An Al_(2)O_(3)/Al-Cu-Mn composite was fabricated using a combination of ball milling and liquid-solid reaction,with a nominal composition of Al-4Cu-0.5Mn-2.8γ-Al_(2)O_(3).The composite contains reinforcement particle...An Al_(2)O_(3)/Al-Cu-Mn composite was fabricated using a combination of ball milling and liquid-solid reaction,with a nominal composition of Al-4Cu-0.5Mn-2.8γ-Al_(2)O_(3).The composite contains reinforcement particles,including nano-sizedθ’and T(Al_(20)Cu_(2)Mn_(3))particles after T6 heat treatment,as well as in-situ synthesized nano-sizedγ-Al_(2)O_(3)particles.Tensile tests of the Al-4Cu-0.5Mn-2.8γ-Al_(2)O_(3)composite and the Al-4Cu-0.5Mn base alloy after T6 treatment were carried out at room temperature and elevated temperatures(200°C,300°C,and 400°C).Compared with the base alloy,the yield strength of the Al-4Cu-0.5Mn-2.8γ-Al_(2)O_(3)composite after T6 treatment increases significantly from 187 MPa to 263 MPa at room temperature.Simultaneously,at elevated temperatures,the yield strength is also enhanced,with a yield strength of 52 MPa at 400°C for this composite.The in-situ fabricatedγ-Al_(2)O_(3)particles,mainly distributed along the grain boundaries,are supposed to play the main strengthening role,especially at high temperatures.This work acts as a reference for designing composites for high-temperature applications.展开更多
A Y2O3 particle enhanced Ni/TiC composite coating was fabricated in-situ on a TC4 Ti alloy by laser surface cladding.The phase component,microstructure,composition distribution and properties of the composite layer we...A Y2O3 particle enhanced Ni/TiC composite coating was fabricated in-situ on a TC4 Ti alloy by laser surface cladding.The phase component,microstructure,composition distribution and properties of the composite layer were investigated.The composite layer has graded microstructures and compositions,due to the fast melting followed by rapid solidification and cooling during laser cladding.The TiC powders are completely dissolved into the melted layer during melting and segregated as fine dendrites when solidified.The size of TiC dendrites decreases with increasing depth.Y2O3 fine particles distribute in the whole clad layer.The Y2O3 particle enhanced Ni/TiC composite layer has a quite uniform hardness along depth with a maximum value of HV1380,which is 4 times higher than the initial hardness.The wear resistance of the Ti alloy is significantly improved after laser cladding due to the high hardness of the composite coating.展开更多
Two Al2O3/Cu composites containing 0.24 wt.% Al2O3 and 0.60 wt.% Al2O3 separately are prepared by internal oxidation. Effects of sliding speed and pressure on the frictional characteristics of the composites and coppe...Two Al2O3/Cu composites containing 0.24 wt.% Al2O3 and 0.60 wt.% Al2O3 separately are prepared by internal oxidation. Effects of sliding speed and pressure on the frictional characteristics of the composites and copper against brass are investigated and compared. The changes in morphology of the sliding surface and subsurface are examined with scanning electron microscope （SEM） and energy dispersive X-ray spectrum （EDS）. The results show that the wear resistance of the Al2O3/Cu composites is superior to that of copper under the same conditions, Under a given electrical current, the wear rate of Al2O3/Cu composites decreases as the Al2O3-content increases, However, the wear rates of the Al2O3/Cu composites and copper increase as the sliding speed and pressure increase under dry sliding condition. The main wear mechanisms for Al2O3/Cu composites are of abrasion and adhesion; for copper, it is adhesion, although wear by oxidation and electrical erosion can also be observed as the speed and pressure rise.展开更多
The NiCrBSi-Y2O3 composite coatings were prepared on the surface of 45 carbon steel by plasma spray, the microstructure and tribological properties of the coatings were investigated. The results show that the NiCrBSi-...The NiCrBSi-Y2O3 composite coatings were prepared on the surface of 45 carbon steel by plasma spray, the microstructure and tribological properties of the coatings were investigated. The results show that the NiCrBSi-Y2O3 composite coatings are mainly composed of γ-Ni, CrB, Cr7C3 and Y2O3. With addition of Y2O3, hard phases such as CrB, Cr7C3 emerge in composite coating, and the density of the composite coatings also increases. The NiCrBSi-0.5Y2O3 composite coating presents excellent tribological properties. Its friction coefficient is 0.175, which is about 37% of that of the pure NiCrBSi coating. The mass wear loss is 1.2 mg, which is reduced by 43% compared with the pure NiCrBSi coating. When the loads are 6-10 N, the NiCrBSi-0.5Y2O3 composite coating suffers from slight wear and the wear mechanisms are mainly adhesive wear accompany with slight micro-cutting wear and micro-fracture wear. As the load increases to 12 N, the wear mechanisms are adhesive wear and severe micro-cutting wear.展开更多
（TiB2＋Al2O3）/NiAl composites were synthesized by self-propagation high-temperature synthesis, and their phase compositions, microstructures and evolution modes were studied. The microstructures and shapes vary with...（TiB2＋Al2O3）/NiAl composites were synthesized by self-propagation high-temperature synthesis, and their phase compositions, microstructures and evolution modes were studied. The microstructures and shapes vary with the TiB2＋Al2O3 content in the NiAl matrix. TiB2 particles take a great variety of elementary shapes such as white bars, plates, herringbones, regular cubes and cuboids. These results outline a strategy of self-assembly processes in real time to build diversified microstructures. Some TiB2 grains in sizes of 2-5μm are embeded in Al2O3 clusters, while a small number of TiB2 particles disperse in the NiAl matrix. It is believed that the higher the TiB2＋Al2O3 content is, the more the regular shapes and homogeneous distributions of TiB2 and Al2O3 will be present in the NiAl matrix.展开更多
