We report the development of a novel visible response BiVO_4/TiO_2(N_2) nanotubes photoanode for photoelectrocatalytic applications. The nitrogen-treated TiO_2 nanotube shows a high carrier concentration rate, thus re...We report the development of a novel visible response BiVO_4/TiO_2(N_2) nanotubes photoanode for photoelectrocatalytic applications. The nitrogen-treated TiO_2 nanotube shows a high carrier concentration rate, thus resulting in a high efficient charge transportation and low electron–hole recombination in the TiO_2–BiVO_4. Therefore, the BiVO_4/TiO_2(N_2) NTs photoanode enabled with a significantly enhanced photocurrent of 2.73 mA cm^(-2)(at 1 V vs. Ag/Ag Cl) and a degradation efficiency in the oxidation of dyes under visible light. Field emission scanning electron microscopy, X-ray diffractometry, energy-dispersive X-ray spectrometer, and UV–Vis absorption spectrum were conducted to characterize the photoanode and demonstrated the presence of both metal oxides as a junction composite.展开更多
Synergistic interplays involving multiple active centers originating from TiO2 nanotube layers(TNT)and ruthenium(Ru)species comprising of both single atoms(SAs)and nanoparticles(NPs)augment the alkaline hydrogen evolu...Synergistic interplays involving multiple active centers originating from TiO2 nanotube layers(TNT)and ruthenium(Ru)species comprising of both single atoms(SAs)and nanoparticles(NPs)augment the alkaline hydrogen evolution reaction(HER)by enhancing Volmer kinetics from rapid water dissociation and improving Tafel kinetics from efficient H*desorption.Atomic layer deposition of Ru with 50 process cycles results in a mixture of Ru SAs and 2.8-0.4 nm NPs present on TNT layers,and it emerges with the highest HER activity among all the electrodes synthesized.A detailed study of the Ti and Ru species using different high-resolution techniques confirmed the presence of Ti^(3+)states and the coexistence of Ru SAs and NPs.With insights from literature,the role of Ti^(3+),appropriate work functions of TNT layers and Ru,and the synergistic effect of Ru SAs and Ru NPs in improving the performance of alkaline HER were elaborated and justified.The aforementioned characteristics led to a remarkable performance by having 9mV onset potentials and 33 mV dec^(-1) of Tafel slopes and a higher turnover frequency of 1.72 H2 s^(-1) at 30 mV.Besides,a notable stability from 28 h staircase chronopotentiometric measurements for TNT@Ru surpasses TNT@Pt in comparison.展开更多
TiO2 nanotube arrays （TNTs） electrode loaded with Zn nanoparticles was prepared by anodization and the size of Zn nanoparticle loaded on TNTs electrode was controlled by chronoamperometry deposition time. Results of...TiO2 nanotube arrays （TNTs） electrode loaded with Zn nanoparticles was prepared by anodization and the size of Zn nanoparticle loaded on TNTs electrode was controlled by chronoamperometry deposition time. Results of SEM and XRD analysis show that Zn nanoparticles had a diameter of about 15-25 nm when the deposition time was 3-5 s. The UV-Vis diffuse reflectance spectra show the Zn loaded harvest light with 480-780 nm more effectively than the unloaded sample. The photocurrent response of Zn loaded TNTs electrodes were studied, the results showed that TNTs electrodes loaded with Zn nanoparti-cles has 50% increased photocurrent response under high-pressure mercury lamp irradiation compared with unloaded TNTs electrode.展开更多
A novel titanium dioxide （TiO2） film comprising both nanotubes and nanopaticles was fabricated by an anodization process of the modified titanium. The local electric field at the anodized surface was simulated and i...A novel titanium dioxide （TiO2） film comprising both nanotubes and nanopaticles was fabricated by an anodization process of the modified titanium. The local electric field at the anodized surface was simulated and its influence on the morphology of the TiO2 film was discussed. The results show that the electric field strength is enhanced by the covering. The growth rate of TiO2 increases with the assist of the local electric field. However, TiO2 dissolution is hindered since the local electric field prevents [TiF6]6- from diffusing. It means that the balance condition for the formation of nanotubes is broken, and TiO2 nanoparticles are formed. Moreover, the crystal structure of the TiO2 film was confirmed using X-ray diffraction and Raman analysis. The anatase is a main phase for the proposed film.展开更多
Two-dimensional (2D) ultrathin MoS2-modified black Ti^3+-TiO2 nanotubes were fabricated using an electrospinning-hydrothermal treatment-reduction method.Bare TiO2 nanotubes were fabricated via electrospinning.Then,2D ...Two-dimensional (2D) ultrathin MoS2-modified black Ti^3+-TiO2 nanotubes were fabricated using an electrospinning-hydrothermal treatment-reduction method.Bare TiO2 nanotubes were fabricated via electrospinning.Then,2D MoS2 lamellae were grown on the surface of the nanotubes and Ti^3+/Ov ions were introduced by reduction.The photocatalytic performance of the 2D MoS2/Ti^3+-TiO2 nanotubes was^15 times better than that of TiO2.The HER enhancement of the MoS2/Ti^3+-TiO2 nanotubes can be attributed to the Pt-like behavior of 2D MoS2 and the presence of Ti^3+-ions,which facilitated the quick diffusion of the photogenerated electrons to water,reducing the H2 activation barrier.The presence of Ov ions in the nanotubes and their hollow structure increased their solar utilization.展开更多
