To improve the compactness and properties of C/C-SiC-ZrC composites produced by precursor infiltration and pyrolysis(PIP)method,the low-temperature reactive melt infiltration(RMI)process was used to seal the composite...To improve the compactness and properties of C/C-SiC-ZrC composites produced by precursor infiltration and pyrolysis(PIP)method,the low-temperature reactive melt infiltration(RMI)process was used to seal the composites using Zr_(2)Cu as the filler.The microstructure,mechanical properties,and ablation properties of the Zr_(2)Cu packed composites were analyzed.Results show that during Zr_(2)Cu impregnation,the melt efficiently fills the large pores of the composites and is converted to ZrCu due to a partial reaction of zirconium with carbon.This results in an increase in composite density from 1.91 g/cm^(3)to 2.24 g/cm^(3)and a reduction in open porosity by 27.35%.Additionally,the flexural strength of Zr_(2)Cu packed C/C-SiC-ZrC composites is improved from 122.78±8.09 MPa to 135.53±5.40 MPa.After plasma ablation for 20 s,the modified composites demonstrate superior ablative resistance compared to PIP C/C-SiC-ZrC,with mass ablation and linear ablation rates of 2.77×10^(−3)g/s and 2.60×10^(−3)mm/s,respectively.The“selftranspiration”effect of the low-melting point copper-containing phase absorbs the heat of the plasma flame,further reducing the ablation temperature and promoting the formation of refined ZrO_(2)particles within the SiO_(2)melting layer.This provides more stable erosion protection for Zr_(2)Cu packed C/C-SiC-ZrC composites.展开更多
Compared with Cu/Al_(2)O_(3)composites,high-strength Cu/Al_(2)O_(3)composites usually exhibit obviously deteriorated electrical conductivity.A chemical and mechanical alloying-based strategy was adopted to fabricate u...Compared with Cu/Al_(2)O_(3)composites,high-strength Cu/Al_(2)O_(3)composites usually exhibit obviously deteriorated electrical conductivity.A chemical and mechanical alloying-based strategy was adopted to fabricate ultrafine composite powders with lowcontent reinforcement and constructed a combined structure of Cu ultrafine powders covered with in-situ Al_(2)O_(3)nanoparticles.After consolidation at a relatively lower sintering temperature of 550℃,high-volume-fraction ultrafine grains were introduced into the Cu/Al_(2)O_(3)composite,and many in-situ Al_(2)O_(3)nanoparticles with an average size of 11.7±7.5 nm were dispersed homogeneously in the Cu grain.Results show that the composite demonstrates an excellent balance of high tensile strength(654±1 MPa)and high electrical conductivity(84.5±0.1%IACS),which is ascribed to the synergistic strengthening effect of ultrafine grains,dislocations,and in-situ Al_(2)O_(3)nanoparticles.This approach,which utilizes ultrafine composite powder with low-content reinforcement as a precursor and employs low-temperature and high-pressure sintering subsequently,may hold promising potential for large-scale industrial production of high-performance oxide dispersion strengthened alloys.展开更多
Two Al2O3/Cu composites containing 0.24 wt.% Al2O3 and 0.60 wt.% Al2O3 separately are prepared by internal oxidation. Effects of sliding speed and pressure on the frictional characteristics of the composites and coppe...Two Al2O3/Cu composites containing 0.24 wt.% Al2O3 and 0.60 wt.% Al2O3 separately are prepared by internal oxidation. Effects of sliding speed and pressure on the frictional characteristics of the composites and copper against brass are investigated and compared. The changes in morphology of the sliding surface and subsurface are examined with scanning electron microscope （SEM） and energy dispersive X-ray spectrum （EDS）. The results show that the wear resistance of the Al2O3/Cu composites is superior to that of copper under the same conditions, Under a given electrical current, the wear rate of Al2O3/Cu composites decreases as the Al2O3-content increases, However, the wear rates of the Al2O3/Cu composites and copper increase as the sliding speed and pressure increase under dry sliding condition. The main wear mechanisms for Al2O3/Cu composites are of abrasion and adhesion; for copper, it is adhesion, although wear by oxidation and electrical erosion can also be observed as the speed and pressure rise.展开更多
Cu2O/TiOa/Pt three-layer films were deposited on glass substrates using magnetron sputtering method. The surface morphology and the optical properties of the composite film were characterized by X-ray diffraction （XR...Cu2O/TiOa/Pt three-layer films were deposited on glass substrates using magnetron sputtering method. The surface morphology and the optical properties of the composite film were characterized by X-ray diffraction （XRD）, scanning electron microscopy （SEM）, ultraviolet- visible spectroscopy （UV-Vis） and photoluminescence spectroscopy （PL）. The photocatalytic activity of the samples was evaluated by the photocatalytic degradation of methyl orange （MO） aqueous solution under visible light irradiation. The results indicate that the Cu2O/TiO2/Pt composite films are made up of three layers which are Pt layer, anatase-TiO2 layer and Cu2O layer from bottom to top. The surface of the films is even and composed of regular-shaped spherical particles. The photocatalytic activity of the Cu2O/TiO2/Pt three-layer film is much higher than that of the Cu2O/TiO2 double-layer film. Such enhancement is ascribed to the presence of Pt layer, which further inhibits the photogenerated electron-hole recombination, prolongs the lifetime of the photogenerated carriers, increases the quantum efficiency and hence improves the photocatalytic activity of the film effectively.展开更多
