5Cr-1.5Zr-1Mo-0.1B alloy. As the growth rate increases, the solid/liquid interface turns from cellular growth to dendric growth. The interlamellar spacing (λs) decreases with the increase of growth rate according to the relationship of λs=3.39V -0.31. The solidification segregation occurs due to the enrichment of β-stabilizing element Nb, Cr in primary β phase during solidification;moreover, the degree of the segregation increases with the growth rate, resulting in the emergence of B2 phase in lamellar colonies at high growth rates. The microhardness (Hv) grows with the growth rate based on the equation of HV=328.69V 0.072, which mainly attributes to the microstructure refinement.