A layer of graphene(GR)particles was successfully deposited at the interface between Co(OH)2 nanoparticles and TiO2 nanotubes,aiming to improve the photoelectrochemical performance of the large-bandgap semiconductor T...A layer of graphene(GR)particles was successfully deposited at the interface between Co(OH)2 nanoparticles and TiO2 nanotubes,aiming to improve the photoelectrochemical performance of the large-bandgap semiconductor TiO2.The obtained Co(OH)2/GR/TiO2 was extensively characterized by X-ray diffraction(XRD),scanning electron microscopy(SEM),transmission electron microscopy(TEM),X-ray photoelectron spectroscopy(XPS),UV–vis absorption spectra and photoluminescence(PL)emission spectra.Electrochemical impedance spectra,photogenerated potential-time(E-t),photocurrent density-time(i-t)and i-E curves and open circuit potential(OCP)curves were measured to investigate the photoelectrochemical activities and photogenerated cathodic protection properties.The results revealed that Co(OH)2/GR/TiO2 exhibits excellent photoelectrochemical and photogenerated cathodic performance due to synergistic effect between Co(OH)2 and graphene.Co(OH)2 and graphene co-modified TiO2 photoanode could provide an effective protection for 304 stainless steel(304 SS)in 3.5 wt%Na Cl solution for 12 h,which would be promising for future practical applications in the field of marine corrosion protection.展开更多
Due to increasingly serious environmental problems,many researchers are investigating green cleanenergy to solve the world’s energy supply issues.So the strategy that Au nanoparticles(Au NPs)and bismuth sulfide(Bi2S3...Due to increasingly serious environmental problems,many researchers are investigating green cleanenergy to solve the world’s energy supply issues.So the strategy that Au nanoparticles(Au NPs)and bismuth sulfide(Bi2S3)NPs are used to evenly decorate TiO2 nanotube arrays(TiO2 NTAs)was carried out.Composite materials demonstrated enhanced solar light absorption ability and excellent photoelectrochemical performance.This was attributed to the presence of Bi2S3 NPs with a narrow band gap and the decoration with noble metallic Au NPs which resulted in local surface plasmon resonance(LSPR)effects.The Au/Bi2S3@TiO2 NTAs composites exhibit improved photocatalytic activity for the degradation of methylene blue(MB)under irradiation of UV and visible light.Moreover,the Au/Bi2S3@TiO2 NTAs exhibits high fluorescence emission at 822 nm.Due to the better binding affinity between Bi2S3,TiO2 and Fe3+ions,the synthesized nanocomposites exhibit high selectivity to Fe3+ions.The number of binding sites for Au/Bi2S3@TiO2 NTAs was estimated to be 1.41 according to the double logarithmic regression method.The calculated value of"K"was 1862 M-1.Fluorescence emission intensity decreases with increasing concentration(30μM–5000μM).The detection limit of the synthesized sensor is 0.221μM.展开更多
IrO2 and IrRuOx(Ir:Ru 60:40 at%),supported by 50 wt%onto titania nanotubes(TNTs)and(3 at%Nb)Nb-doped titania nanotubes(Nb-TNTs),as electrocatalysts for the oxygen evolution reaction(OER),were synthesized and character...IrO2 and IrRuOx(Ir:Ru 60:40 at%),supported by 50 wt%onto titania nanotubes(TNTs)and(3 at%Nb)Nb-doped titania nanotubes(Nb-TNTs),as electrocatalysts for the oxygen evolution reaction(OER),were synthesized and characterized by means of structural,surface analytical and electrochemical techniques.Nb doping of titania significantly increased the surface area of the support from 145(TNTs)to 260 m2g-1(Nb-TNTs),which was significantly higher than those of the Nb-doped titania supports previously reported in the literature.The surface analytical techniques showed good dispersion of the catalysts onto the supports.The X-ray photoelectron spectroscopy analyses showed that Nb was mainly in the form of Nb(IV)species,the suitable form to behave as a donor introducing free electrons to the conduction band of titania.The redox transitions of the cyclic voltammograms,in agreement with the XPS results,were found to be reversible.Despite the supported materials presented bigger crystallite sizes than the unsupported ones,the total number of active sites of the former was also higher due to their better catalyst dispersion.Considering the outer and the total charges of the cyclic voltammograms in the range 0.1–1.4 V,stability and electrode potentials at given current densities,the preferred catalyst was Ir O2 supported on the Nb-TNTs.The electrode potentials corresponding to given current densities were between the smallest ones given in the literature despite the small oxide loading used in this work and its Nb doping,thus making the Nb-TNTs-supported IrO2 catalyst a promising candidate for the OER.The good dispersion of IrO2,high specific surface area of the Nb-doped supports,accessibility of the electroactive centers,increased stability due to Nb doping and electron donor properties of the Nb(IV)oxide species were considered the main reasons for its good performance.展开更多
TiO2 nanotube arrays were prepared by means of an electrochemical anodization technique in an organic electrolyte solution doped with polyvinyl pyrrolidone (PVP) and were subsequently modified with phosphomolybdic aci...TiO2 nanotube arrays were prepared by means of an electrochemical anodization technique in an organic electrolyte solution doped with polyvinyl pyrrolidone (PVP) and were subsequently modified with phosphomolybdic acid (PMoA) to obtain PMoA/TiO2 nanotube arrays. The microstructure and photochromic properties were investigated via X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), transmission electron microscopy (TEM), ultraviolet-visible spectroscopy (UV-vis), and X-ray photoelectron spectroscopy (XPS). The results indicated that the Keggin structure of PMoA and the nanotube structure of TiO2 were not destroyed, and there was a strong degree of interaction between PMoA and TiO2 at the biphasic interface with lattice interlacing during the compositing process. The XPS results further indicated that there was a change in the chemical microenvironment during the formation process of the composite, and a new charge transfer bridge was formed through the Mo-O-Ti bond. Under visible light irradiation, the colorless PMoA/TiO2 nanotube array quickly turned blue and exhibited a photochromic response together with reversible photochromism in the presence of H2O2. After visible light irradiation for 60s, the appearance of Mo^5+ species in the XPS spectra indicated a photoreduction process in accordance with a photoinduced electron transfer mechanism.展开更多
