Although magnesium-aluminum alloys,such as AZ80 and AZ91 have promising application potential in automotive,high-speed train and aerospace fields,their age-hardening response is generally not very appreciable.In this ...Although magnesium-aluminum alloys,such as AZ80 and AZ91 have promising application potential in automotive,high-speed train and aerospace fields,their age-hardening response is generally not very appreciable.In this work,the aging-hardening response of AZ80 alloy was effectively enhanced by applying cold-rolling deformation before conducting conventional aging treatment at 200°C.Compared to the directly aged sample,the yield strength of the pre-rolling and aged sample was increased by 35 MPa.Electron microscope examination confirmed that profuse{10¯11}and{10¯11}-{10¯12}twins,consisting of high density of dislocations and stacking faults,were generated by cold rolling.Blocky or ellipsoidal Mg_(17)Al_(12)precipitates formed at the twin boundaries(TBs)during subsequent aging treatment.Crystallographic analysis indicated that the precipitates at{10¯11}TBs always held an identical Potter OR with both the matrix and twin,while the precipitates at{10¯11}-{10¯12}TBs exhibited three different ORs:Burgers OR,Potter OR and P-S OR with either the matrix or the twin.Moreover,recrystallized grains were found inside{10¯11}-{10¯12}double twins after peak-aging at 200°C,implying that precipitation and recrystallization might occur concurrently along TBs at a relatively low temperature.It was speculated that the highly stored energy inside twins and the high elastic energy between the precipitates and twins were driving factors for the occurrence of recrystallization.展开更多
The effect ofωiso andαprecipitation on microstructure,microhardness,tensile properties and impact toughness of Ti-25Nb-10Ta-1Zr-0.2Fe(TNTZF)alloy was investigated.The results showed that the solution treated TNTZF a...The effect ofωiso andαprecipitation on microstructure,microhardness,tensile properties and impact toughness of Ti-25Nb-10Ta-1Zr-0.2Fe(TNTZF)alloy was investigated.The results showed that the solution treated TNTZF alloy with a small amount of nano-sizedωath particles inβmatrix possesses tensile strength of 697 MPa,elongation of~34%,Young’s modulus(YM)of 75 GPa,and impact toughness of 58.7 J/cm^(2).After aging at relatively lower temperatures of 400℃,the hardness and modulus of the alloy increased significantly,while the plasticity and toughness dropped sharply due to the precipitation ofωiso phase.ωiso phase displayed an ellipsoidal morphology with high volume fraction and a size of about 50 nm after aging at 400℃,leading to the highest hardness of 364 HV and YM of 108 GPa,along with completely embrittlement since elongation and toughness were almost zero.A brittle impact fracture morphology was observed in the alloy,which is dominated by intergranular fracture,with a mixed fracture characteristics of cleavage surfaces,terraces and tiny dimples.When aged at 550℃,plate-likeαdistributed inβmatrix uniformly and inβgrain boundaries in parallel,resulting in the high strength of 804 MPa,as well as lowest YM of 72 GPa,elongation of 9%and toughness of 35.8 J/cm^(2).The fracture morphology of the alloy aged at 550℃showed a ductile fracture mechanism with a large number of dimples.展开更多
Boundary engineering has proven effective in enhancing the thermoelectric performance of materials.SnSe,known for its low thermal conductivity,has garnered significant interest;however,its application is hindered by p...Boundary engineering has proven effective in enhancing the thermoelectric performance of materials.SnSe,known for its low thermal conductivity,has garnered significant interest;however,its application is hindered by poor electrical conductivity.Herein,the Ag_(8)GeSe_(6) is introduced into the p-type polycrystalline SnSe matrix to optimize the thermoelectric performance,and the in-situ Ag_(2)Se precipitates are formed in grain boundaries,which play dual roles,acting as an electron attraction center for improving hole concentration and a phonon scattering center for reducing lattice thermal conductivity.It effectively decouples the thermal and electrical transport properties to optimize the thermoelectric performance.Importantly,the amount of Ag_(2)Se can be controlled by adjusting the amount of Ag_(8)GeSe_(6) added to the SnSe matrix.The introduction of Ag_(8)GeSe_(6) enhances electrical conductivity due to the increased hole carrier caused by the introduced Ag+and the formed electron attraction center(in-situ Ag_(2)Se precipitates).Based on the DFT calculations,the band gap of the Ag_(8)GeSe_(6)-doped samples is considerably decreased,facilitating carrier transport.As a result,the electrical transport properties increase to 808μW m^(−1) K^(−2) at 823 K for SnSe+0.5 wt%Ag_(8)GeSe_(6).In addition,in-situ Ag_(2)Se precipitates in grain boundaries strongly enhance phonon scattering,causing a decrease in lattice thermal conductivity.Furthermore,the presence of defects contributes to a reduction in lattice thermal conductivity.Specifically,the thermal conductivity of SnSe+1.0 wt%Ag_(8)GeSe_(6) decreases to 0.29 W m^(−1) K^(−1) at 823 K.Consequently,SnSe+0.5 wt%Ag_(8)GeSe_(6) obtains a high ZT value of 1.7 at 823 K and maintains a high average ZT value of 0.57 over the temperature range of 323−773 K.Additionally,the mechanical properties of Ag_(8)GeSe_(6)-doped also show an improvement.These advancements can be applied to energy supply applications during deep space exploration.展开更多
Creep aging behavior of retrogression and re-aged(RRAed)7150 aluminum alloy(AA7150)was systematically investigated using the creep aging experiments,mechanical properties tests,electrical conductivity tests and transm...Creep aging behavior of retrogression and re-aged(RRAed)7150 aluminum alloy(AA7150)was systematically investigated using the creep aging experiments,mechanical properties tests,electrical conductivity tests and transmission electron microscope(TEM)observations.Creep aging results show that the steady-state creep mechanism of RRAed alloys is mainly dislocation climb(stress exponent≈5.8),which is insensitive to the grain interior and boundary precipitates.However,the total creep deformation increases over the re-aging time.In addition,the yield strength and tensile strength of the four RRAed samples are essentially the same after creep aging at 140℃ for 16 h,but the elongation decreases slightly with the re-aging time.What’s more,the retrogression and re-aging treatment are beneficial to increase the hardness and electrical conductivity of the creep-aged 7150 aluminum alloy.It can be concluded that the retrogression and re-aging treatment before creep aging forming process can improve the microstructure within grain and at grain boundary,forming efficiency and comprehensive performance of mechanical properties and electrical conductivity of 7150 aluminum alloy.展开更多