A heat-resistant dispersion-strengthening nano-Al_2O_3/Cu composite with highstrength and high electric conductivity was fabricated in a multiplex medium. The internaloxidation product, microstructures and properties ...A heat-resistant dispersion-strengthening nano-Al_2O_3/Cu composite with highstrength and high electric conductivity was fabricated in a multiplex medium. The internaloxidation product, microstructures and properties of the composite, and the process flow weresystematically studied. It is confirmed that this new technique simplifies the process and improvesthe properties of the composite. X-ray analysis indicates that the alumina particles formed duringinternal oxidation consist of a large mount of gamma-Al_2O_3 and a certain amount of theta-Al_2O_3and alpha-Al_2O_3. TEM observation shows that the obtained gamma-Al_2O_3 nano-particles areuniformly distributed in the copper grains; their mean size and space between particles are 7 runand 30 nm, respectively. The main properties of the composite with 50 percent cold deformation areas follows: the electric conductivity is 51 MS/m (87 percent IACS), sigma_b = 628 MPa, and thehardness is HRB86. After annealing at 1273 K, all or most of the above properties remain, and themicrostructures are still dependent on elongated fiber-form grains.展开更多
The preferred internal oxidation of aluminum in Cu Al alloy was used to obtain in situ Al 2O 3/Cu composites. The reinforcement particles were mainly γ Al 2O 3, some θ Al 2O 3 and a little α Al 2O 3. Thermodynamics...The preferred internal oxidation of aluminum in Cu Al alloy was used to obtain in situ Al 2O 3/Cu composites. The reinforcement particles were mainly γ Al 2O 3, some θ Al 2O 3 and a little α Al 2O 3. Thermodynamics analyses show that the chemical reactions are 3Cu 2O+2Al=6Cu+Al 2O 3 or 3CuO+2Al=3Cu+Al 2O 3. A related equilibrium diagram was drawn. The experiments and investigation show that the formation rate of Al 2O 3 was controlled by the diffusion of oxygen in matrix.展开更多
Ni(Co/Zn/Cu)Fe_2O_4/SiC@SiO_2, a microwave absorber, was prepared by the sol-gel method. The phase structure and the morphology of the microwave absorbers were characterized by X-Ray Diffraction(XRD) and scanning elec...Ni(Co/Zn/Cu)Fe_2O_4/SiC@SiO_2, a microwave absorber, was prepared by the sol-gel method. The phase structure and the morphology of the microwave absorbers were characterized by X-Ray Diffraction(XRD) and scanning electron microscopy(SEM), respectively. Laser sizer(LS) and X-ray photoelectron spectroscopy(XPS) analysis show the core-shell structure of SiC@SiO_2. Coaxial method was used to measure the microwave absorption properties of the prepared composites in the frequency range of 2-18 GHz. When 70 wt% SiC is wrapped by 30 wt% SiO_2,and 50 wt% NiFe_2O_4 is added into 50 wt% SiC@SiO_2, the as-prepared powders are found to have advanced microwave absorption properties with a minimum reflection loss(RL) of -32.26 dB at about 6.08 GHz, and the available bandwidth is approximately 2.1 GHz when the RL is below -10 dB.展开更多
A magnetically separable Cu2O/Fe3O4 magnetic composite photocatalyst was synthesized in large quantities by a fast and simple route. The as-prepared photocatalysts were characterized by scanning electron microscopy （...A magnetically separable Cu2O/Fe3O4 magnetic composite photocatalyst was synthesized in large quantities by a fast and simple route. The as-prepared photocatalysts were characterized by scanning electron microscopy （SEM）, transmission electron microscopy （TEM）, X-ray photoelectron spectroscopy （XPS） and X-ray diffraction （XRD）. Furthermore, the Cu2O/Fe3O4 composite photocatalysts were tested using methyl orange （MO） degradation reaction under visible light irradiation （100 mW/cm2） and demonstrated to have a high photocatalytic efficiency toward the decomposition of MO under visible light irradiation with good recyclability.展开更多
ZrO2/TiO2 composite photocatalytic film was produced on the pure titanium substrate using in-situ Zr（OH）4 colloidal particle by the micro-arc oxidation technique and characterized by scanning electron microscope （...ZrO2/TiO2 composite photocatalytic film was produced on the pure titanium substrate using in-situ Zr（OH）4 colloidal particle by the micro-arc oxidation technique and characterized by scanning electron microscope （SEM）, energy dispersive X-ray （EDX）, X-ray diffraction （XRD） and ultraviolet-visible （UV-Vis） spectrophotometer. The composite film shows a lamellar and porous structure which consists of anatase, futile and ZrO2 phases. The optical absorption edge of film is shifted to longer wavelength when ZrO2 is introduced to TiO2. Furthermore, the photocatalytic reaction rate constants of degradation of rhodamine B solution with ZrO2/TiO2 composite film and pure TiO2 film under ultraviolet irradiation are measured as 0.0442 and 0.0186 h 1, respectively.展开更多