Al-5%Si-AI2O3 composites were prepared by powder metallurgy and in-situ reactive synthesis technology. Friction and wear properties of Al-5%Si-Al2O3 composites were studied using an M-2000 wear tester. The effects of ...Al-5%Si-AI2O3 composites were prepared by powder metallurgy and in-situ reactive synthesis technology. Friction and wear properties of Al-5%Si-Al2O3 composites were studied using an M-2000 wear tester. The effects of load, sliding speed and long time continuous friction on friction and wear properties of Al-5%Si-Al2O3 composites were investigated, respectively. Wear surface and wear mechanism of Al-5%Si-Al2O3 composites were studied by Quanta 200 FE-SEM. Results showed that with load increasing, wear loss and coefficient of friction increased. With sliding speed going up, the surface temperature of sample made the rate of the producing of oxidation layer increase, while wear loss and coefficient of friction decreased. With the sliding distance increasing, coefficient of friction increased because the adhesive wear mechanism occurred in the initial stage, then formation and destruction of the oxide layer on the surface of the sample tended to a dynamic equilibrium, the surface state of the sample was relatively stable and so did the coefficient of friction. The experiment shows that the main wear mechanism of Al-5%Si-Al2O3 composites includes abrasive wear, adhesive wear and oxidation wear.展开更多
The deformation behaviors of Al2O3/Al composites were investigated by compressive tests conducted at temperature of 300-450 °C and strain rates of 0.001-1.0 s-1 with Gleeble-1500 D thermal simulator system. The r...The deformation behaviors of Al2O3/Al composites were investigated by compressive tests conducted at temperature of 300-450 °C and strain rates of 0.001-1.0 s-1 with Gleeble-1500 D thermal simulator system. The results show that the flow stress increases with increasing strain rate and decreasing temperature. The hyperbolic sine constitutive equation can describe the flow stress behavior of Al2O3/Al composites, and the deformation activation energy and constitutive equations were calculated. The processing maps of Al2O3/Al-2 μm and Al2O3/Al-1 μm composites at strain of 0.6 were obtained and the optimum processing domains are in ranges of 300-330 °C, 0.007-0.03 s-1 and 335-360 °C, 0.015-0.06 s-1 for hot working, respectively. The instability zones of flow behavior can also be recognized by the maps.展开更多
Al2O3/Au nano-laminated composite coatings were prepared by means of magnetron sputtering. The coating was compact and comprised of nano-laminated Al2O3 and Au layers. High temperature cyclic oxidation test was employ...Al2O3/Au nano-laminated composite coatings were prepared by means of magnetron sputtering. The coating was compact and comprised of nano-laminated Al2O3 and Au layers. High temperature cyclic oxidation test was employed to investigate the oxidation resistance of the composite coatings. The results revealed that the applied Al2O3/Au nano-laminated composite coatings improved the oxidation and spallation resistance of the stainless steel substrate significantly. The mechanism accounting for oxidation resistance was related with the suppression of inward oxygen diffusion and selective oxidation of Cr in the substrate. The mechanism accounting for spallation resistance was attributed to the relaxation of thermal stress by the nano-laminated structure.展开更多
Al2O3p-Al composites were synthesized using an in-situ reaction in the 80%Al-20%CuO （mass fraction） system. The effects of the CuO particle size on the synthesis temperature and microstructure of the composites were...Al2O3p-Al composites were synthesized using an in-situ reaction in the 80%Al-20%CuO （mass fraction） system. The effects of the CuO particle size on the synthesis temperature and microstructure of the composites were investigated by various methods. The results indicate that the CuO particle size has a significant effect on the temperature at which the complete reaction in the Al-CuO system occurs：the temperature is 200 ℃ lower in the Al-CuO system containing CuO particles with sizes less than 6μm than that containing CuO particles with sizes less than 100μm. The interfacial bonding between Al2O3 particles and Al is not complete when the temperature is below a critical value. The morphology of the Al2O3 particles varies from ribbon-like shape to near spherical shape when the temperature is above a critical value. These two critical temperatures are affected by the particle size of CuO, and the critical temperature of the sample containing CuO particles with sizes less than 6μm is 100 ℃ lower than that of the sample containing CuO particles with sizes less than 100μm.展开更多
The influence of Mo on the microstructure,bending strength and HV of Ti/Al 2O 3 composite was studied,and the influence mechanism was analyzed.The results indicate that after the addition of Mo,the composite organiz...The influence of Mo on the microstructure,bending strength and HV of Ti/Al 2O 3 composite was studied,and the influence mechanism was analyzed.The results indicate that after the addition of Mo,the composite organization is finer and phases distribution is better-proportioned which make the microstructure denser,the bending strength and HV of composite are also increased to a degree.But the bending strength increases first then decreases with the increasing of Mo content,so the appropriate Mo content for the Ti/Al 2O 3 composite is to be further confirmed.展开更多
