In this study,sulfur-doped TiO2 /Ti photoelectrodes were prepared by anodization. The morphology, crystalline structure,composition of sulfur-doped TiO2 /Ti film and light absorption property were examined by SEM,XRD,...In this study,sulfur-doped TiO2 /Ti photoelectrodes were prepared by anodization. The morphology, crystalline structure,composition of sulfur-doped TiO2 /Ti film and light absorption property were examined by SEM,XRD,XRF,XPS and UV/VIS respectively. Dimethyl phthalate( DMP) ,one kind of environmental disrupting chemicals( EDCs) ,was degraded by the optimized photoelectrodes. Power of xenon light,initial concentration of DMP,photoelectrocatalytic( PEC) area of photoelectrode and bias were investigated in the study on kinetics of PEC degradation of DMP. Hence,this study concluded that the optimum conditions were power of xenon light 150 W,initial concentration of DMP 1 mg/L,PEC area of sulfur-doped TiO2 /Ti photoelectrode 10 cm2,bias 1. 3 V in the PEC reaction system.展开更多
The preparation and study of supported TiO2 for photocatalytic application in solar cell devices is a relevant research field. Thin films of TiO2 prepared on Ti by thermal oxidation in a wide range of temperatures (45...The preparation and study of supported TiO2 for photocatalytic application in solar cell devices is a relevant research field. Thin films of TiO2 prepared on Ti by thermal oxidation in a wide range of temperatures (450°C - 900°C) were characterized by electrochemical impedance spectroscopy, potentiometry and amperometry. This material presents photoelectrochemical activity, which depends dramatically of the oxidation temperature and the exposition time at the studied temperatures. The flatband potential as well as the donor density and the resistance to the charge transfer were measured. All these parameters are temperature dependent, and the optimal values are observed on the photoelectrodes prepared at 750°C. This result is consistent with the photochemical response reported in the literature for thin films of Ti/TiO2 prepared under similar conditions.展开更多
Self-made TiO2 nanoparticles were used as photoelectrode material of dye sensitized solar cell. The TiO2 thin film coats through spreading nanoparticles evenly onto the ITO glass via self-made spin-heat platform, and ...Self-made TiO2 nanoparticles were used as photoelectrode material of dye sensitized solar cell. The TiO2 thin film coats through spreading nanoparticles evenly onto the ITO glass via self-made spin-heat platform, and then TiO2 thin film is soaked in the dye N-719 more than 12 h to prepare the photoelectrode device. The TiO2 nanoparticles produced by electric-discharge-nanofluid-process have premium anatase crystal property, and its diameter can be controlled within a range of 20-50 nm. The surface energy zeta potential of nanofluid is from -22 mV to -28.8 mV, it is a stable particle suspension in the deionized water. A trace of surfactant Triton X-100 put upon the surface of ITO glass can produce a uniform and dense TiO2 thin film and heating up the spin platform to 200 oC is able to eliminate mixed surfac-tant. Self-made TiO2 film presents excellent dye absorption performance and even doesn＇t need heat treatment procedure to enhance essential property. Results of energy analysis show the thicker film structure will increase the short-circuit current density that causes higher conversion efficiency. But, as the film structure is large and thick, both the open-circuit voltage and fill factor will decline gradually to lead bad efficiency of dye-sensitized solar cell.展开更多
Nanostructured TiO 2 porous film supported on nickel was prepared through sol-gel process,and was used as photoelectrode in solar energy photoelectrochemical cell.It was found that short circuit photocurrent and open ...Nanostructured TiO 2 porous film supported on nickel was prepared through sol-gel process,and was used as photoelectrode in solar energy photoelectrochemical cell.It was found that short circuit photocurrent and open circuit photovoltage of the photoelectrodes increased with the increment of sintering temperature and thickness of TiO 2 film.Through STM,the pore quantity and diameter of nanostructured TiO 2 film were found to increase with the increment of sintering temperature.It was found that the transparence of different thickness nanostructured TiO 2 films coated on quartz did not change much.展开更多
基金Sponsored by the National Natural Science Foundation of China ( Grant No 50678044)
文摘In this study,sulfur-doped TiO2 /Ti photoelectrodes were prepared by anodization. The morphology, crystalline structure,composition of sulfur-doped TiO2 /Ti film and light absorption property were examined by SEM,XRD,XRF,XPS and UV/VIS respectively. Dimethyl phthalate( DMP) ,one kind of environmental disrupting chemicals( EDCs) ,was degraded by the optimized photoelectrodes. Power of xenon light,initial concentration of DMP,photoelectrocatalytic( PEC) area of photoelectrode and bias were investigated in the study on kinetics of PEC degradation of DMP. Hence,this study concluded that the optimum conditions were power of xenon light 150 W,initial concentration of DMP 1 mg/L,PEC area of sulfur-doped TiO2 /Ti photoelectrode 10 cm2,bias 1. 3 V in the PEC reaction system.