In situ TiB2/Cu composites were fabricated by both solid-liquid(S-L)and liquid-liquid(L-L)reactive spray deposition in combination with cold rolling and annealing.The microstructure and properties of the fabricated Ti...In situ TiB2/Cu composites were fabricated by both solid-liquid(S-L)and liquid-liquid(L-L)reactive spray deposition in combination with cold rolling and annealing.The microstructure and properties of the fabricated TiB2/Cu composites were investigated.The results show that the reactive mode and rolling treatment are the main factors affecting the microstructure and properties of the TiB2/Cu composite.The in situ reaction in the L-L reaction can be carried out more completely.By controlling the rolling and annealing process,the relative density and the properties of the as-deposited composites are optimized.The comprehensive performance of the deformed TiB2/Cu composite prepared by L-L reactive spray deposition(401 MPa and 83.5%IACS)is better than that by S-L reactive spray deposition(520 MPa and 20.2%IACS).展开更多
Al2O3 particle-reinforced ZL109 composite was prepared by in situ reaction between CuO and Al2O3 . The microstructure was observed by means of OM, SEM and TEM. The Al2O3 particles in sub-micron sizes distribute unifo...Al2O3 particle-reinforced ZL109 composite was prepared by in situ reaction between CuO and Al2O3 . The microstructure was observed by means of OM, SEM and TEM. The Al2O3 particles in sub-micron sizes distribute uniformly in the matrix, and the Cu displaced from the in situ reaction forms net-like alloy phases with other alloy elements. The hardness and the tensile strength of the composites at room temperature have a slight increase as compared to that of the matrix. However, the tensile strength at 350℃ has reached 90.23 MPa, or 16.92 MPa higher than that of the matrix. The mechanism of the reaction in the CuO/AI system was studied by using of differential scanning calorimetry（DSC） and thermodynamic calculation. The reaction between CuO and Al involves two steps. First, CuO reacts with Al to form Cu20 and Al2O3 at the melting temperature of the matrix alloy, and second, Cu20 reacts with Al to form Cu and Al2O3 at a higher temperature. At ZL109 casting temperature of 750- 780 ℃, the second step can also take place because of the effect of exothermic reaction of the first step.展开更多
TiO2-coated activated carbon surface （TAs） composites were prepared by a sol-gel method with supercritical pretreatment. The photocatalytic degradation of acid yellow （AY） was investigated under UV radiation to es...TiO2-coated activated carbon surface （TAs） composites were prepared by a sol-gel method with supercritical pretreatment. The photocatalytic degradation of acid yellow （AY） was investigated under UV radiation to estimate activity of catalysts and determine the kinetics. And the effects of parameters including the initial concentration of AY, light intensity and TiO2 content in catalysts were examined. The results indicate that TAs has a higher efficiency in decomposition of AY than P25, pure TiO2 particles as well as the mixture of TiO2 powder and active carbon. The photocatalytic degradation rate is found to follow the pseudo-first order kinetics with respect to the AY concentration. The new kinetic model fairly resembles the classic Langmuir-Hinshelwood equation, and the rate constant is proportional to the square root of the light intensity in a wide range. However, its absorption performance depends on the surface areas of catalysts. The model fits quite well with the experimental data and elucidates phenomena about the effects of the TiO2 content in TAs on the degradation rate.展开更多
A facile ammonium-dichromate solution immersion method was introduced to synthesize the copperwettable Cr3C2 coating on and inside the carbon-carbon （C/C） preform. The formation mechanism and the microstructures of ...A facile ammonium-dichromate solution immersion method was introduced to synthesize the copperwettable Cr3C2 coating on and inside the carbon-carbon （C/C） preform. The formation mechanism and the microstructures of the Cr3C2 coatings were studied. The contact angle between molten copper and the C/C decreased from 140°to 60°, demonstrating the significant improvement in the wettability. The Cr3C2- coated C/C-Cu composite with only 4.2% porosity and 3.69 gcm^-3 density was manufactured through copper infiltration. As a result, the thermal and electrical conductivity of the modified C/C-Cu increased significantly due to the infiltrated copper. Also the mechanical properties of the composites including both the flexural and compressive strengths were enhanced by over 100%. The modified C/C-Cu composite exhibited lower friction coefficients and wear rates for different load levels than those of the commercial C/Cu composite. These results demonstrate the potential of the modified C/C-Cu material for use in electrical contacts.展开更多