UPR/Al2O3 composite particles were synthesized from unsaturated polyester resin(UPR) and nanometer/ultra-fine Al2O3 powders by means of suspension polymerization.The effects of Al2O3 with two different particle diamet...UPR/Al2O3 composite particles were synthesized from unsaturated polyester resin(UPR) and nanometer/ultra-fine Al2O3 powders by means of suspension polymerization.The effects of Al2O3 with two different particle diameters on the density and hardness of the composite particles during the synthesis were studied.The results show UPR/Al2O3 composite particles synthesized by suspension polymerization are spherical,smooth,with a yield of 60%～75%(wt),and the particle diameters are 140～250μm;Al2O3 can effectively improves the density and hardness of the composite particles;when the contet is the same,effect of ultra-fine Al2O3 on the density and hardness of the composite particles is better than that of nanometer Al2O3;When the mass fraction of Al2O3 is 55%,the maximum hardness of ultra-fine Al2O3 composite particles and nanometer Al2O3 composite particles are 39.42HV and 25.66HV respectively.展开更多
Many steel components are needed to be reinforced on their surface to have a high abrasive resistance and corrosion resistance. Based on self-propagating hightemperature synthesis, a process to making Al2O3 composite ...Many steel components are needed to be reinforced on their surface to have a high abrasive resistance and corrosion resistance. Based on self-propagating hightemperature synthesis, a process to making Al2O3 composite coatings on mild steel substrate in atmospheric environment with the help of simple auxiliary facilities was developed successfully. A pre-coated bilayer coating was employed. The effects of Fe content in pre-coated transition layer on phase composition, porosity and interfacial bon ding were studied using scanning electron microscopy (SEM), energy-dispersive spectrum (EDS) and X-ray diffraction (XRD). The thermal shock resistance and abrasive resistance were investigated. When Fe content changes from 0 wt% to 50 wt%, the bond quality at first becomes better and then worse gradually. When Fe content is less 20 wt%, there is a small gap between the transition layer and the substrate;when Fe contents are 30 wt% and 40 wt%, working layer, the transition layer and the substrate bond together well. The working layer is mainly composed of Al2O3, Fe-Cr and Al(Cr)2O3 phases and has a dense structure with porosity of less than 1 %. The coating has a good thermal shock resistance and abrasive resistance. The abrasive resistance of the working layer is about ten times that of the substrate.展开更多
Ti3AlC2/TiC-Al2O3 composite was synthesized by a combustion reaction in TiO2-Al-C system. The effect of the compositions in raw materials on the products was investigated. Ti3AlC2/TiC-Al2O3 composite was obtained at t...Ti3AlC2/TiC-Al2O3 composite was synthesized by a combustion reaction in TiO2-Al-C system. The effect of the compositions in raw materials on the products was investigated. Ti3AlC2/TiC-Al2O3 composite was obtained at the molar ratio of TiO2：Al：C=3.0：5.0～5.1：1.8～2.0. The reaction path for the 3TiO2-5Al- 2C system was proposed. Al3Ti, Ti203, TiO, and 6-Al2O3 are found to be transitional phases. Finally, Ti3AlC2/TiC-Al2O3 composite forms at～900℃ of furnace temperature. The measured Vickers hardness, fracture toughness, and flexural strength of the nearly dense sample from 3TiO2-5Al-2C are 13.3±1.1 GPa, 5.8±0.3 MPa.m^1/2, and 466±39 MPa, respectively.展开更多
Ni-P-nano Al2O3 composite coatings were deposited by electroless plating,and their microstructures were observed by SEM（scanning electron microscope）.The microhardness and the wear resistance of the Ni-P-nano Al2O3 ...Ni-P-nano Al2O3 composite coatings were deposited by electroless plating,and their microstructures were observed by SEM（scanning electron microscope）.The microhardness and the wear resistance of the Ni-P-nano Al2O3 composite coatings were measured using microhardness tester and block-on-ring tribometer,respectively,and the comparison with those of Ni-P coatings or Ni-P-micro Al2O3 coating was given.The influences of aging temperature on their hardness and wear resistance were analyzed.The results showed that the nano Al2O3 particles were distributed uniformly in the Ni-P-Al2O3 coatings.Among three kinds of Ni-P based coatings,the hardness and wear resistance of Ni-P-nano Al2O3 coatings were largest,and the maximum values could be obtained at 400 ℃.This indicated that the precipitation of nano Al2O3 particles would improve the hardness and wear resistance of the Ni-P coatings.展开更多
Two kinds of Cu-Al_2O_3 composites(with and without La) were prepared via mechanical alloying-spark plasma sintering(MA-SPS) method. Microstructure, mechanical properties and electrical resistivity were investigated s...Two kinds of Cu-Al_2O_3 composites(with and without La) were prepared via mechanical alloying-spark plasma sintering(MA-SPS) method. Microstructure, mechanical properties and electrical resistivity were investigated systematically using metallography, scanning electron microscopy, transmission electron microscopy, mechanical and electrical properties testing. The results indicate that an appropriate amount of La can homogenize the distribution of Al_2O_3. As such, yield strength, ultimate tensile strength and elongation of Cu-Al_2O_3-La are greatly increased. Some semi-coherent interface between Cu and Al_2O_3 is found, which means a low interface energy. The grain shape of Cu changes to irregular band with the addition of La. This change results in a density decrease of grain boundary and reduces electrical resistance. Lanthanum may exist in the form of La_2O_3.展开更多
