Calcium hexaluminate （ CA6 ） was synthesized by mixing light-weight calcium carbonate and Al2O3 mi- cropowder （calcined α-Al2O3, activated α-Al2O3 or α-Al2O3） according to the stoichimetric ratio of CA6, and ...Calcium hexaluminate （ CA6 ） was synthesized by mixing light-weight calcium carbonate and Al2O3 mi- cropowder （calcined α-Al2O3, activated α-Al2O3 or α-Al2O3） according to the stoichimetric ratio of CA6, and reaction sintering at 1 200, 1 300, 1 400 and 1 500 ℃fin 3 h, respectiely. Efcts of the three alu- mina micropowders on the phase composition, micro- structure and properties of CA were investigated. The re- sults show that ： （ 1 ） for the three Al2O3 micropowders, the reaction to generate CA6 in specimens basically com- plete. at about 1 500 ℃ ; CA6 generated in all specimens is planar, bat the array modes are slightly different; （2） the specimel＇s prepared from, calcined α-Al2O3or ρ-Al2O3 shrink almost, while the specimens prepared from activated α-Al2O3 expand ; （ 3 ） the cold crushing strength of the specimen prepared from activated α-Al2O3 is the highest, reaching 42.5 MPa when only CA6 exists （ after firing at 1 500 ℃ ） ; （ 4 ） the specimen prepared from ρ-Al2O3 has the lowest generation temperature of CA6 and the highest apparent porosity, reaching 70. 1% when only CA exists （after firing at 1 500 ℃）; （5） the specimen prepared from calcined α-Al2O3 has the biggest bulk density.展开更多
facile one-step method is presented for the synthesis of indolizines in moder-ate to high yields by reaction of pyridinium, quinolinium and isoquinolinium ylideswith acrylonitrile, methyl acrylate and diethyl maleate ...facile one-step method is presented for the synthesis of indolizines in moder-ate to high yields by reaction of pyridinium, quinolinium and isoquinolinium ylideswith acrylonitrile, methyl acrylate and diethyl maleate respectively in the presenceof tetrakis-pyridino-cobalt(Ⅱ)dichromate (TPCD) in DMF.展开更多
文摘Calcium hexaluminate （ CA6 ） was synthesized by mixing light-weight calcium carbonate and Al2O3 mi- cropowder （calcined α-Al2O3, activated α-Al2O3 or α-Al2O3） according to the stoichimetric ratio of CA6, and reaction sintering at 1 200, 1 300, 1 400 and 1 500 ℃fin 3 h, respectiely. Efcts of the three alu- mina micropowders on the phase composition, micro- structure and properties of CA were investigated. The re- sults show that ： （ 1 ） for the three Al2O3 micropowders, the reaction to generate CA6 in specimens basically com- plete. at about 1 500 ℃ ; CA6 generated in all specimens is planar, bat the array modes are slightly different; （2） the specimel＇s prepared from, calcined α-Al2O3or ρ-Al2O3 shrink almost, while the specimens prepared from activated α-Al2O3 expand ; （ 3 ） the cold crushing strength of the specimen prepared from activated α-Al2O3 is the highest, reaching 42.5 MPa when only CA6 exists （ after firing at 1 500 ℃ ） ; （ 4 ） the specimen prepared from ρ-Al2O3 has the lowest generation temperature of CA6 and the highest apparent porosity, reaching 70. 1% when only CA exists （after firing at 1 500 ℃）; （5） the specimen prepared from calcined α-Al2O3 has the biggest bulk density.
文摘facile one-step method is presented for the synthesis of indolizines in moder-ate to high yields by reaction of pyridinium, quinolinium and isoquinolinium ylideswith acrylonitrile, methyl acrylate and diethyl maleate respectively in the presenceof tetrakis-pyridino-cobalt(Ⅱ)dichromate (TPCD) in DMF.