Al-5%Si-AI2O3 composites were prepared by powder metallurgy and in-situ reactive synthesis technology. Friction and wear properties of Al-5%Si-Al2O3 composites were studied using an M-2000 wear tester. The effects of ...Al-5%Si-AI2O3 composites were prepared by powder metallurgy and in-situ reactive synthesis technology. Friction and wear properties of Al-5%Si-Al2O3 composites were studied using an M-2000 wear tester. The effects of load, sliding speed and long time continuous friction on friction and wear properties of Al-5%Si-Al2O3 composites were investigated, respectively. Wear surface and wear mechanism of Al-5%Si-Al2O3 composites were studied by Quanta 200 FE-SEM. Results showed that with load increasing, wear loss and coefficient of friction increased. With sliding speed going up, the surface temperature of sample made the rate of the producing of oxidation layer increase, while wear loss and coefficient of friction decreased. With the sliding distance increasing, coefficient of friction increased because the adhesive wear mechanism occurred in the initial stage, then formation and destruction of the oxide layer on the surface of the sample tended to a dynamic equilibrium, the surface state of the sample was relatively stable and so did the coefficient of friction. The experiment shows that the main wear mechanism of Al-5%Si-Al2O3 composites includes abrasive wear, adhesive wear and oxidation wear.展开更多
Alumina dispersion strengthened copper composite （nano-Al2O3/Cu composite） was recently emerged as a kind of potentially viable and attractive engineering material for applications requiring high strength, high ther...Alumina dispersion strengthened copper composite （nano-Al2O3/Cu composite） was recently emerged as a kind of potentially viable and attractive engineering material for applications requiring high strength, high thermal and electrical conductivities and resistance to softening at elevated temperatures. The nano-Al2O3/Cu composite was produced by internal oxidation. The microstructures of the composite were analyzed by the TEM and its hot deformation behavior was investigated by means of continuous compression tests performed on a Gleeble 1500 thermo-simulator. Making use of the modified algorithm-Levenberg-Marquardt （L-M） algorithm BP neural network, a model for predicting the flow stresses during hot deformation was set up on the base of the experimental data. Results show that the microstructures of the composite are characterized by uniform distribution of nano-Al2O3 particles in Cu-matrix. The sliding of dislocations is the main deformation mechanism. The dynamic recovery is the main softening mode with the flow stress decreasing gently from 500℃ to 850 ~C. The recrystallization of Cu-matrix can be retarded late into as high as 850 ℃, when it happens only partially. The well-trained BP neural network model can accurately describe the influence of the temperature, strain rate, and true strain on the flow stresses, therefore, it can precisely predict the flow stresses of the composite under given deforming conditions and provide a new way to optimize hot deforming process parameters.展开更多
Ni-La2O3/CeO2 composite films were prepared by electrodeposition from a nickel sulfate bath containing certain content of micrometer and nanometer La2O3/CeO2 particles. The effect of La2O3 or CeO2 particle size on the...Ni-La2O3/CeO2 composite films were prepared by electrodeposition from a nickel sulfate bath containing certain content of micrometer and nanometer La2O3/CeO2 particles. The effect of La2O3 or CeO2 particle size on the oxidation resistance of the electrodeposited Ni-La2O3/CeO2 composites in air at 1000 °C was studied. The results indicate that, compared with the electrodeposited Ni-film, Ni-La2O3/CeO2 composites exhibit a superior oxidation resistance due to the codeposited La2O3 or CeO2 particles blocking the outward diffusion of nickel. Moreover, compared with nanoparticles, La2O3 or CeO2 microparticles have stronger effect because La2O3 or CeO2 microparticles also act as a diffusion barrier layer at the onset of oxidation.展开更多
（TiB2＋Al2O3）/NiAl composites were synthesized by self-propagation high-temperature synthesis, and their phase compositions, microstructures and evolution modes were studied. The microstructures and shapes vary with...（TiB2＋Al2O3）/NiAl composites were synthesized by self-propagation high-temperature synthesis, and their phase compositions, microstructures and evolution modes were studied. The microstructures and shapes vary with the TiB2＋Al2O3 content in the NiAl matrix. TiB2 particles take a great variety of elementary shapes such as white bars, plates, herringbones, regular cubes and cuboids. These results outline a strategy of self-assembly processes in real time to build diversified microstructures. Some TiB2 grains in sizes of 2-5μm are embeded in Al2O3 clusters, while a small number of TiB2 particles disperse in the NiAl matrix. It is believed that the higher the TiB2＋Al2O3 content is, the more the regular shapes and homogeneous distributions of TiB2 and Al2O3 will be present in the NiAl matrix.展开更多
The effects of reduction ratio during roll bonding on the microstructural evolution at interface and subsequent mechanical properties of roll-bonded Al/Cu 2-ply sheets were investigated. The interface microstructures ...The effects of reduction ratio during roll bonding on the microstructural evolution at interface and subsequent mechanical properties of roll-bonded Al/Cu 2-ply sheets were investigated. The interface microstructures for several Al/Cu 2-ply sheets fabricated under different reduction ratios between 30% and 65% were verified by transmission electron microscopy(TEM). Taking the difference of interface microstructure into consideration, 3-point bending and peel tests were performed for obtaining flexural and bonding strengths for Al/Cu 2-ply sheets. The effect of the quantified areas of metallurgical bonding at interfaces on the bonding strength was also discussed. The results show that both the bonding and flexural strengths for Al/Cu 2-ply sheets are reduced by decreasing the reduction ratio during the roll bonding process, which is strongly correlated with the interface microstructure. This was especially verified by observing the interface delamination from the 3-point bent samples.展开更多
