A series of CoMo/ZrO2-Al2O3 catalysts with different contents of ZrO2 were prepared and characterized through XRD,XPS,NH3-TPD,H2-TPR,HR-TEM,and N2 adsorption-desorption technologies.The performance of the catalysts fo...A series of CoMo/ZrO2-Al2O3 catalysts with different contents of ZrO2 were prepared and characterized through XRD,XPS,NH3-TPD,H2-TPR,HR-TEM,and N2 adsorption-desorption technologies.The performance of the catalysts for low-temperature coal tar(LTCT)hydrocracking reaction was investigated.The interaction between active metals and Al2O3 was weakened with the introduction of ZrO2,which increased the MoS2 content and the stack layer number of MoS2 slabs to further promote the catalytic performance.At the same time,the amount of acid sites increased with an increasing ZrO2 content.When the ZrO2 content reached 32%,the pore volume of the catalyst decreased significantly.This phenomenon reduced the content of MoS2 and the stack layer number of MoS2 slabs,which were not conducive to improving the catalytic performance.The catalyst containing 24%of ZrO2 exhibited the best catalytic performance for hydrocracking reaction,with the residue conversion and the total yield of gasoline and diesel fractions reaching 60.64%and 66.54%,respectively,which could fulfill the requirements for hydrocracking LTCT.展开更多
A S 2O 2- 8/ZrO 2 Al 2O 3 type solid superacid catalyst was prepared from ZrOCl 2·8H 2O, AlCl 3· 6H 2O and (NH 4) 2S 2O 8 by coprecipitation, maceration and calcination processes. Their crystal structures an...A S 2O 2- 8/ZrO 2 Al 2O 3 type solid superacid catalyst was prepared from ZrOCl 2·8H 2O, AlCl 3· 6H 2O and (NH 4) 2S 2O 8 by coprecipitation, maceration and calcination processes. Their crystal structures and acidities were determined by XRD and Hammett method, respectively. The activity of the catalyst was studied as function of Al 2O 3 content, calcination temperature and time in the esterification of acetic acid with butanol, and a conversion of 96 5% was obtained. The catalyst gave also higher yields in syntheses of ketals and acetals: cyclohexanone ethylene ketal(86 2%), acetophenone ethylene ketal(78 5%), acetylacetic ester ketal(88 5%), benzaldehyde glycol acetal(76 3%). The chemical structures of the products were confirmed by IR spectra.展开更多
Nickel catalysts supported on CeO2-ZrO2-CeO2,ZrO2-Al2O3 and Al2O3 were prepared and characterized by means of X-ray diffraction（XRD）,BET areas,H2 temperature-programmed reduction（H2-TPR）,and X-ray photoelectron sp...Nickel catalysts supported on CeO2-ZrO2-CeO2,ZrO2-Al2O3 and Al2O3 were prepared and characterized by means of X-ray diffraction（XRD）,BET areas,H2 temperature-programmed reduction（H2-TPR）,and X-ray photoelectron spectroscopy（XPS）.Through the test of catalytic partial oxidation of methane（CPOM）,Ni/CeO2-ZrO2-Al2O3 displayed the highest activity,which resulted from its largest BET area and best NiO dispersion.Furthermore,Ni/CeO2-ZrO2-Al2O3 maintained a long-time stability in CPOM,which was attributed to its best coking resistance among all the prepared catalysts.展开更多
Composite supports CeO2-ZrO2-Al2O3（CZA） and CeO2-ZrO2-Al2O3-La2O3（CZALa） were prepared by co-precipitation method. Palladium catalysts were prepared by impregnation and their purification ability for CH4, CO and N...Composite supports CeO2-ZrO2-Al2O3（CZA） and CeO2-ZrO2-Al2O3-La2O3（CZALa） were prepared by co-precipitation method. Palladium catalysts were prepared by impregnation and their purification ability for CH4, CO and NOx in the mixture gas simulated the exhaust from natural gas vehicles （NGVs） operated under stoichiometric condition was investigated. The effect of La2O3 on the physicochemical properties of supports and catalysts was characterized by various techniques. The characterizations with X-ray diffraction （XRD） and Raman spectroscopy revealed that the doping of La2O3 restrained effectively the sintering of crystallite particles, maintained the crystallite particles in nanoscale and stabilized the crystal phase after calcination at 1000 ℃. The results of N2-adsorption, H2-temperatnre-programmed reduction （H2-TPR） and oxygen storage capacity （OSC） measurements indicated that La2O3 improved the textural properties, reducibility and OSC of composite supports. Activity testing results showed that the catalysts exhibit excellent activities for the simultaneous removal of methane, CO and NOx in the simulated exhaust gas. The catalysts supported on CZALa showed remarkable thermal stability and catalytic activity for the three pollutants, especially for NOx. The prepared palladium catalysts have high ability to remove NOx, CH4 and CO, and they can be used as excellent catalysts for the purification of exhaust from NGVs operated under stoichiometric condition. The catalysts reported in this work also have significant potential in industrial application because of their high performance and low cost.展开更多
基金Financial support from the National Nature Science Foundation of China(21968034)is gratefully acknowledged.
