To improve the oxidation resistance of carbon/carbon （C/C） composites in air at high temperatures, a SiC- MoSi2/ZrO2-MoSi2 coating was prepared on the surface of C/C composites by pack cementation and slurry method....To improve the oxidation resistance of carbon/carbon （C/C） composites in air at high temperatures, a SiC- MoSi2/ZrO2-MoSi2 coating was prepared on the surface of C/C composites by pack cementation and slurry method. The microstructures and phase compositions of the coated C/C composites were analyzed by scanning electron microscopy and X-ray diffraction, respectively. The result shows that the SiC-MoSi2/ZrO2-MoSi2 coating is dense and crack-free with a thickness of 250-300 μm. The preparation and the high temperature oxidation property of the coated composites were investigated. The as-received coating has excellent oxidation protection ability and can protect C/C composites from oxidation for 260 h at 1773 K in air. The excellent anti-oxidation performance of the coating is considered to come from the formation of ZrSiO4, which improves the stability of the coating at high temperatures.展开更多
To improve the oxidation resistance of carbon/carbon composites,ZrB2-MoSi2/SiC coating on the carbon/carbon substrate was prepared.The inner coating of SiC was prepared by pack cementation and the outer coating of ZrB...To improve the oxidation resistance of carbon/carbon composites,ZrB2-MoSi2/SiC coating on the carbon/carbon substrate was prepared.The inner coating of SiC was prepared by pack cementation and the outer coating of ZrB2-MoSi2 was prepared by slurry painting.The phase compositions and microstructures of the coating were characterized by XRD and SEM,respectively.The preparation and the high temperature oxidation property of the coated composites were investigated.The results show that the outer coating of carbon/carbon composites is composed of ZrB2,MoSi2 and SiC phases.The mass losses of the ZrB2-MoSi2/SiC coated samples with SiC nano-whiskers after 30 h and 10 h of oxidation at 1 273 K and 1 773 K were,respectively,5.3% and 3.0%.The ZrB2-MoSi2/SiC coated samples exhibit self-sealing performance and good oxidation resistance at high temperature.展开更多
ZrO2/TiO2 composite photocatalytic film was produced on the pure titanium substrate using in-situ Zr（OH）4 colloidal particle by the micro-arc oxidation technique and characterized by scanning electron microscope （...ZrO2/TiO2 composite photocatalytic film was produced on the pure titanium substrate using in-situ Zr（OH）4 colloidal particle by the micro-arc oxidation technique and characterized by scanning electron microscope （SEM）, energy dispersive X-ray （EDX）, X-ray diffraction （XRD） and ultraviolet-visible （UV-Vis） spectrophotometer. The composite film shows a lamellar and porous structure which consists of anatase, futile and ZrO2 phases. The optical absorption edge of film is shifted to longer wavelength when ZrO2 is introduced to TiO2. Furthermore, the photocatalytic reaction rate constants of degradation of rhodamine B solution with ZrO2/TiO2 composite film and pure TiO2 film under ultraviolet irradiation are measured as 0.0442 and 0.0186 h 1, respectively.展开更多
The deformation behaviors of Al2O3/Al composites were investigated by compressive tests conducted at temperature of 300-450 °C and strain rates of 0.001-1.0 s-1 with Gleeble-1500 D thermal simulator system. The r...The deformation behaviors of Al2O3/Al composites were investigated by compressive tests conducted at temperature of 300-450 °C and strain rates of 0.001-1.0 s-1 with Gleeble-1500 D thermal simulator system. The results show that the flow stress increases with increasing strain rate and decreasing temperature. The hyperbolic sine constitutive equation can describe the flow stress behavior of Al2O3/Al composites, and the deformation activation energy and constitutive equations were calculated. The processing maps of Al2O3/Al-2 μm and Al2O3/Al-1 μm composites at strain of 0.6 were obtained and the optimum processing domains are in ranges of 300-330 °C, 0.007-0.03 s-1 and 335-360 °C, 0.015-0.06 s-1 for hot working, respectively. The instability zones of flow behavior can also be recognized by the maps.展开更多