基金Open Fund of Zhijian Laboratory,Rocket Force University of Engineering(2024-ZJSYS-KF02-09)National Natural Science Foundation of China(51902028,52272034)+1 种基金Key Research and Development Program of Shaanxi(2023JBGS-15)Fundamental Research Funds for the Central Universities(Changan University,300102313202,300102312406)。
文摘To improve the compactness and properties of C/C-SiC-ZrC composites produced by precursor infiltration and pyrolysis(PIP)method,the low-temperature reactive melt infiltration(RMI)process was used to seal the composites using Zr_(2)Cu as the filler.The microstructure,mechanical properties,and ablation properties of the Zr_(2)Cu packed composites were analyzed.Results show that during Zr_(2)Cu impregnation,the melt efficiently fills the large pores of the composites and is converted to ZrCu due to a partial reaction of zirconium with carbon.This results in an increase in composite density from 1.91 g/cm^(3)to 2.24 g/cm^(3)and a reduction in open porosity by 27.35%.Additionally,the flexural strength of Zr_(2)Cu packed C/C-SiC-ZrC composites is improved from 122.78±8.09 MPa to 135.53±5.40 MPa.After plasma ablation for 20 s,the modified composites demonstrate superior ablative resistance compared to PIP C/C-SiC-ZrC,with mass ablation and linear ablation rates of 2.77×10^(−3)g/s and 2.60×10^(−3)mm/s,respectively.The“selftranspiration”effect of the low-melting point copper-containing phase absorbs the heat of the plasma flame,further reducing the ablation temperature and promoting the formation of refined ZrO_(2)particles within the SiO_(2)melting layer.This provides more stable erosion protection for Zr_(2)Cu packed C/C-SiC-ZrC composites.
基金Foundation of Northwest Institute for Non-ferrous Metal Research(YK2020-9,ZZXJ2203)Capital Projects of Financial Department of Shaanxi Province(YK22C-12)+4 种基金National Natural Science Foundation of China(62204207)Innovation Capability Support Plan in Shaanxi Province of China(2022KJXX-82,2023KJXX-083)Natural Science Foundation of Shaanxi Province(2022JQ-332)Shaanxi Innovative Research Team for Key Science and Technology(2023-CX-TD-46)Key Research and Development Projects of Shaanxi Province(2024GX-YBXM-351)。
文摘Compared with Cu/Al_(2)O_(3)composites,high-strength Cu/Al_(2)O_(3)composites usually exhibit obviously deteriorated electrical conductivity.A chemical and mechanical alloying-based strategy was adopted to fabricate ultrafine composite powders with lowcontent reinforcement and constructed a combined structure of Cu ultrafine powders covered with in-situ Al_(2)O_(3)nanoparticles.After consolidation at a relatively lower sintering temperature of 550℃,high-volume-fraction ultrafine grains were introduced into the Cu/Al_(2)O_(3)composite,and many in-situ Al_(2)O_(3)nanoparticles with an average size of 11.7±7.5 nm were dispersed homogeneously in the Cu grain.Results show that the composite demonstrates an excellent balance of high tensile strength(654±1 MPa)and high electrical conductivity(84.5±0.1%IACS),which is ascribed to the synergistic strengthening effect of ultrafine grains,dislocations,and in-situ Al_(2)O_(3)nanoparticles.This approach,which utilizes ultrafine composite powder with low-content reinforcement as a precursor and employs low-temperature and high-pressure sintering subsequently,may hold promising potential for large-scale industrial production of high-performance oxide dispersion strengthened alloys.
基金National Natural Science Foundation of China (50432020)Henan Innovation Project for University Prominent Re- search Talents (2007KYCX008)+3 种基金Henan Education Department Science and Technology Project (2007430004)Henan Plan Project for College Youth Backbone TeacherHenan University of Science and Technology Major Pre-research Foundation (2005ZD003)Henan University of Science and Technology Personnel Scientific Research Foundation (of023)
文摘Two Al2O3/Cu composites containing 0.24 wt.% Al2O3 and 0.60 wt.% Al2O3 separately are prepared by internal oxidation. Effects of sliding speed and pressure on the frictional characteristics of the composites and copper against brass are investigated and compared. The changes in morphology of the sliding surface and subsurface are examined with scanning electron microscope （SEM） and energy dispersive X-ray spectrum （EDS）. The results show that the wear resistance of the Al2O3/Cu composites is superior to that of copper under the same conditions, Under a given electrical current, the wear rate of Al2O3/Cu composites decreases as the Al2O3-content increases, However, the wear rates of the Al2O3/Cu composites and copper increase as the sliding speed and pressure increase under dry sliding condition. The main wear mechanisms for Al2O3/Cu composites are of abrasion and adhesion; for copper, it is adhesion, although wear by oxidation and electrical erosion can also be observed as the speed and pressure rise.
