In order to reduce the friction coefficients and improve the wear resistance of mechanical parts, which work in the severe friction and wear conditions at heavy loads, the graphite/CaFg/TiC/Ni-base alloy composite coa...In order to reduce the friction coefficients and improve the wear resistance of mechanical parts, which work in the severe friction and wear conditions at heavy loads, the graphite/CaFg/TiC/Ni-base alloy composite coatings were prepared by plasma spray and their tribological behavior and mechanisms were investigated. The results show that the friction coefficients of the composite coatings are in the range of 0.22-0.288, which are reduced by 25.9% to 53% compared with those of the pure Ni-base alloy coatings, and the wear rates of the former are 18.6%-70.1% less than those of the latter. When wear against GCr15 steel balls, a transferred layer mainly composed of ferric oxides, graphite and CaF2 may gradually develop on the worn surface of the composite coatings, which made the friction and wear between GCr15 steel ball and the composite coatings change into that between the former and the transferred layer. So the friction coefficients and the wear lubrication effect of the transferred layer. The main wear layer in friction process. rates of the composite coatings are greatly reduced because of the solid mechanism of the composite coatings is delamination of the transferred展开更多
TiO2 filled polytetrafluoroethylene (PTFE) composite were fabricated for microwave circuit applications. PTFE/TiO2 composites were prepared by cold pressing and hot treating. The particle size of TiO2 varied from 5 μ...TiO2 filled polytetrafluoroethylene (PTFE) composite were fabricated for microwave circuit applications. PTFE/TiO2 composites were prepared by cold pressing and hot treating. The particle size of TiO2 varied from 5 μm to 11 μm.TiO2 powders with different sizes were prepared by the solid state ceramic route. The effects of TiO2 particle size on the microstructure, density, moisture absorption, thermal conductivity and microwave dielectric properties of PTFE/TiO2 composites were investigated. The density showed an increasing trend as the TiO2 particle size increased, while the dielectric loss (tanδ) and moisture absorption decreased with the increase of TiO2 particle size. The dielectric constant (εr) and thermal conductivity (λ) decreased up to D50 = 6.5 μm and then sharply increased. Good properties with values of εr = 6.8, tanδ = 0.0012 and λ = 0.533 W?m?1?K?1 were obtained in PTFE/TiO2 composites when the particle size of TiO2 was 11 μm.展开更多
In this paper, a detailed study was carried out on the PTFE reinforced with TiO2 and CaTiO3. The filler content of ceramic powder was a fixed value of 61 wt% and the content of CaTiO3 in PTFE matrix varied from 0 wt% ...In this paper, a detailed study was carried out on the PTFE reinforced with TiO2 and CaTiO3. The filler content of ceramic powder was a fixed value of 61 wt% and the content of CaTiO3 in PTFE matrix varied from 0 wt% to 16 wt% with a step size of 4 wt%. The effects of CaTiO3 loading on the density, moisture absorption, thermal expansion, microstructure and microwave dielectric properties were investigated. As CaTiO3 loading content increased from 0 wt% to 16 wt%, the thermal expansion initially displayed a sharp increase, and showed a slight enhancement when the content of CaTiO3 exceeded 12 wt%. The density experienced a continuous decrease with the addition of CaTiO3. The moisture absorption displayed a steady increase with the increasing CaTiO3 loading amount. The changing of dielectric constant (εr) and loss tangent (tanδ) were similar to that of the moisture absorption in a manner. Good dielectric properties with values of εr = 11.60, tanδ = 0.002 were obtained in the PTFE matrix with 16 wt% CaTiO3 and 45 wt% TiO2.展开更多
In this work, TiO2/Ti composite films were fabricated by 2-setp MCT and the following high temperature oxidation. Antibacterial activity of the composite films treated by ultrasonic cleaning to increase the performanc...In this work, TiO2/Ti composite films were fabricated by 2-setp MCT and the following high temperature oxidation. Antibacterial activity of the composite films treated by ultrasonic cleaning to increase the performance reliability was examined. The prepared TiO2/Ti composite films showed high photocatalytic activity in the degradation of methylene blue solution. It is obvious that? TiO2/Ti composite films have antibacterial activity under UV irradiation.展开更多
