This paper presents the principle,properties,advantage and disadvantage,associated problems and trend of laser protection with VO 2 film for infrared detectors in the range of 3～5μm and 8～12μm regions and suggest...This paper presents the principle,properties,advantage and disadvantage,associated problems and trend of laser protection with VO 2 film for infrared detectors in the range of 3～5μm and 8～12μm regions and suggests VO 2 film is a potential protection material for infrared detectors.展开更多
We synthesized a mesoporous film based on TiO2-reduced graphene oxide(RGO)hybrids using a one-step vapor-thermal method without the need for an additional annealing process.The vapor-thermally prepared TiO2-graphene h...We synthesized a mesoporous film based on TiO2-reduced graphene oxide(RGO)hybrids using a one-step vapor-thermal method without the need for an additional annealing process.The vapor-thermally prepared TiO2-graphene hybrid(VTH)features unique structures with an ultra-large specific surface area of^260 m^2 g^-1 and low aggregation,giving rise to enhanced light harvesting and increased charge generation and separation efficiency.It was observed that a mesoporous film with uniform pore distribution is simultaneously obtained during the VTH growth process.When a 5.0 wt%RGO VTH film was used as the active layer in photocatalysis,the highest photocatalytic activity for degradation of methyl orange was achieved.For another,when a 0.75 wt%RGO VTH film was used as the photoanode in a dye-sensitized solar cell,the power conversion efficiency reached 7.58%,which represents an increase of 73.1%compared to a solar cell using an a photoanode of pure TiO2 synthesized by a traditional solvothermal method.It is expected that this facile method for the synthesis of TiO2/graphene hybrid mesoporous films will be useful in practical applications for preparing other metal oxide/graphene hybrids with ultra-high photocatalytic activity and photovoltaic performance.展开更多
High ultraviolet(UV)stability and low dark current(Idark)are necessary for high-quality perovskite photodetectors(PDs).TiO^(2)thin film is known as effective electron-transport-layer(ETL)for perovskite devices.However...High ultraviolet(UV)stability and low dark current(Idark)are necessary for high-quality perovskite photodetectors(PDs).TiO^(2)thin film is known as effective electron-transport-layer(ETL)for perovskite devices.However,common spin-coated TiO^(2)ETLs endow many surface defects and have strong UV photocatalytic effect to decompose perovskite materials,resulting in inferior stability of devices.In this work,TiO^(2)bilayer film(Bi-TiO^(2))has been fabricated by combining spin-coating and atomic-layer-deposition process and its positive effects on UV stability and Idarkof Cs2 AgBiBr6-based PDs have been revealed for the first time.It is demonstrated that Bi-TiO^(2)possesses fewer surface defects and smoother morphology with type II band alignment,which is beneficial to suppress photocatalytic activity of TiO^(2)and reduce carrier recombination at the interface.After accelerated strong UV aging treatment,the PD with Bi-TiO^(2)maintains excellent performance,whereas the PD with spin-coated TiO^(2)film dramatically deteriorate with on-off ratio drops from~102 to~2.Besides,the Idarkof PD remarkably decreases from~10^(-8) A to~10^(-10) A after bilayer optimization.Furthermore,we have integrated the corresponding PDs into a self-built imaging system adopting diffuse reflection mode.This work suggests a feasible approach to fabricate TiO^(2)/Cs2 AgBiBr6-based PDs with remarkable UV tolerance for imaging applications.展开更多
We investigated the effects of using different thicknesses of pure and vanadium-doped thin films of TiO2 as the electron transport layer in the inverted configuration of organic photovoltaic cells based on poly（3-hex...We investigated the effects of using different thicknesses of pure and vanadium-doped thin films of TiO2 as the electron transport layer in the inverted configuration of organic photovoltaic cells based on poly（3-hexylthiophene） P3HT：[6-6] phenyl-（6） butyric acid methyl ester（PCBM）. 1% vanadium-doped TiO2nanoparticles were synthesized via the solvothermal method. Crystalline structure, morphology, and optical properties of pure and vanadium-doped TiO2 thin films were studied by different techniques such as x-ray diffraction, scanning electron microscopy, transmittance electron microscopy, and UV–visible transmission spectrum. The doctor blade method which is compatible with roll-2-roll printing was used for deposition of pure and vanadium-doped TiO2 thin films with thicknesses of 30 nm and 60 nm. The final results revealed that the best thickness of TiO2 thin films for our fabricated cells was 30 nm. The cell with vanadium-doped TiO2 thin film showed slightly higher power conversion efficiency and great Jsc of 10.7 mA/cm^2 compared with its pure counterpart. In the cells using 60 nm pure and vanadium-doped TiO2 layers, the cell using the doped layer showed much higher efficiency. It is remarkable that the external quantum efficiency of vanadium-doped TiO2 thin film was better in all wavelengths.展开更多