Controllable synthesis of insertion-type anode materials with beneficial micro-and nanostructures is a promising approach for the synthesis of sodium-ion storage devices with high-reactivity and excellent electrochemi...Controllable synthesis of insertion-type anode materials with beneficial micro-and nanostructures is a promising approach for the synthesis of sodium-ion storage devices with high-reactivity and excellent electrochemical performance.In this study,we developed a sacrificial-templating route to synthesize TiO_(2)@N-doped carbon nanotubes(TiO_(2)@NC-NTs)with excellent electrochemical performance.The asprepared mesoporous TiO_(2)@NC-NTs with tiny nanocrystals of anatase TiO_(2) wrapped in N-doped carbon layers showed a well-defined tube structure with a large specific surface area of 198 m^(2) g^(-1) and a large pore size of~5 nm.The TiO_(2)@NC-NTs delivered high reversible capacities of 158 m A h g^(-1) at 2 C(1 C=335 m A g^(-1))for 2200 cycles and 146 m A h g^(-1) at 5 C for 4000 cycles,as well as an ultrahigh rate capability of up to 40 C with a capacity of 98 m A h g^(-1).Even at a high current density of 10 C,a capacity of 138 m A h g^(-1) could be delivered over 10,000 cycles.Thus,the synthesis of mesoporous TiO_(2)@NC-NTs was demonstrated to be an efficient approach for developing electrode materials with high sodium storage and long cycle life.展开更多
TiO2 nanotubes(NT)has been demonstrated its potential in orthopaedic applications due to its enhanced surface wettability and bio-osteointegration.However,the fretting biocorrosion is the main concern that limited its...TiO2 nanotubes(NT)has been demonstrated its potential in orthopaedic applications due to its enhanced surface wettability and bio-osteointegration.However,the fretting biocorrosion is the main concern that limited its successfully application in orthopaedic application.In this study,a structure optimised thin TiO2 nanotube(SONT)layer was successfully created on Ti6Al4V bone screw,and its fretting corrosion performance was investigated and compared to the pristine Ti6Al4V bone screws and NT decorated screw in a bone-screw fretting simulation rig.The results have shown that the debonding TiO2 nanotube from the bone screw reduced significantly,as a result of structure optimisation.The SONT layer also exhibited enhanced bio-corrosion resistance compared pristine bone screw and conventionally NT modified bone screw.It is postulated that interfacial layer between TiO2 nanotube and Ti6Al4V substrate,generated during structure optimisation process,enhanced bonding of TiO2 nanotube layer to the Ti6Al4V bone screws that leading to the improvement in fretting corrosion resistance.The results highlighted the potential SONT in orthopaedic application as bone fracture fixation devices.展开更多
Effective utilization of hot electrons generated from the decay of surface plasmon resonance in metal nanoparticles is conductive to improve solar water splitting efficiency.Herein,Ag nanoparticles and reduced graphen...Effective utilization of hot electrons generated from the decay of surface plasmon resonance in metal nanoparticles is conductive to improve solar water splitting efficiency.Herein,Ag nanoparticles and reduced graphene oxide(rGO)co-decorated hierarchical TiO2 nanoring/nanotube arrays(TiO2 R/T)were facilely fabricated by using two-step electrochemical anodization,electrodeposition,and photoreduction methods.Comparative studies were conducted to elucidate the effects of rGO and Ag on the morphology,photoresponse,charge transfer,and photoelectric properties of TiO2.Firstly,scanning electron microscope images confirm that the Ag nanoparticles adhered on TiO2 R/T and TiO2 R/T-rGO have similar diameter of 20 nm except for TiO2 R-rGO/T.Then,the UV-Vis DRS and scatter spectra reveal that the optical property of the Ag-TiO2 R/T-rGO ternary composite is enhanced,ascribing to the visible light absorption of plasmonic Ag nanoparticles and the weakening effect of rGO on light scattering.Meanwhile,intensity-modulated photocurrent spectroscopy and photoluminescence spectra demonstrate that rGO can promote the hot electrons transfer from Ag nanoparticles to Ti substrate,reducing the photogenerated electron-hole recombination.Finally,Ag-TiO2 R/T-rGO photoanode exhibits high photocurrent density(0.98 mA cm?2)and photovoltage(0.90 V),and the stable H2 evolution rate of 413μL h?1 cm?2 within 1.5 h under AM 1.5 which exceeds by 1.30 times than that of pristine TiO2 R/T.In line with the above results,this work provides a reliable route synergizing rGO with plasmonic metal nanoparticles for photocatalysis,in which,rGO presents a broad absorption spectrum and effective photogenerated electrons transfer.展开更多
Au nanoparticle-decorated TiO2 nanotube arrays are prepared by a simple method, which is a thermal annealing thin gold film deposited on anodie oxidized TiO2 nanotube arrays. These electron microscope images present t...Au nanoparticle-decorated TiO2 nanotube arrays are prepared by a simple method, which is a thermal annealing thin gold film deposited on anodie oxidized TiO2 nanotube arrays. These electron microscope images present that Au nanoparticles are well dispersed within the wall and on the surface of the XiO2 nanotubes. Meanwhile, the morphologies of Au nanoparticles can be controlled by changing the thickness of the deposited gold film. Associ- ated with the excitation of localized surface plasmon resonances, the prepared Au nanoparticle-decorated TiO2 nanotube arrays could work as visible light responsive photocatalysts to produce a greatly enhanced photocurrent density. By varying the initial gold film thickness, such Au nanoparticle-decorated TiO2 nanotube arrays could be optimized to obtain the highest photocurrent generation efficiency in the visible and UV light regions.展开更多