Composite powder prepared of calcium oxide stabilzed ZrO2(CSZ) and NiCr by vacuum sintering is studied,and the effect of additive TiO2 on its properties is discussed. The morphology and phases of the powder were measu...Composite powder prepared of calcium oxide stabilzed ZrO2(CSZ) and NiCr by vacuum sintering is studied,and the effect of additive TiO2 on its properties is discussed. The morphology and phases of the powder were measured and determined by SEM. EPMA, XRD methods and the testing of flowability, bulk density and microhard-ness. The results show that the metallic components in the powder are in homogeneous distribution , the flowability, bulk density and microhardness are superior to the ZrO2-NiCr powder prepared by mechanically mixing. All components in the coating made of the composite powder are well-distributed because of avoiding segregation in the middle of mixing. It proves that the composite powder is an excellent material for plasma spraying.展开更多
The interfacial interaction existing in the Ni ZrO 2 composite plating has been investigated. The experimental results show that no new phases were formed in the interfacial regions between matrix Ni and ZrO 2 part...The interfacial interaction existing in the Ni ZrO 2 composite plating has been investigated. The experimental results show that no new phases were formed in the interfacial regions between matrix Ni and ZrO 2 particles, but an orbital interaction through the mutual overlap of the d orbits does exist in the interfacial regions between Ni atoms and Zr 3+ ions.展开更多
The cermet composites WC-20wt%Co/ZrO2（E6）with four different comtents of ZrO2（3Y）were prepared by normal vacuum sinter processing;the optical microscope and SEMwere used to characterize their microstructures.The h...The cermet composites WC-20wt%Co/ZrO2（E6）with four different comtents of ZrO2（3Y）were prepared by normal vacuum sinter processing;the optical microscope and SEMwere used to characterize their microstructures.The hardness.bending strength and impact toughness of the specimens were determined.The experimental results show that ZrO2（3Y） particles in WC-20wt%Co matrix are sphcrical particles in different sizes which are distributed uniformly in Co phases and WC phases,the bending strength and impact toughness of the WC-20wt%Co cermet composites added ZrO2（3Y）improve remarkably.but the hardness values have little change.展开更多
The effects of microwave sintering on the properties, phases and microstructure of W-2OCu alloy, using composite powder fabricated by spray pyrolysis-continuous reduction technology, were investigated. Compared with t...The effects of microwave sintering on the properties, phases and microstructure of W-2OCu alloy, using composite powder fabricated by spray pyrolysis-continuous reduction technology, were investigated. Compared with the conventional hot-press sintering, microwave sintering to W-2OCu composites could be achieved with lower sintering temperature and shorter sintering time. Furthermore, microwave sintered W-Cu composites with high densification, homogenous microstructure and excellent properties were obtained. Microwave sintering could also result in finer microstructures. ：~展开更多
W-2 wt.%Y2O3 composite material with uniform distribution of yttrium element was fabricated through processes of mechanical alloying （MA） and spark plasma sintering （SPS）. The relevant productions were characteriz...W-2 wt.%Y2O3 composite material with uniform distribution of yttrium element was fabricated through processes of mechanical alloying （MA） and spark plasma sintering （SPS）. The relevant productions were characterized by scanning electron microscopy （SEM）, energy dispersive spectroscopy （EDS）, X-ray diffraction （XRD）, and transmission electron microscopy （TEM）. The XRD showed that the W-2 wt.%Y2O3 composite powder, including tungsten matrix and Y2O3 particles, was refined to nanometer sizes during the MA process. The SEM and TEM micrographs showed that the MA produced composite powder presented a lamellar morphology and contained many dislocations and microcracks. The EDS showed that the Y and O elements were uniformly distributed in the W matrix after mechanically alloying for 15 h. The W-2 wt.%Y2O3 composite material with uniform distribution of yttrium was obtained by sintering of the MA produced composite powder.展开更多
