ZrO2-Y2O3 ceramic coating was produced by plasma electrolytic oxidation （PEO） on ZAlSil2Cu3Ni2 alloy. The microstructure and phase composition of the coating were investigated by SEM and XRD.： The results show that...ZrO2-Y2O3 ceramic coating was produced by plasma electrolytic oxidation （PEO） on ZAlSil2Cu3Ni2 alloy. The microstructure and phase composition of the coating were investigated by SEM and XRD.： The results show that adding an appropriate amount of yttrium ion can improve the growing rate of ceramic coating at different oxidation stages and decrease arc voltage. The thickness of ZrO2-Y2O3 coating is 16 μn thicker than that of ZrO2 coating and the maximum oxidation rate improves by 0.6 μm/min. In addition, the arc voltage decreases from 227 to 172 V. It can be seen that the rate of oxidation firstly increases to some extent and then decreases with the content of yttrium ion increasing. The growth rate reaches the maximum while the content of yttrium ion is 0.05 g-L-1The maximum thickness is 90 μm.Compared to ZrO2 coating, the micropores of ZrO2-Y2O3 coating are less and the ceramic layer is repeatedly deposited by ZrO2 and Y2O3 ceramic particles. Meanwhile, the binding force between coating and substrate is better and the coating is uniform and compact. The ceramic layer is mainly composed of c-Y0.15Zr0.85O1.93□0.07, m-ZrO2, α-Al2O3, ,γ-Al2O3 and Y2O3. It is indicated that ZrO2 has beert fully stabilized by yttrium ion through the formation of solid solution.展开更多
Agglomeration-free nanosized ZrO2-HfO2-Y2O3-Sc2O3 composite powders were successfully synthesized by Sol-Gel technique in heated aqueous solution of alcohol, using analytically pure ZrOCl2 · 8H2O, HfOCl2·8H2...Agglomeration-free nanosized ZrO2-HfO2-Y2O3-Sc2O3 composite powders were successfully synthesized by Sol-Gel technique in heated aqueous solution of alcohol, using analytically pure ZrOCl2 · 8H2O, HfOCl2·8H2O, Y（NO3）3·6H2O, and Sc2O3 as raw materials. The effect of synthesis condition on the size and dispersity of the composite powders was investigated by means of XRD, TEM, and TG-DSC techniques. The results showed that well-dispersed predecessor of ZrO2-HfO2-Y2O3-Sc2O3 composite nanopowders could be obtained. The optional condition ： PEG6000 as dispersant was 1%, alcohol/H2O ratio was 5/1, metallic ion concentration in whole solution was 0.5 mol·L^-1 and the pH value of the solution was 12. After calcined at 620 ℃, the powder obtained was in uniform cubic structure, and its average particle size was about 13 nm, which was good for producing nanocrystalline solid electrolyte.展开更多
以纳米ZrO 、微米Al O 为原料,采用无压烧结方式制备了ZTA 复相陶瓷。结果表明:nano-ZrO 的 2 2 3 2加入有利于制备细晶ZTA 复相陶瓷。此外,nano-ZrO 的加入对 Al O 陶瓷的显微结构也产生影响,ZrO ...以纳米ZrO 、微米Al O 为原料,采用无压烧结方式制备了ZTA 复相陶瓷。结果表明:nano-ZrO 的 2 2 3 2加入有利于制备细晶ZTA 复相陶瓷。此外,nano-ZrO 的加入对 Al O 陶瓷的显微结构也产生影响,ZrO 颗粒以 2 2 3 2“晶内型”和晶界型两种形式存在。合理的配方组成及制备工艺有利于 Z r O 以四方亚稳相存在。Z r O 含量为 2 23 0 w t % 时,其四方相含量可达 6 9 %,有利于应力诱导相变增韧,该 Z T A 复相陶瓷的抗弯强度、断裂韧性分别达到 604MPa、6.87MPa·m1/2。展开更多
基金Funded by the National Natural Science Foundation of China(No.51401155)the School Foundation(No.XAGDXJJ1012)The Open Fund of Shaanxi Key Laboratory of Photoelectric Functional Materials and Devices(No.ZSKJ201416)
文摘ZrO2-Y2O3 ceramic coating was produced by plasma electrolytic oxidation （PEO） on ZAlSil2Cu3Ni2 alloy. The microstructure and phase composition of the coating were investigated by SEM and XRD.： The results show that adding an appropriate amount of yttrium ion can improve the growing rate of ceramic coating at different oxidation stages and decrease arc voltage. The thickness of ZrO2-Y2O3 coating is 16 μn thicker than that of ZrO2 coating and the maximum oxidation rate improves by 0.6 μm/min. In addition, the arc voltage decreases from 227 to 172 V. It can be seen that the rate of oxidation firstly increases to some extent and then decreases with the content of yttrium ion increasing. The growth rate reaches the maximum while the content of yttrium ion is 0.05 g-L-1The maximum thickness is 90 μm.Compared to ZrO2 coating, the micropores of ZrO2-Y2O3 coating are less and the ceramic layer is repeatedly deposited by ZrO2 and Y2O3 ceramic particles. Meanwhile, the binding force between coating and substrate is better and the coating is uniform and compact. The ceramic layer is mainly composed of c-Y0.15Zr0.85O1.93□0.07, m-ZrO2, α-Al2O3, ,γ-Al2O3 and Y2O3. It is indicated that ZrO2 has beert fully stabilized by yttrium ion through the formation of solid solution.
基金Project supported by the National Natural Science Foundation of China (20101006)Nano Technology Special Foundationof Shanghai Science and Technology Committee (0452nm073) and Shanghai Education Committee
文摘Agglomeration-free nanosized ZrO2-HfO2-Y2O3-Sc2O3 composite powders were successfully synthesized by Sol-Gel technique in heated aqueous solution of alcohol, using analytically pure ZrOCl2 · 8H2O, HfOCl2·8H2O, Y（NO3）3·6H2O, and Sc2O3 as raw materials. The effect of synthesis condition on the size and dispersity of the composite powders was investigated by means of XRD, TEM, and TG-DSC techniques. The results showed that well-dispersed predecessor of ZrO2-HfO2-Y2O3-Sc2O3 composite nanopowders could be obtained. The optional condition ： PEG6000 as dispersant was 1%, alcohol/H2O ratio was 5/1, metallic ion concentration in whole solution was 0.5 mol·L^-1 and the pH value of the solution was 12. After calcined at 620 ℃, the powder obtained was in uniform cubic structure, and its average particle size was about 13 nm, which was good for producing nanocrystalline solid electrolyte.
文摘以纳米ZrO 、微米Al O 为原料,采用无压烧结方式制备了ZTA 复相陶瓷。结果表明:nano-ZrO 的 2 2 3 2加入有利于制备细晶ZTA 复相陶瓷。此外,nano-ZrO 的加入对 Al O 陶瓷的显微结构也产生影响,ZrO 颗粒以 2 2 3 2“晶内型”和晶界型两种形式存在。合理的配方组成及制备工艺有利于 Z r O 以四方亚稳相存在。Z r O 含量为 2 23 0 w t % 时,其四方相含量可达 6 9 %,有利于应力诱导相变增韧,该 Z T A 复相陶瓷的抗弯强度、断裂韧性分别达到 604MPa、6.87MPa·m1/2。