Polyaniline （PAn） sensitized nanocrystalline TiO2 composites （TiO2/PAn） were successfully prepared and used as an efficient photocatalyst for the degradation of dye methylene blue （MB）. The results showed that P...Polyaniline （PAn） sensitized nanocrystalline TiO2 composites （TiO2/PAn） were successfully prepared and used as an efficient photocatalyst for the degradation of dye methylene blue （MB）. The results showed that PAn was able to sensitize TiO2 efficiently and the composite photocatalyst could be activated by absorbing both the ultraviolet and visible light （λ： 190 ～ 800 nm）, whereas pure TiO2 absorbed ultraviolet light only （λ 〈 380 nm）. Under the irradiation of natural light, MB could be degraded more efficiently on the TiO2/PAn composites than on the TiO2 Furthermore, it could be easily separated from the solution by simple sedimentation.展开更多
Silver/titanium dioxide composite nanoparticles imbedded in polyacrylonitrile (PAN) nanofibers and converted into carbon nanofibers by stabilization and calcination was obtained and tested for capacitive deionization ...Silver/titanium dioxide composite nanoparticles imbedded in polyacrylonitrile (PAN) nanofibers and converted into carbon nanofibers by stabilization and calcination was obtained and tested for capacitive deionization technology. First, the silver ions were converted to metallic silver nanoparticles, through reduction of silver nitrate with dilute solution of PAN. Second, the TiO2 precursor (Titanium Isopropoxide) was added to the solution to form Ag/TiO2 composites imbedded in the PAN polymer solution. Last step involves electrospinning of viscous PAN solution containing silver/TiO2 nanoparticles, thus obtaining PAN nanofibers containing silver/TiO2 nanoparticles. Scanning electron microscopy (SEM) revealed that the diameter of the nanofibers ranged between 50 and 300 nm. Transmission electron microscopy (TEM) and energy dispersive spectroscopy (EDS) showed silver/TiO2 nanoparticles dispersed on the surface of the carbon nanofibers. The obtained fiber was fully characterized by measuring and comparing the FTIR spectra and thermogravimetric analysis (TGA) diagrams of PAN nanofiber with and without imbedded nanoparticles, in order to show the effect of silver/TiO2 nanoparticles on the electrospun fiber properties.展开更多
文摘Polyaniline （PAn） sensitized nanocrystalline TiO2 composites （TiO2/PAn） were successfully prepared and used as an efficient photocatalyst for the degradation of dye methylene blue （MB）. The results showed that PAn was able to sensitize TiO2 efficiently and the composite photocatalyst could be activated by absorbing both the ultraviolet and visible light （λ： 190 ～ 800 nm）, whereas pure TiO2 absorbed ultraviolet light only （λ 〈 380 nm）. Under the irradiation of natural light, MB could be degraded more efficiently on the TiO2/PAn composites than on the TiO2 Furthermore, it could be easily separated from the solution by simple sedimentation.
文摘Silver/titanium dioxide composite nanoparticles imbedded in polyacrylonitrile (PAN) nanofibers and converted into carbon nanofibers by stabilization and calcination was obtained and tested for capacitive deionization technology. First, the silver ions were converted to metallic silver nanoparticles, through reduction of silver nitrate with dilute solution of PAN. Second, the TiO2 precursor (Titanium Isopropoxide) was added to the solution to form Ag/TiO2 composites imbedded in the PAN polymer solution. Last step involves electrospinning of viscous PAN solution containing silver/TiO2 nanoparticles, thus obtaining PAN nanofibers containing silver/TiO2 nanoparticles. Scanning electron microscopy (SEM) revealed that the diameter of the nanofibers ranged between 50 and 300 nm. Transmission electron microscopy (TEM) and energy dispersive spectroscopy (EDS) showed silver/TiO2 nanoparticles dispersed on the surface of the carbon nanofibers. The obtained fiber was fully characterized by measuring and comparing the FTIR spectra and thermogravimetric analysis (TGA) diagrams of PAN nanofiber with and without imbedded nanoparticles, in order to show the effect of silver/TiO2 nanoparticles on the electrospun fiber properties.