The solution-treated (ST) condition and aging precipitation behavior of 18Cr-16Mn-2Mo-1.1N high nitrogen austenitic stainless steel (HNS) were investigated by optical microscope (OM), scanning electron microscope (SEM...The solution-treated (ST) condition and aging precipitation behavior of 18Cr-16Mn-2Mo-1.1N high nitrogen austenitic stainless steel (HNS) were investigated by optical microscope (OM), scanning electron microscope (SEM), and transmission electron microscope (TEM). The results show that the ST condition of 18Cr-16Mn-2Mo-1.1N HNS with wN above 1% is identified as 1100 ℃ for 90 min, followed by water quenching to make sure the secondary phases completely dissolve into austenitic matrix and prevent the grains coarsening too much. Initial time-temperature-precipitation (TTP) curve of aged 18Cr-16Mn-2Mo-1.1N HNS which starts with precipitation of 0.05% in volume fraction is defined and the 'nose' temperature of precipitation is found to be 850 ℃ with an incubation period of 1 min. Hexagonal intergranular and cellular Cr2N with a=0.478 nm and c=0.444 nm precipitates gradually increase in the isothermal aging treatment. The matrix nitrogen depletion due to the intergranular and a few cellular Cr2N precipitates induces the decay of Vickers hardness, and the increment of cellular Cr2N causes the increase in the values. Impact toughness presents a monotonic decrease and SEM morphologies show the leading brittle intergranular fracture. The ultimate tensile strength (UTS), yield strength (YS) and elongation (El) deteriorate obviously. Stress concentration occurs when the matrix dislocations pile up at the interfaces of precipitation and matrix, and the interfacial dislocations may become precursors to the misfit dislocations, which can form small cleavage facets and accelerate the formation of cracks.展开更多
The interaction between precipitation and recrystallization and its effect on t he properties of the Cu-Ni-Si-Cr alloy during aging were discussed.The result s show that the deformation results in much more dispersed...The interaction between precipitation and recrystallization and its effect on t he properties of the Cu-Ni-Si-Cr alloy during aging were discussed.The result s show that the deformation results in much more dispersed precipitation of the phases. The precipitations have accelerating or retarding effects on the recryst allization. On the formation and growth of recrystallization, the precipitated p hases are coarsed or dissolved in front of grain boundaries following a re-prec ipitation in the recrystallization area.展开更多
The effects of interrupted aging on mechanical properties and corrosion resistance of 7A75 aluminum alloy extruded bar were investigated through various analyses,including electrical conductivity,mechanical properties...The effects of interrupted aging on mechanical properties and corrosion resistance of 7A75 aluminum alloy extruded bar were investigated through various analyses,including electrical conductivity,mechanical properties,local corrosion properties,and slow strain rate tensile stress corrosion tests.Microstructure characterization techniques such as metallographic microscopy,scanning electron microscopy(SEM),and transmission electron microscopy(TEM)were also employed.The results indicate that the tensile strength of the alloy produced by T6I6 aging is similar to that produced by T6I4 aging,and it even exceeds 700 MPa.Furthermore,the yield strength increases by 52.7 MPa,reaching 654.8 MPa after T6I6 aging treatment.The maximum depths of intergranular corrosion(IGC)and exfoliation corrosion(EXCO)decrease from 116.3 and 468.5μm to 89.5 and 324.3μm,respectively.The stress corrosion factor also decreases from 2.1%to 1.6%.These findings suggest that the alloy treated with T6I6 aging exhibits both high strength and excellent stress corrosion cracking resistance.Similarly,when the alloy is treated with T6I4,T6I6 and T6I7 aging,the sizes of grain boundary precipitates(GBPs)are found to be 5.2,18.4,and 32.8 nm,respectively.The sizes of matrix precipitates are 4.8,5.7 and 15.7 nm,respectively.The atomic fractions of Zn in GBPs are 9.92 at.%,8.23 at.%and 6.87 at.%,respectively,while the atomic fractions of Mg are 12.66 at.%,8.43 at.%and 7.00 at.%,respectively.Additionally,the atomic fractions of Cu are 1.83 at.%,2.47 at.%and 3.41 at.%,respectively.展开更多
In the present study, the tested hypereutectic Al-21wt.%Si alloys were prepared by modifying the melt using different proportions of P and Ce, and then applying T6 heat treatment. The modification effects and mechanis...In the present study, the tested hypereutectic Al-21wt.%Si alloys were prepared by modifying the melt using different proportions of P and Ce, and then applying T6 heat treatment. The modification effects and mechanism of P＋Ce complex modifier on the Si phase of hypereutectic Al-21wt.%Si alloy were studied, and the aging precipitation behavior after modification was characterized by means of tensile strength measurement, OM, SEM and TEM analysis. The results show that the massive primary silicon phase particles are significantly refined after modification, while the needle-like eutectic silicon crystals become fibrous and short. It was found that the mechanism of phosphorus modification on the primary silicon can be attributed to heterogeneous nucleation of AlP, while the modification mechanism of Ce can be explained by adsorbing-twinning theory. In the aged microstructure of the modified hypereutectic Al-21wt.%Si alloy, there existed some strengthening phases such as AI4Cu9, Al2Cu, AlCu3, and Al57Mn12. The P＋Ce complex modifier not only affected the size of primary silicon and eutectic silicon, but also the aging behavior of alloys under the heat treatment process. When Al-21wt.%Si alloy was modified using 0.08%wt.P ＋ 0.6wt.% Ce, the aging precipitates were dispersed uniformly in the alloy, and its mechanical properties at room and elevated temperatures are optimized （Rm = 287.6 MPa at RT, Rm = 210 MPa at 300 ℃）.展开更多
The aging precipitation behavior in solution treated Cu-Ni-Si-Cr alloy has been studied in terms of the analyses of the variations in electrical conductivity. On the basis of the linear relationship between the electr...The aging precipitation behavior in solution treated Cu-Ni-Si-Cr alloy has been studied in terms of the analyses of the variations in electrical conductivity. On the basis of the linear relationship between the electrical conductivity and the volume fraction of the precipitates, the phase transformation kinetics equation was deduced from the Avrami empiricai formula. On the basis of this equation, transformation kinetics curves corresponding to 5% and 50% transformation were established.展开更多
The influence of chemical composition and cold deformation on aging precipitation behavior of 18Cr-16Mn-2Mo-I.IN （HNS-A）, 18Cr-16Mn-I.3N （HNS-B）, 18Cr-18Mn-2Mo-0.96N （HNS-C） and 18Cr-18Mn-2Mo-0.77N （I-INS-D） h...The influence of chemical composition and cold deformation on aging precipitation behavior of 18Cr-16Mn-2Mo-I.IN （HNS-A）, 18Cr-16Mn-I.3N （HNS-B）, 18Cr-18Mn-2Mo-0.96N （HNS-C） and 18Cr-18Mn-2Mo-0.77N （I-INS-D） high nitrogen austenitic stainless steels was investigated. The results show that the ＂nose＂ temperatures and incubation periods of the initial time-temperature-precipitation （TTP） curves of aged HNSs are found to be 850 ℃, 60 s; 850 ℃, 45 s; 850 ℃, 60 s and 900 ℃, 90 s, respectively. Based on the analysis of SAD patterns, the coarse cellular Cr2N precipitate which presents a lamellar structure has a hexagonal structure of a=0.478 nm and c=0.444 nm. The Z phase corresponding to a composition of Fe36Cr^2Mo10, is determined to be a body-centered cubic structure ofa=0.892 nm. The precipitating sensitivity presents no more difference with the nitrogen content increasing from 0.77% to 0.96%, but exhibits so obviously that the cellular precipitates nearly overspread the whole field. The addition of Mo element can restrain the TTP curves moving left and down, which means decreasing the sensitivity of aging precipitation. With increasing the cold deformation, the sensitivity of precipitation increases obviously.展开更多