ZrO2/TiO2 composite photocatalytic film was produced on the pure titanium substrate using in-situ Zr（OH）4 colloidal particle by the micro-arc oxidation technique and characterized by scanning electron microscope （...ZrO2/TiO2 composite photocatalytic film was produced on the pure titanium substrate using in-situ Zr（OH）4 colloidal particle by the micro-arc oxidation technique and characterized by scanning electron microscope （SEM）, energy dispersive X-ray （EDX）, X-ray diffraction （XRD） and ultraviolet-visible （UV-Vis） spectrophotometer. The composite film shows a lamellar and porous structure which consists of anatase, futile and ZrO2 phases. The optical absorption edge of film is shifted to longer wavelength when ZrO2 is introduced to TiO2. Furthermore, the photocatalytic reaction rate constants of degradation of rhodamine B solution with ZrO2/TiO2 composite film and pure TiO2 film under ultraviolet irradiation are measured as 0.0442 and 0.0186 h 1, respectively.展开更多
The titanium oxide （TiO2） nanotubes have attracted attention for their use in dye-sensitized solar cells as photoanode. In this study semiconducting cadmium sulfide （CdS） nanoparticles arc grown on top opened TiO2...The titanium oxide （TiO2） nanotubes have attracted attention for their use in dye-sensitized solar cells as photoanode. In this study semiconducting cadmium sulfide （CdS） nanoparticles arc grown on top opened TiO2 nanotubes arrays by radio-frequency magnetron sputtering. X-ray diffraction, scanning electron mieroscopy, transmission electron microscopy and diffuse reflection spectra are used to study structural, morphological and optical properties of the CdS/TiO2 bilayer.展开更多
A novel WO3-x/TiO2 film as photoanode was synthesized for photoelectrocatalytic（PEC） reduction of CO2 into formic acid（HCOOH）. The films prepared by doctor blade method were characterized with X-ray diffractometer...A novel WO3-x/TiO2 film as photoanode was synthesized for photoelectrocatalytic（PEC） reduction of CO2 into formic acid（HCOOH）. The films prepared by doctor blade method were characterized with X-ray diffractometer（XRD）, scanning electron microscope（SEM） and transmission electron microscope（TEM）. The existence of oxygen vacancies in the WO3-x was confirmed with an X-ray photoelectron spectroscopy（XPS）, and the accurate oxygen index was determined by a modified potentiometric titrimetry method. After 3h of photoelectrocatalytic reduction, the formic acid yield of the WO3-x/TiO2 film is 872 nmol/cm^2, which is 1.83 times that of the WO3/TiO2 film. The results of PEC performance demonstrate that the introduction of WO3-x nanoparticles can improve the charge transfer performance so as to enhance the performance of PEC reduction of CO2 into formic acid.展开更多
Nano sized powders of TiO2 （titanium dioxide） and Nb2O5 （Niobium （V） oxide） were used to fabricate TiO2/Nb2O5 composites thin films by EPD （electrophoretic deposition） technique. The metal oxide powders, toget...Nano sized powders of TiO2 （titanium dioxide） and Nb2O5 （Niobium （V） oxide） were used to fabricate TiO2/Nb2O5 composites thin films by EPD （electrophoretic deposition） technique. The metal oxide powders, together with magnesium nitrate hexahydrate pellets, were suspended in propan-2-ol inside an EPD cell. The electrodes, placed 1.2 cm apart, were partially immersed in the suspension and a DC potential applied across them. Key EPD process parameters, which include applied DC electric field, deposition time and solid concentration in suspension, were optimized through visual inspection and from UV-Vis-NIR spectrophotometer spectra. The highest （55%） transmittance was obtained for films with deposition time of 90 s, powder concentration of 0.01 g/40 mL, and 35 V DC （direct current） voltage. XRD micrographs confirmed that TiO2 and Nb2O5 particles were presented in the composite film. SEM （scanning electron microscope） micrographs of the composite electrode thin films showed that porous films of high quality with well controlled morphology were deposited by using the EPD technique.展开更多
