The Ti/SnO2 Sb2O4 electrode has been prepared by the electroplate sinter method. The effect of SbCl3 adding amount and sintering temperature on its electrode lifetime and oxygen evolution potential were investigated b...The Ti/SnO2 Sb2O4 electrode has been prepared by the electroplate sinter method. The effect of SbCl3 adding amount and sintering temperature on its electrode lifetime and oxygen evolution potential were investigated by means of EDX, SEM and XRD analysis. The results indicated that the electrode appeared the best performance when the SbCl3 adding amounts was 0.2g and the sintering temperature was 550℃. In optimized conditions Ti substrate was entirely covered by SnO2 Sb2O4 and the combinations among them were tight. Due to the use of electroplate method, the electrical conductivity, the oxygen evolution potential and the electrode lifetime were increased, so the electro catalytic activity and the electrochemical stability of the prepared electrode were found to be superior.展开更多
采用超声涂覆-热分解法制备稀土金属Ce掺杂Ti/SnO_2-Sb电极,利用SEM对电极表面形态进行表征,并考察了Ce掺杂量和电流密度对修饰电极电催化性能和稳定性的影响。结果表明,掺杂后电极涂层中引入了新物质CeO_2,优化了电极的表面结构和形态...采用超声涂覆-热分解法制备稀土金属Ce掺杂Ti/SnO_2-Sb电极,利用SEM对电极表面形态进行表征,并考察了Ce掺杂量和电流密度对修饰电极电催化性能和稳定性的影响。结果表明,掺杂后电极涂层中引入了新物质CeO_2,优化了电极的表面结构和形态;制备得到的电极对苯酚和对甲酚都有较好的降解效果,当Ce掺杂量为1%时降解苯酚性能最优,Ce掺杂量为2%时降解对甲酚性能最优;在最优掺杂量下,当电流密度为10 m A/cm2时降解苯酚性能最佳,电流密度为20 m A/cm2时降解对甲酚性能最佳。展开更多
文摘The Ti/SnO2 Sb2O4 electrode has been prepared by the electroplate sinter method. The effect of SbCl3 adding amount and sintering temperature on its electrode lifetime and oxygen evolution potential were investigated by means of EDX, SEM and XRD analysis. The results indicated that the electrode appeared the best performance when the SbCl3 adding amounts was 0.2g and the sintering temperature was 550℃. In optimized conditions Ti substrate was entirely covered by SnO2 Sb2O4 and the combinations among them were tight. Due to the use of electroplate method, the electrical conductivity, the oxygen evolution potential and the electrode lifetime were increased, so the electro catalytic activity and the electrochemical stability of the prepared electrode were found to be superior.
文摘采用超声涂覆-热分解法制备稀土金属Ce掺杂Ti/SnO_2-Sb电极,利用SEM对电极表面形态进行表征,并考察了Ce掺杂量和电流密度对修饰电极电催化性能和稳定性的影响。结果表明,掺杂后电极涂层中引入了新物质CeO_2,优化了电极的表面结构和形态;制备得到的电极对苯酚和对甲酚都有较好的降解效果,当Ce掺杂量为1%时降解苯酚性能最优,Ce掺杂量为2%时降解对甲酚性能最优;在最优掺杂量下,当电流密度为10 m A/cm2时降解苯酚性能最佳,电流密度为20 m A/cm2时降解对甲酚性能最佳。