Highly ordered TiO_2 nanotube arrays(NTAs) on Si substrate possess broad applications due to its high surfaceto-volume ratio and novel functionalities, however, there are still some challenges on facile synthesis. Her...Highly ordered TiO_2 nanotube arrays(NTAs) on Si substrate possess broad applications due to its high surfaceto-volume ratio and novel functionalities, however, there are still some challenges on facile synthesis. Here, we report a simple and cost-effective high-field(90–180V) anodization method to grow highly ordered TiO_2 NTAs on Si substrate,and investigate the effect of anodization time, voltage, and fluoride content on the formation of TiO_2 NTAs. The current density–time curves, recorded during anodization processes, can be used to determine the optimum anodization time. It is found that the growth rate of TiO_2 NTAs is improved significantly under high field, which is nearly 8 times faster than that under low fields(40–60 V). The length and growth rate of the nanotubes are further increased with the increase of fluoride content in the electrolyte.展开更多
Pt-TiO2 nanotubes with tube diameter of -120 nm and uniformly dispersed Pt particles（size of -2 nm） were successfully synthesized via a carbon nanotube（CNT） templating method followed by a photo-deposition process...Pt-TiO2 nanotubes with tube diameter of -120 nm and uniformly dispersed Pt particles（size of -2 nm） were successfully synthesized via a carbon nanotube（CNT） templating method followed by a photo-deposition processing of Pt nanoparticles. The as-obtained Pt-TiO2 NTs possess both enhanced visible light absorption and reduced recombination of photogenerated electrons and holes. These merits boost the Pt-TiO2 NTs an excellent photocatalytic material toward photooxidation of a variety of low molecular hydrocarbons under atmospheric environment.展开更多
We report the in vitro cell test and in vivo animal test results of titanium oxide nanotubes (TiO2 NTs) as a potential therapeutic agent used for cancer thermotherapy in combination with near-infrared (NIR) laser. The...We report the in vitro cell test and in vivo animal test results of titanium oxide nanotubes (TiO2 NTs) as a potential therapeutic agent used for cancer thermotherapy in combination with near-infrared (NIR) laser. The in vitro cell test results show that both the cells exposed to NIR laser without TiO2 NTs treatment and the cells treated with TiO2 NTs but not with NIR irradiation had cell viabilities higher than 96%. Combination of these two techniques, however, shows cell viability less than 1%. The cell death rate strongly depended on the concentration of TiO2 NTs. Also, the cell deaths were mostly due to necrosis but partly due to late apoptosis. The in vivo animal test results show that tumor cells can be completely destroyed without nearly giving damage to surrounding healthy cells by an injection of an adequate amount of TiO2 NTs/NaCl suspension and a subsequent single continuous laser treatment at a moderately low laser illumina-tion intensity for the exposure time optimized for the tumor size. These results suggest that TiO2 NTs can be effectively utilized as a therapeutic agent for cancer thermotherapy due to their excellent photothermal property and high bio-compatibility.展开更多
Nitrogen-doped TiO2 nanotubes(TNTs)were prepared by ion implantation and anodic oxidation.The prepared samples were applied in photocatalytic(PC)oxidation of methyl blue,rhodamine B,and bisphenol A under light irradia...Nitrogen-doped TiO2 nanotubes(TNTs)were prepared by ion implantation and anodic oxidation.The prepared samples were applied in photocatalytic(PC)oxidation of methyl blue,rhodamine B,and bisphenol A under light irradiation.To explore the influence of doped ions on the band and electronic structure of TiO2,computer simulations were performed using the VASP code implementing spin-polarized density functional theory(DFT).Both substitutional and interstitial nitrogen atoms were considered.The experimental and computational results propose that the electronic structure of TiO2 was modified because of the emergence of impurity states in the band gap by introducing nitrogen into the lattice,leading to the absorption of visible light.The synergy effects of tubular structures and doped nitrogen ions were responsible for highly efficient and stable PC activities induced by visible and ultraviolet(UV)light.展开更多
基金the National Nature Science Foundation of China(21507085,21576162)Shanghai Sailing Program of China(14YF1401500)for financial support
文摘We report the development of a novel visible response BiVO_4/TiO_2(N_2) nanotubes photoanode for photoelectrocatalytic applications. The nitrogen-treated TiO_2 nanotube shows a high carrier concentration rate, thus resulting in a high efficient charge transportation and low electron–hole recombination in the TiO_2–BiVO_4. Therefore, the BiVO_4/TiO_2(N_2) NTs photoanode enabled with a significantly enhanced photocurrent of 2.73 mA cm^(-2)(at 1 V vs. Ag/Ag Cl) and a degradation efficiency in the oxidation of dyes under visible light. Field emission scanning electron microscopy, X-ray diffractometry, energy-dispersive X-ray spectrometer, and UV–Vis absorption spectrum were conducted to characterize the photoanode and demonstrated the presence of both metal oxides as a junction composite.
