TiO2 nanotube （TINT） electrodes anodized in fluorinated organic solutions were successfully prepared on Ti sheets. Field-emission scanning electron microscopy （FE-SEM） and X-ray diffraction （XRD） were performed ...TiO2 nanotube （TINT） electrodes anodized in fluorinated organic solutions were successfully prepared on Ti sheets. Field-emission scanning electron microscopy （FE-SEM） and X-ray diffraction （XRD） were performed to characterize the TiNT electrodes. The linear voltammetry results under irradiation showed that the TiNT electrode annealed at 450℃ presented the highest photoelectrochemical activity. By combining photocatalytic with electrochemical process, a significantly synergetic effect on ammonia degradation was observed with Na2SO4 as supporting electrolyte at pH 10.7. Furthermore, the photoelectrocatalytic efficiency on the ammonia degradation was greatly enhanced in presence of chloride ions without the limitation ofpH. The degradation rate was improved by 14.8 times reaching 4.98 × 10^-2 min^-1 at pH 10.7 and a faster degradation rate of 6.34 × 10^-2 min^-1 was obtained at pH 3.01. The in situ photoelectrocatalytic generated active chlorine was proposed to be responsible for the improved efficiency. On the other hand, an enhanced degradation of ammonia using TiNT electrode fabricated in fluorinated organic solution was also confirmed compared to TiNT electrode anodized in fluorinated water solution and TiO2 film electrode fabricated by sol-gel method. Finally, the effect of chloride concentration was also discussed.展开更多
Pd-MnO2/TiO2 nanotube arrays（NTAs） photo-electrodes were successfully fabricated via anodization and electro deposition subsequently; the obtained Pd-MnO2/TiO2 NTAs photo electrodes were analyzed by scanning electro...Pd-MnO2/TiO2 nanotube arrays（NTAs） photo-electrodes were successfully fabricated via anodization and electro deposition subsequently; the obtained Pd-MnO2/TiO2 NTAs photo electrodes were analyzed by scanning electron microscopy（SEM）, X-ray diffraction（XRD） and characterized accordingly. Moreover, the light harvesting and absorption properties were investigated via ultraviolet–visible diffuse reflectance spectrum（DRS）; photo degradation efficiency was investigated via analyzing the photo catalytic degradation of Rhodamine B under visible illumination（xenon light）. The performed analyses illustrated that Pd-MnO2 codoped particles were successfully deposited onto the surface of the TiO2 nanotube arrays;DRS results showed significant improvement in visible light absorption which was between400 and 700 nm. Finally, the photo catalytic degradation efficiency results of the designated organic pollutant（Rhodamine B） illustrated a superior photocatalytic（PC） efficiency of approximately 95% compared to the bare TiO2 NTAs, which only exhibited a photo catalytic degradation efficiency of approximately 61%, thus it indicated the significant enhancement of the light absorption properties of fabricated photo electrodes and their yield of UOH radicals.展开更多
In this work, CdS sensitized TiO2 nanotube arrays （CdS/TiO2NTs） electrode was synthesized with the CdS deposition on the highly ordered titanium dioxide nanotube arrays （TiO2NTs） by sequential chemical bath deposi...In this work, CdS sensitized TiO2 nanotube arrays （CdS/TiO2NTs） electrode was synthesized with the CdS deposition on the highly ordered titanium dioxide nanotube arrays （TiO2NTs） by sequential chemical bath deposition method （S-CBD）. The as-prepared CdS/TiO2NTs was characterized by field-emission scanning electron mi- croscopy （FE-SEM） and X-ray diffraction （XRD）. The results indicated that the CdS nanoparticles were effectively deposited on the surface of TiOeNTs. The amperometric I-t curve on the CdS/TiO2NTs electrode was also presented. It was found that the photocurrent density was enhanced significantly from 0.5 to 1.85 mA/cm2 upon illumination with applied potential of 0.5 V at the central wavelength of 253.7 nm. The photoelectrocatalytic （PEC） activity of the CdS/TiO2NTs electrode was investigated by degradation of methyl orange （MO） in aqueous solution. Compared with TiO2NTs electrode, the degradation efficiencies of CdS/TiO2NTs electrode increased from 78% to 99.2% under UV light in 2 h, and from 14% to 99.2% under visible light in 3 h, which was caused by effective separation of the electrons and holes due to the effect of CdS, hence inhibiting the recombination of electron/hole pairs of TiO2NTs.展开更多
