Heterogeneous photocatalytic degradation of γ-HCH on soil surfaces was carried out to evaluate the photocatalytic effectiveness of α-Fe 2O 3 and TiO 2 toward degrading γ-HCH on soil surfaces. After being spiked ...Heterogeneous photocatalytic degradation of γ-HCH on soil surfaces was carried out to evaluate the photocatalytic effectiveness of α-Fe 2O 3 and TiO 2 toward degrading γ-HCH on soil surfaces. After being spiked with γ-HCH, soil samples were loaded with α-Fe 2O 3 or TiO 2 and exposed to UV-light irradiation. Different catalyst loads, 0%, 2%, 5%, 7%, and 10% (wt.)α-Fe 2O 3; 0%, 0.5%, 1%, 2:(wt.)TiO 2, were tested for up to 7 d irradiation. The effects of soil thickness, acidity, and humic substances were also investigated. The obtained results indicated that the γ-HCH photodegradation follows the pseudo-first-order kinetics. The addition of α-Fe 2O 3 or TiO 2 accelerates the photodegradation of γ-HCH, while the photodegradation rate decreases when the content of α-Fe 2O 3 exceeds 7%(wt.). The degradation rate increases with the soil pH value. Humic substances inhibit the photocatalytic degradation of γ-HCH. Pentachlorocyclohexene, tetrachlorocyclohexene, and trichlorobenzene are detected as photodegradation intermediates, which are gradually degraded with the photodegradation evolution.展开更多
This paper presented a scientific study of the effects of four dispersion methods on the dispersion capability of nano La2O3 suspensions, which are ball milling, ultrasonic, ultrasonic followed by ball milling and bal...This paper presented a scientific study of the effects of four dispersion methods on the dispersion capability of nano La2O3 suspensions, which are ball milling, ultrasonic, ultrasonic followed by ball milling and ball milling followed by ultrasonic. For the purposes of com- paring their dispersion capability, sedimentation test, Zeta-potential measurement test, particles size measurement test and transmission electron microscopy （TEM） test were carried out. Suspension ability coefficient was also defined with expectation to estimate the stability of nano La2O3 suspension through granularity size, and their relationship curve was worked out. The results showed that ultrasonic followed by ball milling enjoyed an excellent capability of dispersion for nano La2O3 suspension. Its mechanism was discussed, and breakage models of nano La2O3 particles were developed. The study results indicated that ultrasonic followed by ball milling could break through both the limits of ultrasonic dispersion size range and thermo-effect, and thus was able to overcome the problem of the secondary aggregation of nanoparticles. Moreover, aggregations could be further de-agglomerated. As a result, dispersion capability of nano La2O3 suspension could be improved more greatly by ultrasonic followed by ball milling. And its suspension stability was the best with the highest suspension ability coefficient of the nanoparticles. It was found in the experiment that there was almost no obvious phenomenon of stratification for the suspension with a little sediment after being deposited for 8 d.展开更多
Thermodynamic models of calculating mass action concentrations for structural units or ion couples in RbCl-H2O binary and RbCl-RbNO3-H2O ternary strong electrolyte aqueous solutions were developed based on the ion and...Thermodynamic models of calculating mass action concentrations for structural units or ion couples in RbCl-H2O binary and RbCl-RbNO3-H2O ternary strong electrolyte aqueous solutions were developed based on the ion and molecule coexistence theory at 298.15 K.A transformation coefficient is needed to compare the calculated mass action concentration and the reported activity because they are obtained at different standard states and concentration units.The results show that the transformation coefficients between the calculated mass action concentrations and the reported activities of the same structural units or ion couples in RbCl-H2O binary and RbCl-RbNO3-H2O ternary strong electrolyte aqueous solutions change in a very narrow range.The transformed mass action concentrations of structural units or ion couples in RbCl-H2O binary system are in good agreement with the reported activities. The transformed mass action concentrations of RbCl and RbNO3 in RbCl-RbNO3-H2O ternary solution are also in good agreement with the reported activities,aRbCl and 3RbNOa,with different total ionic strengths as 0.01,0.05,0.1,0.5,1.0,1.5,2.0,3.0 and 3.5 mol/kg,respectively.All those results mean the developed thermodynamic model of strong electrolyte aqueous solutions can reflect structural characteristics of RbCl-H2O binary and RbCl-RbNO3-H2O ternary strong electrolyte aqueous solutions and the mass action concentration also strictly follows the mass action law.展开更多
Synthetic method of solid superacid TiSiW 12 O 40 /TiO 2 was described.The synthesis of iso amyl propionate catalyzed by TiSiW 12 O 40 /TiO 2 has been studied and the factors influencing on the yield is discussed.It s...Synthetic method of solid superacid TiSiW 12 O 40 /TiO 2 was described.The synthesis of iso amyl propionate catalyzed by TiSiW 12 O 40 /TiO 2 has been studied and the factors influencing on the yield is discussed.It shows that it’s an excellent catalyst,the yield of the iso amyl propionate can be over 77% when the molar ratio of iso amyl alcohol and propionic acid is 1.2,the quality of TiSiW 12 O 40 /TiO 2 is equal to 1.5% feed stock,the reaction time is 80min and the reaction temperature is about 103～107℃.展开更多