Nanosized ZrO2 powder was prepared by evaporative decomposition of solution（EDS）. The particle size is from 50 nm to 200 nm. This process has such advantages as high purity, precise compositional control, simple pro...Nanosized ZrO2 powder was prepared by evaporative decomposition of solution（EDS）. The particle size is from 50 nm to 200 nm. This process has such advantages as high purity, precise compositional control, simple procedure and successive auto-operating. In this process, mixed solution of zirconium acetate and yttrium nitrate was atomized to from a fine mist and blown into the hot zone from the bottom of furnace. The solution was rapidly decomposed at 900℃ and the powder was collected by a filter system. The powder characteristics can be controlled by adjusting the concentration, droplet volume and decomposition temperature of the solution.展开更多
A lead-free solder composite was prepared by adding ZrO2 nanopowders in eutectic Sn-Ag alloy. Microstrucrural features and microhardness properties of those solders with different ZrO2 nanopowder fraction were examine...A lead-free solder composite was prepared by adding ZrO2 nanopowders in eutectic Sn-Ag alloy. Microstrucrural features and microhardness properties of those solders with different ZrO2 nanopowder fraction were examined. Results indicate that the addition of ZrO2 nanopowders reduced the size of β-Sn grains and restrained the formation of bulk Ag3Sn intermetallic compounds （IMCs） due to the adsorption effect of the ZrO2 particles. The Vicker＇s hardness of the obtained lead-free solder composites fits well with the HalI-Petch relationship. The refinement of β-Sn grains favors to improve the microhardness of composite solders.展开更多
To improve the properties of low-carbonization of MgO–C refractories,the introduction of composite additives is an effective strategy.Al_(2)O_(3)–SiC composite powder was prepared from clay using electromagnetic ind...To improve the properties of low-carbonization of MgO–C refractories,the introduction of composite additives is an effective strategy.Al_(2)O_(3)–SiC composite powder was prepared from clay using electromagnetic induction heating and carbon embedded methods.Further,the Al_(2)O_(3)–SiC composite powder synthesized by electromagnetic induction heating at 600 A was added into low-carbon MgO–C refractories(4 wt.%)to improve their properties.The results showed that when the addition amount of Al_(2)O_(3)–SiC composite powder is within the range of 2.5–5.0 wt.%,the properties of low-carbon MgO–C samples were significantly improved,e.g.,the apparent porosity of 7.58%–8.04%,the bulk density of 2.98–2.99 g cm-3,the cold compressive strength of 55.72–57.93 MPa,the residual strength after three air quenching at 1100°C of 74.86%–78.04%,and the decarburized layer depth after oxidized at 1400°C for 2 h of 14.03–14.87 mm.Consequently,the idea for the rapid synthesis of Al_(2)O_(3)–SiC composite powder provides an alternative low-carbon MgO–C refractories performance optimization strategy.展开更多
Zircon （mesh size ≤ 44μm ） and carbon black （mesh size ≤30μm ） were used as the starting materials, weighed with re（zircon） ： re（carbon black） of 100 ： 20 and mixed fully. The specimens with the diameter...Zircon （mesh size ≤ 44μm ） and carbon black （mesh size ≤30μm ） were used as the starting materials, weighed with re（zircon） ： re（carbon black） of 100 ： 20 and mixed fully. The specimens with the diameter of 20ram and length of 5ram were prepared by pressing at 100 MPa, then dried at 120℃ for 12h, put into a furnace with 1. 5L ·min^-1 argon gas and fired at 1450℃, 1500℃, 1550℃, 1600℃ and 1650℃ for 4h, respectively. The chemical composition, phase composition and microstructure of the specimens were studied by chemical analysis, X-ray diffraction and scanning electronic microscope, and the carbothermal reduction reaction process was discussed by thermodynamic analysis. The results showed that the ZrO2-SiC composite could be synthesized by carbothermal reduction reaction using zircon and carbon black as the starting materials in argon atmosphere. The composite with different composition was obtained by controlling the firing temperature and partial pressure of CO gas. The proper temperature to synthesize ZrO2-SiC composite was 1600℃ in this experiment.展开更多