Cerium-zirconium composite oxides with high performance were synthesized by a co-precipitation method, using zirconium oxychloride and rare earth chloride as raw materials. The effects of precipitate aging time on the...Cerium-zirconium composite oxides with high performance were synthesized by a co-precipitation method, using zirconium oxychloride and rare earth chloride as raw materials. The effects of precipitate aging time on the properties of cerium-zirconium composite oxides were investigated. The prepared cerium-zirconium composite oxides were characterized by X-ray diffraction（XRD）, BET specific surface area, pulsed oxygen chemical adsorption, H2 temperature-programmed-reduction（H2-TPR）, scanning electron microscopy（SEM）, etc. The results showed that the precipitate aging time caused great effects on the properties of cerium zirconium composite oxides. With the increase of aging time, the cerium zirconium composite oxides showed enhanced specific surface area, good thermal stability, and high oxygen storage capacity（OSC）. The best performance sample was obtained while the precipitate aging time up to 48 h, with the specific surface area of 140.7 m2/g, and OSC of 657.24 μmolO2/g for the fresh sample. Even after thermal aged under 1000 oC for 4 h, the aged specific surface area was 41.6 m2/g, moreover with a good OSC of 569.9 μmolO2/g.展开更多
To study the influence of aging heat treatments on the microstructure of single crystal superalloys with high content of refractory elements and optimal the aging heat treatment regimes, a single crystal superalloy co...To study the influence of aging heat treatments on the microstructure of single crystal superalloys with high content of refractory elements and optimal the aging heat treatment regimes, a single crystal superalloy containing 22 wt% refractory elements was investigated.Results show that for the experimental alloy, even the homogenization-solution heat treatment for 25 h cannot homogenize the alloying elements completely. During primary aging heat treatment, γ＇ phase grows larger and turns to regular cubes. Higher aging temperature induces larger γ＇ cubes. For specimens with primary aging heat treated at 1120 ℃,γ＇ morphology does not change apparently during secondary aging heat treatment. For specimens with primary aging heat treatment at 1150 ℃,γ＇phase in interdendrite grows obviously comparing with that in dendrites. By analyzing the precipitating kinetics of γ＇phase, it is found that owning to the dendrite segregation and different aging heat treatment temperatures, γ＇ phase at different regions grows under the control of different factors at different aging heat treatment stages. The two controlling factors that are driving forces of phase transformation and element diffusion rate induce obviously different growth rates of γ＇ phase. As a result, the γ＇-precipitating behaviors are variable based on different solute concentrations and aging temperatures. For advanced single crystal superalloys that are supposed to be used at relatively high temperatures, the final γ＇ size after aging heat treatment is suggested to be close to the crossing point of diffusion controlling curve and driving force controlling curve corresponding to the serving temperature. And then,high-temperature properties can be improved.展开更多
In this paper,the evolutions of microstructure and mechanical properties of Cu-l.9Be-0.3Ni-0.15Co alloy were studied.The alloys in the condition of the solution treated（soft state） and 37% cold rolled（hard state） ...In this paper,the evolutions of microstructure and mechanical properties of Cu-l.9Be-0.3Ni-0.15Co alloy were studied.The alloys in the condition of the solution treated（soft state） and 37% cold rolled（hard state） were aged at 320 ℃for different time,respectively.The mechanical properties,electrical conductivity and microstructure of the alloy aged for different time were analyzed.Additionally,the precipitation kinetics of Cu-1.9Be-0.3Ni-0.15Co alloys was investigated.X-ray diffraction and transmission electron microscopy results reveal that both continuous precipitation and discontinuous precipitation existed in the hard-state Cu-l.9Be-0.3Ni-0.15Co alloy during the whole aging process;the sequence of continuous precipitation is G.P.zone →γ″→γ′→γ.Furthermore,the precipitation transformation mechanism of softstate alloy is homogeneous nucleation,while hard-state alloy shows the heterogeneous nucleation（interface nucleation）with the nucleation rate of both states decaying rapidly to zero during aging at 320 ℃.展开更多
The effect of aging on the mechanical properties and microstructures of a new ZG12Cr9 MolColNiVNbNB ferritic heat resistant steel was investigated in this work to satisfy the high steam parameters of the ultra-supercr...The effect of aging on the mechanical properties and microstructures of a new ZG12Cr9 MolColNiVNbNB ferritic heat resistant steel was investigated in this work to satisfy the high steam parameters of the ultra-supercritical power plant.The results show that the main precipitates during aging are Fe（Cr,Mo）23C6,V（Nb）C,and（Fe2Mo） Laves in the steel.The amounts of the precipitated phases increase during aging,and correspondingly,the morphologies of phases are similar to be round.Fe（Cr,Mo）23C6 appears along boundaries and grows with increasing temperature.In addition,it is revealed that the martensitic laths are coarsened and eventually happen to be polygonization.The hardness and strength decrease gradually,whereas the plasticity of the steel increases.What＇s more,the hardness of this steel after creep is similar to that of other 9%-12%Cr ferritic steels.Thus,ZG12Cr9 MolColNiVNbNB can be used in the project.展开更多
The shape memory behavior of [111]-oriented Ni_（51）Ti_（49） （at.%） single crystals was investigated after stressassisted aging at 500 °C for 1.5 h under a compressive stress of-150 MPa.It was found that a si...The shape memory behavior of [111]-oriented Ni_（51）Ti_（49） （at.%） single crystals was investigated after stressassisted aging at 500 °C for 1.5 h under a compressive stress of-150 MPa.It was found that a single family of Ni_4Ti_3 precipitates with two crystallographically equivalent variants was formed after aging under compressive stress.Stressassisted aging resulted in tensile two-way shape memory effect strain of 1.56% under-5 MPa.Thermal cycling under-600 MPa resulted in a transformation strain of-2.15%,while the subsequent thermal cycling under-5 MPa resulted in a tensile two-way shape memory effect strain of 2.2%.展开更多
The effects of pre-aging treatments on subsequent artificial aging response were investigated by means of transmission electron microscopy observations and hardness test in age hardened Al-3.95Cu-(1.32Mg)-0.52Mn-0.11 ...The effects of pre-aging treatments on subsequent artificial aging response were investigated by means of transmission electron microscopy observations and hardness test in age hardened Al-3.95Cu-(1.32Mg)-0.52Mn-0.11 Zr alloys. In Al-3.95Cu-0.52Mn-0.11 Zr alloy, when the pre-aging temperature is 25 °C, the pre-aging treatment has no evident effect on the peak hardness of subsequent artificial aging, while a positive effect(increase of peak hardness) appears when pre-aging temperature is50 °C. However, in Al-3.95Cu-1.32Mg-0.52Mn-0.11 Zr alloy, it is found that whether the pre-aging temperature is 25 °C or 50 °C,the peak artificial aging hardness is lower than that of T6 treated alloy, that is to say, pre-aging treatment has a negative effect on the peak hardness of subsequent artificial aging in the alloys.展开更多
