As an Hg-free lamp using phosphor, the Bi^3＋ and EH^3＋ co-doped Y2O2S phosphors were prepared and their luminescence properties under vacuum ultraviolet（VUV） excitation were investigated. The VUV photoluminescent ...As an Hg-free lamp using phosphor, the Bi^3＋ and EH^3＋ co-doped Y2O2S phosphors were prepared and their luminescence properties under vacuum ultraviolet（VUV） excitation were investigated. The VUV photoluminescent intensity of Y2O2S：Eu^3＋ was weak, however, considerably stronger red emission at 626 nm with good color purity was observed in Y2O2S：Eu^3＋,Bi^3＋ systems. Investigation on the photoluminescence reveals that the strong VUV luminescence of Y2O2S：Eu^3＋,Bi^3＋ at 147 nm is mainly because the Bi^3＋ acts as a medium and effectively performs the energy transfer process： Y^3＋-O^2-→Bi^3＋→Eu^3＋, while the intense emission band at 172 nm is attributed to the absorption of the characteristic ^1So-^1P1 transition of Bi^3＋ and the direct energy transfer from Bi^3＋ to Eu^3＋. The Y2O2S：Eu^3＋,Bi^3＋ shows excellent VUV optical properties compared with the commercial （Y,Gd）BO3：Eu^3＋. Thus, the Y2O2S：Eu^3＋,Bi^3＋ can be a potential red VUV-excited candidate applied in Hg-free lamps for backlight of liquid crystal display.展开更多
At low temperature, some long-lasting phosphors could not work well in practical applications. So it is necessary to investigate the temperature dependence of the phosphors. The Y2O2S.Eu, Ti, Mg microcrystalline sampl...At low temperature, some long-lasting phosphors could not work well in practical applications. So it is necessary to investigate the temperature dependence of the phosphors. The Y2O2S.Eu, Ti, Mg microcrystalline samples were prepared by solid state reaction method. Phosphors were sintered at 1150 ℃ for 20 min in air, putting in and taking out both at high temperature. The emission spectra and the afterglow spectra as well as the thermoluminescence curve were measured for Y2O2S：Eu,展开更多
基金Supported by the Project of the Combination of Industry and Research by the Ministry of Education of China and Guang-dong Province, China(No.0712226100023)
文摘As an Hg-free lamp using phosphor, the Bi^3＋ and EH^3＋ co-doped Y2O2S phosphors were prepared and their luminescence properties under vacuum ultraviolet（VUV） excitation were investigated. The VUV photoluminescent intensity of Y2O2S：Eu^3＋ was weak, however, considerably stronger red emission at 626 nm with good color purity was observed in Y2O2S：Eu^3＋,Bi^3＋ systems. Investigation on the photoluminescence reveals that the strong VUV luminescence of Y2O2S：Eu^3＋,Bi^3＋ at 147 nm is mainly because the Bi^3＋ acts as a medium and effectively performs the energy transfer process： Y^3＋-O^2-→Bi^3＋→Eu^3＋, while the intense emission band at 172 nm is attributed to the absorption of the characteristic ^1So-^1P1 transition of Bi^3＋ and the direct energy transfer from Bi^3＋ to Eu^3＋. The Y2O2S：Eu^3＋,Bi^3＋ shows excellent VUV optical properties compared with the commercial （Y,Gd）BO3：Eu^3＋. Thus, the Y2O2S：Eu^3＋,Bi^3＋ can be a potential red VUV-excited candidate applied in Hg-free lamps for backlight of liquid crystal display.
文摘At low temperature, some long-lasting phosphors could not work well in practical applications. So it is necessary to investigate the temperature dependence of the phosphors. The Y2O2S.Eu, Ti, Mg microcrystalline samples were prepared by solid state reaction method. Phosphors were sintered at 1150 ℃ for 20 min in air, putting in and taking out both at high temperature. The emission spectra and the afterglow spectra as well as the thermoluminescence curve were measured for Y2O2S：Eu,