基金support from the European Union Horizon 2020 program(project HERMES,nr.952184)the Ministry of Education,Youth and Sports of the Czech Republic for supporting CEMNAT(LM2023037)+1 种基金Czech-NanoLab(LM2023051)infrastructures for providing ALD,SEM,EDX,XPS,TEM,and XRDCzech Science Foundation(project 23-08019X,EXPRO).
文摘Synergistic interplays involving multiple active centers originating from TiO2 nanotube layers(TNT)and ruthenium(Ru)species comprising of both single atoms(SAs)and nanoparticles(NPs)augment the alkaline hydrogen evolution reaction(HER)by enhancing Volmer kinetics from rapid water dissociation and improving Tafel kinetics from efficient H*desorption.Atomic layer deposition of Ru with 50 process cycles results in a mixture of Ru SAs and 2.8-0.4 nm NPs present on TNT layers,and it emerges with the highest HER activity among all the electrodes synthesized.A detailed study of the Ti and Ru species using different high-resolution techniques confirmed the presence of Ti^(3+)states and the coexistence of Ru SAs and NPs.With insights from literature,the role of Ti^(3+),appropriate work functions of TNT layers and Ru,and the synergistic effect of Ru SAs and Ru NPs in improving the performance of alkaline HER were elaborated and justified.The aforementioned characteristics led to a remarkable performance by having 9mV onset potentials and 33 mV dec^(-1) of Tafel slopes and a higher turnover frequency of 1.72 H2 s^(-1) at 30 mV.Besides,a notable stability from 28 h staircase chronopotentiometric measurements for TNT@Ru surpasses TNT@Pt in comparison.
基金ACKNOWLEDGMENTS This work was supported by the Science Foundation of Chongqing Science and Technology Committee （No.CSTS2009BB4047）, and Innovative Talent Training Project, the Third Stage of ＂211 Project＂ of Chongqing University （No.S-09109）.
文摘TiO2 nanotube arrays （TNTs） electrode loaded with Zn nanoparticles was prepared by anodization and the size of Zn nanoparticle loaded on TNTs electrode was controlled by chronoamperometry deposition time. Results of SEM and XRD analysis show that Zn nanoparticles had a diameter of about 15-25 nm when the deposition time was 3-5 s. The UV-Vis diffuse reflectance spectra show the Zn loaded harvest light with 480-780 nm more effectively than the unloaded sample. The photocurrent response of Zn loaded TNTs electrodes were studied, the results showed that TNTs electrodes loaded with Zn nanoparti-cles has 50% increased photocurrent response under high-pressure mercury lamp irradiation compared with unloaded TNTs electrode.
文摘A novel titanium dioxide （TiO2） film comprising both nanotubes and nanopaticles was fabricated by an anodization process of the modified titanium. The local electric field at the anodized surface was simulated and its influence on the morphology of the TiO2 film was discussed. The results show that the electric field strength is enhanced by the covering. The growth rate of TiO2 increases with the assist of the local electric field. However, TiO2 dissolution is hindered since the local electric field prevents [TiF6]6- from diffusing. It means that the balance condition for the formation of nanotubes is broken, and TiO2 nanoparticles are formed. Moreover, the crystal structure of the TiO2 film was confirmed using X-ray diffraction and Raman analysis. The anatase is a main phase for the proposed film.
基金supported by the National Natural Science Foundation of China(Grant Nos.51672249,51802282,and 11804301)the Zhejiang Provincial Natural Science Foundation of China(Grant Nos.LQ17F040004 and LY17E020001)Fundamental Research Funds of Zhejiang Sci-Tech University(No.2019Q062)。
文摘Two-dimensional (2D) ultrathin MoS2-modified black Ti^3+-TiO2 nanotubes were fabricated using an electrospinning-hydrothermal treatment-reduction method.Bare TiO2 nanotubes were fabricated via electrospinning.Then,2D MoS2 lamellae were grown on the surface of the nanotubes and Ti^3+/Ov ions were introduced by reduction.The photocatalytic performance of the 2D MoS2/Ti^3+-TiO2 nanotubes was^15 times better than that of TiO2.The HER enhancement of the MoS2/Ti^3+-TiO2 nanotubes can be attributed to the Pt-like behavior of 2D MoS2 and the presence of Ti^3+-ions,which facilitated the quick diffusion of the photogenerated electrons to water,reducing the H2 activation barrier.The presence of Ov ions in the nanotubes and their hollow structure increased their solar utilization.