Based on the available experimental phase equilibrium relations and aging precipitation sequences,the Mg–Gd–Y ternary system has been thermodynamically re-assessed by means of CALPHAD technique.To simulate the exper...Based on the available experimental phase equilibrium relations and aging precipitation sequences,the Mg–Gd–Y ternary system has been thermodynamically re-assessed by means of CALPHAD technique.To simulate the experimentally reported aging precipitation sequence,α(Mg)_(SS)(supersaturated)→GP zones(D019-type,metastable)→β’-Mg_(7)Gd(c-bco,metastable)→β_(1)-Mg_(3)Gd(fcc,metastable)→β-Mg_(5)Gd(fcc,stable)near the Mg–Gd side,andα(Mg)SS(supersaturated)→β’-Mg_(7)Y(c-bco,metastable)→β-Mg_(24)Y_(5)(bcc,stable)near the Mg–Y side,the effective nucleation driving forces obtained by deducting the nucleation resistances from the thermodynamic driving forces are calculated and analyzed.Two metastable components,GP zones(D019-type)andβ’(c-bco)ordered fromα(Mg)_(SS),do not exist in the stable equilibrium phase diagram but appear in the annealing process of typical alloys.The Redlich–Kister equations are adopted to describe three solution phases,Liquid,HCP_A3 and BCC_A2.The intermediate compounds Mg_(2)Y,Mg_(24)Y_(5),Mg_(2)Gd,Mg_(3)Gd and Mg_(5)Gd are expressed by the formulas of(Mg,Y)_(2/3)(Gd,Mg,Y)_(1/3),Mg_(24/29)(Gd,Mg,Y)_(4/29)Y1/29,(Gd,Mg)_(2/3)(Gd,Mg,Y)_(1/3),(Gd,Mg)_(3/4)(Gd,Mg,Y)_(1/4)and Mg_(5/6)(Gd,Mg,Y)_(1/6),respectively.In particular,the two-sublattice models(Gd,Mg,Y)_(1/2)(Gd,Mg,Y)_(1/2),(Gd,Mg,Y)_(3/4)(Gd,Mg,Y)_(1/4)and(Gd,Mg,Y)_(7/8)(Gd,Mg,Y)_(1/8)have been respectively used to describe the stable Mg(Gd,Y)(BCC_B2)alloy compound as well as the metastable GP zones(D019-type)andβ’(c-bco)phase,in order to cope with the order-disorder transitions.A set of self-consistent thermodynamic parameters has been obtained to ensure the thermodynamic calculations well consistent with the reported experimental data,containing not only the stable equilibrium phase diagram but also the aging precipitation sequence.展开更多
Microstructure and mechanical properties of aged Mg-10Gd-2Y-0.4Zr-0.4Ag alloy sheets prepared by different rolling routes were investigated.The results showed that the cross rolling aged(CRA)sheet possesses larger gra...Microstructure and mechanical properties of aged Mg-10Gd-2Y-0.4Zr-0.4Ag alloy sheets prepared by different rolling routes were investigated.The results showed that the cross rolling aged(CRA)sheet possesses larger grain size than unidirectional rolling aged(URA)sheet due to the occurrence of dynamic recovery during rolling which reduces the dislocation density and delays dynamic recrystallization(DRX).The URA sheet has basal texture and RD favored texture while CRA sheet has multiple-peak texture.Both sheets precipitate β'phase and CRA sheet exhibits a stronger aging response.The CRA sheet has higher yield strength and tensile strength than URA sheet,with reduced yield strength anisotropy but increased tensile strength anisotropy.Taking into account different strengthening mechanisms,although the finer grain size of URA sheet enhances grain boundary strengthening,CRA sheet is more responsive to aging,leading to superior aging-precipitated phase strengthening and consequently higher yield strength.展开更多
The mechanical properties (σb,σ0.2,and δ) and fracture behavior of tensile specimens of the refined A356 alloys were investigated as a function of the addition level of Al-Ti-B master alloy under both as-cast and T...The mechanical properties (σb,σ0.2,and δ) and fracture behavior of tensile specimens of the refined A356 alloys were investigated as a function of the addition level of Al-Ti-B master alloy under both as-cast and T6 heat-treated conditions. The results show that as the addition level of Al-5Ti-1B master alloy increases from 0.1 wt.% to 5.0 wt.%,the mechanical properties of refined A356 alloys improve steadily and then decrease slightly under both as-cast and T6 heat-treated conditions. Also,they display exc...展开更多
The microstructure evolution and mechanical properties of Mg–6Zn–0.5Ce–xMn(x=0 and 1 wt.%)wrought magnesium alloys were researched,and the morphologies and role of Mn element in the experimental alloys were analyze...The microstructure evolution and mechanical properties of Mg–6Zn–0.5Ce–xMn(x=0 and 1 wt.%)wrought magnesium alloys were researched,and the morphologies and role of Mn element in the experimental alloys were analyzed.The research shows that all of Mn elements form theα-Mn pure phases,which do not participate in the formation of other phases,such as theτ-phases.The mechanical properties of Mn-containing alloys in as-extruded and aged states are superior to Mn-free alloys.During the hot extrusion process,the dispersed fineα-Mn particle phase hinders the migration of grain boundaries and inhibits dynamic recrystallization,which mainly takes effect of grain refining and dispersion hardening.During the aging treatments,the dispersed fineα-Mn particle phase not only hinders the growth of the solution-treated grains,but also becomes the nucleation cores ofβ1 rod-like precipitate phase,which is conducive to increasing the nucleation rate of the precipitate phase.For the aged alloy,the Mn addition mainly takes effect of grain refining and promoting aging strengthening.展开更多
基金financially supported by the National Natural Science Foundation of China(No.52071040 and 51871036)Natural Science Foundation of Shandong Province,China(No.ZR2022QE008)China Postdoctoral Science Foundation(No.2022M712984)。
文摘Although magnesium-aluminum alloys,such as AZ80 and AZ91 have promising application potential in automotive,high-speed train and aerospace fields,their age-hardening response is generally not very appreciable.In this work,the aging-hardening response of AZ80 alloy was effectively enhanced by applying cold-rolling deformation before conducting conventional aging treatment at 200°C.Compared to the directly aged sample,the yield strength of the pre-rolling and aged sample was increased by 35 MPa.Electron microscope examination confirmed that profuse{10¯11}and{10¯11}-{10¯12}twins,consisting of high density of dislocations and stacking faults,were generated by cold rolling.Blocky or ellipsoidal Mg_(17)Al_(12)precipitates formed at the twin boundaries(TBs)during subsequent aging treatment.Crystallographic analysis indicated that the precipitates at{10¯11}TBs always held an identical Potter OR with both the matrix and twin,while the precipitates at{10¯11}-{10¯12}TBs exhibited three different ORs:Burgers OR,Potter OR and P-S OR with either the matrix or the twin.Moreover,recrystallized grains were found inside{10¯11}-{10¯12}double twins after peak-aging at 200°C,implying that precipitation and recrystallization might occur concurrently along TBs at a relatively low temperature.It was speculated that the highly stored energy inside twins and the high elastic energy between the precipitates and twins were driving factors for the occurrence of recrystallization.
