An energy-efficient route was adopted to treat titanium-bearing blast furnace slag(TBBFS)in this study.Titanium,aluminum,and magnesium were simultaneously extracted and silicon was separated by low temperature sulfuri...An energy-efficient route was adopted to treat titanium-bearing blast furnace slag(TBBFS)in this study.Titanium,aluminum,and magnesium were simultaneously extracted and silicon was separated by low temperature sulfuric acid curing and low concentration sulfuric acid leaching.The process parameters of sulfuric acid curing TBBFS were systematically studied.Under the optimal conditions,the recovery of titanium,aluminum,and magnesium reached 85.96%,81.17%,and 93.82%,respectively.The rapid leaching model was used to limit the dissolution and polymerization of silicon,and the dissolution of silicon was only 3.18%.The mechanism of sulfuric acid curing-leaching was investigated.During the curing process,the reaction occurred rapidly and released heat massively.Under the attack of hydrogen ions,the structure of TBBFS was destroyed,silicate was depolymerized to form filterable silica,and titanium,magnesium,aluminum,and calcium ions were replaced to form sulfates and enriched on the surface of silica particles.Titanium,aluminum,and magnesium were recovered in the leaching solution,and calcium sulfate and silica were enriched in the residue after leaching.This method could effectively avoid the formation of silica sol during the leaching process and accelerate the solid-liquid separation.展开更多
With the natural rosin derivative （maleopimaric acid, MPA） as the raw material, imide modified vinyl poly（dimethylsiloxane） （MP-VMS） was synthesized and characterized by ^1H NMR and ^13C NMR. The curing kinetic ...With the natural rosin derivative （maleopimaric acid, MPA） as the raw material, imide modified vinyl poly（dimethylsiloxane） （MP-VMS） was synthesized and characterized by ^1H NMR and ^13C NMR. The curing kinetic parameters of MP-VMS were determined by differential scanning calorimetry （DSC） at various heating rates （5, 8, 10, 15 ℃/min） from the Kissingner, Ozawa and Crane methods. The activation energy （Ea）, pre-exponential factor （A） and reaction order （n） were respectively 18.6 kJ/mol, 71,108 and 0.902. The low-temperature and high-temperature resistance of its curing product were respectively investigated by DSC and thermogravimetric analysis. The results showed that incorporation of MPA could significantly improve the thermal stability of silicone while had no effect on the low-temperature resistance, and the Tmax （the temperature corresponding to the maximum weight loss rate） increased by 70.7 ℃.展开更多
基金financially supported by the National Key Projects for Fundamental Research and Development of China(No.2016YFB0600904)the Sichuan University-Panzhihua city joint strategic cooperation special fund project,China(No.2018CDPZH-7)。
文摘An energy-efficient route was adopted to treat titanium-bearing blast furnace slag(TBBFS)in this study.Titanium,aluminum,and magnesium were simultaneously extracted and silicon was separated by low temperature sulfuric acid curing and low concentration sulfuric acid leaching.The process parameters of sulfuric acid curing TBBFS were systematically studied.Under the optimal conditions,the recovery of titanium,aluminum,and magnesium reached 85.96%,81.17%,and 93.82%,respectively.The rapid leaching model was used to limit the dissolution and polymerization of silicon,and the dissolution of silicon was only 3.18%.The mechanism of sulfuric acid curing-leaching was investigated.During the curing process,the reaction occurred rapidly and released heat massively.Under the attack of hydrogen ions,the structure of TBBFS was destroyed,silicate was depolymerized to form filterable silica,and titanium,magnesium,aluminum,and calcium ions were replaced to form sulfates and enriched on the surface of silica particles.Titanium,aluminum,and magnesium were recovered in the leaching solution,and calcium sulfate and silica were enriched in the residue after leaching.This method could effectively avoid the formation of silica sol during the leaching process and accelerate the solid-liquid separation.
基金supported by the National Natural Science Foundation of China(No.31200446)
文摘With the natural rosin derivative （maleopimaric acid, MPA） as the raw material, imide modified vinyl poly（dimethylsiloxane） （MP-VMS） was synthesized and characterized by ^1H NMR and ^13C NMR. The curing kinetic parameters of MP-VMS were determined by differential scanning calorimetry （DSC） at various heating rates （5, 8, 10, 15 ℃/min） from the Kissingner, Ozawa and Crane methods. The activation energy （Ea）, pre-exponential factor （A） and reaction order （n） were respectively 18.6 kJ/mol, 71,108 and 0.902. The low-temperature and high-temperature resistance of its curing product were respectively investigated by DSC and thermogravimetric analysis. The results showed that incorporation of MPA could significantly improve the thermal stability of silicone while had no effect on the low-temperature resistance, and the Tmax （the temperature corresponding to the maximum weight loss rate） increased by 70.7 ℃.