TiB2-Al2O3 composite powders were produced by self-propagating high-temperature synthesis（SHS） method with reductive process from B2O3-TiO2-AI system. X-ray diffraction（XRD） and scanning electron microscopy（SEM...TiB2-Al2O3 composite powders were produced by self-propagating high-temperature synthesis（SHS） method with reductive process from B2O3-TiO2-AI system. X-ray diffraction（XRD） and scanning electron microscopy（SEM） analyses show the presence of TiB2 and Al2O3 only in the composite powders produced by SHS. The powders are uniform and free-agglomerate. Transmission electron microscopy （TEM） and high resolution electron microscopy （HREM） observation of microstructure of the composite powders indicate that the interfaces of the TiB2-Al2O3 bond well, without any interfacial reaction products. It is proposed that the good interfacial bonding of the composite powders can be resulted from the TiB2 particles crystallizing and growing on the Al2O3 particles surface with surface defects acting as nucleation centers.展开更多
The Ni/ZrO2 was used as raw materials to fabricate the surface infiltrated composite layer with 1-4 mm thickness on cast steel substrate through vacuum infiltrated casting technology. The microstructure indicated that...The Ni/ZrO2 was used as raw materials to fabricate the surface infiltrated composite layer with 1-4 mm thickness on cast steel substrate through vacuum infiltrated casting technology. The microstructure indicated that the infiltrated composite layer included surface composite layer and transition layer. Wear property was investigated under room temperature and 450 ~C. The results indicated that the abrasion volume of substrate was 8 times that of the infiltrated composite layer at room temperature. The friction coefficient of infiltrated composite layer decreased with the increasing load. The wear resistance of infiltrated composite layer with different ZrO2 contents had been improved obviously under high temperature. The friction coefficient of infiltrated composite layer was decreased comparing with that at room temperature. The oxidation, abrasive and fatigue abrasion was the main wear mechanism at room temperature. Oxidation abrasion, fatigue wear and adhesive wear dominated the wearin~ process under elevated temperature.展开更多
TiAl3 particle reinforced pure Al composite has been made by direct reaction among molten Al, TiO2 and a flux. The composite exhibits high Synthetically properties. The strength and hardness are higher than those of p...TiAl3 particle reinforced pure Al composite has been made by direct reaction among molten Al, TiO2 and a flux. The composite exhibits high Synthetically properties. The strength and hardness are higher than those of pure Al matrix by 71.5% and 134% respectively However, the elongation is 20.36%, slightly lower than that of the Al matrix.展开更多
Al 2O 3-SiO 2-TiO 2-ZrO 2 supported membranes were prepar ed by Sol-Gel method. These composite ceramic membranes are level, even and no macro crack. There exist several crystalline phases such as Al 2O 3, TiO...Al 2O 3-SiO 2-TiO 2-ZrO 2 supported membranes were prepar ed by Sol-Gel method. These composite ceramic membranes are level, even and no macro crack. There exist several crystalline phases such as Al 2O 3, TiO 2(a natase), Al 2SiO 5, and ZrO 2 in these membranes. Changing the molar ratio of Al∶Si∶Ti∶Zr,the kinds and content of crystal phases of composite membranes could be different, which may lead to a variety of microstructure of membranes. The surface nanoscale topography and microstructure of membranes were investiga ted by XRD,SEM,AFM,EPMA. The effects of additives and heat treatments on the sur face nanoscale topography and microstructure of composite ceramic membranes were also analyzed.展开更多