Different semiconductive SiC foam supports were prepared by varying the sintering temperature and atmosphere, and with or without alkaline solution treatment and high temperature oxidation following a macromolecule py...Different semiconductive SiC foam supports were prepared by varying the sintering temperature and atmosphere, and with or without alkaline solution treatment and high temperature oxidation following a macromolecule pyrogenation combined with reaction bonding method. Nano-TiO2 particles were immobilized onto these SiC foam supports by a composite sol-gel method. The phase, surface morphology, the type of conduction and the photocatalytic activity of the TiO2-SiC composite photocatalysts were studied. The TiO2 coated on p-type Si-free SiC support showed the highest photocatalytic efficiency in degradation of 4- aminobenzenesulfonic acid （4-ABS） in aqueous solution as compared to that coated on n-type SiC support and p-type SiC supports with residual Si or Si02 on the surface. The result showed that the TiO2 coatings immobilized on p-type semiconductive SiC foam supports exhibited obviously higher photocatalytic activity in comparison to that coated on n-type SiC foam support. The p-n heterojunctions formed between the p-type SiC supports and n-type TiO2 coatings might be able to account for the better charge separation and transfer as well as the photocatalytic activity of the TiO2-SiC composite photocatalyst.展开更多
TiO 2 nanoparticles were obtained from industrial TiOSO 4 by hydrolysis method. SnO 2/TiO 2 and SnO 2-TiO 2 composite powders were prepared by stepwise precipitation method and coating method, respectively. The phase ...TiO 2 nanoparticles were obtained from industrial TiOSO 4 by hydrolysis method. SnO 2/TiO 2 and SnO 2-TiO 2 composite powders were prepared by stepwise precipitation method and coating method, respectively. The phase transformation of TiO 2 and the effect of composite mode of SnO 2 on phase transformation of TiO 2 have been investigated by TG-DTA and XRD. The phase transform of pure TiO 2 from anatase to rutile begins at 750 ℃ and the presence of SnO 2 markedly reduces the transform temperature: for coated SnO 2-TiO 2 composite with ω(SnO 2)=20% it was 400 ℃. The SnO 2/TiO 2 composite prepared by precipitation method and followed by calcination at 400 ℃ for 30 min possesses 55% rutile TiO 2. The formation of SnO 2-TiO 2 solid- solution occurrs mainly due to the substitution of Ti 4+ crystal lattice sites by Sn 4+ ions of SnO 2.展开更多
文摘In order to reduce the friction coefficients and improve the wear resistance of mechanical parts, which work in the severe friction and wear conditions at heavy loads, the graphite/CaFg/TiC/Ni-base alloy composite coatings were prepared by plasma spray and their tribological behavior and mechanisms were investigated. The results show that the friction coefficients of the composite coatings are in the range of 0.22-0.288, which are reduced by 25.9% to 53% compared with those of the pure Ni-base alloy coatings, and the wear rates of the former are 18.6%-70.1% less than those of the latter. When wear against GCr15 steel balls, a transferred layer mainly composed of ferric oxides, graphite and CaF2 may gradually develop on the worn surface of the composite coatings, which made the friction and wear between GCr15 steel ball and the composite coatings change into that between the former and the transferred layer. So the friction coefficients and the wear lubrication effect of the transferred layer. The main wear layer in friction process. rates of the composite coatings are greatly reduced because of the solid mechanism of the composite coatings is delamination of the transferred
文摘TiO2 filled polytetrafluoroethylene (PTFE) composite were fabricated for microwave circuit applications. PTFE/TiO2 composites were prepared by cold pressing and hot treating. The particle size of TiO2 varied from 5 μm to 11 μm.TiO2 powders with different sizes were prepared by the solid state ceramic route. The effects of TiO2 particle size on the microstructure, density, moisture absorption, thermal conductivity and microwave dielectric properties of PTFE/TiO2 composites were investigated. The density showed an increasing trend as the TiO2 particle size increased, while the dielectric loss (tanδ) and moisture absorption decreased with the increase of TiO2 particle size. The dielectric constant (εr) and thermal conductivity (λ) decreased up to D50 = 6.5 μm and then sharply increased. Good properties with values of εr = 6.8, tanδ = 0.0012 and λ = 0.533 W?m?1?K?1 were obtained in PTFE/TiO2 composites when the particle size of TiO2 was 11 μm.
