为制备具有可见光响应的高效光催化剂,采用水热法制备了点-线型形貌的TiO_2纳米线/Bi_2WO_6复合催化剂,考查了钛源、水热温度、溶剂、复合配比等制备因素对复合催化剂形貌的影响,并采用X射线衍射(XRD)、紫外-可见吸收光谱(UV-Vis)、扫...为制备具有可见光响应的高效光催化剂,采用水热法制备了点-线型形貌的TiO_2纳米线/Bi_2WO_6复合催化剂,考查了钛源、水热温度、溶剂、复合配比等制备因素对复合催化剂形貌的影响,并采用X射线衍射(XRD)、紫外-可见吸收光谱(UV-Vis)、扫描电子显微镜(SEM)、透射电子显微镜(TEM)等方法进行表征.结果表明:采用钛酸丁酯制备的TiO_2纳米线为锐钛矿相且结晶度良好;水热温度为180℃,溶剂为乙二醇,TiO_2纳米线复合配比为50%(质量分数)时所制备的TiO_2纳米线/Bi_2WO_6复合催化剂点-线形貌最优;TiO_2纳米线复合窄带隙半导体Bi_2WO_6明显拓宽了光谱响应范围,复合催化剂的禁带宽度达Eg=2.70 e V.展开更多
Novel Bi2WO6-BiPO4 photocatalysts with heterojunction structure were fabricated through a facile hydrothermal route. The photocatalytic properties of Bi2WO6-BiPO4 composites were evaluated by photocatalytic degradatio...Novel Bi2WO6-BiPO4 photocatalysts with heterojunction structure were fabricated through a facile hydrothermal route. The photocatalytic properties of Bi2WO6-BiPO4 composites were evaluated by photocatalytic degradation of rhodamine B （Rh B） under simulated sunlight irradiation. The results showed that Bi2WO6-BiPO4 photocatalysts displayed much higher photocatalytic performances for Rh B degradation than the single BiPO4 and Bi2WO6. The best photocatalytic activity of Bi2WO6-BiPO4 with nearly 100% Rh B degradation located at molar ratio of 1：1 after 20 min irradiation. The enhanced photo-catalytic performance could be mainly ascribed to the formation of heterojunction interface in Bi2WO6-BiPO4 which facilitated the transfer and separation of photogenerated electron-hole pairs, as well as the strong visible light absorption originating from the sensitization role of Bi2WO6 to BiPO4. It was also found that the photodegradation of Rh B molecules was mainly attributed to the oxidation action of the generated O2^· - radicals and partly to the action of hvb^＋ via direct hole oxidation process.展开更多
以TiO2 P25纳米颗粒为原料,通过碱-水热法制备TiO2纳米带,再采用水热法成功制备出Bi2WO6/TiO2纳米带材料.利用X射线衍射仪(X-ray diffraction,XRD)、扫描电子显微镜(scanning electron microscope,SEM)以及透射电子显微镜(transmission ...以TiO2 P25纳米颗粒为原料,通过碱-水热法制备TiO2纳米带,再采用水热法成功制备出Bi2WO6/TiO2纳米带材料.利用X射线衍射仪(X-ray diffraction,XRD)、扫描电子显微镜(scanning electron microscope,SEM)以及透射电子显微镜(transmission electron microscope,TEM)分别对该材料的物相和形貌进行了分析,并研究了其在可见光下的光催化的性能和催化机理.研究结果表明:制备出的Bi2WO6纳米带通过分子间作用力成功负载在TiO2纳米带上.制备出的Bi2WO6/TiO2在可见光下具有优越的光催化性能,这归因于材料较好的光生电子-空穴分离效率以及材料特定的物理性质,不仅为光催化反应提供了丰富的活性位点,还有效促进了电子的轴向迁移率.展开更多
Bismuth tungstate(Bi_(2)WO_(6))has become a research hotspot due to its potential in photocatalytic energy conversion and environmental purification.Nevertheless,the limited light absorption and fast recombination of ...Bismuth tungstate(Bi_(2)WO_(6))has become a research hotspot due to its potential in photocatalytic energy conversion and environmental purification.Nevertheless,the limited light absorption and fast recombination of photogenerated carriers hinder the further improvement of the photocatalytic performance of Bi_(2)WO_(6).Herein,we provide a systematic review for the recent advances on Bi_(2)WO_(6)‐based photocatalysts.It starts with the crystal structure,optical properties and photocatalytic fundamentals of Bi_(2)WO_(6).Then,we focus on the modification strategies of Bi_(2)WO_(6)based on morphology control,atomic modulation and composite fabrication for diverse photocatalytic applications,such as organic synthesis,water splitting,CO2 reduction,water treatment,air purification,bacterial inactivation,etc.Finally,some current challenges and future development prospects are proposed.We expect that this review can provide a useful reference and guidance for the development of efficient Bi_(2)WO_(6)photocatalysts.展开更多