The thermal shock fatigue behaviors of pure hot-pressed alumina and 30 wt.% TiC/Al2O3 composites were studied. The effect of TiC and Al2O3 starting particle size on the mechanical properties of the composites was disc...The thermal shock fatigue behaviors of pure hot-pressed alumina and 30 wt.% TiC/Al2O3 composites were studied. The effect of TiC and Al2O3 starting particle size on the mechanical properties of the composites was discussed. Indentation-quench test was conducted to evaluate the effect of thermal fatigue temperature difference （ΔT） and number of thermal cycles （Ⅳ） on fatigue crack growth （Δa）. The mechanical properties and thermal fatigue resistance of TiC/Al203 composites are remarkably improved by the addition of TiC. The thermal shock fatigue of monolithic alumina and TiC/Al2O3 composites is due to a ＂true＂ cycling effect （thermal fatigue）. Crack deflection and bridging are the predominant reasons for the improvement of thermal shock fatigue resistance of the composites.展开更多
In situ Al2O3 whiskers reinforced Ti-Al intermetallic composites were fabricated at ~1200℃ by reaction sintering of cold-consolidated fillets consisting mainly of Ti, Al, and different additives. The phases and micro...In situ Al2O3 whiskers reinforced Ti-Al intermetallic composites were fabricated at ~1200℃ by reaction sintering of cold-consolidated fillets consisting mainly of Ti, Al, and different additives. The phases and microstructures of the sintered composites were characterized using X-ray diffraction (XRD) and scanning electron microscopy (SEM) coupled with energy dispersive spectroscopy (EDS). The process of synthesis was investigated using differential thermal analysis (DTA). The effects of processing parameters and additives on the microstructures of the composites and the development of whisker were examined. It is found that the morphology of the whisker is strongly influenced by the additives, the exothermal reaction process, and the processing parameters.展开更多
Two-dimensional(2D)Ti3C2Tx MXene is an attractive additive not only used in base oil due to its low friction coefficient,but also used in composites due to its high aspect ratio and rich surface functional groups.So f...Two-dimensional(2D)Ti3C2Tx MXene is an attractive additive not only used in base oil due to its low friction coefficient,but also used in composites due to its high aspect ratio and rich surface functional groups.So far there has been intense research into polymer matrix composites reinforced with Ti3C2Tx,Here we report on the use of 2D Ti3C2Tx to enhance the mechanical and frictional properties of Al matrix composites.Ti3C2Tx/Al composites were designed and prepared by pre s sureless sintering followed by hot extrusion technique.The prepared composites exhibit a homogeneous distribution of Ti3C2Tx.The Vickers hardness and the tensile strength continuously increase with increasing Ti3C2Tx content.A hardness of 0.52 GPa and a tensile strength of 148 MPa were achieved in the 3 wt%Ti3C2Tx/Al composite.The frictional properties of pure Al and the Ti3C2Tx/Al composite were comparably studied under dry sliding.A low friction coefficient of 0.2,twice lower than that of pure Al,was achieved in the 3 wt%Ti3C2Tx/Al composite.Ti3C2Tx acting as a solid lubricant reduces the abrasive wear in the composite,improving the frictional properties of Al matrix composites.展开更多
The influence of Er_2 O_3 addition on the phase evolution and mechanical properties of sintered(1600 ℃,4 h) ZTA(yttria stabilized zirconia toughened alumina)-TiO_2 composites was investigated. The SEM and XRD results...The influence of Er_2 O_3 addition on the phase evolution and mechanical properties of sintered(1600 ℃,4 h) ZTA(yttria stabilized zirconia toughened alumina)-TiO_2 composites was investigated. The SEM and XRD results reveal the formation of a new erbium zirconium oxide,Zr_3 Er_4 O_(12),with a granulate morphology when Er_2 O_3 content is higher than 1 wt%. The grain sizes of both Al_2 O_3 and yttria-stabilized zirconia phases decrease with an increase in the Er_2 O_3 content. The relative density, Vickers hardness and fracture toughness of the composites are found to be strongly dependent on their grain sizes, relative densities and the formation of the Zr_3 Er_4 O_(12) secondary phases. The composite with 5 wt% Er_2 O_3 shows the highest relative density(99.93%), Vickers hardness(1752 HV) and fracture toughness(7.92 MPa·m^(1/2)).展开更多
Ag3PO4 is widely used in the field of photocatalysis because of its unique activity. However, photocorrosion limits its practical application. Therefore, it is very urgent to find a solution to improve the light corro...Ag3PO4 is widely used in the field of photocatalysis because of its unique activity. However, photocorrosion limits its practical application. Therefore, it is very urgent to find a solution to improve the light corrosion resistance of Ag3PO4. Herein, the Z-scheme WO3(H2O)0.333/Ag3PO4 composites are successfully prepared through microwave hydrothermal and simple stirring. The WO3(H2O)0.333/Ag3PO4 composites are characterized by X-ray diffraction, scanning electron microscopy, X-ray photoelectron spectroscopy and UV-Vis spectroscopy. In the degradation of organic pollutants, WO3(H2O)0.333/Ag3PO4 composites exhibit excellent performance under visible light. This is mainly attributed to the synergy of WO3(H2O)0.333 and Ag3PO4. Especially, the photocatalytic activity of 15%WO3(H2O)0.333/Ag3PO4 is the highest, and the methylene blue can be completely degraded in 4 min. In addition, the stability of the composites is also greatly enhanced. After five cycles of testing, the photocatalytic activity of 15%WO3(H2O)0.333/Ag3PO4 is not obviously decreased. However, the degradation efficiency of Ag3PO4 was only 20.2%. This indicates that adding WO3(H2O)0.333 can significantly improve the photoetching resistance of Ag3PO4. Finally, Z-scheme photocatalytic mechanism is investigated.展开更多
基金supported by the National Natural Science Foundation of China(No.52471040)the Natural Science Foundation of Shandong Province(No.ZR2022ME005).