This work aims at solving the problems of difficult dispersion,easy oxidation and high cost of nano carbon during application,carbon/magnesium aluminate spinel(C/MgAl_(2)O_(4))composite powders were prepared using MgC...This work aims at solving the problems of difficult dispersion,easy oxidation and high cost of nano carbon during application,carbon/magnesium aluminate spinel(C/MgAl_(2)O_(4))composite powders were prepared using MgC2O4·2H2O,MgO2,Al2O3 powder,and Al powder as raw materials by combustion synthesis.The results indicate that with the maximum MgC2O4·2H2O addition of 33.34 mass%,the prepared powder contains 1.17 mass%of carbon and carbon distributes among spinel grains.The MgAl_(2)O_(4)spinel shows both granular and rod-like morphologies.The granular MgAl_(2)O_(4)spinel is generated from mutual diffusion between MgO and Al2O3;while the rod-like MgAl_(2)O_(4)spinel is mainly formed by the vapor-solid growth mechanism from Mg vapor and Al2O3.展开更多
基金Projects(51221001,51222207)supported by the National Natural Science Foundation of ChinaProject(090677)supported by the Program for New Century Excellent Talents in University of ChinaProject(B08040)supported by Program of Introducing Talents of Discipline to Universities,China
文摘To improve the oxidation resistance of carbon/carbon （C/C） composites in air at high temperatures, a SiC- MoSi2/ZrO2-MoSi2 coating was prepared on the surface of C/C composites by pack cementation and slurry method. The microstructures and phase compositions of the coated C/C composites were analyzed by scanning electron microscopy and X-ray diffraction, respectively. The result shows that the SiC-MoSi2/ZrO2-MoSi2 coating is dense and crack-free with a thickness of 250-300 μm. The preparation and the high temperature oxidation property of the coated composites were investigated. The as-received coating has excellent oxidation protection ability and can protect C/C composites from oxidation for 260 h at 1773 K in air. The excellent anti-oxidation performance of the coating is considered to come from the formation of ZrSiO4, which improves the stability of the coating at high temperatures.
基金Project(50721003) supported by the Innovation Community Foundation of National Natural Science of ChinaProject(2011CB605805) supported by the National Basic Research Program of China
文摘To improve the oxidation resistance of carbon/carbon composites,ZrB2-MoSi2/SiC coating on the carbon/carbon substrate was prepared.The inner coating of SiC was prepared by pack cementation and the outer coating of ZrB2-MoSi2 was prepared by slurry painting.The phase compositions and microstructures of the coating were characterized by XRD and SEM,respectively.The preparation and the high temperature oxidation property of the coated composites were investigated.The results show that the outer coating of carbon/carbon composites is composed of ZrB2,MoSi2 and SiC phases.The mass losses of the ZrB2-MoSi2/SiC coated samples with SiC nano-whiskers after 30 h and 10 h of oxidation at 1 273 K and 1 773 K were,respectively,5.3% and 3.0%.The ZrB2-MoSi2/SiC coated samples exhibit self-sealing performance and good oxidation resistance at high temperature.
基金Project(gf200901002)supported by the Open Research Fund of National Defense Key Disciplines Laboratory of Light Alloy Processing Science and Technology of Nanchang Hangkong University,China
文摘ZrO2/TiO2 composite photocatalytic film was produced on the pure titanium substrate using in-situ Zr（OH）4 colloidal particle by the micro-arc oxidation technique and characterized by scanning electron microscope （SEM）, energy dispersive X-ray （EDX）, X-ray diffraction （XRD） and ultraviolet-visible （UV-Vis） spectrophotometer. The composite film shows a lamellar and porous structure which consists of anatase, futile and ZrO2 phases. The optical absorption edge of film is shifted to longer wavelength when ZrO2 is introduced to TiO2. Furthermore, the photocatalytic reaction rate constants of degradation of rhodamine B solution with ZrO2/TiO2 composite film and pure TiO2 film under ultraviolet irradiation are measured as 0.0442 and 0.0186 h 1, respectively.
