The electrical transport properties and structures of Y2 O3/ZrO2 solid solution have been studied under high pressure up to 23.2 GPa by means of in situ impedance spectroscopy and x-ray diffraction(XRD) measurements.I...The electrical transport properties and structures of Y2 O3/ZrO2 solid solution have been studied under high pressure up to 23.2 GPa by means of in situ impedance spectroscopy and x-ray diffraction(XRD) measurements.In the impedance spectra, it can be found that the pressure-dependent resistance of Y2 O3/ZrO2 presents two different change trends before and after 13.3 GPa, but the crystal symmetry still remains stable in the cubic structure revealed by the XRD measurement and Rietveld refinement.The pressure dependence of the lattice constant and unit cell volume shows that the Y2 O3/ZrO2 solid solution undergoes an isostructural phase transition at 13.1 GPa, which is responsible for the abnormal change in resistance.By fitting the volume data with the Birch–Murnaghan equation of state, we found that the bulk modulus B0 of the Y2 O3/ZrO2 solid solution increases by 131.9% from 125.2 GPa to 290.3 GPa due to the pressure-induced isostructural phase transition.展开更多
将耐热合金钢基体进行活化处理后,以Ni Co Cr Al Y为粘接过渡层,采用等离子喷涂法和喷枪快速喷涂工艺相结合制备包覆复合粉体Al_2O_3-Zr O_2/Y_2O_3和未包覆粉体Zr O_2/Y_2O_3的2种不同厚度的热障涂层材料样品,通过涂层的结合强度试验...将耐热合金钢基体进行活化处理后,以Ni Co Cr Al Y为粘接过渡层,采用等离子喷涂法和喷枪快速喷涂工艺相结合制备包覆复合粉体Al_2O_3-Zr O_2/Y_2O_3和未包覆粉体Zr O_2/Y_2O_3的2种不同厚度的热障涂层材料样品,通过涂层的结合强度试验、涂层微观结构和高温隔热试验比较相同厚度的2种陶瓷涂层的结合强度及隔热效果,并探讨涂层厚度与隔热效果的关系。结果表明:采用纳米Al_2O_3包覆Zr O_2/Y_2O_3粉体制备的热障涂层其结构和性能都优于未包覆粉体Zr O_2/Y_2O_3制备的热障涂层,且该热障涂层隔热性能随涂层厚度的增加而提高,温度越高性能优势越明显。展开更多
基金Project supported by the National Key Research and Development Program of China(Grant No.2018YFA0305900)the National Natural Science Foundation of China(Grant Nos.11774126,11774174,1674404,and 51772125)
文摘The electrical transport properties and structures of Y2 O3/ZrO2 solid solution have been studied under high pressure up to 23.2 GPa by means of in situ impedance spectroscopy and x-ray diffraction(XRD) measurements.In the impedance spectra, it can be found that the pressure-dependent resistance of Y2 O3/ZrO2 presents two different change trends before and after 13.3 GPa, but the crystal symmetry still remains stable in the cubic structure revealed by the XRD measurement and Rietveld refinement.The pressure dependence of the lattice constant and unit cell volume shows that the Y2 O3/ZrO2 solid solution undergoes an isostructural phase transition at 13.1 GPa, which is responsible for the abnormal change in resistance.By fitting the volume data with the Birch–Murnaghan equation of state, we found that the bulk modulus B0 of the Y2 O3/ZrO2 solid solution increases by 131.9% from 125.2 GPa to 290.3 GPa due to the pressure-induced isostructural phase transition.
文摘将耐热合金钢基体进行活化处理后,以Ni Co Cr Al Y为粘接过渡层,采用等离子喷涂法和喷枪快速喷涂工艺相结合制备包覆复合粉体Al_2O_3-Zr O_2/Y_2O_3和未包覆粉体Zr O_2/Y_2O_3的2种不同厚度的热障涂层材料样品,通过涂层的结合强度试验、涂层微观结构和高温隔热试验比较相同厚度的2种陶瓷涂层的结合强度及隔热效果,并探讨涂层厚度与隔热效果的关系。结果表明:采用纳米Al_2O_3包覆Zr O_2/Y_2O_3粉体制备的热障涂层其结构和性能都优于未包覆粉体Zr O_2/Y_2O_3制备的热障涂层,且该热障涂层隔热性能随涂层厚度的增加而提高,温度越高性能优势越明显。