文摘Heterogeneous photocatalytic degradation of γ-HCH on soil surfaces was carried out to evaluate the photocatalytic effectiveness of α-Fe 2O 3 and TiO 2 toward degrading γ-HCH on soil surfaces. After being spiked with γ-HCH, soil samples were loaded with α-Fe 2O 3 or TiO 2 and exposed to UV-light irradiation. Different catalyst loads, 0%, 2%, 5%, 7%, and 10% (wt.)α-Fe 2O 3; 0%, 0.5%, 1%, 2:(wt.)TiO 2, were tested for up to 7 d irradiation. The effects of soil thickness, acidity, and humic substances were also investigated. The obtained results indicated that the γ-HCH photodegradation follows the pseudo-first-order kinetics. The addition of α-Fe 2O 3 or TiO 2 accelerates the photodegradation of γ-HCH, while the photodegradation rate decreases when the content of α-Fe 2O 3 exceeds 7%(wt.). The degradation rate increases with the soil pH value. Humic substances inhibit the photocatalytic degradation of γ-HCH. Pentachlorocyclohexene, tetrachlorocyclohexene, and trichlorobenzene are detected as photodegradation intermediates, which are gradually degraded with the photodegradation evolution.
基金supported by the Aeronautical Science Foundation of China (2010ZE52056)Natural Science Foundation of Jiangsu Province (BK2011479)Open Foundation of Jiangsu Key Laboratory of Precision and Micro-Manufacturing Technology (2012)
文摘This paper presented a scientific study of the effects of four dispersion methods on the dispersion capability of nano La2O3 suspensions, which are ball milling, ultrasonic, ultrasonic followed by ball milling and ball milling followed by ultrasonic. For the purposes of com- paring their dispersion capability, sedimentation test, Zeta-potential measurement test, particles size measurement test and transmission electron microscopy （TEM） test were carried out. Suspension ability coefficient was also defined with expectation to estimate the stability of nano La2O3 suspension through granularity size, and their relationship curve was worked out. The results showed that ultrasonic followed by ball milling enjoyed an excellent capability of dispersion for nano La2O3 suspension. Its mechanism was discussed, and breakage models of nano La2O3 particles were developed. The study results indicated that ultrasonic followed by ball milling could break through both the limits of ultrasonic dispersion size range and thermo-effect, and thus was able to overcome the problem of the secondary aggregation of nanoparticles. Moreover, aggregations could be further de-agglomerated. As a result, dispersion capability of nano La2O3 suspension could be improved more greatly by ultrasonic followed by ball milling. And its suspension stability was the best with the highest suspension ability coefficient of the nanoparticles. It was found in the experiment that there was almost no obvious phenomenon of stratification for the suspension with a little sediment after being deposited for 8 d.
基金Project supported by Publication Foundation of National Science and Technology Academic Books of China
文摘Thermodynamic models of calculating mass action concentrations for structural units or ion couples in RbCl-H2O binary and RbCl-RbNO3-H2O ternary strong electrolyte aqueous solutions were developed based on the ion and molecule coexistence theory at 298.15 K.A transformation coefficient is needed to compare the calculated mass action concentration and the reported activity because they are obtained at different standard states and concentration units.The results show that the transformation coefficients between the calculated mass action concentrations and the reported activities of the same structural units or ion couples in RbCl-H2O binary and RbCl-RbNO3-H2O ternary strong electrolyte aqueous solutions change in a very narrow range.The transformed mass action concentrations of structural units or ion couples in RbCl-H2O binary system are in good agreement with the reported activities. The transformed mass action concentrations of RbCl and RbNO3 in RbCl-RbNO3-H2O ternary solution are also in good agreement with the reported activities,aRbCl and 3RbNOa,with different total ionic strengths as 0.01,0.05,0.1,0.5,1.0,1.5,2.0,3.0 and 3.5 mol/kg,respectively.All those results mean the developed thermodynamic model of strong electrolyte aqueous solutions can reflect structural characteristics of RbCl-H2O binary and RbCl-RbNO3-H2O ternary strong electrolyte aqueous solutions and the mass action concentration also strictly follows the mass action law.
文摘Synthetic method of solid superacid TiSiW 12 O 40 /TiO 2 was described.The synthesis of iso amyl propionate catalyzed by TiSiW 12 O 40 /TiO 2 has been studied and the factors influencing on the yield is discussed.It shows that it’s an excellent catalyst,the yield of the iso amyl propionate can be over 77% when the molar ratio of iso amyl alcohol and propionic acid is 1.2,the quality of TiSiW 12 O 40 /TiO 2 is equal to 1.5% feed stock,the reaction time is 80min and the reaction temperature is about 103～107℃.