Series of TiO 2-ZnO heterojunction composite films with different n（Zn）/n（Ti） ratios were prepared by UDP450 magnetron sputter ion plating equipment, and the mole ratio of Zn to Ti was controlled by adjusting the ...Series of TiO 2-ZnO heterojunction composite films with different n（Zn）/n（Ti） ratios were prepared by UDP450 magnetron sputter ion plating equipment, and the mole ratio of Zn to Ti was controlled by adjusting the current values of sputtering target. The effects of n（Zn）/n（Ti） on the microstructures of TiO2-ZnO films were investigated by SEM, AFM, Raman and XPS, and their photocatalytic decomposition of methyl orange solutions was evaluated. The results show that an increase in n（Zn）/n（Ti） typically results in a decrease in the grain size of composite films firstly and then an increase of grain size, while an increase in n（Zn）/n（Ti） leads to an increase in film roughness firstly and then a decrease in film roughness. Both grain size and roughness of TiO2-ZnO films reach the maximum and minimum at n（Zn）/n（Ti） of 1/9.3, respectively. The n（Zn）/n（Ti） shows little effect on the valences of Zn and Ti elements, which mainly exist in the form of TiO2 and ZnO phases. The n（Zn）/n（Ti） has influence on the amount of anatase/rutile TiO2 heterojunction in the film. With increase of the n（Zn）/n（Ti）, the absorption intensity of the composite film increases and the absorption region extends to 450 nm, which is redshifted as much as 150 nm in comparison with the pure TiO2 films. However, the photocatalytic abilities of heterogeneous composite films do not depend on the n（Zn）/n（Ti） but rather on the microstructures of the TiO2-ZnO composite films. Degradation rate of the film reaches the maximum and the photocatalytic decomposition of pollutants works best when n（Zn）/n（Ti）=1：9.3.展开更多
A novel titanium dioxide （TiO2） film comprising both nanotubes and nanopaticles was fabricated by an anodization process of the modified titanium. The local electric field at the anodized surface was simulated and i...A novel titanium dioxide （TiO2） film comprising both nanotubes and nanopaticles was fabricated by an anodization process of the modified titanium. The local electric field at the anodized surface was simulated and its influence on the morphology of the TiO2 film was discussed. The results show that the electric field strength is enhanced by the covering. The growth rate of TiO2 increases with the assist of the local electric field. However, TiO2 dissolution is hindered since the local electric field prevents [TiF6]6- from diffusing. It means that the balance condition for the formation of nanotubes is broken, and TiO2 nanoparticles are formed. Moreover, the crystal structure of the TiO2 film was confirmed using X-ray diffraction and Raman analysis. The anatase is a main phase for the proposed film.展开更多
TiO2 mesocrystals can considerably enhance charge separation owing to their oriented superstructures,with fewer internal defects and porous properties providing more active sites.In this work,we prepared TiO2 mesocrys...TiO2 mesocrystals can considerably enhance charge separation owing to their oriented superstructures,with fewer internal defects and porous properties providing more active sites.In this work,we prepared TiO2 mesocrystal films by a direct annealing method.The morphology and crystal phase of the film were controlled by adjusting the ratio of NH4F and the calcination temperature.Moreover,we found that Au nanoparticles loaded on a TiO2 mesocrystal film enabled highly efficient visible light photocatalytic properties.The photocatalytic activities were studied by hydrogen generation and photoreduction of Cr(VI).This work represents a considerable advance in the development and application of the TiO2 mesocrystals.展开更多
Anatase TiO2 films were successfully prepared on foam nickel substrates by sol-gel technique using tetrabutyl titanate as precursor. The characteristics of the TiO2 films were investigated by XPS, XRD, FE-SEM, TEM and...Anatase TiO2 films were successfully prepared on foam nickel substrates by sol-gel technique using tetrabutyl titanate as precursor. The characteristics of the TiO2 films were investigated by XPS, XRD, FE-SEM, TEM and UV-Vis absorption spectra. The photocatalytic activities of TiO2 films were investigated by photocatalytic degradation reactions of gaseous acetaldehyde, an indoor pollutant, under ultraviolet light irradiation. It was found that Ni^2＋ doping into TiO2 films due to the foam nickel substrates resulted in the extension of absorption edges of TiO2 films from UV region to visible light region. The pre-heating for foam nickel substrates resulted in the formation of NiO layer, which prevented effectively the injection of photogenerated electrons from TiO2 films to metal nickel. The TiO2 films displayed high photocatalytic activity for the degradation of acetaldehyde, and were enhanced by calcining the substrates and coating TiO2 films repeatedly. The high activity was mainly attributed to the improvement of the characteristics of substrate surface and the increase of active sites on photocatalyst.展开更多