基金supported by the National Natural Science Foundation of China (Nos. 21277134, 21107103)the State Key Laboratory of Environmental, Criteria and Risk Assessment Chinese Research Academy of Environmental Sciences
文摘TiO2 nanotube （TINT） electrodes anodized in fluorinated organic solutions were successfully prepared on Ti sheets. Field-emission scanning electron microscopy （FE-SEM） and X-ray diffraction （XRD） were performed to characterize the TiNT electrodes. The linear voltammetry results under irradiation showed that the TiNT electrode annealed at 450℃ presented the highest photoelectrochemical activity. By combining photocatalytic with electrochemical process, a significantly synergetic effect on ammonia degradation was observed with Na2SO4 as supporting electrolyte at pH 10.7. Furthermore, the photoelectrocatalytic efficiency on the ammonia degradation was greatly enhanced in presence of chloride ions without the limitation ofpH. The degradation rate was improved by 14.8 times reaching 4.98 × 10^-2 min^-1 at pH 10.7 and a faster degradation rate of 6.34 × 10^-2 min^-1 was obtained at pH 3.01. The in situ photoelectrocatalytic generated active chlorine was proposed to be responsible for the improved efficiency. On the other hand, an enhanced degradation of ammonia using TiNT electrode fabricated in fluorinated organic solution was also confirmed compared to TiNT electrode anodized in fluorinated water solution and TiO2 film electrode fabricated by sol-gel method. Finally, the effect of chloride concentration was also discussed.
基金supported by the National Natural Science Foundation of China (No. 51178138)the National Creative Research Groups of China (No. 51121062)the State Key Laboratory of Urban Water Resources and Environment (No. 2010DX03)
文摘Pd-MnO2/TiO2 nanotube arrays（NTAs） photo-electrodes were successfully fabricated via anodization and electro deposition subsequently; the obtained Pd-MnO2/TiO2 NTAs photo electrodes were analyzed by scanning electron microscopy（SEM）, X-ray diffraction（XRD） and characterized accordingly. Moreover, the light harvesting and absorption properties were investigated via ultraviolet–visible diffuse reflectance spectrum（DRS）; photo degradation efficiency was investigated via analyzing the photo catalytic degradation of Rhodamine B under visible illumination（xenon light）. The performed analyses illustrated that Pd-MnO2 codoped particles were successfully deposited onto the surface of the TiO2 nanotube arrays;DRS results showed significant improvement in visible light absorption which was between400 and 700 nm. Finally, the photo catalytic degradation efficiency results of the designated organic pollutant（Rhodamine B） illustrated a superior photocatalytic（PC） efficiency of approximately 95% compared to the bare TiO2 NTAs, which only exhibited a photo catalytic degradation efficiency of approximately 61%, thus it indicated the significant enhancement of the light absorption properties of fabricated photo electrodes and their yield of UOH radicals.
文摘In this work, CdS sensitized TiO2 nanotube arrays （CdS/TiO2NTs） electrode was synthesized with the CdS deposition on the highly ordered titanium dioxide nanotube arrays （TiO2NTs） by sequential chemical bath deposition method （S-CBD）. The as-prepared CdS/TiO2NTs was characterized by field-emission scanning electron mi- croscopy （FE-SEM） and X-ray diffraction （XRD）. The results indicated that the CdS nanoparticles were effectively deposited on the surface of TiOeNTs. The amperometric I-t curve on the CdS/TiO2NTs electrode was also presented. It was found that the photocurrent density was enhanced significantly from 0.5 to 1.85 mA/cm2 upon illumination with applied potential of 0.5 V at the central wavelength of 253.7 nm. The photoelectrocatalytic （PEC） activity of the CdS/TiO2NTs electrode was investigated by degradation of methyl orange （MO） in aqueous solution. Compared with TiO2NTs electrode, the degradation efficiencies of CdS/TiO2NTs electrode increased from 78% to 99.2% under UV light in 2 h, and from 14% to 99.2% under visible light in 3 h, which was caused by effective separation of the electrons and holes due to the effect of CdS, hence inhibiting the recombination of electron/hole pairs of TiO2NTs.