文摘A series of CoMo/ZrO2-Al2O3 catalysts with different contents of ZrO2 were prepared and characterized through XRD,XPS,NH3-TPD,H2-TPR,HR-TEM,and N2 adsorption-desorption technologies.The performance of the catalysts for low-temperature coal tar(LTCT)hydrocracking reaction was investigated.The interaction between active metals and Al2O3 was weakened with the introduction of ZrO2,which increased the MoS2 content and the stack layer number of MoS2 slabs to further promote the catalytic performance.At the same time,the amount of acid sites increased with an increasing ZrO2 content.When the ZrO2 content reached 32%,the pore volume of the catalyst decreased significantly.This phenomenon reduced the content of MoS2 and the stack layer number of MoS2 slabs,which were not conducive to improving the catalytic performance.The catalyst containing 24%of ZrO2 exhibited the best catalytic performance for hydrocracking reaction,with the residue conversion and the total yield of gasoline and diesel fractions reaching 60.64%and 66.54%,respectively,which could fulfill the requirements for hydrocracking LTCT.
文摘A S 2O 2- 8/ZrO 2 Al 2O 3 type solid superacid catalyst was prepared from ZrOCl 2·8H 2O, AlCl 3· 6H 2O and (NH 4) 2S 2O 8 by coprecipitation, maceration and calcination processes. Their crystal structures and acidities were determined by XRD and Hammett method, respectively. The activity of the catalyst was studied as function of Al 2O 3 content, calcination temperature and time in the esterification of acetic acid with butanol, and a conversion of 96 5% was obtained. The catalyst gave also higher yields in syntheses of ketals and acetals: cyclohexanone ethylene ketal(86 2%), acetophenone ethylene ketal(78 5%), acetylacetic ester ketal(88 5%), benzaldehyde glycol acetal(76 3%). The chemical structures of the products were confirmed by IR spectra.
基金Project supported by State Key Fundamental Research Project(G1999022400)
文摘Nickel catalysts supported on CeO2-ZrO2-CeO2,ZrO2-Al2O3 and Al2O3 were prepared and characterized by means of X-ray diffraction（XRD）,BET areas,H2 temperature-programmed reduction（H2-TPR）,and X-ray photoelectron spectroscopy（XPS）.Through the test of catalytic partial oxidation of methane（CPOM）,Ni/CeO2-ZrO2-Al2O3 displayed the highest activity,which resulted from its largest BET area and best NiO dispersion.Furthermore,Ni/CeO2-ZrO2-Al2O3 maintained a long-time stability in CPOM,which was attributed to its best coking resistance among all the prepared catalysts.
基金supported by the National Natural Science Foundation of China (No. 20773090, 20803049)the National High Technology Researchand Development Program of China (863 Program, No. 2006AA06Z347)the Specialized Research Fund for the Doctoral Program of Higher Education(20070610026)
文摘Composite supports CeO2-ZrO2-Al2O3（CZA） and CeO2-ZrO2-Al2O3-La2O3（CZALa） were prepared by co-precipitation method. Palladium catalysts were prepared by impregnation and their purification ability for CH4, CO and NOx in the mixture gas simulated the exhaust from natural gas vehicles （NGVs） operated under stoichiometric condition was investigated. The effect of La2O3 on the physicochemical properties of supports and catalysts was characterized by various techniques. The characterizations with X-ray diffraction （XRD） and Raman spectroscopy revealed that the doping of La2O3 restrained effectively the sintering of crystallite particles, maintained the crystallite particles in nanoscale and stabilized the crystal phase after calcination at 1000 ℃. The results of N2-adsorption, H2-temperatnre-programmed reduction （H2-TPR） and oxygen storage capacity （OSC） measurements indicated that La2O3 improved the textural properties, reducibility and OSC of composite supports. Activity testing results showed that the catalysts exhibit excellent activities for the simultaneous removal of methane, CO and NOx in the simulated exhaust gas. The catalysts supported on CZALa showed remarkable thermal stability and catalytic activity for the three pollutants, especially for NOx. The prepared palladium catalysts have high ability to remove NOx, CH4 and CO, and they can be used as excellent catalysts for the purification of exhaust from NGVs operated under stoichiometric condition. The catalysts reported in this work also have significant potential in industrial application because of their high performance and low cost.