The paper presents the main conclusions of the Russian monograph “Geochemistry of Phosphorus” (2020). Based on statistical processing of ~6100 sample averages (from ~190,000 analyses), new estimations of World avera...The paper presents the main conclusions of the Russian monograph “Geochemistry of Phosphorus” (2020). Based on statistical processing of ~6100 sample averages (from ~190,000 analyses), new estimations of World averages (Clarke values) for Р<sub>2</sub>O<sub>5</sub>, % (and P, %), phosphorus-titanium module (P<sub>2</sub>О<sub>5</sub>/TiO<sub>2</sub>), phosphorus-calcium module (P<sub>2</sub>O<sub>5</sub>/CaO), phosphorus-iron module (P<sub>2</sub>О<sub>5</sub>/Fe<sub>2</sub>O<sub>3</sub>), and phosphorus-total iron module (P<sub>2</sub>O<sub>5</sub>/Fe<sub>2</sub>O<sub>3</sub> + FeO). Many estimates have been made for the first time. In addition to the new Clarke estimates, sometimes very different from previous ones, the work carried out has led to a number of new conclusions. In particular, the titanium geochemical barrier for phosphorus has been first estimated, all the 11 genotypes of phosphogenesis have been named and characterized, five genetic correlations of phosphogenesis have been described, lithochemistry methods have been successfully applied to characterize the phosphorites. Due to the large breadth of generalization, the monograph has a large theoretical and applied value.展开更多
Intercritical annealing（IA） at various temperatures followed by quenching and partitioning（IAQP） treatments was conducted on a cold-rolled Fe-0.2C-1.42Si-l.87Mn（wt%） sheet steel.Optimized microstructure and enha...Intercritical annealing（IA） at various temperatures followed by quenching and partitioning（IAQP） treatments was conducted on a cold-rolled Fe-0.2C-1.42Si-l.87Mn（wt%） sheet steel.Optimized microstructure and enhanced mechanical properties were achieved through appropriate adjustment of IA temperatures.The steel which was annealed at1,033 K for 600 s,then quenched to 573 K and partitioned at 693 K for 20 min,designated as 1033 QP steel,exhibits maximum 16.3 vol% retained austenite（RA） with good mechanical properties（ultimate tensile strength 886 MPa and total elongation 27%）.It was found that the thermal and mechanical stabilities of RA are mainly influenced by the combined effect of its average carbon content and amount of adjacent martensite.Furthermore,the transformation-induced plasticity effect increased the peak n-values observed at the second stage of the work hardening of IAQP steels.展开更多
文摘The paper presents the main conclusions of the Russian monograph “Geochemistry of Phosphorus” (2020). Based on statistical processing of ~6100 sample averages (from ~190,000 analyses), new estimations of World averages (Clarke values) for Р<sub>2</sub>O<sub>5</sub>, % (and P, %), phosphorus-titanium module (P<sub>2</sub>О<sub>5</sub>/TiO<sub>2</sub>), phosphorus-calcium module (P<sub>2</sub>O<sub>5</sub>/CaO), phosphorus-iron module (P<sub>2</sub>О<sub>5</sub>/Fe<sub>2</sub>O<sub>3</sub>), and phosphorus-total iron module (P<sub>2</sub>O<sub>5</sub>/Fe<sub>2</sub>O<sub>3</sub> + FeO). Many estimates have been made for the first time. In addition to the new Clarke estimates, sometimes very different from previous ones, the work carried out has led to a number of new conclusions. In particular, the titanium geochemical barrier for phosphorus has been first estimated, all the 11 genotypes of phosphogenesis have been named and characterized, five genetic correlations of phosphogenesis have been described, lithochemistry methods have been successfully applied to characterize the phosphorites. Due to the large breadth of generalization, the monograph has a large theoretical and applied value.
基金financially supported by the National Natural Science Foundation of China (No. 51174251)the National Basic Research Program of China (No. 2010CB630803)
文摘Intercritical annealing（IA） at various temperatures followed by quenching and partitioning（IAQP） treatments was conducted on a cold-rolled Fe-0.2C-1.42Si-l.87Mn（wt%） sheet steel.Optimized microstructure and enhanced mechanical properties were achieved through appropriate adjustment of IA temperatures.The steel which was annealed at1,033 K for 600 s,then quenched to 573 K and partitioned at 693 K for 20 min,designated as 1033 QP steel,exhibits maximum 16.3 vol% retained austenite（RA） with good mechanical properties（ultimate tensile strength 886 MPa and total elongation 27%）.It was found that the thermal and mechanical stabilities of RA are mainly influenced by the combined effect of its average carbon content and amount of adjacent martensite.Furthermore,the transformation-induced plasticity effect increased the peak n-values observed at the second stage of the work hardening of IAQP steels.