TiO2 films were deposited at room temperature by DC pulse magnetron sputtering system.The crystalline structures,morphological features and photocatalytic activity of TiO2 films were systematically investigated by X-r...TiO2 films were deposited at room temperature by DC pulse magnetron sputtering system.The crystalline structures,morphological features and photocatalytic activity of TiO2 films were systematically investigated by X-ray diffraction（XRD）,atomic force microscopy（AFM） and ultraviolet spectrophotometer,respectively.The results indicated that working pressure was the key deposition parameter in？uencing the TiO2 film phase composition at room temperature,which directly affected its photocatalytic activity.With increasing working pressure,the target self-bias decreases monotonously.Therefore,low temperature TiO2 phase（anatase） could be deposited with high working pressure.The anatase TiO2 films deposited with 1.4 Pa working pressure displayed the highest photocatalytic activity by the decomposition of Methyl Orange solution,which the degradation rate reached the maximum（35%） after irradiation by ultraviolet light for 1 h.展开更多
The Ni-P/TiO2 composite film on sintered NdFeB permanent magnet was investigated by X-ray diffraction （XRD）,environmental scanning electron microscopy （ESEM）,and energy dispersive X-ray spectrometer （EDX）. The c...The Ni-P/TiO2 composite film on sintered NdFeB permanent magnet was investigated by X-ray diffraction （XRD）,environmental scanning electron microscopy （ESEM）,and energy dispersive X-ray spectrometer （EDX）. The corrosion resistance of Ni-P/TiO2 film coated on NdFeB magnet,in 0.5 mol/L NaCl solution,was studied by potentiodynamic polarization,salt spray test and electrochemical impedance spectroscopy （EIS） techniques. The self-corrosion current density （icorr） and the polarization resistance （Rp） of Ni-P/TiO2 film are 0.22 μA/cm2 （about 14% of that of Ni-P coating）,and 120 kΩ·cm2 （about 2 times of that of Ni-P coating）,respectively. The anti-salt spray time of Ni-P/TiO2 film is about 2.5 times of that of the Ni-P coating. The results indicate that Ni-P/TiO2 film has a better corrosion resistance than Ni-P coating,and the composite film increases the corrosion resistance of NdFeB magnet markedly.展开更多
Zn-doped TiO2 (Zn?TiO2) thin films were prepared by the sol?gel method on titanium substrates with heat treatment at different temperatures. The effects of heat treatment temperatures and Zn doping on the structure, p...Zn-doped TiO2 (Zn?TiO2) thin films were prepared by the sol?gel method on titanium substrates with heat treatment at different temperatures. The effects of heat treatment temperatures and Zn doping on the structure, photocathodic protection and photoelectrochemical properties of TiO2 thin films were investigated. It is indicated that the photoelectrical performance of the Zn?TiO2 films is enhanced with the addition of Zn element compared with the pure-TiO2 film and the largest decline by 897 mV in the electrode potential is achieved under 300 °C heat treatment. SEM?EDS analyses show that Zn element is unevenly distributed in Zn?TiO2 films; XRD patterns reveal that the grain size of Zn?TiO2 is smaller than that of pure-TiO2; FTIR results indicate that Zn - O bond forms on Zn?TiO2 surface. Ultraviolet visible absorption spectra prove that Zn?TiO2 shifts to visible light region.Mott?Shottky curves show that the flat-band potential of Zn?TiO2 is more negative and charge carrier density is bigger than that ofpure-TiO2, implying that under the synergy of the width of the space-charge layer, carrier density and flat-band potential, Zn?TiO2 with 300 °C heat treatment displays the best photocathodic protection performance.展开更多
With rapid progressive application of TiO2 thin films, magnetron sputtering becomes a very interesting method to prepare such multi-functional thin films. This paper focuses on influences of various deposition process...With rapid progressive application of TiO2 thin films, magnetron sputtering becomes a very interesting method to prepare such multi-functional thin films. This paper focuses on influences of various deposition processes and deposition rate on the structures and properties of TiO2 thin films. Anatase, rutile or amorphous TiO2 films with various crystalline structures and different photocatalytic, optical and electrical properties can be produced by varying sputtering gases, substrate temperature, annealing process, deposition rate and the characteristics of magnetron sputtering. This may in turn affect the functions of TiO2 films in many applications. Furthermore, TiO2-based composites films can overcome many limitations and improve the properties of TiO2 films.展开更多
文摘This paper presents the principle,properties,advantage and disadvantage,associated problems and trend of laser protection with VO 2 film for infrared detectors in the range of 3～5μm and 8～12μm regions and suggests VO 2 film is a potential protection material for infrared detectors.
