The SrFe12O19@carbonyl iron(CI) core–shell composites used in microwave absorption are prepared by the metal–organic chemical vapor deposition(MOCVD). The x-ray diffractometer, scanning electron microscope, energy d...The SrFe12O19@carbonyl iron(CI) core–shell composites used in microwave absorption are prepared by the metal–organic chemical vapor deposition(MOCVD). The x-ray diffractometer, scanning electron microscope, energy dispersive spectrometer, and vector network analyzer are used to characterize the structural, electromagnetic, and absorption properties of the composites. The results show that the SrFe12O19@CI composites with a core–shell structure could be successfully prepared under the condition: deposition temperatures above 180℃, deposition time 30 min, and gas flow rate 30 m L/min.The electromagnetic properties of the composites change significantly, and their absorption capacities are improved. Of the obtained samples, those samples prepared at a deposition temperature of 180℃ exhibit the best absorption performance.The reflection loss of SrFe12O19@CI(180℃) with 1.5 mm–2.5 mm in thickness is less than-10 dB in a frequency range of 8 GHz–18 GHz, which covers the whole X band and Ku band.展开更多
为了与低温共烧陶瓷(LTCC)技术兼容,采用热压烧结工艺在870℃制备了添加不同Bi_2O_3含量的SrFe_(12)O_(19)铁氧体材料,着重研究了材料的晶相组成、烧结密度、气孔率和磁性能等低温烧结特性。研究结果表明,材料在870℃烧结时,Bi_2O_3的...为了与低温共烧陶瓷(LTCC)技术兼容,采用热压烧结工艺在870℃制备了添加不同Bi_2O_3含量的SrFe_(12)O_(19)铁氧体材料,着重研究了材料的晶相组成、烧结密度、气孔率和磁性能等低温烧结特性。研究结果表明,材料在870℃烧结时,Bi_2O_3的添加促进了SrFe_(12)O_(19)晶相结构的形成,提高了材料的烧结致密度和磁性能。当Bi_2O_3的添加量(质量分数)为2%~4%,材料可以获得致密的结构,烧结密度达到4.65 g·cm^(-3)以上,气孔率低于10%,材料的饱和磁化强度Ms和内禀矫顽力Hci较高,分别达到252.4 k A·m^(-1)和312.9k A·m^(-1)以上。此外,基于SrFe_(12)O_(19)材料的低温烧结特性讨论了该材料在微波LTCC环行器当中的应用。展开更多
采用水热法合成了M型Sr Fe12O19铁氧体粉末,并对其烧结前后的结构和磁性能进行了研究。实验发现,无论烧结前还是后样品都是单相铁氧体结构。烧结后,样品的矫顽力和饱和磁化强度分别从42.9 k A/m和48.1 emu/g显著增加到237.8 k A/m和64.9...采用水热法合成了M型Sr Fe12O19铁氧体粉末,并对其烧结前后的结构和磁性能进行了研究。实验发现,无论烧结前还是后样品都是单相铁氧体结构。烧结后,样品的矫顽力和饱和磁化强度分别从42.9 k A/m和48.1 emu/g显著增加到237.8 k A/m和64.9 emu/g,这与高温烧结后其晶粒的长大密切相关。实验还发现,烧结后样品中存在着剩磁增强效应,其原因可归于样品中不同磁硬度的纳米晶相之间的磁耦合作用。展开更多
文摘The SrFe12O19@carbonyl iron(CI) core–shell composites used in microwave absorption are prepared by the metal–organic chemical vapor deposition(MOCVD). The x-ray diffractometer, scanning electron microscope, energy dispersive spectrometer, and vector network analyzer are used to characterize the structural, electromagnetic, and absorption properties of the composites. The results show that the SrFe12O19@CI composites with a core–shell structure could be successfully prepared under the condition: deposition temperatures above 180℃, deposition time 30 min, and gas flow rate 30 m L/min.The electromagnetic properties of the composites change significantly, and their absorption capacities are improved. Of the obtained samples, those samples prepared at a deposition temperature of 180℃ exhibit the best absorption performance.The reflection loss of SrFe12O19@CI(180℃) with 1.5 mm–2.5 mm in thickness is less than-10 dB in a frequency range of 8 GHz–18 GHz, which covers the whole X band and Ku band.
基金The Scientific Research Foundation of Education Office of Sichuan Province(13Z198)The Young and Middle-aged Academic Leaders of Scientific Research Funds of Chengdu University of Information Technology(J201222)
文摘为了与低温共烧陶瓷(LTCC)技术兼容,采用热压烧结工艺在870℃制备了添加不同Bi_2O_3含量的SrFe_(12)O_(19)铁氧体材料,着重研究了材料的晶相组成、烧结密度、气孔率和磁性能等低温烧结特性。研究结果表明,材料在870℃烧结时,Bi_2O_3的添加促进了SrFe_(12)O_(19)晶相结构的形成,提高了材料的烧结致密度和磁性能。当Bi_2O_3的添加量(质量分数)为2%~4%,材料可以获得致密的结构,烧结密度达到4.65 g·cm^(-3)以上,气孔率低于10%,材料的饱和磁化强度Ms和内禀矫顽力Hci较高,分别达到252.4 k A·m^(-1)和312.9k A·m^(-1)以上。此外,基于SrFe_(12)O_(19)材料的低温烧结特性讨论了该材料在微波LTCC环行器当中的应用。
文摘采用水热法合成了M型Sr Fe12O19铁氧体粉末,并对其烧结前后的结构和磁性能进行了研究。实验发现,无论烧结前还是后样品都是单相铁氧体结构。烧结后,样品的矫顽力和饱和磁化强度分别从42.9 k A/m和48.1 emu/g显著增加到237.8 k A/m和64.9 emu/g,这与高温烧结后其晶粒的长大密切相关。实验还发现,烧结后样品中存在着剩磁增强效应,其原因可归于样品中不同磁硬度的纳米晶相之间的磁耦合作用。