A titania support with a large surface area was developed, which has a BET surface area of 380.5 m^2/g, four times that of a traditional titania support. The support was ultrasonically impregnated with 5 wt% vanadia. ...A titania support with a large surface area was developed, which has a BET surface area of 380.5 m^2/g, four times that of a traditional titania support. The support was ultrasonically impregnated with 5 wt% vanadia. A special heat treatment was used in the calcination to maintain the large surface area and high dispersion of vanadium species. This catalyst was compared to a common V2O5-TiO2 catalyst with the same vanadia loading prepared by a traditional method. The new catalyst has a surface area of 117.7 m^2/g, which was 38% higher than the traditional V2O5-TiO2 catalyst. The selective catalytic reduction（SCR） performance demonstrated that the new catalyst had a wider temperature window and better N2 selectivity compared to the traditional one. The NO conversion was 80% from 200 to 450 °C. The temperature window was 100 °C wider than the traditional catalyst. Raman spectra indicated that the vanadium species formed more V-O-V linkages on the catalyst prepared by the traditional method. The amount of V-O-Ti and V=O was larger for the new catalyst. Temperature programmed desorption of NH3, temperature programmed reduction by H2 and X-ray photoelectron spectroscopy results showed that its redox ability and total acidity were enhanced. The results are helpful for developing a more efficient SCR catalyst for the removal of NOx in flue gases.展开更多
Vanadium oxide cathode materials with stable crystal structure and fast Zn^(2+) storage capabilities are extremely important to achieving outstanding electrochemical performance in aqueous zinc‐ion batteries.In this ...Vanadium oxide cathode materials with stable crystal structure and fast Zn^(2+) storage capabilities are extremely important to achieving outstanding electrochemical performance in aqueous zinc‐ion batteries.In this work,a one‐step hydrothermal method was used to manipulate the bimetallic ion intercalation into the interlayer of vanadium oxide.The pre‐intercalated Cu ions act as pillars to pin the vanadium oxide(V‐O)layers,establishing stabilized two‐dimensional channels for fast Zn^(2+) diffusion.The occupation of Mn ions between V‐O interlayer further expands the layer spacing and increases the concentration of oxygen defects(Od),which boosts the Zn^(2+) diffusion kinetics.As a result,as‐prepared Cu_(0.17)Mn_(0.03)V_(2)O_(5−□)·2.16H_(2)O cathode shows outstanding Zn‐storage capabilities under room‐and lowtemperature environments(e.g.,440.3 mAh g^(−1) at room temperature and 294.3 mAh g^(−1)at−60°C).Importantly,it shows a long cycling life and high capacity retention of 93.4%over 2500 cycles at 2 A g^(−1) at−60°C.Furthermore,the reversible intercalation chemistry mechanisms during discharging/charging processes were revealed via operando X‐ray powder diffraction and ex situ Raman characterizations.The strategy of a couple of 3d transition metal doping provides a solution for the development of superior room‐/lowtemperature vanadium‐based cathode materials.展开更多
Bi12O17Br2and Bi4O5Br2visible‐light driven photocatalysts,were respectively fabricated by hydrothermal and room‐temperature deposition methods with the use of BiBr3and NaOH as precursors.Both Bi12O17Br2and Bi4O5Br2w...Bi12O17Br2and Bi4O5Br2visible‐light driven photocatalysts,were respectively fabricated by hydrothermal and room‐temperature deposition methods with the use of BiBr3and NaOH as precursors.Both Bi12O17Br2and Bi4O5Br2were composed of irregular nanosheets.The Bi4O5Br2nanosheets exhibited high and stable visible‐light photocatalytic efficiency for ppb‐level NO removal.The performance of Bi4O5Br2was markedly higher than that of the Bi12O17Br2nanosheets.The hydroxyl radical(?OH)was determined to be the main reactive oxygen species for the photo‐degradation processes of both Bi12O17Br2and Bi4O5Br2.However,in situ diffuse reflectance infrared Fourier transform spectroscopy analysis revealed that Bi12O17Br2and Bi4O5Br2featured different conversion pathways for visible light driven photocatalytic NO oxidation.The excellent photocatalytic activity of Bi4O5Br2resulted from a high surface area and large pore volumes,which facilitated the transport of reactants and intermediate products,and provided more active sites for photochemical reaction.Furthermore,the Bi4O5Br2nanosheets produced more?OH and presented stronger valence band holeoxidation.In addition,the oxygen atoms of NO could insert into oxygen‐vacancies of Bi4O5Br2,whichprovided more active sites for the reaction.This work gives insight into the photocatalytic pollutant‐degradation mechanism of bismuth oxyhalide.展开更多
基金supported by the National Natural Science Foundation of China(21325731,21221004)the National High Technology Research and Development Program of China(863 Program)the State Environmental Protection Key Laboratory of Sources and Control of Air Pollution Complex
文摘A titania support with a large surface area was developed, which has a BET surface area of 380.5 m^2/g, four times that of a traditional titania support. The support was ultrasonically impregnated with 5 wt% vanadia. A special heat treatment was used in the calcination to maintain the large surface area and high dispersion of vanadium species. This catalyst was compared to a common V2O5-TiO2 catalyst with the same vanadia loading prepared by a traditional method. The new catalyst has a surface area of 117.7 m^2/g, which was 38% higher than the traditional V2O5-TiO2 catalyst. The selective catalytic reduction（SCR） performance demonstrated that the new catalyst had a wider temperature window and better N2 selectivity compared to the traditional one. The NO conversion was 80% from 200 to 450 °C. The temperature window was 100 °C wider than the traditional catalyst. Raman spectra indicated that the vanadium species formed more V-O-V linkages on the catalyst prepared by the traditional method. The amount of V-O-Ti and V=O was larger for the new catalyst. Temperature programmed desorption of NH3, temperature programmed reduction by H2 and X-ray photoelectron spectroscopy results showed that its redox ability and total acidity were enhanced. The results are helpful for developing a more efficient SCR catalyst for the removal of NOx in flue gases.