文摘We synthesized a mesoporous film based on TiO2-reduced graphene oxide(RGO)hybrids using a one-step vapor-thermal method without the need for an additional annealing process.The vapor-thermally prepared TiO2-graphene hybrid(VTH)features unique structures with an ultra-large specific surface area of^260 m^2 g^-1 and low aggregation,giving rise to enhanced light harvesting and increased charge generation and separation efficiency.It was observed that a mesoporous film with uniform pore distribution is simultaneously obtained during the VTH growth process.When a 5.0 wt%RGO VTH film was used as the active layer in photocatalysis,the highest photocatalytic activity for degradation of methyl orange was achieved.For another,when a 0.75 wt%RGO VTH film was used as the photoanode in a dye-sensitized solar cell,the power conversion efficiency reached 7.58%,which represents an increase of 73.1%compared to a solar cell using an a photoanode of pure TiO2 synthesized by a traditional solvothermal method.It is expected that this facile method for the synthesis of TiO2/graphene hybrid mesoporous films will be useful in practical applications for preparing other metal oxide/graphene hybrids with ultra-high photocatalytic activity and photovoltaic performance.
基金financial supports from National Natural Science Foundation of China(51772135)the Ministry of Education of China(6141A02022516)+4 种基金the Fundamental Research Funds for the Central Universities(11619103)the China Postdoctoral Science Foundation(2019M663376)the Natural Science Foundation of Guangdong Province,China(Grant Nos.2017A020215135 and2018A030310659)Guangdong Basic and Applied Basic Research Foundation(2020A1515011377)the Science and Technology Program of Guangzhou,China(Grant No.201804010432)。
文摘High ultraviolet(UV)stability and low dark current(Idark)are necessary for high-quality perovskite photodetectors(PDs).TiO^(2)thin film is known as effective electron-transport-layer(ETL)for perovskite devices.However,common spin-coated TiO^(2)ETLs endow many surface defects and have strong UV photocatalytic effect to decompose perovskite materials,resulting in inferior stability of devices.In this work,TiO^(2)bilayer film(Bi-TiO^(2))has been fabricated by combining spin-coating and atomic-layer-deposition process and its positive effects on UV stability and Idarkof Cs2 AgBiBr6-based PDs have been revealed for the first time.It is demonstrated that Bi-TiO^(2)possesses fewer surface defects and smoother morphology with type II band alignment,which is beneficial to suppress photocatalytic activity of TiO^(2)and reduce carrier recombination at the interface.After accelerated strong UV aging treatment,the PD with Bi-TiO^(2)maintains excellent performance,whereas the PD with spin-coated TiO^(2)film dramatically deteriorate with on-off ratio drops from~102 to~2.Besides,the Idarkof PD remarkably decreases from~10^(-8) A to~10^(-10) A after bilayer optimization.Furthermore,we have integrated the corresponding PDs into a self-built imaging system adopting diffuse reflection mode.This work suggests a feasible approach to fabricate TiO^(2)/Cs2 AgBiBr6-based PDs with remarkable UV tolerance for imaging applications.