文摘An Al_(2)O_(3)/Al-Cu-Mn composite was fabricated using a combination of ball milling and liquid-solid reaction,with a nominal composition of Al-4Cu-0.5Mn-2.8γ-Al_(2)O_(3).The composite contains reinforcement particles,including nano-sizedθ’and T(Al_(20)Cu_(2)Mn_(3))particles after T6 heat treatment,as well as in-situ synthesized nano-sizedγ-Al_(2)O_(3)particles.Tensile tests of the Al-4Cu-0.5Mn-2.8γ-Al_(2)O_(3)composite and the Al-4Cu-0.5Mn base alloy after T6 treatment were carried out at room temperature and elevated temperatures(200°C,300°C,and 400°C).Compared with the base alloy,the yield strength of the Al-4Cu-0.5Mn-2.8γ-Al_(2)O_(3)composite after T6 treatment increases significantly from 187 MPa to 263 MPa at room temperature.Simultaneously,at elevated temperatures,the yield strength is also enhanced,with a yield strength of 52 MPa at 400°C for this composite.The in-situ fabricatedγ-Al_(2)O_(3)particles,mainly distributed along the grain boundaries,are supposed to play the main strengthening role,especially at high temperatures.This work acts as a reference for designing composites for high-temperature applications.
基金Projects(51101096,51002093)supported by the National Natural Science Foundation of ChinaProject(1052nm05000)supported by Special Foundation of the Shanghai Science and Technology Commission for Nano-Materials ResearchProject(J51042)supported by Leading Academic Discipline Project of the Shanghai Education Commission,China
文摘A Y2O3 particle enhanced Ni/TiC composite coating was fabricated in-situ on a TC4 Ti alloy by laser surface cladding.The phase component,microstructure,composition distribution and properties of the composite layer were investigated.The composite layer has graded microstructures and compositions,due to the fast melting followed by rapid solidification and cooling during laser cladding.The TiC powders are completely dissolved into the melted layer during melting and segregated as fine dendrites when solidified.The size of TiC dendrites decreases with increasing depth.Y2O3 fine particles distribute in the whole clad layer.The Y2O3 particle enhanced Ni/TiC composite layer has a quite uniform hardness along depth with a maximum value of HV1380,which is 4 times higher than the initial hardness.The wear resistance of the Ti alloy is significantly improved after laser cladding due to the high hardness of the composite coating.
基金National Natural Science Foundation of China (50432020)Henan Innovation Project for University Prominent Re- search Talents (2007KYCX008)+3 种基金Henan Education Department Science and Technology Project (2007430004)Henan Plan Project for College Youth Backbone TeacherHenan University of Science and Technology Major Pre-research Foundation (2005ZD003)Henan University of Science and Technology Personnel Scientific Research Foundation (of023)
文摘Two Al2O3/Cu composites containing 0.24 wt.% Al2O3 and 0.60 wt.% Al2O3 separately are prepared by internal oxidation. Effects of sliding speed and pressure on the frictional characteristics of the composites and copper against brass are investigated and compared. The changes in morphology of the sliding surface and subsurface are examined with scanning electron microscope （SEM） and energy dispersive X-ray spectrum （EDS）. The results show that the wear resistance of the Al2O3/Cu composites is superior to that of copper under the same conditions, Under a given electrical current, the wear rate of Al2O3/Cu composites decreases as the Al2O3-content increases, However, the wear rates of the Al2O3/Cu composites and copper increase as the sliding speed and pressure increase under dry sliding condition. The main wear mechanisms for Al2O3/Cu composites are of abrasion and adhesion; for copper, it is adhesion, although wear by oxidation and electrical erosion can also be observed as the speed and pressure rise.
文摘The NiCrBSi-Y2O3 composite coatings were prepared on the surface of 45 carbon steel by plasma spray, the microstructure and tribological properties of the coatings were investigated. The results show that the NiCrBSi-Y2O3 composite coatings are mainly composed of γ-Ni, CrB, Cr7C3 and Y2O3. With addition of Y2O3, hard phases such as CrB, Cr7C3 emerge in composite coating, and the density of the composite coatings also increases. The NiCrBSi-0.5Y2O3 composite coating presents excellent tribological properties. Its friction coefficient is 0.175, which is about 37% of that of the pure NiCrBSi coating. The mass wear loss is 1.2 mg, which is reduced by 43% compared with the pure NiCrBSi coating. When the loads are 6-10 N, the NiCrBSi-0.5Y2O3 composite coating suffers from slight wear and the wear mechanisms are mainly adhesive wear accompany with slight micro-cutting wear and micro-fracture wear. As the load increases to 12 N, the wear mechanisms are adhesive wear and severe micro-cutting wear.
