tricalcium phosphate(α TCP)/tetracalcium phosphate(TTCP) composite bone cement had good hydration characteristic.In our system,α TCP/TTCP powder mixture was mixed with water at a powder/liquid (P/L) ratio of 1.50g...tricalcium phosphate(α TCP)/tetracalcium phosphate(TTCP) composite bone cement had good hydration characteristic.In our system,α TCP/TTCP powder mixture was mixed with water at a powder/liquid (P/L) ratio of 1.50g·mL -1 .The setting time could be adjusted,the maximum compressive strength was 45.36MPa,and the hydration product was hydroxyapatite (HAP).In vitro biological simulated experiments indicate that α TCP/TTCP bone cement has α certain dissolubility.The hardened product is mainly HAP after soaking in simulated body fluid (SBF) for 10 weeks.The results of in vitro test and animal experiments and SEM analyses show that no local or general toxicity response,no muscle stimulation,no haemolysis,no cruor,no inflammatory reaction and no exclusion response are caused by α TCP/TTCP cement, which can be contributed to bone tissue spreading and impinging.α TCP/TTCP cement hydrated and hardened continually in vivo.The materials fused with host bone together with implanting time prolonging.Therefore,it is believed that α TCP/TTCP composite bone cement has a high biocompatibility and bioactivity,a certain biodegradation and good osteogenesis as well.展开更多
The calcium phosphate cement (α-TCP/TTCP) was reinforced with oxidation-t reated carbon fibers. The effect of aspect ratio and content of carbon fiber on the compression strength and bending strength of the hardened ...The calcium phosphate cement (α-TCP/TTCP) was reinforced with oxidation-t reated carbon fibers. The effect of aspect ratio and content of carbon fiber on the compression strength and bending strength of the hardened body was discussed . The results show that the reinforcing effect is optimal as the aspect ratio is 375 and the additive amount is 0.3%(mass fraction). Under this condition,the c ompressive strength is increased by 55% (maximum 63.46 MPa),and the bending st rength is nearly increased by 100% (maximum 11.95 MPa),respectively. However,if the additive quantity and aspect ratio are too high,the effect of the carbon fibers is limited because it can not be dispersed uniformly in the hardened bod y. The biological evaluation indicates that the calcium phosphate cement reinfor ced by carbon fibers has good biocompatibility.展开更多
文摘tricalcium phosphate(α TCP)/tetracalcium phosphate(TTCP) composite bone cement had good hydration characteristic.In our system,α TCP/TTCP powder mixture was mixed with water at a powder/liquid (P/L) ratio of 1.50g·mL -1 .The setting time could be adjusted,the maximum compressive strength was 45.36MPa,and the hydration product was hydroxyapatite (HAP).In vitro biological simulated experiments indicate that α TCP/TTCP bone cement has α certain dissolubility.The hardened product is mainly HAP after soaking in simulated body fluid (SBF) for 10 weeks.The results of in vitro test and animal experiments and SEM analyses show that no local or general toxicity response,no muscle stimulation,no haemolysis,no cruor,no inflammatory reaction and no exclusion response are caused by α TCP/TTCP cement, which can be contributed to bone tissue spreading and impinging.α TCP/TTCP cement hydrated and hardened continually in vivo.The materials fused with host bone together with implanting time prolonging.Therefore,it is believed that α TCP/TTCP composite bone cement has a high biocompatibility and bioactivity,a certain biodegradation and good osteogenesis as well.
文摘The calcium phosphate cement (α-TCP/TTCP) was reinforced with oxidation-t reated carbon fibers. The effect of aspect ratio and content of carbon fiber on the compression strength and bending strength of the hardened body was discussed . The results show that the reinforcing effect is optimal as the aspect ratio is 375 and the additive amount is 0.3%(mass fraction). Under this condition,the c ompressive strength is increased by 55% (maximum 63.46 MPa),and the bending st rength is nearly increased by 100% (maximum 11.95 MPa),respectively. However,if the additive quantity and aspect ratio are too high,the effect of the carbon fibers is limited because it can not be dispersed uniformly in the hardened bod y. The biological evaluation indicates that the calcium phosphate cement reinfor ced by carbon fibers has good biocompatibility.