基金supported financially by the National Natural Science Foundation of China(Nos.51622106 and 51871049)the Fundamental Research Funds for the Central Universities(No.160708001).
文摘A layer of graphene(GR)particles was successfully deposited at the interface between Co(OH)2 nanoparticles and TiO2 nanotubes,aiming to improve the photoelectrochemical performance of the large-bandgap semiconductor TiO2.The obtained Co(OH)2/GR/TiO2 was extensively characterized by X-ray diffraction(XRD),scanning electron microscopy(SEM),transmission electron microscopy(TEM),X-ray photoelectron spectroscopy(XPS),UV–vis absorption spectra and photoluminescence(PL)emission spectra.Electrochemical impedance spectra,photogenerated potential-time(E-t),photocurrent density-time(i-t)and i-E curves and open circuit potential(OCP)curves were measured to investigate the photoelectrochemical activities and photogenerated cathodic protection properties.The results revealed that Co(OH)2/GR/TiO2 exhibits excellent photoelectrochemical and photogenerated cathodic performance due to synergistic effect between Co(OH)2 and graphene.Co(OH)2 and graphene co-modified TiO2 photoanode could provide an effective protection for 304 stainless steel(304 SS)in 3.5 wt%Na Cl solution for 12 h,which would be promising for future practical applications in the field of marine corrosion protection.
基金supported by the National Natural Science Foundation of China(Nos.51972063 and 21501127)the 111 Project(No.D17005)the Priority Academic Program Development of Jiangsu Higher Education Institutions(PAPD).
文摘Due to increasingly serious environmental problems,many researchers are investigating green cleanenergy to solve the world’s energy supply issues.So the strategy that Au nanoparticles(Au NPs)and bismuth sulfide(Bi2S3)NPs are used to evenly decorate TiO2 nanotube arrays(TiO2 NTAs)was carried out.Composite materials demonstrated enhanced solar light absorption ability and excellent photoelectrochemical performance.This was attributed to the presence of Bi2S3 NPs with a narrow band gap and the decoration with noble metallic Au NPs which resulted in local surface plasmon resonance(LSPR)effects.The Au/Bi2S3@TiO2 NTAs composites exhibit improved photocatalytic activity for the degradation of methylene blue(MB)under irradiation of UV and visible light.Moreover,the Au/Bi2S3@TiO2 NTAs exhibits high fluorescence emission at 822 nm.Due to the better binding affinity between Bi2S3,TiO2 and Fe3+ions,the synthesized nanocomposites exhibit high selectivity to Fe3+ions.The number of binding sites for Au/Bi2S3@TiO2 NTAs was estimated to be 1.41 according to the double logarithmic regression method.The calculated value of"K"was 1862 M-1.Fluorescence emission intensity decreases with increasing concentration(30μM–5000μM).The detection limit of the synthesized sensor is 0.221μM.
文摘IrO2 and IrRuOx(Ir:Ru 60:40 at%),supported by 50 wt%onto titania nanotubes(TNTs)and(3 at%Nb)Nb-doped titania nanotubes(Nb-TNTs),as electrocatalysts for the oxygen evolution reaction(OER),were synthesized and characterized by means of structural,surface analytical and electrochemical techniques.Nb doping of titania significantly increased the surface area of the support from 145(TNTs)to 260 m2g-1(Nb-TNTs),which was significantly higher than those of the Nb-doped titania supports previously reported in the literature.The surface analytical techniques showed good dispersion of the catalysts onto the supports.The X-ray photoelectron spectroscopy analyses showed that Nb was mainly in the form of Nb(IV)species,the suitable form to behave as a donor introducing free electrons to the conduction band of titania.The redox transitions of the cyclic voltammograms,in agreement with the XPS results,were found to be reversible.Despite the supported materials presented bigger crystallite sizes than the unsupported ones,the total number of active sites of the former was also higher due to their better catalyst dispersion.Considering the outer and the total charges of the cyclic voltammograms in the range 0.1–1.4 V,stability and electrode potentials at given current densities,the preferred catalyst was Ir O2 supported on the Nb-TNTs.The electrode potentials corresponding to given current densities were between the smallest ones given in the literature despite the small oxide loading used in this work and its Nb doping,thus making the Nb-TNTs-supported IrO2 catalyst a promising candidate for the OER.The good dispersion of IrO2,high specific surface area of the Nb-doped supports,accessibility of the electroactive centers,increased stability due to Nb doping and electron donor properties of the Nb(IV)oxide species were considered the main reasons for its good performance.