基金supported by the Natural Science Foundation of Hunan Province(2023JJ50055,2023JJ30081)the Science Research Foundation of Hunan Provincial Education Department(21A0546)+1 种基金the Youth Project of the National Natural Science Foundation of China(62003056)the Open Fund of Hunan Engineering Research Center of Research and Development of Degradable Materials and Molding Technology(2023KFKT05).
文摘The effect ofωiso andαprecipitation on microstructure,microhardness,tensile properties and impact toughness of Ti-25Nb-10Ta-1Zr-0.2Fe(TNTZF)alloy was investigated.The results showed that the solution treated TNTZF alloy with a small amount of nano-sizedωath particles inβmatrix possesses tensile strength of 697 MPa,elongation of~34%,Young’s modulus(YM)of 75 GPa,and impact toughness of 58.7 J/cm^(2).After aging at relatively lower temperatures of 400℃,the hardness and modulus of the alloy increased significantly,while the plasticity and toughness dropped sharply due to the precipitation ofωiso phase.ωiso phase displayed an ellipsoidal morphology with high volume fraction and a size of about 50 nm after aging at 400℃,leading to the highest hardness of 364 HV and YM of 108 GPa,along with completely embrittlement since elongation and toughness were almost zero.A brittle impact fracture morphology was observed in the alloy,which is dominated by intergranular fracture,with a mixed fracture characteristics of cleavage surfaces,terraces and tiny dimples.When aged at 550℃,plate-likeαdistributed inβmatrix uniformly and inβgrain boundaries in parallel,resulting in the high strength of 804 MPa,as well as lowest YM of 72 GPa,elongation of 9%and toughness of 35.8 J/cm^(2).The fracture morphology of the alloy aged at 550℃showed a ductile fracture mechanism with a large number of dimples.
基金supported by the Outstanding Youth Fund of Yunnan Province(Grant No.202201AV070005)the National Natural Science Foundation of China(Grant No.52162029)the National Key R&D Program of China(Grant No.2022YFF0503804).
文摘Boundary engineering has proven effective in enhancing the thermoelectric performance of materials.SnSe,known for its low thermal conductivity,has garnered significant interest;however,its application is hindered by poor electrical conductivity.Herein,the Ag_(8)GeSe_(6) is introduced into the p-type polycrystalline SnSe matrix to optimize the thermoelectric performance,and the in-situ Ag_(2)Se precipitates are formed in grain boundaries,which play dual roles,acting as an electron attraction center for improving hole concentration and a phonon scattering center for reducing lattice thermal conductivity.It effectively decouples the thermal and electrical transport properties to optimize the thermoelectric performance.Importantly,the amount of Ag_(2)Se can be controlled by adjusting the amount of Ag_(8)GeSe_(6) added to the SnSe matrix.The introduction of Ag_(8)GeSe_(6) enhances electrical conductivity due to the increased hole carrier caused by the introduced Ag+and the formed electron attraction center(in-situ Ag_(2)Se precipitates).Based on the DFT calculations,the band gap of the Ag_(8)GeSe_(6)-doped samples is considerably decreased,facilitating carrier transport.As a result,the electrical transport properties increase to 808μW m^(−1) K^(−2) at 823 K for SnSe+0.5 wt%Ag_(8)GeSe_(6).In addition,in-situ Ag_(2)Se precipitates in grain boundaries strongly enhance phonon scattering,causing a decrease in lattice thermal conductivity.Furthermore,the presence of defects contributes to a reduction in lattice thermal conductivity.Specifically,the thermal conductivity of SnSe+1.0 wt%Ag_(8)GeSe_(6) decreases to 0.29 W m^(−1) K^(−1) at 823 K.Consequently,SnSe+0.5 wt%Ag_(8)GeSe_(6) obtains a high ZT value of 1.7 at 823 K and maintains a high average ZT value of 0.57 over the temperature range of 323−773 K.Additionally,the mechanical properties of Ag_(8)GeSe_(6)-doped also show an improvement.These advancements can be applied to energy supply applications during deep space exploration.
基金Project(2017YFB0306300)supported by the National Key Research and Development Program of ChinaProject(2017ZX04005001)supported by the National Science and Technology Major Project,China+2 种基金Project(JCKY2014203A001)supported by National Defense Program of ChinaProjects(51905551,51675538,51601060)supported by the National Natural Science Foundation of ChinaProjects(Kfkt2018-03,zzYJKT2019-11)supported by State Key Laboratory of High-Performance Complex Manufacturing,China。
文摘Creep aging behavior of retrogression and re-aged(RRAed)7150 aluminum alloy(AA7150)was systematically investigated using the creep aging experiments,mechanical properties tests,electrical conductivity tests and transmission electron microscope(TEM)observations.Creep aging results show that the steady-state creep mechanism of RRAed alloys is mainly dislocation climb(stress exponent≈5.8),which is insensitive to the grain interior and boundary precipitates.However,the total creep deformation increases over the re-aging time.In addition,the yield strength and tensile strength of the four RRAed samples are essentially the same after creep aging at 140℃ for 16 h,but the elongation decreases slightly with the re-aging time.What’s more,the retrogression and re-aging treatment are beneficial to increase the hardness and electrical conductivity of the creep-aged 7150 aluminum alloy.It can be concluded that the retrogression and re-aging treatment before creep aging forming process can improve the microstructure within grain and at grain boundary,forming efficiency and comprehensive performance of mechanical properties and electrical conductivity of 7150 aluminum alloy.
