Thin-walled copper tubes are usually produced by multi-pass float-plug drawing deformation.In general,the annealing treatment subsequently is necessary to release the stored energy and adjusts the microstructure.In th...Thin-walled copper tubes are usually produced by multi-pass float-plug drawing deformation.In general,the annealing treatment subsequently is necessary to release the stored energy and adjusts the microstructure.In this study,an investigation on the evolution of annealing twins as well as textures in the thin-walled(Φ6 mm×0.3 mm)copper tube underwent holding time-free heat treatment was reported.Electron backscattered diffraction analysis reveals that a large number ofΣ3 boundaries(600<111>twin relationship)are produced at the early stage of heat treatment,which is due to the lower boundary energy.With the recrystallization proceeding,the migration rate of grain boundaries decreases on account of the grain growth;meanwhile,the uniqueΣ9 boundaries(38.9°<110>relationship)are formed due to the interaction of theΣ3 boundaries.As a result,the number fractions ofΣ3 boundaries and high-angle grain boundaries decrease rapidly.During the grain growth stage,a strong recrystallization texture was formed due to the fact that the grains of Goss orientation have a growth advantage over the others.As a result,the initial copper texture was transferred into the Goss texture in domination.展开更多
基金financially supported by the Natural Science Foundation of Shandong Province under Grant No.ZR2018MEE005。
文摘Thin-walled copper tubes are usually produced by multi-pass float-plug drawing deformation.In general,the annealing treatment subsequently is necessary to release the stored energy and adjusts the microstructure.In this study,an investigation on the evolution of annealing twins as well as textures in the thin-walled(Φ6 mm×0.3 mm)copper tube underwent holding time-free heat treatment was reported.Electron backscattered diffraction analysis reveals that a large number ofΣ3 boundaries(600<111>twin relationship)are produced at the early stage of heat treatment,which is due to the lower boundary energy.With the recrystallization proceeding,the migration rate of grain boundaries decreases on account of the grain growth;meanwhile,the uniqueΣ9 boundaries(38.9°<110>relationship)are formed due to the interaction of theΣ3 boundaries.As a result,the number fractions ofΣ3 boundaries and high-angle grain boundaries decrease rapidly.During the grain growth stage,a strong recrystallization texture was formed due to the fact that the grains of Goss orientation have a growth advantage over the others.As a result,the initial copper texture was transferred into the Goss texture in domination.