Low-valent titanium reagent prepared in situ from TiCl_4 and Zn was employed to induce the intramolecular coupling of nitro group with carbonyl group to give substituted hydroxyl pyrrolines, pyrroles and lactam in goo...Low-valent titanium reagent prepared in situ from TiCl_4 and Zn was employed to induce the intramolecular coupling of nitro group with carbonyl group to give substituted hydroxyl pyrrolines, pyrroles and lactam in good yields.展开更多
Laser cladding,together with laser nitriding was used to synthesize a titanium nickel intermetallic compound layer on the nickel substrate and a TiN coating on the cladding layer. During the laser cladding, Ti and Ni ...Laser cladding,together with laser nitriding was used to synthesize a titanium nickel intermetallic compound layer on the nickel substrate and a TiN coating on the cladding layer. During the laser cladding, Ti and Ni powders were blown into the melting pool by a six-hole coaxial nozzle powder injection system. Exothermic reactions between Ti and Ni took place in the melting pool, and a cladding layer of titanium nickel intermetallic compounds was produced. Laser nitriding in a nitrogen-rich atmosphere followed the production of the cladding layer, and formed a golden yellow TiN layer over it. An optical and a scanning electron microscope were used to investigate the microstructures and measure the thicknesses of the cladding layer and the TiN layer. Phase identification was carried out by XRD. For the nitriding sample, the microhardness profile of the clad layer was tested. The optimal process parameters of the in situ synthesis of titanium nickel intermetallic compounds were obtained.展开更多
A new organo-directed titanium phosphate, [NH3CH2CH2NH3]·[TiO(HPO4)2], was synthesized by the solvothermal method and its structure was determined by single crystal X-ray diffraction. The structure consists of 1-...A new organo-directed titanium phosphate, [NH3CH2CH2NH3]·[TiO(HPO4)2], was synthesized by the solvothermal method and its structure was determined by single crystal X-ray diffraction. The structure consists of 1-D zigzag chains built up from trans-corner-sharing titanium oxo octahedra running along the b axis, with fused Ti2P three-membered rings being attached to the ( Ti ( O ( Ti ( O ( backbone.展开更多
To realize the resource and high-value utilization,a new approach,named bagasse lignin(BL) used to produce aryl oxygen-containing compounds by catalytic pyrolysis over perovskite,was proposed,LaTi0.2Fe0.8O3(LTF) sampl...To realize the resource and high-value utilization,a new approach,named bagasse lignin(BL) used to produce aryl oxygen-containing compounds by catalytic pyrolysis over perovskite,was proposed,LaTi0.2Fe0.8O3(LTF) samples prepared by the sol-gel method(SG) and the solid-state reaction method(SS)were characterized.The catalytic action on BL pyrolysis was performed by the test of TG-DTG and the evaluation of the fixed bed micro-reactor,the components and contents of the products were determined.The results show that LTF samples have cubic perovskite phase,LTF prepared by SG(LTF-SG) is porous with larger specific surface area than LTF prepared by SS(LTF-SS).During the pyrolysis of BL,the addition of LTF lowers the pyrolysis temperature and the activation energy,the contents of CO2 and CO in gaseous products reduce by 4.6%-8.0% and 30.7%-34.3%,respectively,the total content of aryl oxygencontaining compounds(including phenolics,guaiacols,syringols and phenylates) in liquid products increases from 62 wt% to more than 72 wt%,and LTF-SG shows better catalytic performance.LTF samples have nice phase and catalytic stabilities for BL pyrolysis after five successive redox cycles.展开更多
Two kinds of packaged processes by nickel on the surface of titanium carbide particle are studied in this work. One is the chemical nickel-plating, the other is the organometallic compound decomposition. The compositi...Two kinds of packaged processes by nickel on the surface of titanium carbide particle are studied in this work. One is the chemical nickel-plating, the other is the organometallic compound decomposition. The composition, structure and morphology of the packaged powder were analyzed with XRD, DAT/TGA, SEM, EPMA etc. It has been shown that nickel was even dispersed on the surface of titanium carbide particle by the. two kinds of processes, deposited nickel exists as spherical particles of about 0.1 μm in diameter. The merits and demerits of the two kinds of processes have been compared, the organometallic copmound decomposition among them is a kind of hopeful method, which is not used by other researchers.展开更多
文摘Low-valent titanium reagent prepared in situ from TiCl_4 and Zn was employed to induce the intramolecular coupling of nitro group with carbonyl group to give substituted hydroxyl pyrrolines, pyrroles and lactam in good yields.