文摘We investigated the effects of using different thicknesses of pure and vanadium-doped thin films of TiO2 as the electron transport layer in the inverted configuration of organic photovoltaic cells based on poly（3-hexylthiophene） P3HT：[6-6] phenyl-（6） butyric acid methyl ester（PCBM）. 1% vanadium-doped TiO2nanoparticles were synthesized via the solvothermal method. Crystalline structure, morphology, and optical properties of pure and vanadium-doped TiO2 thin films were studied by different techniques such as x-ray diffraction, scanning electron microscopy, transmittance electron microscopy, and UV–visible transmission spectrum. The doctor blade method which is compatible with roll-2-roll printing was used for deposition of pure and vanadium-doped TiO2 thin films with thicknesses of 30 nm and 60 nm. The final results revealed that the best thickness of TiO2 thin films for our fabricated cells was 30 nm. The cell with vanadium-doped TiO2 thin film showed slightly higher power conversion efficiency and great Jsc of 10.7 mA/cm^2 compared with its pure counterpart. In the cells using 60 nm pure and vanadium-doped TiO2 layers, the cell using the doped layer showed much higher efficiency. It is remarkable that the external quantum efficiency of vanadium-doped TiO2 thin film was better in all wavelengths.
基金Project(gf200901002)supported by the Open Research Fund of National Defense Key Disciplines Laboratory of Light Alloy Processing Science and Technology of Nanchang Hangkong University,China
文摘ZrO2/TiO2 composite photocatalytic film was produced on the pure titanium substrate using in-situ Zr（OH）4 colloidal particle by the micro-arc oxidation technique and characterized by scanning electron microscope （SEM）, energy dispersive X-ray （EDX）, X-ray diffraction （XRD） and ultraviolet-visible （UV-Vis） spectrophotometer. The composite film shows a lamellar and porous structure which consists of anatase, futile and ZrO2 phases. The optical absorption edge of film is shifted to longer wavelength when ZrO2 is introduced to TiO2. Furthermore, the photocatalytic reaction rate constants of degradation of rhodamine B solution with ZrO2/TiO2 composite film and pure TiO2 film under ultraviolet irradiation are measured as 0.0442 and 0.0186 h 1, respectively.
文摘The titanium oxide （TiO2） nanotubes have attracted attention for their use in dye-sensitized solar cells as photoanode. In this study semiconducting cadmium sulfide （CdS） nanoparticles arc grown on top opened TiO2 nanotubes arrays by radio-frequency magnetron sputtering. X-ray diffraction, scanning electron mieroscopy, transmission electron microscopy and diffuse reflection spectra are used to study structural, morphological and optical properties of the CdS/TiO2 bilayer.
基金Project(21471054)supported by the National Natural Science Foundation of China
文摘A novel WO3-x/TiO2 film as photoanode was synthesized for photoelectrocatalytic（PEC） reduction of CO2 into formic acid（HCOOH）. The films prepared by doctor blade method were characterized with X-ray diffractometer（XRD）, scanning electron microscope（SEM） and transmission electron microscope（TEM）. The existence of oxygen vacancies in the WO3-x was confirmed with an X-ray photoelectron spectroscopy（XPS）, and the accurate oxygen index was determined by a modified potentiometric titrimetry method. After 3h of photoelectrocatalytic reduction, the formic acid yield of the WO3-x/TiO2 film is 872 nmol/cm^2, which is 1.83 times that of the WO3/TiO2 film. The results of PEC performance demonstrate that the introduction of WO3-x nanoparticles can improve the charge transfer performance so as to enhance the performance of PEC reduction of CO2 into formic acid.
文摘Nano sized powders of TiO2 （titanium dioxide） and Nb2O5 （Niobium （V） oxide） were used to fabricate TiO2/Nb2O5 composites thin films by EPD （electrophoretic deposition） technique. The metal oxide powders, together with magnesium nitrate hexahydrate pellets, were suspended in propan-2-ol inside an EPD cell. The electrodes, placed 1.2 cm apart, were partially immersed in the suspension and a DC potential applied across them. Key EPD process parameters, which include applied DC electric field, deposition time and solid concentration in suspension, were optimized through visual inspection and from UV-Vis-NIR spectrophotometer spectra. The highest （55%） transmittance was obtained for films with deposition time of 90 s, powder concentration of 0.01 g/40 mL, and 35 V DC （direct current） voltage. XRD micrographs confirmed that TiO2 and Nb2O5 particles were presented in the composite film. SEM （scanning electron microscope） micrographs of the composite electrode thin films showed that porous films of high quality with well controlled morphology were deposited by using the EPD technique.