基金Project(51272141)supported by the National Natural Science Foundation of ChinaProject(ts20110828)supported by the Taishan Scholars Project of Shandong Province,ChinaProject(2015AA034404)supported by the Ministry of Science and Technology of China
文摘（TiB2＋Al2O3）/NiAl composites were synthesized by self-propagation high-temperature synthesis, and their phase compositions, microstructures and evolution modes were studied. The microstructures and shapes vary with the TiB2＋Al2O3 content in the NiAl matrix. TiB2 particles take a great variety of elementary shapes such as white bars, plates, herringbones, regular cubes and cuboids. These results outline a strategy of self-assembly processes in real time to build diversified microstructures. Some TiB2 grains in sizes of 2-5μm are embeded in Al2O3 clusters, while a small number of TiB2 particles disperse in the NiAl matrix. It is believed that the higher the TiB2＋Al2O3 content is, the more the regular shapes and homogeneous distributions of TiB2 and Al2O3 will be present in the NiAl matrix.
基金Project(51201143)supported by the National Natural Science Foundation of ChinaProject(SWJTU12BR004)supported by the Fundamental Research Funds for the Central Universities,China
文摘Al-5%Si-AI2O3 composites were prepared by powder metallurgy and in-situ reactive synthesis technology. Friction and wear properties of Al-5%Si-Al2O3 composites were studied using an M-2000 wear tester. The effects of load, sliding speed and long time continuous friction on friction and wear properties of Al-5%Si-Al2O3 composites were investigated, respectively. Wear surface and wear mechanism of Al-5%Si-Al2O3 composites were studied by Quanta 200 FE-SEM. Results showed that with load increasing, wear loss and coefficient of friction increased. With sliding speed going up, the surface temperature of sample made the rate of the producing of oxidation layer increase, while wear loss and coefficient of friction decreased. With the sliding distance increasing, coefficient of friction increased because the adhesive wear mechanism occurred in the initial stage, then formation and destruction of the oxide layer on the surface of the sample tended to a dynamic equilibrium, the surface state of the sample was relatively stable and so did the coefficient of friction. The experiment shows that the main wear mechanism of Al-5%Si-Al2O3 composites includes abrasive wear, adhesive wear and oxidation wear.
基金Project(2012AA030311)supported by the National High-tech Research and Development Program of ChinaProject(2010BB4074)supported by the Natural Science Foundation of Chongqing Municipality,ChinaProject(2010ZD-02)supported by the State Key Laboratory for Advanced Metals and Materials,China
文摘The deformation behaviors of Al2O3/Al composites were investigated by compressive tests conducted at temperature of 300-450 °C and strain rates of 0.001-1.0 s-1 with Gleeble-1500 D thermal simulator system. The results show that the flow stress increases with increasing strain rate and decreasing temperature. The hyperbolic sine constitutive equation can describe the flow stress behavior of Al2O3/Al composites, and the deformation activation energy and constitutive equations were calculated. The processing maps of Al2O3/Al-2 μm and Al2O3/Al-1 μm composites at strain of 0.6 were obtained and the optimum processing domains are in ranges of 300-330 °C, 0.007-0.03 s-1 and 335-360 °C, 0.015-0.06 s-1 for hot working, respectively. The instability zones of flow behavior can also be recognized by the maps.
基金Project (50771021) supported by the National Natural Science Foundation of China
文摘Al2O3/Au nano-laminated composite coatings were prepared by means of magnetron sputtering. The coating was compact and comprised of nano-laminated Al2O3 and Au layers. High temperature cyclic oxidation test was employed to investigate the oxidation resistance of the composite coatings. The results revealed that the applied Al2O3/Au nano-laminated composite coatings improved the oxidation and spallation resistance of the stainless steel substrate significantly. The mechanism accounting for oxidation resistance was related with the suppression of inward oxygen diffusion and selective oxidation of Cr in the substrate. The mechanism accounting for spallation resistance was attributed to the relaxation of thermal stress by the nano-laminated structure.
基金Project(2012MS0801)supported by the Natural Science Foundation of Inner Mongolia,China
文摘Al2O3p-Al composites were synthesized using an in-situ reaction in the 80%Al-20%CuO （mass fraction） system. The effects of the CuO particle size on the synthesis temperature and microstructure of the composites were investigated by various methods. The results indicate that the CuO particle size has a significant effect on the temperature at which the complete reaction in the Al-CuO system occurs：the temperature is 200 ℃ lower in the Al-CuO system containing CuO particles with sizes less than 6μm than that containing CuO particles with sizes less than 100μm. The interfacial bonding between Al2O3 particles and Al is not complete when the temperature is below a critical value. The morphology of the Al2O3 particles varies from ribbon-like shape to near spherical shape when the temperature is above a critical value. These two critical temperatures are affected by the particle size of CuO, and the critical temperature of the sample containing CuO particles with sizes less than 6μm is 100 ℃ lower than that of the sample containing CuO particles with sizes less than 100μm.
文摘The influence of Mo on the microstructure,bending strength and HV of Ti/Al 2O 3 composite was studied,and the influence mechanism was analyzed.The results indicate that after the addition of Mo,the composite organization is finer and phases distribution is better-proportioned which make the microstructure denser,the bending strength and HV of composite are also increased to a degree.But the bending strength increases first then decreases with the increasing of Mo content,so the appropriate Mo content for the Ti/Al 2O 3 composite is to be further confirmed.