基金supported by the National Natural Science Foundation of China (No.61774073)Open Project of State Key Laboratory of Inorganic Synthesis and Preparative Chemistry, Jilin University (No. 2016-25)Science and Technology Development Program of Jilin province (No. 20170101086JC)
文摘TiO2 nanotube arrays were prepared by means of an electrochemical anodization technique in an organic electrolyte solution doped with polyvinyl pyrrolidone (PVP) and were subsequently modified with phosphomolybdic acid (PMoA) to obtain PMoA/TiO2 nanotube arrays. The microstructure and photochromic properties were investigated via X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), transmission electron microscopy (TEM), ultraviolet-visible spectroscopy (UV-vis), and X-ray photoelectron spectroscopy (XPS). The results indicated that the Keggin structure of PMoA and the nanotube structure of TiO2 were not destroyed, and there was a strong degree of interaction between PMoA and TiO2 at the biphasic interface with lattice interlacing during the compositing process. The XPS results further indicated that there was a change in the chemical microenvironment during the formation process of the composite, and a new charge transfer bridge was formed through the Mo-O-Ti bond. Under visible light irradiation, the colorless PMoA/TiO2 nanotube array quickly turned blue and exhibited a photochromic response together with reversible photochromism in the presence of H2O2. After visible light irradiation for 60s, the appearance of Mo^5+ species in the XPS spectra indicated a photoreduction process in accordance with a photoinduced electron transfer mechanism.
基金the financial support provided by internal reseach funding of Khalifa University of Science and Technology,United Arab Emirates(Grant No.CIRA-2018-16)。
文摘Controllable synthesis of insertion-type anode materials with beneficial micro-and nanostructures is a promising approach for the synthesis of sodium-ion storage devices with high-reactivity and excellent electrochemical performance.In this study,we developed a sacrificial-templating route to synthesize TiO_(2)@N-doped carbon nanotubes(TiO_(2)@NC-NTs)with excellent electrochemical performance.The asprepared mesoporous TiO_(2)@NC-NTs with tiny nanocrystals of anatase TiO_(2) wrapped in N-doped carbon layers showed a well-defined tube structure with a large specific surface area of 198 m^(2) g^(-1) and a large pore size of~5 nm.The TiO_(2)@NC-NTs delivered high reversible capacities of 158 m A h g^(-1) at 2 C(1 C=335 m A g^(-1))for 2200 cycles and 146 m A h g^(-1) at 5 C for 4000 cycles,as well as an ultrahigh rate capability of up to 40 C with a capacity of 98 m A h g^(-1).Even at a high current density of 10 C,a capacity of 138 m A h g^(-1) could be delivered over 10,000 cycles.Thus,the synthesis of mesoporous TiO_(2)@NC-NTs was demonstrated to be an efficient approach for developing electrode materials with high sodium storage and long cycle life.
基金financially supported by the European Union via the H2020-MSCA-RISE-2016 program(BAMOS Project,734156)Royal Society via the International Exchange Program(IE161349)+2 种基金Key Research Project from the National Key Research and Development Program of China(2016YFC1100401)National Natural Science Foundation of China(51705507)Young Elite Scientists Sponsorship Program by CAST(2017QNRC0181)。
文摘TiO2 nanotubes(NT)has been demonstrated its potential in orthopaedic applications due to its enhanced surface wettability and bio-osteointegration.However,the fretting biocorrosion is the main concern that limited its successfully application in orthopaedic application.In this study,a structure optimised thin TiO2 nanotube(SONT)layer was successfully created on Ti6Al4V bone screw,and its fretting corrosion performance was investigated and compared to the pristine Ti6Al4V bone screws and NT decorated screw in a bone-screw fretting simulation rig.The results have shown that the debonding TiO2 nanotube from the bone screw reduced significantly,as a result of structure optimisation.The SONT layer also exhibited enhanced bio-corrosion resistance compared pristine bone screw and conventionally NT modified bone screw.It is postulated that interfacial layer between TiO2 nanotube and Ti6Al4V substrate,generated during structure optimisation process,enhanced bonding of TiO2 nanotube layer to the Ti6Al4V bone screws that leading to the improvement in fretting corrosion resistance.The results highlighted the potential SONT in orthopaedic application as bone fracture fixation devices.
基金the National Natural Science Foundation of China(Grant No.51776009)for the financial support.
文摘Effective utilization of hot electrons generated from the decay of surface plasmon resonance in metal nanoparticles is conductive to improve solar water splitting efficiency.Herein,Ag nanoparticles and reduced graphene oxide(rGO)co-decorated hierarchical TiO2 nanoring/nanotube arrays(TiO2 R/T)were facilely fabricated by using two-step electrochemical anodization,electrodeposition,and photoreduction methods.Comparative studies were conducted to elucidate the effects of rGO and Ag on the morphology,photoresponse,charge transfer,and photoelectric properties of TiO2.Firstly,scanning electron microscope images confirm that the Ag nanoparticles adhered on TiO2 R/T and TiO2 R/T-rGO have similar diameter of 20 nm except for TiO2 R-rGO/T.Then,the UV-Vis DRS and scatter spectra reveal that the optical property of the Ag-TiO2 R/T-rGO ternary composite is enhanced,ascribing to the visible light absorption of plasmonic Ag nanoparticles and the weakening effect of rGO on light scattering.Meanwhile,intensity-modulated photocurrent spectroscopy and photoluminescence spectra demonstrate that rGO can promote the hot electrons transfer from Ag nanoparticles to Ti substrate,reducing the photogenerated electron-hole recombination.Finally,Ag-TiO2 R/T-rGO photoanode exhibits high photocurrent density(0.98 mA cm?2)and photovoltage(0.90 V),and the stable H2 evolution rate of 413μL h?1 cm?2 within 1.5 h under AM 1.5 which exceeds by 1.30 times than that of pristine TiO2 R/T.In line with the above results,this work provides a reliable route synergizing rGO with plasmonic metal nanoparticles for photocatalysis,in which,rGO presents a broad absorption spectrum and effective photogenerated electrons transfer.