基金financially supported by the National Natural Science Foundation of China (No.51301118)the Projects of International Cooperation in Shanxi (No.2014081002)the Scientific and Technological Innovation Programs of Higher Education Institutions in Shanxi (No.2013108)
文摘Cu2O/TiOa/Pt three-layer films were deposited on glass substrates using magnetron sputtering method. The surface morphology and the optical properties of the composite film were characterized by X-ray diffraction （XRD）, scanning electron microscopy （SEM）, ultraviolet- visible spectroscopy （UV-Vis） and photoluminescence spectroscopy （PL）. The photocatalytic activity of the samples was evaluated by the photocatalytic degradation of methyl orange （MO） aqueous solution under visible light irradiation. The results indicate that the Cu2O/TiO2/Pt composite films are made up of three layers which are Pt layer, anatase-TiO2 layer and Cu2O layer from bottom to top. The surface of the films is even and composed of regular-shaped spherical particles. The photocatalytic activity of the Cu2O/TiO2/Pt three-layer film is much higher than that of the Cu2O/TiO2 double-layer film. Such enhancement is ascribed to the presence of Pt layer, which further inhibits the photogenerated electron-hole recombination, prolongs the lifetime of the photogenerated carriers, increases the quantum efficiency and hence improves the photocatalytic activity of the film effectively.
文摘A heat-resistant dispersion-strengthening nano-Al_2O_3/Cu composite with highstrength and high electric conductivity was fabricated in a multiplex medium. The internaloxidation product, microstructures and properties of the composite, and the process flow weresystematically studied. It is confirmed that this new technique simplifies the process and improvesthe properties of the composite. X-ray analysis indicates that the alumina particles formed duringinternal oxidation consist of a large mount of gamma-Al_2O_3 and a certain amount of theta-Al_2O_3and alpha-Al_2O_3. TEM observation shows that the obtained gamma-Al_2O_3 nano-particles areuniformly distributed in the copper grains; their mean size and space between particles are 7 runand 30 nm, respectively. The main properties of the composite with 50 percent cold deformation areas follows: the electric conductivity is 51 MS/m (87 percent IACS), sigma_b = 628 MPa, and thehardness is HRB86. After annealing at 1273 K, all or most of the above properties remain, and themicrostructures are still dependent on elongated fiber-form grains.
文摘The preferred internal oxidation of aluminum in Cu Al alloy was used to obtain in situ Al 2O 3/Cu composites. The reinforcement particles were mainly γ Al 2O 3, some θ Al 2O 3 and a little α Al 2O 3. Thermodynamics analyses show that the chemical reactions are 3Cu 2O+2Al=6Cu+Al 2O 3 or 3CuO+2Al=3Cu+Al 2O 3. A related equilibrium diagram was drawn. The experiments and investigation show that the formation rate of Al 2O 3 was controlled by the diffusion of oxygen in matrix.
基金financially supported by the Military Project of the Ministry of National Defense of China (No. JPPT-125-2-168)
文摘Ni(Co/Zn/Cu)Fe_2O_4/SiC@SiO_2, a microwave absorber, was prepared by the sol-gel method. The phase structure and the morphology of the microwave absorbers were characterized by X-Ray Diffraction(XRD) and scanning electron microscopy(SEM), respectively. Laser sizer(LS) and X-ray photoelectron spectroscopy(XPS) analysis show the core-shell structure of SiC@SiO_2. Coaxial method was used to measure the microwave absorption properties of the prepared composites in the frequency range of 2-18 GHz. When 70 wt% SiC is wrapped by 30 wt% SiO_2,and 50 wt% NiFe_2O_4 is added into 50 wt% SiC@SiO_2, the as-prepared powders are found to have advanced microwave absorption properties with a minimum reflection loss(RL) of -32.26 dB at about 6.08 GHz, and the available bandwidth is approximately 2.1 GHz when the RL is below -10 dB.
基金financially supported by National Natural Science Foundation of China(No.21073113)Shanxi Province Science Foundation for Youths(No.2012021006-1)Doctoral Fund of Shanxi Datong University
文摘A magnetically separable Cu2O/Fe3O4 magnetic composite photocatalyst was synthesized in large quantities by a fast and simple route. The as-prepared photocatalysts were characterized by scanning electron microscopy （SEM）, transmission electron microscopy （TEM）, X-ray photoelectron spectroscopy （XPS） and X-ray diffraction （XRD）. Furthermore, the Cu2O/Fe3O4 composite photocatalysts were tested using methyl orange （MO） degradation reaction under visible light irradiation （100 mW/cm2） and demonstrated to have a high photocatalytic efficiency toward the decomposition of MO under visible light irradiation with good recyclability.
