TS-2 microspheres,consisting of intergrown primary nanocrystals,was prepared by controlling the synthetic parameters.The effects of the amount of quaternary ammonium cations as structure-directing agent,H2O/Si ratio,t...TS-2 microspheres,consisting of intergrown primary nanocrystals,was prepared by controlling the synthetic parameters.The effects of the amount of quaternary ammonium cations as structure-directing agent,H2O/Si ratio,the presence of alcohol and the temperature were carefully investigated on the crystallization process.The high alkalinity was proved to be highly important for the preservation of the microsphere morphology initially formed,due to the unique intergrown stacking style.An alkali treatment with the aqueous solution of structure-directing agent,organic amine and ammonium salt and subsequent Na+ion-exchange were performed to enhance the catalytic activity of TS-2 microsphere in the cyclohexanone ammoximation reactions,with both the conversion and selectivity higher than 99%.In the continuous reaction,the TS-2 microspheres exhibited to be durable catalyst with potential application in industrial ammoximation processes.展开更多
The propylene epoxidation over TS-1/SiO2 catalyst hydrothermally treated was investigated. It was found by EPR characterization that two types of Ti (IV)-superoxide radicals, A (gz=2.0271; gy=2.0074; gx=2.0010) and ...The propylene epoxidation over TS-1/SiO2 catalyst hydrothermally treated was investigated. It was found by EPR characterization that two types of Ti (IV)-superoxide radicals, A (gz=2.0271; gy=2.0074; gx=2.0010) and B (gz=2.0247; gy= 2.0074; gx= 2.0010), were observed for TS-1/SiO2. The superoxo species A converted to B after TS-1/SiO2 catalyst was hydrothermally treated. The results show that over TS-1/SiO2 catalyst hydrothermally treated at 170℃, about 95% conversion of H2O2 with above 94% PO selectivity is obtained during continuous running for 300 h under the conditions of reaction temperature 45℃, 0.5 h-1WHSV of propylene.展开更多
文摘TS-2 microspheres,consisting of intergrown primary nanocrystals,was prepared by controlling the synthetic parameters.The effects of the amount of quaternary ammonium cations as structure-directing agent,H2O/Si ratio,the presence of alcohol and the temperature were carefully investigated on the crystallization process.The high alkalinity was proved to be highly important for the preservation of the microsphere morphology initially formed,due to the unique intergrown stacking style.An alkali treatment with the aqueous solution of structure-directing agent,organic amine and ammonium salt and subsequent Na+ion-exchange were performed to enhance the catalytic activity of TS-2 microsphere in the cyclohexanone ammoximation reactions,with both the conversion and selectivity higher than 99%.In the continuous reaction,the TS-2 microspheres exhibited to be durable catalyst with potential application in industrial ammoximation processes.
基金Supported by the National Key Basic Research Project of China(G2000048009)the Doctorate Foundation of Liaoning Province(2001102085)
文摘The propylene epoxidation over TS-1/SiO2 catalyst hydrothermally treated was investigated. It was found by EPR characterization that two types of Ti (IV)-superoxide radicals, A (gz=2.0271; gy=2.0074; gx=2.0010) and B (gz=2.0247; gy= 2.0074; gx= 2.0010), were observed for TS-1/SiO2. The superoxo species A converted to B after TS-1/SiO2 catalyst was hydrothermally treated. The results show that over TS-1/SiO2 catalyst hydrothermally treated at 170℃, about 95% conversion of H2O2 with above 94% PO selectivity is obtained during continuous running for 300 h under the conditions of reaction temperature 45℃, 0.5 h-1WHSV of propylene.