文摘UPR/Al2O3 composite particles were synthesized from unsaturated polyester resin(UPR) and nanometer/ultra-fine Al2O3 powders by means of suspension polymerization.The effects of Al2O3 with two different particle diameters on the density and hardness of the composite particles during the synthesis were studied.The results show UPR/Al2O3 composite particles synthesized by suspension polymerization are spherical,smooth,with a yield of 60%～75%(wt),and the particle diameters are 140～250μm;Al2O3 can effectively improves the density and hardness of the composite particles;when the contet is the same,effect of ultra-fine Al2O3 on the density and hardness of the composite particles is better than that of nanometer Al2O3;When the mass fraction of Al2O3 is 55%,the maximum hardness of ultra-fine Al2O3 composite particles and nanometer Al2O3 composite particles are 39.42HV and 25.66HV respectively.
基金financially supported by the National Natural Science Foundation of China (No.51379070)the Fundamental Research Funds for the Central Universities (No. 2017B40314)
文摘Many steel components are needed to be reinforced on their surface to have a high abrasive resistance and corrosion resistance. Based on self-propagating hightemperature synthesis, a process to making Al2O3 composite coatings on mild steel substrate in atmospheric environment with the help of simple auxiliary facilities was developed successfully. A pre-coated bilayer coating was employed. The effects of Fe content in pre-coated transition layer on phase composition, porosity and interfacial bon ding were studied using scanning electron microscopy (SEM), energy-dispersive spectrum (EDS) and X-ray diffraction (XRD). The thermal shock resistance and abrasive resistance were investigated. When Fe content changes from 0 wt% to 50 wt%, the bond quality at first becomes better and then worse gradually. When Fe content is less 20 wt%, there is a small gap between the transition layer and the substrate;when Fe contents are 30 wt% and 40 wt%, working layer, the transition layer and the substrate bond together well. The working layer is mainly composed of Al2O3, Fe-Cr and Al(Cr)2O3 phases and has a dense structure with porosity of less than 1 %. The coating has a good thermal shock resistance and abrasive resistance. The abrasive resistance of the working layer is about ten times that of the substrate.
文摘Ti3AlC2/TiC-Al2O3 composite was synthesized by a combustion reaction in TiO2-Al-C system. The effect of the compositions in raw materials on the products was investigated. Ti3AlC2/TiC-Al2O3 composite was obtained at the molar ratio of TiO2：Al：C=3.0：5.0～5.1：1.8～2.0. The reaction path for the 3TiO2-5Al- 2C system was proposed. Al3Ti, Ti203, TiO, and 6-Al2O3 are found to be transitional phases. Finally, Ti3AlC2/TiC-Al2O3 composite forms at～900℃ of furnace temperature. The measured Vickers hardness, fracture toughness, and flexural strength of the nearly dense sample from 3TiO2-5Al-2C are 13.3±1.1 GPa, 5.8±0.3 MPa.m^1/2, and 466±39 MPa, respectively.
基金Item Sponsored by Jiangsu Natural Science Foundation of China(04KJB430013)Jiangsu Key Laboratory of Friction Wear Opening Foundation
文摘Ni-P-nano Al2O3 composite coatings were deposited by electroless plating,and their microstructures were observed by SEM（scanning electron microscope）.The microhardness and the wear resistance of the Ni-P-nano Al2O3 composite coatings were measured using microhardness tester and block-on-ring tribometer,respectively,and the comparison with those of Ni-P coatings or Ni-P-micro Al2O3 coating was given.The influences of aging temperature on their hardness and wear resistance were analyzed.The results showed that the nano Al2O3 particles were distributed uniformly in the Ni-P-Al2O3 coatings.Among three kinds of Ni-P based coatings,the hardness and wear resistance of Ni-P-nano Al2O3 coatings were largest,and the maximum values could be obtained at 400 ℃.This indicated that the precipitation of nano Al2O3 particles would improve the hardness and wear resistance of the Ni-P coatings.
基金Project supported by the National Natural Science Foundation of China(51471023,51571021,11775018)the Beijing Municipal Natural Science Foundation(2152031)
文摘Two kinds of Cu-Al_2O_3 composites(with and without La) were prepared via mechanical alloying-spark plasma sintering(MA-SPS) method. Microstructure, mechanical properties and electrical resistivity were investigated systematically using metallography, scanning electron microscopy, transmission electron microscopy, mechanical and electrical properties testing. The results indicate that an appropriate amount of La can homogenize the distribution of Al_2O_3. As such, yield strength, ultimate tensile strength and elongation of Cu-Al_2O_3-La are greatly increased. Some semi-coherent interface between Cu and Al_2O_3 is found, which means a low interface energy. The grain shape of Cu changes to irregular band with the addition of La. This change results in a density decrease of grain boundary and reduces electrical resistance. Lanthanum may exist in the form of La_2O_3.
文摘The thermal shock fatigue behaviors of pure hot-pressed alumina and 30 wt.% TiC/Al2O3 composites were studied. The effect of TiC and Al2O3 starting particle size on the mechanical properties of the composites was discussed. Indentation-quench test was conducted to evaluate the effect of thermal fatigue temperature difference （ΔT） and number of thermal cycles （Ⅳ） on fatigue crack growth （Δa）. The mechanical properties and thermal fatigue resistance of TiC/Al203 composites are remarkably improved by the addition of TiC. The thermal shock fatigue of monolithic alumina and TiC/Al2O3 composites is due to a ＂true＂ cycling effect （thermal fatigue）. Crack deflection and bridging are the predominant reasons for the improvement of thermal shock fatigue resistance of the composites.