基金Project(2012AA030311)supported by the National High-tech Research and Development Program of ChinaProject(2010BB4074)supported by the Natural Science Foundation of Chongqing Municipality,ChinaProject(2010ZD-02)supported by the State Key Laboratory for Advanced Metals and Materials,China
文摘The deformation behaviors of Al2O3/Al composites were investigated by compressive tests conducted at temperature of 300-450 °C and strain rates of 0.001-1.0 s-1 with Gleeble-1500 D thermal simulator system. The results show that the flow stress increases with increasing strain rate and decreasing temperature. The hyperbolic sine constitutive equation can describe the flow stress behavior of Al2O3/Al composites, and the deformation activation energy and constitutive equations were calculated. The processing maps of Al2O3/Al-2 μm and Al2O3/Al-1 μm composites at strain of 0.6 were obtained and the optimum processing domains are in ranges of 300-330 °C, 0.007-0.03 s-1 and 335-360 °C, 0.015-0.06 s-1 for hot working, respectively. The instability zones of flow behavior can also be recognized by the maps.
文摘Composite powder prepared of calcium oxide stabilzed ZrO2(CSZ) and NiCr by vacuum sintering is studied,and the effect of additive TiO2 on its properties is discussed. The morphology and phases of the powder were measured and determined by SEM. EPMA, XRD methods and the testing of flowability, bulk density and microhard-ness. The results show that the metallic components in the powder are in homogeneous distribution , the flowability, bulk density and microhardness are superior to the ZrO2-NiCr powder prepared by mechanically mixing. All components in the coating made of the composite powder are well-distributed because of avoiding segregation in the middle of mixing. It proves that the composite powder is an excellent material for plasma spraying.
文摘The interfacial interaction existing in the Ni ZrO 2 composite plating has been investigated. The experimental results show that no new phases were formed in the interfacial regions between matrix Ni and ZrO 2 particles, but an orbital interaction through the mutual overlap of the d orbits does exist in the interfacial regions between Ni atoms and Zr 3+ ions.
文摘The cermet composites WC-20wt%Co/ZrO2（E6）with four different comtents of ZrO2（3Y）were prepared by normal vacuum sinter processing;the optical microscope and SEMwere used to characterize their microstructures.The hardness.bending strength and impact toughness of the specimens were determined.The experimental results show that ZrO2（3Y） particles in WC-20wt%Co matrix are sphcrical particles in different sizes which are distributed uniformly in Co phases and WC phases,the bending strength and impact toughness of the WC-20wt%Co cermet composites added ZrO2（3Y）improve remarkably.but the hardness values have little change.
基金the Project for Science and Technology Plan of Wuhan City (No. 200910321092)the Youth Science Plan for Light of the Morning Sun of Wuhan City (No. 200750731270)the Fundamental Research Funds for the Central Universities (No. 2010-Ⅱ-020)
文摘The effects of microwave sintering on the properties, phases and microstructure of W-2OCu alloy, using composite powder fabricated by spray pyrolysis-continuous reduction technology, were investigated. Compared with the conventional hot-press sintering, microwave sintering to W-2OCu composites could be achieved with lower sintering temperature and shorter sintering time. Furthermore, microwave sintered W-Cu composites with high densification, homogenous microstructure and excellent properties were obtained. Microwave sintering could also result in finer microstructures. ：~
文摘W-2 wt.%Y2O3 composite material with uniform distribution of yttrium element was fabricated through processes of mechanical alloying （MA） and spark plasma sintering （SPS）. The relevant productions were characterized by scanning electron microscopy （SEM）, energy dispersive spectroscopy （EDS）, X-ray diffraction （XRD）, and transmission electron microscopy （TEM）. The XRD showed that the W-2 wt.%Y2O3 composite powder, including tungsten matrix and Y2O3 particles, was refined to nanometer sizes during the MA process. The SEM and TEM micrographs showed that the MA produced composite powder presented a lamellar morphology and contained many dislocations and microcracks. The EDS showed that the Y and O elements were uniformly distributed in the W matrix after mechanically alloying for 15 h. The W-2 wt.%Y2O3 composite material with uniform distribution of yttrium was obtained by sintering of the MA produced composite powder.
