The Ti/SnO2 Sb2O4 electrode has been prepared by the electroplate sinter method. The effect of SbCl3 adding amount and sintering temperature on its electrode lifetime and oxygen evolution potential were investigated b...The Ti/SnO2 Sb2O4 electrode has been prepared by the electroplate sinter method. The effect of SbCl3 adding amount and sintering temperature on its electrode lifetime and oxygen evolution potential were investigated by means of EDX, SEM and XRD analysis. The results indicated that the electrode appeared the best performance when the SbCl3 adding amounts was 0.2g and the sintering temperature was 550℃. In optimized conditions Ti substrate was entirely covered by SnO2 Sb2O4 and the combinations among them were tight. Due to the use of electroplate method, the electrical conductivity, the oxygen evolution potential and the electrode lifetime were increased, so the electro catalytic activity and the electrochemical stability of the prepared electrode were found to be superior.展开更多
文摘采用电沉积法镀制Ti/Sb-SnO2/β-PbO2电极,研究电沉积时间、镀液温度、pH值、NaF浓度,以及电流密度等因素对电极催化活性和稳定性的影响规律.结果表明,当电沉积时间为1 h,镀液温度为60℃,镀液pH值为1,NaF浓度为0.04 mol.L-1,组合电流密度为600/400 A.m-2(梯度电流密度)时,电极性能最佳,对苯酚降解率达91.4%,强化寿命为23 h.
文摘The Ti/SnO2 Sb2O4 electrode has been prepared by the electroplate sinter method. The effect of SbCl3 adding amount and sintering temperature on its electrode lifetime and oxygen evolution potential were investigated by means of EDX, SEM and XRD analysis. The results indicated that the electrode appeared the best performance when the SbCl3 adding amounts was 0.2g and the sintering temperature was 550℃. In optimized conditions Ti substrate was entirely covered by SnO2 Sb2O4 and the combinations among them were tight. Due to the use of electroplate method, the electrical conductivity, the oxygen evolution potential and the electrode lifetime were increased, so the electro catalytic activity and the electrochemical stability of the prepared electrode were found to be superior.