文摘In this paper, a detailed study was carried out on the PTFE reinforced with TiO2 and CaTiO3. The filler content of ceramic powder was a fixed value of 61 wt% and the content of CaTiO3 in PTFE matrix varied from 0 wt% to 16 wt% with a step size of 4 wt%. The effects of CaTiO3 loading on the density, moisture absorption, thermal expansion, microstructure and microwave dielectric properties were investigated. As CaTiO3 loading content increased from 0 wt% to 16 wt%, the thermal expansion initially displayed a sharp increase, and showed a slight enhancement when the content of CaTiO3 exceeded 12 wt%. The density experienced a continuous decrease with the addition of CaTiO3. The moisture absorption displayed a steady increase with the increasing CaTiO3 loading amount. The changing of dielectric constant (εr) and loss tangent (tanδ) were similar to that of the moisture absorption in a manner. Good dielectric properties with values of εr = 11.60, tanδ = 0.002 were obtained in the PTFE matrix with 16 wt% CaTiO3 and 45 wt% TiO2.
文摘In this work, TiO2/Ti composite films were fabricated by 2-setp MCT and the following high temperature oxidation. Antibacterial activity of the composite films treated by ultrasonic cleaning to increase the performance reliability was examined. The prepared TiO2/Ti composite films showed high photocatalytic activity in the degradation of methylene blue solution. It is obvious that? TiO2/Ti composite films have antibacterial activity under UV irradiation.
基金supported by the National Key Technology R&D Program of China(Grant No.2011BAE03B07)
文摘Different semiconductive SiC foam supports were prepared by varying the sintering temperature and atmosphere, and with or without alkaline solution treatment and high temperature oxidation following a macromolecule pyrogenation combined with reaction bonding method. Nano-TiO2 particles were immobilized onto these SiC foam supports by a composite sol-gel method. The phase, surface morphology, the type of conduction and the photocatalytic activity of the TiO2-SiC composite photocatalysts were studied. The TiO2 coated on p-type Si-free SiC support showed the highest photocatalytic efficiency in degradation of 4- aminobenzenesulfonic acid （4-ABS） in aqueous solution as compared to that coated on n-type SiC support and p-type SiC supports with residual Si or Si02 on the surface. The result showed that the TiO2 coatings immobilized on p-type semiconductive SiC foam supports exhibited obviously higher photocatalytic activity in comparison to that coated on n-type SiC foam support. The p-n heterojunctions formed between the p-type SiC supports and n-type TiO2 coatings might be able to account for the better charge separation and transfer as well as the photocatalytic activity of the TiO2-SiC composite photocatalyst.
文摘TiO 2 nanoparticles were obtained from industrial TiOSO 4 by hydrolysis method. SnO 2/TiO 2 and SnO 2-TiO 2 composite powders were prepared by stepwise precipitation method and coating method, respectively. The phase transformation of TiO 2 and the effect of composite mode of SnO 2 on phase transformation of TiO 2 have been investigated by TG-DTA and XRD. The phase transform of pure TiO 2 from anatase to rutile begins at 750 ℃ and the presence of SnO 2 markedly reduces the transform temperature: for coated SnO 2-TiO 2 composite with ω(SnO 2)=20% it was 400 ℃. The SnO 2/TiO 2 composite prepared by precipitation method and followed by calcination at 400 ℃ for 30 min possesses 55% rutile TiO 2. The formation of SnO 2-TiO 2 solid- solution occurrs mainly due to the substitution of Ti 4+ crystal lattice sites by Sn 4+ ions of SnO 2.