In this paper,a new two-dimensional(2 D)/2 D composite of Bi2 WO6/MoS2 was facile synthesized,and then was used as supporting material for depositing Pt nanoparticles.The as-synthesized Pt-Bi2 WO6/MoS2 was extended in...In this paper,a new two-dimensional(2 D)/2 D composite of Bi2 WO6/MoS2 was facile synthesized,and then was used as supporting material for depositing Pt nanoparticles.The as-synthesized Pt-Bi2 WO6/MoS2 was extended into photo-assisted electrocatalytic oxidation of methanol,which is a model anode reaction for direct methanol fuel cell.Compare with traditional electrocatalytic process,PtBi2 WO6/MoS2 displays 1.5 times enhanced electrocatalytic performance on methanol oxidation with assistance of visible light irradiation and 2.2 times for commercial Pt/C.Besides,from the results of chronoamperometric and chronopotentiometry experiments,the stability of Pt-Bi2 WO6/MoS2 electrode is clearly improved under visible light irradiation.The synergistic effects of photo-and electro-catalytic in the heterojunction of Pt-Bi2 WO6/MoS2 in favor of the above enhancement.This research gives more insights in the fields of photo-assisted traditional electrocatalytic application by constructing of semiconductor heterojunction carrier.展开更多
Rare-earth modification Bi2WO6 composites(RE/Bi2WO6)were studied by experimental performance and theory computation based on the different 4 f orbits of selected rare earth elements(La,Ce,Gd,and Yb).The prepared RE/Bi...Rare-earth modification Bi2WO6 composites(RE/Bi2WO6)were studied by experimental performance and theory computation based on the different 4 f orbits of selected rare earth elements(La,Ce,Gd,and Yb).The prepared RE/Bi2WO6 was characterized by XRD,SEM/TEM,XPS,UV-vis DRS,and N2 adsorption to learn their physical-chemical properties.Azo dye Rhodamine B(RhB)was photodegraded as a target pollutant to investigate the photocatalytic activity of prepared RE/Bi2WO6 composites.The results of experiment and computation show that four rare earth elements with different electron configurations retain the phase and morphology of Bi2 WO6 and enhance the removal efficiency of RhB under simulated solar irradiation.The optimum doping contents are 0.01%,0.05%,0.05%and 0.01%for La-,Ce-,Gd-,and Yb-doped Bi2WO6,respectively.However,light rare earth La and Ce doped composites indicate some difference in visible light adso rption capacity and mineralization on RhB co mpared with heavy rare earth Gd and Yb doped composites.Both La/Bi2WO6 and Ce/Bi2 WO6 possess larger pore size and higher mineralization ability than Gd/Bi2 WO6 and Yb/Bi2WO6 under the same experimental conditions while Gd/Bi2WO6 and Yb/Bi2WO6 show stronger red shift to the visible light due to the more 4 f electrons.The hole oxidation plays a major role in the photodegradation of RhB by all RE/Bi2WO6.展开更多
基金supported by the Natural Science Foundation of China (Grants No.21376126, 81403067)the Program for Young Teachers Scientific Research in Qiqihar University (Grant No.2014K-M03)the Basic Business Special Scientific Research of Heilongjiang Province Education Department (Grant No.135109204)~~
文摘为制备具有可见光响应的高效光催化剂,采用水热法制备了点-线型形貌的TiO_2纳米线/Bi_2WO_6复合催化剂,考查了钛源、水热温度、溶剂、复合配比等制备因素对复合催化剂形貌的影响,并采用X射线衍射(XRD)、紫外-可见吸收光谱(UV-Vis)、扫描电子显微镜(SEM)、透射电子显微镜(TEM)等方法进行表征.结果表明:采用钛酸丁酯制备的TiO_2纳米线为锐钛矿相且结晶度良好;水热温度为180℃,溶剂为乙二醇,TiO_2纳米线复合配比为50%(质量分数)时所制备的TiO_2纳米线/Bi_2WO_6复合催化剂点-线形貌最优;TiO_2纳米线复合窄带隙半导体Bi_2WO_6明显拓宽了光谱响应范围,复合催化剂的禁带宽度达Eg=2.70 e V.
基金This work was supported by the National Natural Science Foundation of China （No.21407059） and the Science Development Project of Jilin Province （No.20130522071JH and No.20140101160JC）.
文摘Novel Bi2WO6-BiPO4 photocatalysts with heterojunction structure were fabricated through a facile hydrothermal route. The photocatalytic properties of Bi2WO6-BiPO4 composites were evaluated by photocatalytic degradation of rhodamine B （Rh B） under simulated sunlight irradiation. The results showed that Bi2WO6-BiPO4 photocatalysts displayed much higher photocatalytic performances for Rh B degradation than the single BiPO4 and Bi2WO6. The best photocatalytic activity of Bi2WO6-BiPO4 with nearly 100% Rh B degradation located at molar ratio of 1：1 after 20 min irradiation. The enhanced photo-catalytic performance could be mainly ascribed to the formation of heterojunction interface in Bi2WO6-BiPO4 which facilitated the transfer and separation of photogenerated electron-hole pairs, as well as the strong visible light absorption originating from the sensitization role of Bi2WO6 to BiPO4. It was also found that the photodegradation of Rh B molecules was mainly attributed to the oxidation action of the generated O2^· - radicals and partly to the action of hvb^＋ via direct hole oxidation process.
