By means of the positron annihilation technique (PAT), superfine TiC powders obtained by ball-milling process were characterized. The results showed that there was a clear correlation between the change in TiC powders...By means of the positron annihilation technique (PAT), superfine TiC powders obtained by ball-milling process were characterized. The results showed that there was a clear correlation between the change in TiC powders and that in the PAT parameters. In the high energy ball-milling process, TiC powders were severely deformed, which caused large increase in the amount of defects and severe distortion of lattice. On the other hand, the extreme refinement of grain size of powders resulted in the increase of grain boundary area and enhancement of system free energy. The spacing between deformed domains in 96 h milled samples is somewhat smaller than those in 48 h milled samples, indicating the size of Type II defects in 96 h milled samples is somewhat smaller than that in 48 h milled samples.展开更多
In this paper, Al/Ni/TiC powders were mixed on the surface of A380 aluminum alloy, by selecting appropriate laser parameters;the cladding layer with good adhesion to the substrate was obtained. The microstructure and ...In this paper, Al/Ni/TiC powders were mixed on the surface of A380 aluminum alloy, by selecting appropriate laser parameters;the cladding layer with good adhesion to the substrate was obtained. The microstructure and properties of the cladding layer under different laser parameters were analyzed. The results show that: the phase composition of the cladding layer is mainly composed of TiC, Al, Ni, C and Ti phases. The hardness of the cladding region is up to 173.3 HV, which is about 2.9 times the matrix (–59.1 HV). The corrosion voltage (–1.8 V) of the cladding layer shifted significantly from the corrosion potential (–1.18 V), the corrosion current density increased, the resistance value decreased and the diameter of the capacitor arc decreased;all these phenomena indicate that the corrosion resistance of the cladding layer is decreased.展开更多
A Ni-base alloy composite coating reinforced with TiC particles of various shapes and sizes on medium carbon steel substrate was produced by multilayer laser cladding. The chemical compositions, microstructures and su...A Ni-base alloy composite coating reinforced with TiC particles of various shapes and sizes on medium carbon steel substrate was produced by multilayer laser cladding. The chemical compositions, microstructures and surface morphology of the cladded layer were analyzed using energy dispersive X-ray spectroscopy （EDX）, scanning electron microscope （SEM）, and X-ray diffractometry （XRD）. The experimental results showed that an excellent metallurgical bonding between the coating and the substrate was obtained. The microstructure of the coating was mainly composed of γ-Ni dendrites, a small amount of CrB, Ni3B, M23C6 and dispersed TiC particles. Much more and larger TiC particles formed in the overlapping zone, which led to a slightly higher microhardness of this zone. The maximum microhardness of the coating was about HV0.21200. The effects of the laser processing parameters on the microstructures and properties of coating were also investigated.展开更多
A type of polymer-coated Al2O3/ZrO2/TiC ceramic powder was prepared. The laser sintering mechanism of polymer-coated Al2O3/ZrO2/TiC powder was investigated by studying the dynamic laser sintering process. It is found ...A type of polymer-coated Al2O3/ZrO2/TiC ceramic powder was prepared. The laser sintering mechanism of polymer-coated Al2O3/ZrO2/TiC powder was investigated by studying the dynamic laser sintering process. It is found that the mechanism is viscous flow when the sintering temperature is between 80 ℃ and 120 ℃, and it is melting/solidification when the temperature is above 120 ℃. The process parameters of selective laser sintering were optimized by using ortho-design method. The results show that the optimal parameters include laser power of 14 W, scanning velocity of 1 400 mm/s, preheating temperature of 50 ℃ and powder depth of 0.15 mm. A two-step post-treatment process is adopted to improve the mechanical properties of laser sintered part, which includes polymer debinding and high temperature sintering. After vacuum sintering for 2 h at 1 650 ℃, the bending strength and fracture toughness of Al2O3/ZrO2/TiC ceramic part reach 358 MPa and 6.9 MPa·m1/2, respectively.展开更多
基金This research is jointly financially supported by the National Natural Science Foundation of China, the Doctoral Edu-cation F
文摘By means of the positron annihilation technique (PAT), superfine TiC powders obtained by ball-milling process were characterized. The results showed that there was a clear correlation between the change in TiC powders and that in the PAT parameters. In the high energy ball-milling process, TiC powders were severely deformed, which caused large increase in the amount of defects and severe distortion of lattice. On the other hand, the extreme refinement of grain size of powders resulted in the increase of grain boundary area and enhancement of system free energy. The spacing between deformed domains in 96 h milled samples is somewhat smaller than those in 48 h milled samples, indicating the size of Type II defects in 96 h milled samples is somewhat smaller than that in 48 h milled samples.
文摘In this paper, Al/Ni/TiC powders were mixed on the surface of A380 aluminum alloy, by selecting appropriate laser parameters;the cladding layer with good adhesion to the substrate was obtained. The microstructure and properties of the cladding layer under different laser parameters were analyzed. The results show that: the phase composition of the cladding layer is mainly composed of TiC, Al, Ni, C and Ti phases. The hardness of the cladding region is up to 173.3 HV, which is about 2.9 times the matrix (–59.1 HV). The corrosion voltage (–1.8 V) of the cladding layer shifted significantly from the corrosion potential (–1.18 V), the corrosion current density increased, the resistance value decreased and the diameter of the capacitor arc decreased;all these phenomena indicate that the corrosion resistance of the cladding layer is decreased.
基金This research was supported by the Natural Science Foundation of Inner Mongolia （No. 200508010704）the Science Foundation of Inner Mongolia University of Technology （No. ZD200521） the Postdoctoral Science Foundation of China.
文摘A Ni-base alloy composite coating reinforced with TiC particles of various shapes and sizes on medium carbon steel substrate was produced by multilayer laser cladding. The chemical compositions, microstructures and surface morphology of the cladded layer were analyzed using energy dispersive X-ray spectroscopy （EDX）, scanning electron microscope （SEM）, and X-ray diffractometry （XRD）. The experimental results showed that an excellent metallurgical bonding between the coating and the substrate was obtained. The microstructure of the coating was mainly composed of γ-Ni dendrites, a small amount of CrB, Ni3B, M23C6 and dispersed TiC particles. Much more and larger TiC particles formed in the overlapping zone, which led to a slightly higher microhardness of this zone. The maximum microhardness of the coating was about HV0.21200. The effects of the laser processing parameters on the microstructures and properties of coating were also investigated.
基金Project(03022) supported by the Key Science Research Program of Education Ministry of China
文摘A type of polymer-coated Al2O3/ZrO2/TiC ceramic powder was prepared. The laser sintering mechanism of polymer-coated Al2O3/ZrO2/TiC powder was investigated by studying the dynamic laser sintering process. It is found that the mechanism is viscous flow when the sintering temperature is between 80 ℃ and 120 ℃, and it is melting/solidification when the temperature is above 120 ℃. The process parameters of selective laser sintering were optimized by using ortho-design method. The results show that the optimal parameters include laser power of 14 W, scanning velocity of 1 400 mm/s, preheating temperature of 50 ℃ and powder depth of 0.15 mm. A two-step post-treatment process is adopted to improve the mechanical properties of laser sintered part, which includes polymer debinding and high temperature sintering. After vacuum sintering for 2 h at 1 650 ℃, the bending strength and fracture toughness of Al2O3/ZrO2/TiC ceramic part reach 358 MPa and 6.9 MPa·m1/2, respectively.