基金National Natural Science Foundation of China,Grant/Award Numbers:52372188,51902090,51922008,520721142023 Introduction of studying abroad talent program,the China Postdoctoral Science Foundation,Grant/Award Number:2019 M652546+3 种基金Xinxiang Major Science and Technology Projects,Grant/Award Number:21ZD001Henan Province Postdoctoral Start‐Up Foundation,Grant/Award Number:1901017Henan Center for Outstanding Overseas Scientists,Grant/Award Number:GZS2018003Overseas Expertise Introduction Project for Discipline Innovation,Grant/Award Number:D17007。
文摘Vanadium oxide cathode materials with stable crystal structure and fast Zn^(2+) storage capabilities are extremely important to achieving outstanding electrochemical performance in aqueous zinc‐ion batteries.In this work,a one‐step hydrothermal method was used to manipulate the bimetallic ion intercalation into the interlayer of vanadium oxide.The pre‐intercalated Cu ions act as pillars to pin the vanadium oxide(V‐O)layers,establishing stabilized two‐dimensional channels for fast Zn^(2+) diffusion.The occupation of Mn ions between V‐O interlayer further expands the layer spacing and increases the concentration of oxygen defects(Od),which boosts the Zn^(2+) diffusion kinetics.As a result,as‐prepared Cu_(0.17)Mn_(0.03)V_(2)O_(5−□)·2.16H_(2)O cathode shows outstanding Zn‐storage capabilities under room‐and lowtemperature environments(e.g.,440.3 mAh g^(−1) at room temperature and 294.3 mAh g^(−1)at−60°C).Importantly,it shows a long cycling life and high capacity retention of 93.4%over 2500 cycles at 2 A g^(−1) at−60°C.Furthermore,the reversible intercalation chemistry mechanisms during discharging/charging processes were revealed via operando X‐ray powder diffraction and ex situ Raman characterizations.The strategy of a couple of 3d transition metal doping provides a solution for the development of superior room‐/lowtemperature vanadium‐based cathode materials.
基金supported by the National Natural Science Foundation of China(51708078,21576034)Chongqing Postdoctoral Science Foundation funded project(Xm2016027)the Innovative Research Team of Chongqing(CXTDG201602014,CXTDX201601016)~~
文摘Bi12O17Br2and Bi4O5Br2visible‐light driven photocatalysts,were respectively fabricated by hydrothermal and room‐temperature deposition methods with the use of BiBr3and NaOH as precursors.Both Bi12O17Br2and Bi4O5Br2were composed of irregular nanosheets.The Bi4O5Br2nanosheets exhibited high and stable visible‐light photocatalytic efficiency for ppb‐level NO removal.The performance of Bi4O5Br2was markedly higher than that of the Bi12O17Br2nanosheets.The hydroxyl radical(?OH)was determined to be the main reactive oxygen species for the photo‐degradation processes of both Bi12O17Br2and Bi4O5Br2.However,in situ diffuse reflectance infrared Fourier transform spectroscopy analysis revealed that Bi12O17Br2and Bi4O5Br2featured different conversion pathways for visible light driven photocatalytic NO oxidation.The excellent photocatalytic activity of Bi4O5Br2resulted from a high surface area and large pore volumes,which facilitated the transport of reactants and intermediate products,and provided more active sites for photochemical reaction.Furthermore,the Bi4O5Br2nanosheets produced more?OH and presented stronger valence band holeoxidation.In addition,the oxygen atoms of NO could insert into oxygen‐vacancies of Bi4O5Br2,whichprovided more active sites for the reaction.This work gives insight into the photocatalytic pollutant‐degradation mechanism of bismuth oxyhalide.