基金Project (2010JQ6008) supported by the Natural Science Foundation of Shaanxi Province,China
文摘Series of TiO 2-ZnO heterojunction composite films with different n（Zn）/n（Ti） ratios were prepared by UDP450 magnetron sputter ion plating equipment, and the mole ratio of Zn to Ti was controlled by adjusting the current values of sputtering target. The effects of n（Zn）/n（Ti） on the microstructures of TiO2-ZnO films were investigated by SEM, AFM, Raman and XPS, and their photocatalytic decomposition of methyl orange solutions was evaluated. The results show that an increase in n（Zn）/n（Ti） typically results in a decrease in the grain size of composite films firstly and then an increase of grain size, while an increase in n（Zn）/n（Ti） leads to an increase in film roughness firstly and then a decrease in film roughness. Both grain size and roughness of TiO2-ZnO films reach the maximum and minimum at n（Zn）/n（Ti） of 1/9.3, respectively. The n（Zn）/n（Ti） shows little effect on the valences of Zn and Ti elements, which mainly exist in the form of TiO2 and ZnO phases. The n（Zn）/n（Ti） has influence on the amount of anatase/rutile TiO2 heterojunction in the film. With increase of the n（Zn）/n（Ti）, the absorption intensity of the composite film increases and the absorption region extends to 450 nm, which is redshifted as much as 150 nm in comparison with the pure TiO2 films. However, the photocatalytic abilities of heterogeneous composite films do not depend on the n（Zn）/n（Ti） but rather on the microstructures of the TiO2-ZnO composite films. Degradation rate of the film reaches the maximum and the photocatalytic decomposition of pollutants works best when n（Zn）/n（Ti）=1：9.3.
文摘A novel titanium dioxide （TiO2） film comprising both nanotubes and nanopaticles was fabricated by an anodization process of the modified titanium. The local electric field at the anodized surface was simulated and its influence on the morphology of the TiO2 film was discussed. The results show that the electric field strength is enhanced by the covering. The growth rate of TiO2 increases with the assist of the local electric field. However, TiO2 dissolution is hindered since the local electric field prevents [TiF6]6- from diffusing. It means that the balance condition for the formation of nanotubes is broken, and TiO2 nanoparticles are formed. Moreover, the crystal structure of the TiO2 film was confirmed using X-ray diffraction and Raman analysis. The anatase is a main phase for the proposed film.
文摘TiO2 mesocrystals can considerably enhance charge separation owing to their oriented superstructures,with fewer internal defects and porous properties providing more active sites.In this work,we prepared TiO2 mesocrystal films by a direct annealing method.The morphology and crystal phase of the film were controlled by adjusting the ratio of NH4F and the calcination temperature.Moreover,we found that Au nanoparticles loaded on a TiO2 mesocrystal film enabled highly efficient visible light photocatalytic properties.The photocatalytic activities were studied by hydrogen generation and photoreduction of Cr(VI).This work represents a considerable advance in the development and application of the TiO2 mesocrystals.
基金Project supported by the Special Foundation of Nanometer Technology from Shanghai Municipal Science and Technology Commis-sion(STCSM) (No. 0552nm002).
文摘Anatase TiO2 films were successfully prepared on foam nickel substrates by sol-gel technique using tetrabutyl titanate as precursor. The characteristics of the TiO2 films were investigated by XPS, XRD, FE-SEM, TEM and UV-Vis absorption spectra. The photocatalytic activities of TiO2 films were investigated by photocatalytic degradation reactions of gaseous acetaldehyde, an indoor pollutant, under ultraviolet light irradiation. It was found that Ni^2＋ doping into TiO2 films due to the foam nickel substrates resulted in the extension of absorption edges of TiO2 films from UV region to visible light region. The pre-heating for foam nickel substrates resulted in the formation of NiO layer, which prevented effectively the injection of photogenerated electrons from TiO2 films to metal nickel. The TiO2 films displayed high photocatalytic activity for the degradation of acetaldehyde, and were enhanced by calcining the substrates and coating TiO2 films repeatedly. The high activity was mainly attributed to the improvement of the characteristics of substrate surface and the increase of active sites on photocatalyst.