基金This work was supported by the National Natural Science Foundation of China (No. 50432010, 50372037).
文摘In situ Al2O3 whiskers reinforced Ti-Al intermetallic composites were fabricated at ~1200℃ by reaction sintering of cold-consolidated fillets consisting mainly of Ti, Al, and different additives. The phases and microstructures of the sintered composites were characterized using X-ray diffraction (XRD) and scanning electron microscopy (SEM) coupled with energy dispersive spectroscopy (EDS). The process of synthesis was investigated using differential thermal analysis (DTA). The effects of processing parameters and additives on the microstructures of the composites and the development of whisker were examined. It is found that the morphology of the whisker is strongly influenced by the additives, the exothermal reaction process, and the processing parameters.
基金supported by the National Natural Science Foundation of China(No.51772020)Beijing Natural Science Foundation(No.2182058)+1 种基金Beijing Government Funds for the Constructive Project of Central UniversitiesEquipment Development Department of the National Military Commission Foundation of China(No.JZX7Y20190262063601)。
文摘Two-dimensional(2D)Ti3C2Tx MXene is an attractive additive not only used in base oil due to its low friction coefficient,but also used in composites due to its high aspect ratio and rich surface functional groups.So far there has been intense research into polymer matrix composites reinforced with Ti3C2Tx,Here we report on the use of 2D Ti3C2Tx to enhance the mechanical and frictional properties of Al matrix composites.Ti3C2Tx/Al composites were designed and prepared by pre s sureless sintering followed by hot extrusion technique.The prepared composites exhibit a homogeneous distribution of Ti3C2Tx.The Vickers hardness and the tensile strength continuously increase with increasing Ti3C2Tx content.A hardness of 0.52 GPa and a tensile strength of 148 MPa were achieved in the 3 wt%Ti3C2Tx/Al composite.The frictional properties of pure Al and the Ti3C2Tx/Al composite were comparably studied under dry sliding.A low friction coefficient of 0.2,twice lower than that of pure Al,was achieved in the 3 wt%Ti3C2Tx/Al composite.Ti3C2Tx acting as a solid lubricant reduces the abrasive wear in the composite,improving the frictional properties of Al matrix composites.
基金Project supported by National Natural Science Foundation of China(51571103,51501079)China Postdoctoral Science Foundation(2017M623319XB,2018T110999)Yunnan Provincial Department of Education Science Research Fund Project(2018JS033)
文摘The influence of Er_2 O_3 addition on the phase evolution and mechanical properties of sintered(1600 ℃,4 h) ZTA(yttria stabilized zirconia toughened alumina)-TiO_2 composites was investigated. The SEM and XRD results reveal the formation of a new erbium zirconium oxide,Zr_3 Er_4 O_(12),with a granulate morphology when Er_2 O_3 content is higher than 1 wt%. The grain sizes of both Al_2 O_3 and yttria-stabilized zirconia phases decrease with an increase in the Er_2 O_3 content. The relative density, Vickers hardness and fracture toughness of the composites are found to be strongly dependent on their grain sizes, relative densities and the formation of the Zr_3 Er_4 O_(12) secondary phases. The composite with 5 wt% Er_2 O_3 shows the highest relative density(99.93%), Vickers hardness(1752 HV) and fracture toughness(7.92 MPa·m^(1/2)).
基金supported by the National Natural Science Foundation of China(51572103 and 51502106)the Distinguished Young Scholar of Anhui Province(1808085J14)+2 种基金the Foundation for Young Talents in College of Anhui Province(gxyqZD2017051)the Key Foundation of Educational Commission of Anhui Province(KJ2016SD53)the Innovation Team of Design and Application of Advanced Energetic Materials(KJ2015TD003)~~
文摘Ag3PO4 is widely used in the field of photocatalysis because of its unique activity. However, photocorrosion limits its practical application. Therefore, it is very urgent to find a solution to improve the light corrosion resistance of Ag3PO4. Herein, the Z-scheme WO3(H2O)0.333/Ag3PO4 composites are successfully prepared through microwave hydrothermal and simple stirring. The WO3(H2O)0.333/Ag3PO4 composites are characterized by X-ray diffraction, scanning electron microscopy, X-ray photoelectron spectroscopy and UV-Vis spectroscopy. In the degradation of organic pollutants, WO3(H2O)0.333/Ag3PO4 composites exhibit excellent performance under visible light. This is mainly attributed to the synergy of WO3(H2O)0.333 and Ag3PO4. Especially, the photocatalytic activity of 15%WO3(H2O)0.333/Ag3PO4 is the highest, and the methylene blue can be completely degraded in 4 min. In addition, the stability of the composites is also greatly enhanced. After five cycles of testing, the photocatalytic activity of 15%WO3(H2O)0.333/Ag3PO4 is not obviously decreased. However, the degradation efficiency of Ag3PO4 was only 20.2%. This indicates that adding WO3(H2O)0.333 can significantly improve the photoetching resistance of Ag3PO4. Finally, Z-scheme photocatalytic mechanism is investigated.