文摘Nanosized ZrO2 powder was prepared by evaporative decomposition of solution（EDS）. The particle size is from 50 nm to 200 nm. This process has such advantages as high purity, precise compositional control, simple procedure and successive auto-operating. In this process, mixed solution of zirconium acetate and yttrium nitrate was atomized to from a fine mist and blown into the hot zone from the bottom of furnace. The solution was rapidly decomposed at 900℃ and the powder was collected by a filter system. The powder characteristics can be controlled by adjusting the concentration, droplet volume and decomposition temperature of the solution.
基金The authors are grateful to the National Natural Science Foundation of China （No. 50401033）FANEDD of China （No. 200335）+1 种基金the Natural Science Foundation of Tianjin City （No. 033608811） Fok Ying Tong Education Foundation （No. 104015） for grant and financial support.
文摘A lead-free solder composite was prepared by adding ZrO2 nanopowders in eutectic Sn-Ag alloy. Microstrucrural features and microhardness properties of those solders with different ZrO2 nanopowder fraction were examined. Results indicate that the addition of ZrO2 nanopowders reduced the size of β-Sn grains and restrained the formation of bulk Ag3Sn intermetallic compounds （IMCs） due to the adsorption effect of the ZrO2 particles. The Vicker＇s hardness of the obtained lead-free solder composites fits well with the HalI-Petch relationship. The refinement of β-Sn grains favors to improve the microhardness of composite solders.
基金This work was financially supported by the National Natural Science Foundation of China(Grant Nos.U20A20239 and U1908227)the Fundamental Research Funds for the Central Universities(Grant No.N2125002)the open research fund for State Key Laboratory of Advance Refractories(Grant No.SKLAR202001).
文摘To improve the properties of low-carbonization of MgO–C refractories,the introduction of composite additives is an effective strategy.Al_(2)O_(3)–SiC composite powder was prepared from clay using electromagnetic induction heating and carbon embedded methods.Further,the Al_(2)O_(3)–SiC composite powder synthesized by electromagnetic induction heating at 600 A was added into low-carbon MgO–C refractories(4 wt.%)to improve their properties.The results showed that when the addition amount of Al_(2)O_(3)–SiC composite powder is within the range of 2.5–5.0 wt.%,the properties of low-carbon MgO–C samples were significantly improved,e.g.,the apparent porosity of 7.58%–8.04%,the bulk density of 2.98–2.99 g cm-3,the cold compressive strength of 55.72–57.93 MPa,the residual strength after three air quenching at 1100°C of 74.86%–78.04%,and the decarburized layer depth after oxidized at 1400°C for 2 h of 14.03–14.87 mm.Consequently,the idea for the rapid synthesis of Al_(2)O_(3)–SiC composite powder provides an alternative low-carbon MgO–C refractories performance optimization strategy.
文摘Zircon （mesh size ≤ 44μm ） and carbon black （mesh size ≤30μm ） were used as the starting materials, weighed with re（zircon） ： re（carbon black） of 100 ： 20 and mixed fully. The specimens with the diameter of 20ram and length of 5ram were prepared by pressing at 100 MPa, then dried at 120℃ for 12h, put into a furnace with 1. 5L ·min^-1 argon gas and fired at 1450℃, 1500℃, 1550℃, 1600℃ and 1650℃ for 4h, respectively. The chemical composition, phase composition and microstructure of the specimens were studied by chemical analysis, X-ray diffraction and scanning electronic microscope, and the carbothermal reduction reaction process was discussed by thermodynamic analysis. The results showed that the ZrO2-SiC composite could be synthesized by carbothermal reduction reaction using zircon and carbon black as the starting materials in argon atmosphere. The composite with different composition was obtained by controlling the firing temperature and partial pressure of CO gas. The proper temperature to synthesize ZrO2-SiC composite was 1600℃ in this experiment.
