The preparation of peroxodisulfated zirconia titania(PSZT) solid super acid has been investigated as function of molar ratio of Ti to Zr, impregnation time, calcination time and temperature in esterification of maleic...The preparation of peroxodisulfated zirconia titania(PSZT) solid super acid has been investigated as function of molar ratio of Ti to Zr, impregnation time, calcination time and temperature in esterification of maleic anhydride with n octanol. The highest yield of dioctyl maleate was 98 2% at the optimum reaction conditions.展开更多
文摘The preparation of peroxodisulfated zirconia titania(PSZT) solid super acid has been investigated as function of molar ratio of Ti to Zr, impregnation time, calcination time and temperature in esterification of maleic anhydride with n octanol. The highest yield of dioctyl maleate was 98 2% at the optimum reaction conditions.
文摘采用溶胶-凝胶法制备高活性Ti基纳米TiO2-ZrO2膜电极.通过X射线衍射分析表明,纳米TiO2-ZrO2粉体呈微-纳二级结构.扫描电子显微镜测试表明,颗粒平均尺寸约为30 nm.通过循环伏安和恒电流电解技术研究发现,Ti/nanoTiO2-ZrO2电极对马来酸电催化还原制备丁二酸的活性要高于Ti/nanoTiO2电极,反应过程受扩散控制.以钛基氧化钌电极为阳极,Ti/nano TiO2-ZrO2膜电极为阴极进行恒电流电解实验.结果表明,控制电流密度20 mA cm-2,温度60℃,丁二酸的产率达到96%.