A novel solid superacid catalyst S2O8^2-/ZrO2-CeO2 was prepared by a coprecipitation method and characterized by means of XRD FTIR, BET, TEM and DSC/TG analysis methods. The results indicated that incorporation of app...A novel solid superacid catalyst S2O8^2-/ZrO2-CeO2 was prepared by a coprecipitation method and characterized by means of XRD FTIR, BET, TEM and DSC/TG analysis methods. The results indicated that incorporation of appropriate amounts of Ce into the catalyst was beneficial to the formation of sole tetragonal ZrO2 and effectively prevented from the formation of monoclinic ZrO〉 and restrained the loss of sulfated species. XRD revealed the presence of tetragonal Ce0.16Zr0.84O2phase in the case of S2O8^2-/ZrO2-CeO2 calcined above 500 ℃. Catalytic activities of S2O8^2-/ZrO2-CeO2 for the esterification of lactic acid with n-butanol was studied. The results showed that the optimum conditions were as follows： calcination temperature of the catalyst 600 ℃, n（lactic acid）：n（n-butyl alcohol）=1.0：3.0, w（S2O8^2-/ZrO2- CeO2）=12.0%, reaction temperature 145 ℃, and reaction time 2 h. The esterification efficiency of lactic acid was about 96.6%.展开更多
The significant decrease of acid sites caused by alkali metal poisoning is the major factor in the deactivation of commercial V_(2)O_(5)-WO_(3)/TiO_(2)NH_(3)-SCR catalysts.In this work,the solid superacid SO_(4)^(2-)-...The significant decrease of acid sites caused by alkali metal poisoning is the major factor in the deactivation of commercial V_(2)O_(5)-WO_(3)/TiO_(2)NH_(3)-SCR catalysts.In this work,the solid superacid SO_(4)^(2-)-TiO_(2) modified by sulfate radicals,was selected as the catalyst support,which showed superior potassium resistance.The physicochemical properties and K-poisoning resistance of the V_(2)O_(5)-WO_(3)/SO_(4)^(2-)-TiO_(2)(VWSTi) catalyst were carried out by XRD,BET,H2-TPR,NH3-TPD,XPS,in situ DRIFTS and TG.The results pointed out that the introduction of SO_(4)^(2-)significantly increased the NH3-SCR catalytic activity at high temperatures,with an exceptionally high NO_(x) conversion over 90% between 275℃ and 500℃.When 0.5%(mass) K_(2)O was doped on the catalysts,the catalytic performance of the traditional V_(2)O_(5)-WO_(3)/TiO_(2)(VWTi) catalyst decreased significantly,while the VWSTi catalyst could still maintain a NOxconversion over 90%in the range of 300–500℃.The characterizations suggested that the support of SO_(4)^(2-)-TiO_(2) greatly increased the number of acidic sites,thereby enhancing the adsorption capacity of the reactant NH_(3).The results above demonstrated a potential approach to achieve superior potassium resistance for NH3-SCR catalysts using solid superacid.展开更多
A solid superacid catalyst Pt-SO42-/ZrO2-A12O3 for n-pentane isomerization, was prepared by incipient-wetness impregnation. Preparetion conditions, namely, calcination temperature, concentration of sulfuric acid solut...A solid superacid catalyst Pt-SO42-/ZrO2-A12O3 for n-pentane isomerization, was prepared by incipient-wetness impregnation. Preparetion conditions, namely, calcination temperature, concentration of sulfuric acid solution used in impregnation and Al2O3 concentration, were varied to investigate the effects on catalytic performance of Pt-SO42-/ZrO2-A12O3. The results showed that the PtSZA catalyst exhibited excellent catalytic performance for n-pentane isomerization. Under optimized preparation conditions of calcination temperature of 650°C, reaction time for 3 h, concentration of sulfuric acid solution for 0.5 mol/L, 30% of Al2O3 concentration and 0.3% of Pt concentration, the n-pentane conversion and isopentane selectivity of Pt-SO42-/ZrO2-A12O3 could reach up to 62.17% and 91.60%, respectively.展开更多
Sulfated zirconia-lanthana （SO4^2-/ZrO2-La2O3） precursors were prepared by ultrasonic coprecipitation method and followed by aging at different temperature. The precursors were treated by 0.5 mol/L H2SO4. Samples of...Sulfated zirconia-lanthana （SO4^2-/ZrO2-La2O3） precursors were prepared by ultrasonic coprecipitation method and followed by aging at different temperature. The precursors were treated by 0.5 mol/L H2SO4. Samples of SO4^2-/ZrO2-La2O3 nano-crystalline catalysts were obtained by baking the treated precursors at different temperatures. The acidic properties of SO4^2-/ZrO2-La2O3 were tested by the Hammett indicator method. The phase composition, specific area, particle structure, and surface state were characterized by X-ray diffraction, BET, transmission electron microscopy, infrared spectrum, and X-ray photoelectron spec- troscopy. The catalytic activities were estimated by esterification of acetic acid with glycerin. It was shown that the catalyst prepared by ultrasonic stirring and low temperature （-15 ℃） exhibited highly active sites and high catalytic property.展开更多