文摘The preparation and study of supported TiO2 for photocatalytic application in solar cell devices is a relevant research field. Thin films of TiO2 prepared on Ti by thermal oxidation in a wide range of temperatures (450°C - 900°C) were characterized by electrochemical impedance spectroscopy, potentiometry and amperometry. This material presents photoelectrochemical activity, which depends dramatically of the oxidation temperature and the exposition time at the studied temperatures. The flatband potential as well as the donor density and the resistance to the charge transfer were measured. All these parameters are temperature dependent, and the optimal values are observed on the photoelectrodes prepared at 750°C. This result is consistent with the photochemical response reported in the literature for thin films of Ti/TiO2 prepared under similar conditions.
文摘Self-made TiO2 nanoparticles were used as photoelectrode material of dye sensitized solar cell. The TiO2 thin film coats through spreading nanoparticles evenly onto the ITO glass via self-made spin-heat platform, and then TiO2 thin film is soaked in the dye N-719 more than 12 h to prepare the photoelectrode device. The TiO2 nanoparticles produced by electric-discharge-nanofluid-process have premium anatase crystal property, and its diameter can be controlled within a range of 20-50 nm. The surface energy zeta potential of nanofluid is from -22 mV to -28.8 mV, it is a stable particle suspension in the deionized water. A trace of surfactant Triton X-100 put upon the surface of ITO glass can produce a uniform and dense TiO2 thin film and heating up the spin platform to 200 oC is able to eliminate mixed surfac-tant. Self-made TiO2 film presents excellent dye absorption performance and even doesn＇t need heat treatment procedure to enhance essential property. Results of energy analysis show the thicker film structure will increase the short-circuit current density that causes higher conversion efficiency. But, as the film structure is large and thick, both the open-circuit voltage and fill factor will decline gradually to lead bad efficiency of dye-sensitized solar cell.
文摘Nanostructured TiO 2 porous film supported on nickel was prepared through sol-gel process,and was used as photoelectrode in solar energy photoelectrochemical cell.It was found that short circuit photocurrent and open circuit photovoltage of the photoelectrodes increased with the increment of sintering temperature and thickness of TiO 2 film.Through STM,the pore quantity and diameter of nanostructured TiO 2 film were found to increase with the increment of sintering temperature.It was found that the transparence of different thickness nanostructured TiO 2 films coated on quartz did not change much.
文摘采用溶胶-凝胶法制备高活性Ti基纳米TiO2-ZrO2膜电极.通过X射线衍射分析表明,纳米TiO2-ZrO2粉体呈微-纳二级结构.扫描电子显微镜测试表明,颗粒平均尺寸约为30 nm.通过循环伏安和恒电流电解技术研究发现,Ti/nanoTiO2-ZrO2电极对马来酸电催化还原制备丁二酸的活性要高于Ti/nanoTiO2电极,反应过程受扩散控制.以钛基氧化钌电极为阳极,Ti/nano TiO2-ZrO2膜电极为阴极进行恒电流电解实验.结果表明,控制电流密度20 mA cm-2,温度60℃,丁二酸的产率达到96%.