基金Project(gf200901002)supported by the Open Research Fund of National Defense Key Disciplines Laboratory of Light Alloy Processing Science and Technology of Nanchang Hangkong University,China
文摘ZrO2/TiO2 composite photocatalytic film was produced on the pure titanium substrate using in-situ Zr（OH）4 colloidal particle by the micro-arc oxidation technique and characterized by scanning electron microscope （SEM）, energy dispersive X-ray （EDX）, X-ray diffraction （XRD） and ultraviolet-visible （UV-Vis） spectrophotometer. The composite film shows a lamellar and porous structure which consists of anatase, futile and ZrO2 phases. The optical absorption edge of film is shifted to longer wavelength when ZrO2 is introduced to TiO2. Furthermore, the photocatalytic reaction rate constants of degradation of rhodamine B solution with ZrO2/TiO2 composite film and pure TiO2 film under ultraviolet irradiation are measured as 0.0442 and 0.0186 h 1, respectively.
基金Projects(U1502274,51834009)supported by the National Natural Science Foundation of ChinaProject(2017ZDXM-GY-028)supported by the Key Research and Development Program of Shaanxi,China。
文摘In situ TiB2/Cu composites were fabricated by both solid-liquid(S-L)and liquid-liquid(L-L)reactive spray deposition in combination with cold rolling and annealing.The microstructure and properties of the fabricated TiB2/Cu composites were investigated.The results show that the reactive mode and rolling treatment are the main factors affecting the microstructure and properties of the TiB2/Cu composite.The in situ reaction in the L-L reaction can be carried out more completely.By controlling the rolling and annealing process,the relative density and the properties of the as-deposited composites are optimized.The comprehensive performance of the deformed TiB2/Cu composite prepared by L-L reactive spray deposition(401 MPa and 83.5%IACS)is better than that by S-L reactive spray deposition(520 MPa and 20.2%IACS).
文摘Al2O3 particle-reinforced ZL109 composite was prepared by in situ reaction between CuO and Al2O3 . The microstructure was observed by means of OM, SEM and TEM. The Al2O3 particles in sub-micron sizes distribute uniformly in the matrix, and the Cu displaced from the in situ reaction forms net-like alloy phases with other alloy elements. The hardness and the tensile strength of the composites at room temperature have a slight increase as compared to that of the matrix. However, the tensile strength at 350℃ has reached 90.23 MPa, or 16.92 MPa higher than that of the matrix. The mechanism of the reaction in the CuO/AI system was studied by using of differential scanning calorimetry（DSC） and thermodynamic calculation. The reaction between CuO and Al involves two steps. First, CuO reacts with Al to form Cu20 and Al2O3 at the melting temperature of the matrix alloy, and second, Cu20 reacts with Al to form Cu and Al2O3 at a higher temperature. At ZL109 casting temperature of 750- 780 ℃, the second step can also take place because of the effect of exothermic reaction of the first step.
基金Project(50802034) supported by the National Natural Science Foundation of ChinaProject(11A093) supported by the Key Project Foundation by the Education Department of Hunan Province,China
文摘TiO2-coated activated carbon surface （TAs） composites were prepared by a sol-gel method with supercritical pretreatment. The photocatalytic degradation of acid yellow （AY） was investigated under UV radiation to estimate activity of catalysts and determine the kinetics. And the effects of parameters including the initial concentration of AY, light intensity and TiO2 content in catalysts were examined. The results indicate that TAs has a higher efficiency in decomposition of AY than P25, pure TiO2 particles as well as the mixture of TiO2 powder and active carbon. The photocatalytic degradation rate is found to follow the pseudo-first order kinetics with respect to the AY concentration. The new kinetic model fairly resembles the classic Langmuir-Hinshelwood equation, and the rate constant is proportional to the square root of the light intensity in a wide range. However, its absorption performance depends on the surface areas of catalysts. The model fits quite well with the experimental data and elucidates phenomena about the effects of the TiO2 content in TAs on the degradation rate.
基金the financial support from of the National Basic Research Program of China (Nos. 2012CB619600 and 2011CB012803)
文摘A facile ammonium-dichromate solution immersion method was introduced to synthesize the copperwettable Cr3C2 coating on and inside the carbon-carbon （C/C） preform. The formation mechanism and the microstructures of the Cr3C2 coatings were studied. The contact angle between molten copper and the C/C decreased from 140°to 60°, demonstrating the significant improvement in the wettability. The Cr3C2- coated C/C-Cu composite with only 4.2% porosity and 3.69 gcm^-3 density was manufactured through copper infiltration. As a result, the thermal and electrical conductivity of the modified C/C-Cu increased significantly due to the infiltrated copper. Also the mechanical properties of the composites including both the flexural and compressive strengths were enhanced by over 100%. The modified C/C-Cu composite exhibited lower friction coefficients and wear rates for different load levels than those of the commercial C/Cu composite. These results demonstrate the potential of the modified C/C-Cu material for use in electrical contacts.