基金supported by the Dalian Foundation for Development of Science and Technology (No.2006A13GX029)
文摘TiO2 films were deposited at room temperature by DC pulse magnetron sputtering system.The crystalline structures,morphological features and photocatalytic activity of TiO2 films were systematically investigated by X-ray diffraction（XRD）,atomic force microscopy（AFM） and ultraviolet spectrophotometer,respectively.The results indicated that working pressure was the key deposition parameter in？uencing the TiO2 film phase composition at room temperature,which directly affected its photocatalytic activity.With increasing working pressure,the target self-bias decreases monotonously.Therefore,low temperature TiO2 phase（anatase） could be deposited with high working pressure.The anatase TiO2 films deposited with 1.4 Pa working pressure displayed the highest photocatalytic activity by the decomposition of Methyl Orange solution,which the degradation rate reached the maximum（35%） after irradiation by ultraviolet light for 1 h.
基金Sponsored by Hi-Tech Research and Development Program of China (2003AA305120)
文摘The Ni-P/TiO2 composite film on sintered NdFeB permanent magnet was investigated by X-ray diffraction （XRD）,environmental scanning electron microscopy （ESEM）,and energy dispersive X-ray spectrometer （EDX）. The corrosion resistance of Ni-P/TiO2 film coated on NdFeB magnet,in 0.5 mol/L NaCl solution,was studied by potentiodynamic polarization,salt spray test and electrochemical impedance spectroscopy （EIS） techniques. The self-corrosion current density （icorr） and the polarization resistance （Rp） of Ni-P/TiO2 film are 0.22 μA/cm2 （about 14% of that of Ni-P coating）,and 120 kΩ·cm2 （about 2 times of that of Ni-P coating）,respectively. The anti-salt spray time of Ni-P/TiO2 film is about 2.5 times of that of the Ni-P coating. The results indicate that Ni-P/TiO2 film has a better corrosion resistance than Ni-P coating,and the composite film increases the corrosion resistance of NdFeB magnet markedly.
基金Project(cstc2011jj A50008)supported by the Natural Science Foundation of Chongqing,ChinaProject(14ZB0025)supported by Education Department of Sichuan Province,China
文摘Zn-doped TiO2 (Zn?TiO2) thin films were prepared by the sol?gel method on titanium substrates with heat treatment at different temperatures. The effects of heat treatment temperatures and Zn doping on the structure, photocathodic protection and photoelectrochemical properties of TiO2 thin films were investigated. It is indicated that the photoelectrical performance of the Zn?TiO2 films is enhanced with the addition of Zn element compared with the pure-TiO2 film and the largest decline by 897 mV in the electrode potential is achieved under 300 °C heat treatment. SEM?EDS analyses show that Zn element is unevenly distributed in Zn?TiO2 films; XRD patterns reveal that the grain size of Zn?TiO2 is smaller than that of pure-TiO2; FTIR results indicate that Zn - O bond forms on Zn?TiO2 surface. Ultraviolet visible absorption spectra prove that Zn?TiO2 shifts to visible light region.Mott?Shottky curves show that the flat-band potential of Zn?TiO2 is more negative and charge carrier density is bigger than that ofpure-TiO2, implying that under the synergy of the width of the space-charge layer, carrier density and flat-band potential, Zn?TiO2 with 300 °C heat treatment displays the best photocathodic protection performance.
文摘With rapid progressive application of TiO2 thin films, magnetron sputtering becomes a very interesting method to prepare such multi-functional thin films. This paper focuses on influences of various deposition processes and deposition rate on the structures and properties of TiO2 thin films. Anatase, rutile or amorphous TiO2 films with various crystalline structures and different photocatalytic, optical and electrical properties can be produced by varying sputtering gases, substrate temperature, annealing process, deposition rate and the characteristics of magnetron sputtering. This may in turn affect the functions of TiO2 films in many applications. Furthermore, TiO2-based composites films can overcome many limitations and improve the properties of TiO2 films.