文摘TiB2-Al2O3 composite powders were produced by self-propagating high-temperature synthesis（SHS） method with reductive process from B2O3-TiO2-AI system. X-ray diffraction（XRD） and scanning electron microscopy（SEM） analyses show the presence of TiB2 and Al2O3 only in the composite powders produced by SHS. The powders are uniform and free-agglomerate. Transmission electron microscopy （TEM） and high resolution electron microscopy （HREM） observation of microstructure of the composite powders indicate that the interfaces of the TiB2-Al2O3 bond well, without any interfacial reaction products. It is proposed that the good interfacial bonding of the composite powders can be resulted from the TiB2 particles crystallizing and growing on the Al2O3 particles surface with surface defects acting as nucleation centers.
基金"Xi-Bu-Zhi-Guang" Foundation of Chinese Academy of Sciences(No.XBZG-2007-5)Gansu Natural Science Foundation of China(No.0806RJYA004)
文摘The Ni/ZrO2 was used as raw materials to fabricate the surface infiltrated composite layer with 1-4 mm thickness on cast steel substrate through vacuum infiltrated casting technology. The microstructure indicated that the infiltrated composite layer included surface composite layer and transition layer. Wear property was investigated under room temperature and 450 ~C. The results indicated that the abrasion volume of substrate was 8 times that of the infiltrated composite layer at room temperature. The friction coefficient of infiltrated composite layer decreased with the increasing load. The wear resistance of infiltrated composite layer with different ZrO2 contents had been improved obviously under high temperature. The friction coefficient of infiltrated composite layer was decreased comparing with that at room temperature. The oxidation, abrasive and fatigue abrasion was the main wear mechanism at room temperature. Oxidation abrasion, fatigue wear and adhesive wear dominated the wearin~ process under elevated temperature.
文摘TiAl3 particle reinforced pure Al composite has been made by direct reaction among molten Al, TiO2 and a flux. The composite exhibits high Synthetically properties. The strength and hardness are higher than those of pure Al matrix by 71.5% and 134% respectively However, the elongation is 20.36%, slightly lower than that of the Al matrix.
文摘Al 2O 3-SiO 2-TiO 2-ZrO 2 supported membranes were prepar ed by Sol-Gel method. These composite ceramic membranes are level, even and no macro crack. There exist several crystalline phases such as Al 2O 3, TiO 2(a natase), Al 2SiO 5, and ZrO 2 in these membranes. Changing the molar ratio of Al∶Si∶Ti∶Zr,the kinds and content of crystal phases of composite membranes could be different, which may lead to a variety of microstructure of membranes. The surface nanoscale topography and microstructure of membranes were investiga ted by XRD,SEM,AFM,EPMA. The effects of additives and heat treatments on the sur face nanoscale topography and microstructure of composite ceramic membranes were also analyzed.
文摘This work aims at solving the problems of difficult dispersion,easy oxidation and high cost of nano carbon during application,carbon/magnesium aluminate spinel(C/MgAl_(2)O_(4))composite powders were prepared using MgC2O4·2H2O,MgO2,Al2O3 powder,and Al powder as raw materials by combustion synthesis.The results indicate that with the maximum MgC2O4·2H2O addition of 33.34 mass%,the prepared powder contains 1.17 mass%of carbon and carbon distributes among spinel grains.The MgAl_(2)O_(4)spinel shows both granular and rod-like morphologies.The granular MgAl_(2)O_(4)spinel is generated from mutual diffusion between MgO and Al2O3;while the rod-like MgAl_(2)O_(4)spinel is mainly formed by the vapor-solid growth mechanism from Mg vapor and Al2O3.