基金Item Sponsored by Key Program of National Science Foundation of China(50534010)Fundamental Research Funds for Central Universities of China(N100402015)
文摘The solution-treated (ST) condition and aging precipitation behavior of 18Cr-16Mn-2Mo-1.1N high nitrogen austenitic stainless steel (HNS) were investigated by optical microscope (OM), scanning electron microscope (SEM), and transmission electron microscope (TEM). The results show that the ST condition of 18Cr-16Mn-2Mo-1.1N HNS with wN above 1% is identified as 1100 ℃ for 90 min, followed by water quenching to make sure the secondary phases completely dissolve into austenitic matrix and prevent the grains coarsening too much. Initial time-temperature-precipitation (TTP) curve of aged 18Cr-16Mn-2Mo-1.1N HNS which starts with precipitation of 0.05% in volume fraction is defined and the 'nose' temperature of precipitation is found to be 850 ℃ with an incubation period of 1 min. Hexagonal intergranular and cellular Cr2N with a=0.478 nm and c=0.444 nm precipitates gradually increase in the isothermal aging treatment. The matrix nitrogen depletion due to the intergranular and a few cellular Cr2N precipitates induces the decay of Vickers hardness, and the increment of cellular Cr2N causes the increase in the values. Impact toughness presents a monotonic decrease and SEM morphologies show the leading brittle intergranular fracture. The ultimate tensile strength (UTS), yield strength (YS) and elongation (El) deteriorate obviously. Stress concentration occurs when the matrix dislocations pile up at the interfaces of precipitation and matrix, and the interfacial dislocations may become precursors to the misfit dislocations, which can form small cleavage facets and accelerate the formation of cracks.
基金Funded by the National High Technology Research Project (No.2002AA331112) and by the Major Science and Technology Projectof Henan Province of China(No.0122021300)
文摘The interaction between precipitation and recrystallization and its effect on t he properties of the Cu-Ni-Si-Cr alloy during aging were discussed.The result s show that the deformation results in much more dispersed precipitation of the phases. The precipitations have accelerating or retarding effects on the recryst allization. On the formation and growth of recrystallization, the precipitated p hases are coarsed or dissolved in front of grain boundaries following a re-prec ipitation in the recrystallization area.
基金the Tianjin Key Laboratory of Fastening and Connection Technology Enterprises 2022—2023,China(No.TKLF2022-02-C-02)the technical support from the School of Materials Science and Engineering,Central South University,China.
文摘The effects of interrupted aging on mechanical properties and corrosion resistance of 7A75 aluminum alloy extruded bar were investigated through various analyses,including electrical conductivity,mechanical properties,local corrosion properties,and slow strain rate tensile stress corrosion tests.Microstructure characterization techniques such as metallographic microscopy,scanning electron microscopy(SEM),and transmission electron microscopy(TEM)were also employed.The results indicate that the tensile strength of the alloy produced by T6I6 aging is similar to that produced by T6I4 aging,and it even exceeds 700 MPa.Furthermore,the yield strength increases by 52.7 MPa,reaching 654.8 MPa after T6I6 aging treatment.The maximum depths of intergranular corrosion(IGC)and exfoliation corrosion(EXCO)decrease from 116.3 and 468.5μm to 89.5 and 324.3μm,respectively.The stress corrosion factor also decreases from 2.1%to 1.6%.These findings suggest that the alloy treated with T6I6 aging exhibits both high strength and excellent stress corrosion cracking resistance.Similarly,when the alloy is treated with T6I4,T6I6 and T6I7 aging,the sizes of grain boundary precipitates(GBPs)are found to be 5.2,18.4,and 32.8 nm,respectively.The sizes of matrix precipitates are 4.8,5.7 and 15.7 nm,respectively.The atomic fractions of Zn in GBPs are 9.92 at.%,8.23 at.%and 6.87 at.%,respectively,while the atomic fractions of Mg are 12.66 at.%,8.43 at.%and 7.00 at.%,respectively.Additionally,the atomic fractions of Cu are 1.83 at.%,2.47 at.%and 3.41 at.%,respectively.
基金funded by the National Natural Science Foundation of China(51371077)
文摘In the present study, the tested hypereutectic Al-21wt.%Si alloys were prepared by modifying the melt using different proportions of P and Ce, and then applying T6 heat treatment. The modification effects and mechanism of P＋Ce complex modifier on the Si phase of hypereutectic Al-21wt.%Si alloy were studied, and the aging precipitation behavior after modification was characterized by means of tensile strength measurement, OM, SEM and TEM analysis. The results show that the massive primary silicon phase particles are significantly refined after modification, while the needle-like eutectic silicon crystals become fibrous and short. It was found that the mechanism of phosphorus modification on the primary silicon can be attributed to heterogeneous nucleation of AlP, while the modification mechanism of Ce can be explained by adsorbing-twinning theory. In the aged microstructure of the modified hypereutectic Al-21wt.%Si alloy, there existed some strengthening phases such as AI4Cu9, Al2Cu, AlCu3, and Al57Mn12. The P＋Ce complex modifier not only affected the size of primary silicon and eutectic silicon, but also the aging behavior of alloys under the heat treatment process. When Al-21wt.%Si alloy was modified using 0.08%wt.P ＋ 0.6wt.% Ce, the aging precipitates were dispersed uniformly in the alloy, and its mechanical properties at room and elevated temperatures are optimized （Rm = 287.6 MPa at RT, Rm = 210 MPa at 300 ℃）.
基金This work was supported by the National High Technology Research Project“863"under Grant No.2002AA331112by the Major Science&Technology Project of Henan Province,China,under Grant No.0122021300.
文摘The aging precipitation behavior in solution treated Cu-Ni-Si-Cr alloy has been studied in terms of the analyses of the variations in electrical conductivity. On the basis of the linear relationship between the electrical conductivity and the volume fraction of the precipitates, the phase transformation kinetics equation was deduced from the Avrami empiricai formula. On the basis of this equation, transformation kinetics curves corresponding to 5% and 50% transformation were established.