基金supported by the Science and Technique Foundation of Shaaxi Province of China (2008K07-32)the Foundation of Shaanxi Educa- tional Committee of China (08JK228)the Graduate Innovation Fund of Shaanxi University of Science and Technology
文摘A novel solid superacid catalyst S2O8^2-/ZrO2-CeO2 was prepared by a coprecipitation method and characterized by means of XRD FTIR, BET, TEM and DSC/TG analysis methods. The results indicated that incorporation of appropriate amounts of Ce into the catalyst was beneficial to the formation of sole tetragonal ZrO2 and effectively prevented from the formation of monoclinic ZrO〉 and restrained the loss of sulfated species. XRD revealed the presence of tetragonal Ce0.16Zr0.84O2phase in the case of S2O8^2-/ZrO2-CeO2 calcined above 500 ℃. Catalytic activities of S2O8^2-/ZrO2-CeO2 for the esterification of lactic acid with n-butanol was studied. The results showed that the optimum conditions were as follows： calcination temperature of the catalyst 600 ℃, n（lactic acid）：n（n-butyl alcohol）=1.0：3.0, w（S2O8^2-/ZrO2- CeO2）=12.0%, reaction temperature 145 ℃, and reaction time 2 h. The esterification efficiency of lactic acid was about 96.6%.
基金supported by the National Natural Science Foundation of China (22108184)China Postdoctoral Science Foundation (2021TQ0221)+1 种基金the Sichuan Science and Technology Program (2021JDRC0117)Chengdu Science and Technology Program (2021-YF05-00378-SN)。
文摘The significant decrease of acid sites caused by alkali metal poisoning is the major factor in the deactivation of commercial V_(2)O_(5)-WO_(3)/TiO_(2)NH_(3)-SCR catalysts.In this work,the solid superacid SO_(4)^(2-)-TiO_(2) modified by sulfate radicals,was selected as the catalyst support,which showed superior potassium resistance.The physicochemical properties and K-poisoning resistance of the V_(2)O_(5)-WO_(3)/SO_(4)^(2-)-TiO_(2)(VWSTi) catalyst were carried out by XRD,BET,H2-TPR,NH3-TPD,XPS,in situ DRIFTS and TG.The results pointed out that the introduction of SO_(4)^(2-)significantly increased the NH3-SCR catalytic activity at high temperatures,with an exceptionally high NO_(x) conversion over 90% between 275℃ and 500℃.When 0.5%(mass) K_(2)O was doped on the catalysts,the catalytic performance of the traditional V_(2)O_(5)-WO_(3)/TiO_(2)(VWTi) catalyst decreased significantly,while the VWSTi catalyst could still maintain a NOxconversion over 90%in the range of 300–500℃.The characterizations suggested that the support of SO_(4)^(2-)-TiO_(2) greatly increased the number of acidic sites,thereby enhancing the adsorption capacity of the reactant NH_(3).The results above demonstrated a potential approach to achieve superior potassium resistance for NH3-SCR catalysts using solid superacid.
文摘A solid superacid catalyst Pt-SO42-/ZrO2-A12O3 for n-pentane isomerization, was prepared by incipient-wetness impregnation. Preparetion conditions, namely, calcination temperature, concentration of sulfuric acid solution used in impregnation and Al2O3 concentration, were varied to investigate the effects on catalytic performance of Pt-SO42-/ZrO2-A12O3. The results showed that the PtSZA catalyst exhibited excellent catalytic performance for n-pentane isomerization. Under optimized preparation conditions of calcination temperature of 650°C, reaction time for 3 h, concentration of sulfuric acid solution for 0.5 mol/L, 30% of Al2O3 concentration and 0.3% of Pt concentration, the n-pentane conversion and isopentane selectivity of Pt-SO42-/ZrO2-A12O3 could reach up to 62.17% and 91.60%, respectively.
文摘Sulfated zirconia-lanthana （SO4^2-/ZrO2-La2O3） precursors were prepared by ultrasonic coprecipitation method and followed by aging at different temperature. The precursors were treated by 0.5 mol/L H2SO4. Samples of SO4^2-/ZrO2-La2O3 nano-crystalline catalysts were obtained by baking the treated precursors at different temperatures. The acidic properties of SO4^2-/ZrO2-La2O3 were tested by the Hammett indicator method. The phase composition, specific area, particle structure, and surface state were characterized by X-ray diffraction, BET, transmission electron microscopy, infrared spectrum, and X-ray photoelectron spec- troscopy. The catalytic activities were estimated by esterification of acetic acid with glycerin. It was shown that the catalyst prepared by ultrasonic stirring and low temperature （-15 ℃） exhibited highly active sites and high catalytic property.