基金Project(51201143)supported by the National Natural Science Foundation of ChinaProject(SWJTU12BR004)supported by the Fundamental Research Funds for the Central Universities,China
文摘Al-5%Si-AI2O3 composites were prepared by powder metallurgy and in-situ reactive synthesis technology. Friction and wear properties of Al-5%Si-Al2O3 composites were studied using an M-2000 wear tester. The effects of load, sliding speed and long time continuous friction on friction and wear properties of Al-5%Si-Al2O3 composites were investigated, respectively. Wear surface and wear mechanism of Al-5%Si-Al2O3 composites were studied by Quanta 200 FE-SEM. Results showed that with load increasing, wear loss and coefficient of friction increased. With sliding speed going up, the surface temperature of sample made the rate of the producing of oxidation layer increase, while wear loss and coefficient of friction decreased. With the sliding distance increasing, coefficient of friction increased because the adhesive wear mechanism occurred in the initial stage, then formation and destruction of the oxide layer on the surface of the sample tended to a dynamic equilibrium, the surface state of the sample was relatively stable and so did the coefficient of friction. The experiment shows that the main wear mechanism of Al-5%Si-Al2O3 composites includes abrasive wear, adhesive wear and oxidation wear.
基金Henan Innovation Project for University Prominent Research Talents (2007KYCX008)Henan Major Science and Technol-ogy Project (0523021500)+1 种基金Henan University of Science and Technology Major Pre-research Foundation (2005ZD003)Henan University of Science and Technology Personnel Scientific Research Foundation
文摘Alumina dispersion strengthened copper composite （nano-Al2O3/Cu composite） was recently emerged as a kind of potentially viable and attractive engineering material for applications requiring high strength, high thermal and electrical conductivities and resistance to softening at elevated temperatures. The nano-Al2O3/Cu composite was produced by internal oxidation. The microstructures of the composite were analyzed by the TEM and its hot deformation behavior was investigated by means of continuous compression tests performed on a Gleeble 1500 thermo-simulator. Making use of the modified algorithm-Levenberg-Marquardt （L-M） algorithm BP neural network, a model for predicting the flow stresses during hot deformation was set up on the base of the experimental data. Results show that the microstructures of the composite are characterized by uniform distribution of nano-Al2O3 particles in Cu-matrix. The sliding of dislocations is the main deformation mechanism. The dynamic recovery is the main softening mode with the flow stress decreasing gently from 500℃ to 850 ~C. The recrystallization of Cu-matrix can be retarded late into as high as 850 ℃, when it happens only partially. The well-trained BP neural network model can accurately describe the influence of the temperature, strain rate, and true strain on the flow stresses, therefore, it can precisely predict the flow stresses of the composite under given deforming conditions and provide a new way to optimize hot deforming process parameters.
基金Project(GC13A113)supported by the Technology Research and Development Program of Heilongjiang Provincial Science and Technology DepartmentProject(12511469)supported by Heilongjiang Provincial Science and Technology Department
文摘Ni-La2O3/CeO2 composite films were prepared by electrodeposition from a nickel sulfate bath containing certain content of micrometer and nanometer La2O3/CeO2 particles. The effect of La2O3 or CeO2 particle size on the oxidation resistance of the electrodeposited Ni-La2O3/CeO2 composites in air at 1000 °C was studied. The results indicate that, compared with the electrodeposited Ni-film, Ni-La2O3/CeO2 composites exhibit a superior oxidation resistance due to the codeposited La2O3 or CeO2 particles blocking the outward diffusion of nickel. Moreover, compared with nanoparticles, La2O3 or CeO2 microparticles have stronger effect because La2O3 or CeO2 microparticles also act as a diffusion barrier layer at the onset of oxidation.
基金Project(51272141)supported by the National Natural Science Foundation of ChinaProject(ts20110828)supported by the Taishan Scholars Project of Shandong Province,ChinaProject(2015AA034404)supported by the Ministry of Science and Technology of China
文摘（TiB2＋Al2O3）/NiAl composites were synthesized by self-propagation high-temperature synthesis, and their phase compositions, microstructures and evolution modes were studied. The microstructures and shapes vary with the TiB2＋Al2O3 content in the NiAl matrix. TiB2 particles take a great variety of elementary shapes such as white bars, plates, herringbones, regular cubes and cuboids. These results outline a strategy of self-assembly processes in real time to build diversified microstructures. Some TiB2 grains in sizes of 2-5μm are embeded in Al2O3 clusters, while a small number of TiB2 particles disperse in the NiAl matrix. It is believed that the higher the TiB2＋Al2O3 content is, the more the regular shapes and homogeneous distributions of TiB2 and Al2O3 will be present in the NiAl matrix.
基金Project(10037273) supported by the Ministry of Knowledge Economy,Korea
文摘The effects of reduction ratio during roll bonding on the microstructural evolution at interface and subsequent mechanical properties of roll-bonded Al/Cu 2-ply sheets were investigated. The interface microstructures for several Al/Cu 2-ply sheets fabricated under different reduction ratios between 30% and 65% were verified by transmission electron microscopy(TEM). Taking the difference of interface microstructure into consideration, 3-point bending and peel tests were performed for obtaining flexural and bonding strengths for Al/Cu 2-ply sheets. The effect of the quantified areas of metallurgical bonding at interfaces on the bonding strength was also discussed. The results show that both the bonding and flexural strengths for Al/Cu 2-ply sheets are reduced by decreasing the reduction ratio during the roll bonding process, which is strongly correlated with the interface microstructure. This was especially verified by observing the interface delamination from the 3-point bent samples.