基金Project(51304041) supported by the National Natural Science Foundation of ChinaProject(N100402015) supported by Fundamental Research Funds for the Central Universities of China+1 种基金Project(2012AA03A502) supported by the National High Technology Research and Development Program of ChinaProject supported by Program for Liaoning Innovative Research Team in University,China
文摘The influence of chemical composition and cold deformation on aging precipitation behavior of 18Cr-16Mn-2Mo-I.IN （HNS-A）, 18Cr-16Mn-I.3N （HNS-B）, 18Cr-18Mn-2Mo-0.96N （HNS-C） and 18Cr-18Mn-2Mo-0.77N （I-INS-D） high nitrogen austenitic stainless steels was investigated. The results show that the ＂nose＂ temperatures and incubation periods of the initial time-temperature-precipitation （TTP） curves of aged HNSs are found to be 850 ℃, 60 s; 850 ℃, 45 s; 850 ℃, 60 s and 900 ℃, 90 s, respectively. Based on the analysis of SAD patterns, the coarse cellular Cr2N precipitate which presents a lamellar structure has a hexagonal structure of a=0.478 nm and c=0.444 nm. The Z phase corresponding to a composition of Fe36Cr^2Mo10, is determined to be a body-centered cubic structure ofa=0.892 nm. The precipitating sensitivity presents no more difference with the nitrogen content increasing from 0.77% to 0.96%, but exhibits so obviously that the cellular precipitates nearly overspread the whole field. The addition of Mo element can restrain the TTP curves moving left and down, which means decreasing the sensitivity of aging precipitation. With increasing the cold deformation, the sensitivity of precipitation increases obviously.
基金Project supported by the Twelfth Five-Year National Science and Technology Pillar Program(2012BAE01B02)National Development and Reform Commission Fund:Development and commercialization of the rare earth based automotive catalytic converter for national V automotive emission standard
文摘Cerium-zirconium composite oxides with high performance were synthesized by a co-precipitation method, using zirconium oxychloride and rare earth chloride as raw materials. The effects of precipitate aging time on the properties of cerium-zirconium composite oxides were investigated. The prepared cerium-zirconium composite oxides were characterized by X-ray diffraction（XRD）, BET specific surface area, pulsed oxygen chemical adsorption, H2 temperature-programmed-reduction（H2-TPR）, scanning electron microscopy（SEM）, etc. The results showed that the precipitate aging time caused great effects on the properties of cerium zirconium composite oxides. With the increase of aging time, the cerium zirconium composite oxides showed enhanced specific surface area, good thermal stability, and high oxygen storage capacity（OSC）. The best performance sample was obtained while the precipitate aging time up to 48 h, with the specific surface area of 140.7 m2/g, and OSC of 657.24 μmolO2/g for the fresh sample. Even after thermal aged under 1000 oC for 4 h, the aged specific surface area was 41.6 m2/g, moreover with a good OSC of 569.9 μmolO2/g.
基金financially supported by the Foundation of Beijing Institute of Aeronautical Materials (No.KJSJ150109)
文摘To study the influence of aging heat treatments on the microstructure of single crystal superalloys with high content of refractory elements and optimal the aging heat treatment regimes, a single crystal superalloy containing 22 wt% refractory elements was investigated.Results show that for the experimental alloy, even the homogenization-solution heat treatment for 25 h cannot homogenize the alloying elements completely. During primary aging heat treatment, γ＇ phase grows larger and turns to regular cubes. Higher aging temperature induces larger γ＇ cubes. For specimens with primary aging heat treated at 1120 ℃,γ＇ morphology does not change apparently during secondary aging heat treatment. For specimens with primary aging heat treatment at 1150 ℃,γ＇phase in interdendrite grows obviously comparing with that in dendrites. By analyzing the precipitating kinetics of γ＇phase, it is found that owning to the dendrite segregation and different aging heat treatment temperatures, γ＇ phase at different regions grows under the control of different factors at different aging heat treatment stages. The two controlling factors that are driving forces of phase transformation and element diffusion rate induce obviously different growth rates of γ＇ phase. As a result, the γ＇-precipitating behaviors are variable based on different solute concentrations and aging temperatures. For advanced single crystal superalloys that are supposed to be used at relatively high temperatures, the final γ＇ size after aging heat treatment is suggested to be close to the crossing point of diffusion controlling curve and driving force controlling curve corresponding to the serving temperature. And then,high-temperature properties can be improved.
基金supported by Materials Forming Processing Control and Simulation Laboratory in University of Science and Technology BeijingCNMC Ningxia Orient Group Co.,Ltd.
文摘In this paper,the evolutions of microstructure and mechanical properties of Cu-l.9Be-0.3Ni-0.15Co alloy were studied.The alloys in the condition of the solution treated（soft state） and 37% cold rolled（hard state） were aged at 320 ℃for different time,respectively.The mechanical properties,electrical conductivity and microstructure of the alloy aged for different time were analyzed.Additionally,the precipitation kinetics of Cu-1.9Be-0.3Ni-0.15Co alloys was investigated.X-ray diffraction and transmission electron microscopy results reveal that both continuous precipitation and discontinuous precipitation existed in the hard-state Cu-l.9Be-0.3Ni-0.15Co alloy during the whole aging process;the sequence of continuous precipitation is G.P.zone →γ″→γ′→γ.Furthermore,the precipitation transformation mechanism of softstate alloy is homogeneous nucleation,while hard-state alloy shows the heterogeneous nucleation（interface nucleation）with the nucleation rate of both states decaying rapidly to zero during aging at 320 ℃.
基金supported by the Science and Technology Program of Sichuan Province,China(No.2013GZX0146)
文摘The effect of aging on the mechanical properties and microstructures of a new ZG12Cr9 MolColNiVNbNB ferritic heat resistant steel was investigated in this work to satisfy the high steam parameters of the ultra-supercritical power plant.The results show that the main precipitates during aging are Fe（Cr,Mo）23C6,V（Nb）C,and（Fe2Mo） Laves in the steel.The amounts of the precipitated phases increase during aging,and correspondingly,the morphologies of phases are similar to be round.Fe（Cr,Mo）23C6 appears along boundaries and grows with increasing temperature.In addition,it is revealed that the martensitic laths are coarsened and eventually happen to be polygonization.The hardness and strength decrease gradually,whereas the plasticity of the steel increases.What＇s more,the hardness of this steel after creep is similar to that of other 9%-12%Cr ferritic steels.Thus,ZG12Cr9 MolColNiVNbNB can be used in the project.
基金supported in part by the NASA Fundamental Aeronautics ProgramSupersonics Project and the NASA EPSCOR program(Grant No.NNX11AQ31A)RFBR Project(Grant No.10-03-0154-a)
文摘The shape memory behavior of [111]-oriented Ni_（51）Ti_（49） （at.%） single crystals was investigated after stressassisted aging at 500 °C for 1.5 h under a compressive stress of-150 MPa.It was found that a single family of Ni_4Ti_3 precipitates with two crystallographically equivalent variants was formed after aging under compressive stress.Stressassisted aging resulted in tensile two-way shape memory effect strain of 1.56% under-5 MPa.Thermal cycling under-600 MPa resulted in a transformation strain of-2.15%,while the subsequent thermal cycling under-5 MPa resulted in a tensile two-way shape memory effect strain of 2.2%.
