The method of Ti/TiO2-NiO photoelectrode prepared by using sol-gel method continued by calcination process was introduced. The prepared TiO2-NiO film was observed with XRD and TEM. The anatase-rutile TiO2 was mainly o...The method of Ti/TiO2-NiO photoelectrode prepared by using sol-gel method continued by calcination process was introduced. The prepared TiO2-NiO film was observed with XRD and TEM. The anatase-rutile TiO2 was mainly on the prepared TiO2-NiO composite surface electrode. In addition to NiO, the composite also formed NiTiO3 that increased with increasing calcination temperature. Photoelectrocatalytic degradation of Rhodamine B (RB) using this electrode was investigated, and anodic potential and pH were optimized. RB degradation was investigated under different conditions, and it showed that photoelectrocatalytic degradation could achieve efficient and complete mineralization of organic pollutant. Through comparison of the photoelectrocatalytic oxidation using the Ti/TiO2-NiO electrode operated by single photoanode with the Ti/TiO2-NiO electrode operated by several photoanode, it was found that the photoelectrocatalytic efficiency of that by series photoanodes was higher. Additionally, photoelectrocatalytic system was performed at the several different photoelectrodes, which verified the higher photocatalytic activity compared with the single photoelectrode.展开更多
文摘The method of Ti/TiO2-NiO photoelectrode prepared by using sol-gel method continued by calcination process was introduced. The prepared TiO2-NiO film was observed with XRD and TEM. The anatase-rutile TiO2 was mainly on the prepared TiO2-NiO composite surface electrode. In addition to NiO, the composite also formed NiTiO3 that increased with increasing calcination temperature. Photoelectrocatalytic degradation of Rhodamine B (RB) using this electrode was investigated, and anodic potential and pH were optimized. RB degradation was investigated under different conditions, and it showed that photoelectrocatalytic degradation could achieve efficient and complete mineralization of organic pollutant. Through comparison of the photoelectrocatalytic oxidation using the Ti/TiO2-NiO electrode operated by single photoanode with the Ti/TiO2-NiO electrode operated by several photoanode, it was found that the photoelectrocatalytic efficiency of that by series photoanodes was higher. Additionally, photoelectrocatalytic system was performed at the several different photoelectrodes, which verified the higher photocatalytic activity compared with the single photoelectrode.
文摘采用溶胶-凝胶法制备高活性Ti基纳米TiO2-ZrO2膜电极.通过X射线衍射分析表明,纳米TiO2-ZrO2粉体呈微-纳二级结构.扫描电子显微镜测试表明,颗粒平均尺寸约为30 nm.通过循环伏安和恒电流电解技术研究发现,Ti/nanoTiO2-ZrO2电极对马来酸电催化还原制备丁二酸的活性要高于Ti/nanoTiO2电极,反应过程受扩散控制.以钛基氧化钌电极为阳极,Ti/nano TiO2-ZrO2膜电极为阴极进行恒电流电解实验.结果表明,控制电流密度20 mA cm-2,温度60℃,丁二酸的产率达到96%.