ZrO2-SiC composite powder was synthesized by carbothermal reduction of zircon in argon atmosphere, and it was used as the additive to prepare Al2O3-C refractories. The effects of heating temperature on the synthesis p...ZrO2-SiC composite powder was synthesized by carbothermal reduction of zircon in argon atmosphere, and it was used as the additive to prepare Al2O3-C refractories. The effects of heating temperature on the synthesis process and the addition of the synthesized composite powder on the properties of the Al2O3-C refractories were investigated. The results show that the synthesized composite powder can be easily obtained by heating the mixture of zircon and carbon black at 1 873 K for 4 h in argon atmosphere, and the relative contents of ZrO2 and SiC in sample reach about 83.7% and 16.3%, respectively. The bulk density, crushing strength and thermal shock resistance of the Al2O3-C refractories can be improved obviously by the addition of the synthesized ZrO2-SiC composite powder.展开更多
Zircon （mesh size ≤ 44μm ） and carbon black （mesh size ≤30μm ） were used as the starting materials, weighed with re（zircon） ： re（carbon black） of 100 ： 20 and mixed fully. The specimens with the diameter...Zircon （mesh size ≤ 44μm ） and carbon black （mesh size ≤30μm ） were used as the starting materials, weighed with re（zircon） ： re（carbon black） of 100 ： 20 and mixed fully. The specimens with the diameter of 20ram and length of 5ram were prepared by pressing at 100 MPa, then dried at 120℃ for 12h, put into a furnace with 1. 5L ·min^-1 argon gas and fired at 1450℃, 1500℃, 1550℃, 1600℃ and 1650℃ for 4h, respectively. The chemical composition, phase composition and microstructure of the specimens were studied by chemical analysis, X-ray diffraction and scanning electronic microscope, and the carbothermal reduction reaction process was discussed by thermodynamic analysis. The results showed that the ZrO2-SiC composite could be synthesized by carbothermal reduction reaction using zircon and carbon black as the starting materials in argon atmosphere. The composite with different composition was obtained by controlling the firing temperature and partial pressure of CO gas. The proper temperature to synthesize ZrO2-SiC composite was 1600℃ in this experiment.展开更多
To improve the oxidation resistance of carbon/carbon （C/C） composites in air at high temperatures, a SiC- MoSi2/ZrO2-MoSi2 coating was prepared on the surface of C/C composites by pack cementation and slurry method....To improve the oxidation resistance of carbon/carbon （C/C） composites in air at high temperatures, a SiC- MoSi2/ZrO2-MoSi2 coating was prepared on the surface of C/C composites by pack cementation and slurry method. The microstructures and phase compositions of the coated C/C composites were analyzed by scanning electron microscopy and X-ray diffraction, respectively. The result shows that the SiC-MoSi2/ZrO2-MoSi2 coating is dense and crack-free with a thickness of 250-300 μm. The preparation and the high temperature oxidation property of the coated composites were investigated. The as-received coating has excellent oxidation protection ability and can protect C/C composites from oxidation for 260 h at 1773 K in air. The excellent anti-oxidation performance of the coating is considered to come from the formation of ZrSiO4, which improves the stability of the coating at high temperatures.展开更多
基金Project(50274021) supported by the National Natural Science Foundation of China and Baoshan Iron and Steel Co. Ltd.
文摘ZrO2-SiC composite powder was synthesized by carbothermal reduction of zircon in argon atmosphere, and it was used as the additive to prepare Al2O3-C refractories. The effects of heating temperature on the synthesis process and the addition of the synthesized composite powder on the properties of the Al2O3-C refractories were investigated. The results show that the synthesized composite powder can be easily obtained by heating the mixture of zircon and carbon black at 1 873 K for 4 h in argon atmosphere, and the relative contents of ZrO2 and SiC in sample reach about 83.7% and 16.3%, respectively. The bulk density, crushing strength and thermal shock resistance of the Al2O3-C refractories can be improved obviously by the addition of the synthesized ZrO2-SiC composite powder.
文摘Zircon （mesh size ≤ 44μm ） and carbon black （mesh size ≤30μm ） were used as the starting materials, weighed with re（zircon） ： re（carbon black） of 100 ： 20 and mixed fully. The specimens with the diameter of 20ram and length of 5ram were prepared by pressing at 100 MPa, then dried at 120℃ for 12h, put into a furnace with 1. 5L ·min^-1 argon gas and fired at 1450℃, 1500℃, 1550℃, 1600℃ and 1650℃ for 4h, respectively. The chemical composition, phase composition and microstructure of the specimens were studied by chemical analysis, X-ray diffraction and scanning electronic microscope, and the carbothermal reduction reaction process was discussed by thermodynamic analysis. The results showed that the ZrO2-SiC composite could be synthesized by carbothermal reduction reaction using zircon and carbon black as the starting materials in argon atmosphere. The composite with different composition was obtained by controlling the firing temperature and partial pressure of CO gas. The proper temperature to synthesize ZrO2-SiC composite was 1600℃ in this experiment.
基金Projects(51221001,51222207)supported by the National Natural Science Foundation of ChinaProject(090677)supported by the Program for New Century Excellent Talents in University of ChinaProject(B08040)supported by Program of Introducing Talents of Discipline to Universities,China
文摘To improve the oxidation resistance of carbon/carbon （C/C） composites in air at high temperatures, a SiC- MoSi2/ZrO2-MoSi2 coating was prepared on the surface of C/C composites by pack cementation and slurry method. The microstructures and phase compositions of the coated C/C composites were analyzed by scanning electron microscopy and X-ray diffraction, respectively. The result shows that the SiC-MoSi2/ZrO2-MoSi2 coating is dense and crack-free with a thickness of 250-300 μm. The preparation and the high temperature oxidation property of the coated composites were investigated. The as-received coating has excellent oxidation protection ability and can protect C/C composites from oxidation for 260 h at 1773 K in air. The excellent anti-oxidation performance of the coating is considered to come from the formation of ZrSiO4, which improves the stability of the coating at high temperatures.