基金Project(2006AA03Z517)supported by the National High-tech Research and Development Program of ChinaProject(CSUZC2013019)supported by Open Fund for the Precision Instruments of Central South University,China
文摘The effects of pre-aging treatments on subsequent artificial aging response were investigated by means of transmission electron microscopy observations and hardness test in age hardened Al-3.95Cu-(1.32Mg)-0.52Mn-0.11 Zr alloys. In Al-3.95Cu-0.52Mn-0.11 Zr alloy, when the pre-aging temperature is 25 °C, the pre-aging treatment has no evident effect on the peak hardness of subsequent artificial aging, while a positive effect(increase of peak hardness) appears when pre-aging temperature is50 °C. However, in Al-3.95Cu-1.32Mg-0.52Mn-0.11 Zr alloy, it is found that whether the pre-aging temperature is 25 °C or 50 °C,the peak artificial aging hardness is lower than that of T6 treated alloy, that is to say, pre-aging treatment has a negative effect on the peak hardness of subsequent artificial aging in the alloys.
基金the National Key Research and Development Program of China(No.2016YFB0701201)the National Natural Science Foundation of China(No.52071011)for the financial supports.
文摘Based on the available experimental phase equilibrium relations and aging precipitation sequences,the Mg–Gd–Y ternary system has been thermodynamically re-assessed by means of CALPHAD technique.To simulate the experimentally reported aging precipitation sequence,α(Mg)_(SS)(supersaturated)→GP zones(D019-type,metastable)→β’-Mg_(7)Gd(c-bco,metastable)→β_(1)-Mg_(3)Gd(fcc,metastable)→β-Mg_(5)Gd(fcc,stable)near the Mg–Gd side,andα(Mg)SS(supersaturated)→β’-Mg_(7)Y(c-bco,metastable)→β-Mg_(24)Y_(5)(bcc,stable)near the Mg–Y side,the effective nucleation driving forces obtained by deducting the nucleation resistances from the thermodynamic driving forces are calculated and analyzed.Two metastable components,GP zones(D019-type)andβ’(c-bco)ordered fromα(Mg)_(SS),do not exist in the stable equilibrium phase diagram but appear in the annealing process of typical alloys.The Redlich–Kister equations are adopted to describe three solution phases,Liquid,HCP_A3 and BCC_A2.The intermediate compounds Mg_(2)Y,Mg_(24)Y_(5),Mg_(2)Gd,Mg_(3)Gd and Mg_(5)Gd are expressed by the formulas of(Mg,Y)_(2/3)(Gd,Mg,Y)_(1/3),Mg_(24/29)(Gd,Mg,Y)_(4/29)Y1/29,(Gd,Mg)_(2/3)(Gd,Mg,Y)_(1/3),(Gd,Mg)_(3/4)(Gd,Mg,Y)_(1/4)and Mg_(5/6)(Gd,Mg,Y)_(1/6),respectively.In particular,the two-sublattice models(Gd,Mg,Y)_(1/2)(Gd,Mg,Y)_(1/2),(Gd,Mg,Y)_(3/4)(Gd,Mg,Y)_(1/4)and(Gd,Mg,Y)_(7/8)(Gd,Mg,Y)_(1/8)have been respectively used to describe the stable Mg(Gd,Y)(BCC_B2)alloy compound as well as the metastable GP zones(D019-type)andβ’(c-bco)phase,in order to cope with the order-disorder transitions.A set of self-consistent thermodynamic parameters has been obtained to ensure the thermodynamic calculations well consistent with the reported experimental data,containing not only the stable equilibrium phase diagram but also the aging precipitation sequence.
基金Project(2023GK2020)supported by the Key Research and Development Program of Hunan Province,China。
文摘Microstructure and mechanical properties of aged Mg-10Gd-2Y-0.4Zr-0.4Ag alloy sheets prepared by different rolling routes were investigated.The results showed that the cross rolling aged(CRA)sheet possesses larger grain size than unidirectional rolling aged(URA)sheet due to the occurrence of dynamic recovery during rolling which reduces the dislocation density and delays dynamic recrystallization(DRX).The URA sheet has basal texture and RD favored texture while CRA sheet has multiple-peak texture.Both sheets precipitate β'phase and CRA sheet exhibits a stronger aging response.The CRA sheet has higher yield strength and tensile strength than URA sheet,with reduced yield strength anisotropy but increased tensile strength anisotropy.Taking into account different strengthening mechanisms,although the finer grain size of URA sheet enhances grain boundary strengthening,CRA sheet is more responsive to aging,leading to superior aging-precipitated phase strengthening and consequently higher yield strength.
基金the National Natural Science Foundation of China (No. 50571081)the Aeronautical Science Foundation of China (No. 04G53042) for financial support
文摘The mechanical properties (σb,σ0.2,and δ) and fracture behavior of tensile specimens of the refined A356 alloys were investigated as a function of the addition level of Al-Ti-B master alloy under both as-cast and T6 heat-treated conditions. The results show that as the addition level of Al-5Ti-1B master alloy increases from 0.1 wt.% to 5.0 wt.%,the mechanical properties of refined A356 alloys improve steadily and then decrease slightly under both as-cast and T6 heat-treated conditions. Also,they display exc...
基金funded by National Natural Science Foundation of China(Project No.51701172)Foundation of China Railway Eryuan Engineering Group Co.Ltd.(Project No.KYY2020035(21-21))+1 种基金Natural Science Foundation of Hunan Province(Project No.2018JJ3504)China Postdoctoral Science Foundation(Project No.2018M632977).
文摘The microstructure evolution and mechanical properties of Mg–6Zn–0.5Ce–xMn(x=0 and 1 wt.%)wrought magnesium alloys were researched,and the morphologies and role of Mn element in the experimental alloys were analyzed.The research shows that all of Mn elements form theα-Mn pure phases,which do not participate in the formation of other phases,such as theτ-phases.The mechanical properties of Mn-containing alloys in as-extruded and aged states are superior to Mn-free alloys.During the hot extrusion process,the dispersed fineα-Mn particle phase hinders the migration of grain boundaries and inhibits dynamic recrystallization,which mainly takes effect of grain refining and dispersion hardening.During the aging treatments,the dispersed fineα-Mn particle phase not only hinders the growth of the solution-treated grains,but also becomes the nucleation cores ofβ1 rod-like precipitate phase,which is conducive to increasing the nucleation rate of the precipitate phase.For the aged alloy,the Mn addition mainly takes effect of grain refining and promoting aging strengthening.