Bulk YBCO samples were prepared by PMP method. The nominal composition was Y123+xwt% Y211+10 wt% Ag2O (x= 0,15,25,40).The result of magnetic measurements indicated the sample with x= 1 5 at 77 K exhibited a J0 of 3. 9...Bulk YBCO samples were prepared by PMP method. The nominal composition was Y123+xwt% Y211+10 wt% Ag2O (x= 0,15,25,40).The result of magnetic measurements indicated the sample with x= 1 5 at 77 K exhibited a J0 of 3. 9 ×104 A/cm2 at 0.1 T and 2. 4 ×104A/cm2 at 1.0 T.The morphology of samples suggested that fine dispersed Y2BaCuO5 phase acts as effective pinning centers.展开更多
文摘Bulk YBCO samples were prepared by PMP method. The nominal composition was Y123+xwt% Y211+10 wt% Ag2O (x= 0,15,25,40).The result of magnetic measurements indicated the sample with x= 1 5 at 77 K exhibited a J0 of 3. 9 ×104 A/cm2 at 0.1 T and 2. 4 ×104A/cm2 at 1.0 T.The morphology of samples suggested that fine dispersed Y2BaCuO5 phase acts as effective pinning centers.