文摘以TiO2 P25纳米颗粒为原料,通过碱-水热法制备TiO2纳米带,再采用水热法成功制备出Bi2WO6/TiO2纳米带材料.利用X射线衍射仪(X-ray diffraction,XRD)、扫描电子显微镜(scanning electron microscope,SEM)以及透射电子显微镜(transmission electron microscope,TEM)分别对该材料的物相和形貌进行了分析,并研究了其在可见光下的光催化的性能和催化机理.研究结果表明:制备出的Bi2WO6纳米带通过分子间作用力成功负载在TiO2纳米带上.制备出的Bi2WO6/TiO2在可见光下具有优越的光催化性能,这归因于材料较好的光生电子-空穴分离效率以及材料特定的物理性质,不仅为光催化反应提供了丰富的活性位点,还有效促进了电子的轴向迁移率.
文摘Bismuth tungstate(Bi_(2)WO_(6))has become a research hotspot due to its potential in photocatalytic energy conversion and environmental purification.Nevertheless,the limited light absorption and fast recombination of photogenerated carriers hinder the further improvement of the photocatalytic performance of Bi_(2)WO_(6).Herein,we provide a systematic review for the recent advances on Bi_(2)WO_(6)‐based photocatalysts.It starts with the crystal structure,optical properties and photocatalytic fundamentals of Bi_(2)WO_(6).Then,we focus on the modification strategies of Bi_(2)WO_(6)based on morphology control,atomic modulation and composite fabrication for diverse photocatalytic applications,such as organic synthesis,water splitting,CO2 reduction,water treatment,air purification,bacterial inactivation,etc.Finally,some current challenges and future development prospects are proposed.We expect that this review can provide a useful reference and guidance for the development of efficient Bi_(2)WO_(6)photocatalysts.
基金support of the National Natural Science Foundation of China (No.21603111)
文摘In this paper,a new two-dimensional(2 D)/2 D composite of Bi2 WO6/MoS2 was facile synthesized,and then was used as supporting material for depositing Pt nanoparticles.The as-synthesized Pt-Bi2 WO6/MoS2 was extended into photo-assisted electrocatalytic oxidation of methanol,which is a model anode reaction for direct methanol fuel cell.Compare with traditional electrocatalytic process,PtBi2 WO6/MoS2 displays 1.5 times enhanced electrocatalytic performance on methanol oxidation with assistance of visible light irradiation and 2.2 times for commercial Pt/C.Besides,from the results of chronoamperometric and chronopotentiometry experiments,the stability of Pt-Bi2 WO6/MoS2 electrode is clearly improved under visible light irradiation.The synergistic effects of photo-and electro-catalytic in the heterojunction of Pt-Bi2 WO6/MoS2 in favor of the above enhancement.This research gives more insights in the fields of photo-assisted traditional electrocatalytic application by constructing of semiconductor heterojunction carrier.
基金Projects supported by the National Natural Science Foundation of China(21408277)China’s Postdoctoral Science Fund(2016T90967)+2 种基金Program of 5511 Talents in Scientific and Technological Innovation of Jiangxi Province(20165BCB18013)Jiangxi Poyang Yingcai 555 ProjectProgram of Qingjiang Excellent Young Talents,JXUST。
文摘Rare-earth modification Bi2WO6 composites(RE/Bi2WO6)were studied by experimental performance and theory computation based on the different 4 f orbits of selected rare earth elements(La,Ce,Gd,and Yb).The prepared RE/Bi2WO6 was characterized by XRD,SEM/TEM,XPS,UV-vis DRS,and N2 adsorption to learn their physical-chemical properties.Azo dye Rhodamine B(RhB)was photodegraded as a target pollutant to investigate the photocatalytic activity of prepared RE/Bi2WO6 composites.The results of experiment and computation show that four rare earth elements with different electron configurations retain the phase and morphology of Bi2 WO6 and enhance the removal efficiency of RhB under simulated solar irradiation.The optimum doping contents are 0.01%,0.05%,0.05%and 0.01%for La-,Ce-,Gd-,and Yb-doped Bi2WO6,respectively.However,light rare earth La and Ce doped composites indicate some difference in visible light adso rption capacity and mineralization on RhB co mpared with heavy rare earth Gd and Yb doped composites.Both La/Bi2WO6 and Ce/Bi2 WO6 possess larger pore size and higher mineralization ability than Gd/Bi2 WO6 and Yb/Bi2WO6 under the same experimental conditions while Gd/Bi2WO6 and Yb/Bi2WO6 show stronger red shift to the visible light due to the more 4 f electrons.The hole oxidation plays a major role in the photodegradation of RhB by all RE/Bi2WO6.