基金Supported by the National Natural Science Foundation of China under Grant Nos 11474215 and 21204058the Priority Academic Program Development of Jiangsu Higher Education Institutions
文摘Au nanoparticle-decorated TiO2 nanotube arrays are prepared by a simple method, which is a thermal annealing thin gold film deposited on anodie oxidized TiO2 nanotube arrays. These electron microscope images present that Au nanoparticles are well dispersed within the wall and on the surface of the XiO2 nanotubes. Meanwhile, the morphologies of Au nanoparticles can be controlled by changing the thickness of the deposited gold film. Associ- ated with the excitation of localized surface plasmon resonances, the prepared Au nanoparticle-decorated TiO2 nanotube arrays could work as visible light responsive photocatalysts to produce a greatly enhanced photocurrent density. By varying the initial gold film thickness, such Au nanoparticle-decorated TiO2 nanotube arrays could be optimized to obtain the highest photocurrent generation efficiency in the visible and UV light regions.
基金supported by National 863 Program 2011AA050518the Natural Science Foundation of China(Grant Nos.11174197,11574203,and 61234005)
文摘Highly ordered TiO_2 nanotube arrays(NTAs) on Si substrate possess broad applications due to its high surfaceto-volume ratio and novel functionalities, however, there are still some challenges on facile synthesis. Here, we report a simple and cost-effective high-field(90–180V) anodization method to grow highly ordered TiO_2 NTAs on Si substrate,and investigate the effect of anodization time, voltage, and fluoride content on the formation of TiO_2 NTAs. The current density–time curves, recorded during anodization processes, can be used to determine the optimum anodization time. It is found that the growth rate of TiO_2 NTAs is improved significantly under high field, which is nearly 8 times faster than that under low fields(40–60 V). The length and growth rate of the nanotubes are further increased with the increase of fluoride content in the electrolyte.
基金financially supported by the National Key Project on Basic Research(No.2013CB933203)the Natural Science Foundation of China(Nos.21373224 and 21577143)+1 种基金the Natural Science Foundation of Fujian Province(Nos.2014H0054 and 2015J0544)the One Hundred Talents Program of the Chinese Academy of Sciences
文摘Pt-TiO2 nanotubes with tube diameter of -120 nm and uniformly dispersed Pt particles（size of -2 nm） were successfully synthesized via a carbon nanotube（CNT） templating method followed by a photo-deposition processing of Pt nanoparticles. The as-obtained Pt-TiO2 NTs possess both enhanced visible light absorption and reduced recombination of photogenerated electrons and holes. These merits boost the Pt-TiO2 NTs an excellent photocatalytic material toward photooxidation of a variety of low molecular hydrocarbons under atmospheric environment.
文摘We report the in vitro cell test and in vivo animal test results of titanium oxide nanotubes (TiO2 NTs) as a potential therapeutic agent used for cancer thermotherapy in combination with near-infrared (NIR) laser. The in vitro cell test results show that both the cells exposed to NIR laser without TiO2 NTs treatment and the cells treated with TiO2 NTs but not with NIR irradiation had cell viabilities higher than 96%. Combination of these two techniques, however, shows cell viability less than 1%. The cell death rate strongly depended on the concentration of TiO2 NTs. Also, the cell deaths were mostly due to necrosis but partly due to late apoptosis. The in vivo animal test results show that tumor cells can be completely destroyed without nearly giving damage to surrounding healthy cells by an injection of an adequate amount of TiO2 NTs/NaCl suspension and a subsequent single continuous laser treatment at a moderately low laser illumina-tion intensity for the exposure time optimized for the tumor size. These results suggest that TiO2 NTs can be effectively utilized as a therapeutic agent for cancer thermotherapy due to their excellent photothermal property and high bio-compatibility.
基金Project supported by the National Natural Science Foundation for Joint Fund Key Project of China(Grant No.U1865206)the National Science and Technology Major Project of China(Grant No.2017-Ⅶ-0012-0107)+1 种基金the National Defense Science and Technology Key Laboratory Fund of China(Grant No.614220207011802)the Key Area Research and Development Program of Guangdong Province,China(Grant No.2019B090909002)。
文摘Nitrogen-doped TiO2 nanotubes(TNTs)were prepared by ion implantation and anodic oxidation.The prepared samples were applied in photocatalytic(PC)oxidation of methyl blue,rhodamine B,and bisphenol A under light irradiation.To explore the influence of doped ions on the band and electronic structure of TiO2,computer simulations were performed using the VASP code implementing spin-polarized density functional theory(DFT).Both substitutional and interstitial nitrogen atoms were considered.The experimental and computational results propose that the electronic structure of TiO2 was modified because of the emergence of impurity states in the band gap by introducing nitrogen into the lattice,leading to the absorption of visible light.The synergy effects of tubular structures and doped nitrogen ions were responsible for highly efficient and stable PC activities induced by visible and ultraviolet(UV)light.