文摘Laser cladding,together with laser nitriding was used to synthesize a titanium nickel intermetallic compound layer on the nickel substrate and a TiN coating on the cladding layer. During the laser cladding, Ti and Ni powders were blown into the melting pool by a six-hole coaxial nozzle powder injection system. Exothermic reactions between Ti and Ni took place in the melting pool, and a cladding layer of titanium nickel intermetallic compounds was produced. Laser nitriding in a nitrogen-rich atmosphere followed the production of the cladding layer, and formed a golden yellow TiN layer over it. An optical and a scanning electron microscope were used to investigate the microstructures and measure the thicknesses of the cladding layer and the TiN layer. Phase identification was carried out by XRD. For the nitriding sample, the microhardness profile of the clad layer was tested. The optimal process parameters of the in situ synthesis of titanium nickel intermetallic compounds were obtained.
文摘A new organo-directed titanium phosphate, [NH3CH2CH2NH3]·[TiO(HPO4)2], was synthesized by the solvothermal method and its structure was determined by single crystal X-ray diffraction. The structure consists of 1-D zigzag chains built up from trans-corner-sharing titanium oxo octahedra running along the b axis, with fused Ti2P three-membered rings being attached to the ( Ti ( O ( Ti ( O ( backbone.
基金Project supported by National Natural Science Foundation of China(51674089)Heilongjiang Provincial Science Fund for Distinguished Youth Scholar(JC2018002)+2 种基金Postdoctoral Scientific Research Development Fund of Heilongjiang Province(LBH-Q16037)Postgraduate Innovative Research Project of Northeast Petroleum University(YJSCX2017-014NEPU)Youth Fund of Northeast Petroleum University(2018QNL-17)
文摘To realize the resource and high-value utilization,a new approach,named bagasse lignin(BL) used to produce aryl oxygen-containing compounds by catalytic pyrolysis over perovskite,was proposed,LaTi0.2Fe0.8O3(LTF) samples prepared by the sol-gel method(SG) and the solid-state reaction method(SS)were characterized.The catalytic action on BL pyrolysis was performed by the test of TG-DTG and the evaluation of the fixed bed micro-reactor,the components and contents of the products were determined.The results show that LTF samples have cubic perovskite phase,LTF prepared by SG(LTF-SG) is porous with larger specific surface area than LTF prepared by SS(LTF-SS).During the pyrolysis of BL,the addition of LTF lowers the pyrolysis temperature and the activation energy,the contents of CO2 and CO in gaseous products reduce by 4.6%-8.0% and 30.7%-34.3%,respectively,the total content of aryl oxygencontaining compounds(including phenolics,guaiacols,syringols and phenylates) in liquid products increases from 62 wt% to more than 72 wt%,and LTF-SG shows better catalytic performance.LTF samples have nice phase and catalytic stabilities for BL pyrolysis after five successive redox cycles.
基金financially supported by the National Basic Research Program of China(Nos.2013CB632601 and 2013CB632604)the National Science Foundation for Distinguished Young Scholars of China(Nos.51125018 and 51504230)+2 种基金the Key Research Program of Chinese Academy of Sciences(No.KGZD-EW-201-2)the National Natural Science Foundation of China(Nos.51374191 and 2110616751104139)China Postdoctoral Science Foundation(Nos.2012M510552 and 2013T60175)
文摘Two kinds of packaged processes by nickel on the surface of titanium carbide particle are studied in this work. One is the chemical nickel-plating, the other is the organometallic compound decomposition. The composition, structure and morphology of the packaged powder were analyzed with XRD, DAT/TGA, SEM, EPMA etc. It has been shown that nickel was even dispersed on the surface of titanium carbide particle by the. two kinds of processes, deposited nickel exists as spherical particles of about 0.1 μm in diameter. The merits and demerits of the two kinds of processes have been compared, the organometallic copmound decomposition among them is a kind of hopeful method, which is not used by other researchers.