Carbon fiber reinforced aluminum matrix （Cf/Al） composite has many excellent properties, and it has received more and more attention. Two-dimensional （2D） Cf/Al composites were fabricated by vacuum and pressure in...Carbon fiber reinforced aluminum matrix （Cf/Al） composite has many excellent properties, and it has received more and more attention. Two-dimensional （2D） Cf/Al composites were fabricated by vacuum and pressure infiltration, which was an integrated technique and could provide high vacuum and high infiltration pressure. The effect of specific pressure on the infiltration quality of the obtained composites was comparatively evaluated through microstructure observation. The experimental results show that satisfied Cf/Al composites could be fabricated at the specific pressure of 75 MPa. In this case, the preform was infiltrated much more completely by aluminum alloy liquid, and the residual porosity was seldom found. It is found that the ultimate tensile strength of the obtained Cf/Al composite reached maximum at the specific pressure of 75 MPa, which was improved by 138.9% compared with that of matrix alloy.展开更多
The plane strain asymmetrical rolling was analyzed using slab method. The contact arc was replaced by parabola, and the constant surface friction status was adopted during the analysis. The deformation area was divide...The plane strain asymmetrical rolling was analyzed using slab method. The contact arc was replaced by parabola, and the constant surface friction status was adopted during the analysis. The deformation area was divided into three zones according to the direction of the friction. Then, the three zones were studied, respectively. A rolling force model and a rolling torque model were developed based on the analysis, and they were used to analyze the influ- ence of asymmetrical rolling factors on deformation area and unit pressure if they had good precision which was determined by comparing the calculated results with the measured ones.展开更多
The fragmentation mechanism of low-grade hematite ore in a high pressure grinding roll(HPGR) was studied based on the characteristics of comminuted products at different specific pressure levels. The major properties ...The fragmentation mechanism of low-grade hematite ore in a high pressure grinding roll(HPGR) was studied based on the characteristics of comminuted products at different specific pressure levels. The major properties included the reduction ratio, liberation, specific surface energy, and specific surface area. The results showed that the fracture of low-grade hematite ore in HPGR was an interactive dynamic process in which the interaction between coarse particles of gangue minerals and fine particles of valuable minerals was alternately continuous with increased compactness and compacting strength of materials. Within a range of 2.8–4.4 N/mm^2, valuable minerals were crushed after preferentially absorbing energy, whereas gangue minerals were not completely crushed and only acted as an energy transfer medium. Within a range of 4.4–5.2 N/mm^2, gangue minerals were adequately crushed after absorbing the remaining energy, whereas preferentially crushed valuable minerals acted as an energy transfer medium. Within a range of 5.2–6.0 N/mm^2 range, the low-grade hematite ore was not further comminuted because of the "size effect" on the strength of materials, and the comminution effect of materials became stable.展开更多
The rotating jet bed(RJB)has been developed by Zhejiang University of Technology,as a noveler type of gas-liquid mass-transfer unit than rotating zigzag bed(RZB).The rotor of RJB is composed of perforated concentric b...The rotating jet bed(RJB)has been developed by Zhejiang University of Technology,as a noveler type of gas-liquid mass-transfer unit than rotating zigzag bed(RZB).The rotor of RJB is composed of perforated concentric baffles fixed to a rotating disc.The top of the baffles is in the grooves of the stationary disc,preventing short cut of the gas.Experiments of total reflux distillation with RZB and two types of RJB were carried out with ethanol-water systems at atmospheric pressure.The two types of RJB are with rotor of mesh baffles and of shutter baffles,respectively.The results showed that the number of theoretical plates per meter of RJB,lower than that of RZB,increased with increasing rotational speed,and increased firstly and then decreased with increasing gas superficial F-factor.The maximum number of theoretical plates per meter is 40.7 for RJB with rotor of mesh baffles and 40.0 for RJB with rotor of shutter baffles.The specific pressure drop of RJB was far less than that of RZB.The gas phase film volumetric mass-transfer coefficients of RJB with rotor of mess baffles and shutter baffles were correlated with the Reynolds number,Grashof number and Schmidt number.The calculated value agreed well with the experimental value,and the average deviation was less than 15%.展开更多
基金Projects(51221001,51275417)supported by the National Natural Science Foundation of ChinaProject(SKLSP201103)supported by the Fund of the State Key Laboratory of Solidification ProcessingProject(B08040)supported by the Introducing Talents of Discipline toUniversities,China
文摘Carbon fiber reinforced aluminum matrix （Cf/Al） composite has many excellent properties, and it has received more and more attention. Two-dimensional （2D） Cf/Al composites were fabricated by vacuum and pressure infiltration, which was an integrated technique and could provide high vacuum and high infiltration pressure. The effect of specific pressure on the infiltration quality of the obtained composites was comparatively evaluated through microstructure observation. The experimental results show that satisfied Cf/Al composites could be fabricated at the specific pressure of 75 MPa. In this case, the preform was infiltrated much more completely by aluminum alloy liquid, and the residual porosity was seldom found. It is found that the ultimate tensile strength of the obtained Cf/Al composite reached maximum at the specific pressure of 75 MPa, which was improved by 138.9% compared with that of matrix alloy.
基金Item Sponsored by National Natural Science Foundation of China (50104006)National Key Technology Research and Development Program of China(2006BAE03A08)
文摘The plane strain asymmetrical rolling was analyzed using slab method. The contact arc was replaced by parabola, and the constant surface friction status was adopted during the analysis. The deformation area was divided into three zones according to the direction of the friction. Then, the three zones were studied, respectively. A rolling force model and a rolling torque model were developed based on the analysis, and they were used to analyze the influ- ence of asymmetrical rolling factors on deformation area and unit pressure if they had good precision which was determined by comparing the calculated results with the measured ones.
基金Project(2012AA062301)supported by the National High Technology Research and Development Program of China
文摘The fragmentation mechanism of low-grade hematite ore in a high pressure grinding roll(HPGR) was studied based on the characteristics of comminuted products at different specific pressure levels. The major properties included the reduction ratio, liberation, specific surface energy, and specific surface area. The results showed that the fracture of low-grade hematite ore in HPGR was an interactive dynamic process in which the interaction between coarse particles of gangue minerals and fine particles of valuable minerals was alternately continuous with increased compactness and compacting strength of materials. Within a range of 2.8–4.4 N/mm^2, valuable minerals were crushed after preferentially absorbing energy, whereas gangue minerals were not completely crushed and only acted as an energy transfer medium. Within a range of 4.4–5.2 N/mm^2, gangue minerals were adequately crushed after absorbing the remaining energy, whereas preferentially crushed valuable minerals acted as an energy transfer medium. Within a range of 5.2–6.0 N/mm^2 range, the low-grade hematite ore was not further comminuted because of the "size effect" on the strength of materials, and the comminution effect of materials became stable.
文摘The rotating jet bed(RJB)has been developed by Zhejiang University of Technology,as a noveler type of gas-liquid mass-transfer unit than rotating zigzag bed(RZB).The rotor of RJB is composed of perforated concentric baffles fixed to a rotating disc.The top of the baffles is in the grooves of the stationary disc,preventing short cut of the gas.Experiments of total reflux distillation with RZB and two types of RJB were carried out with ethanol-water systems at atmospheric pressure.The two types of RJB are with rotor of mesh baffles and of shutter baffles,respectively.The results showed that the number of theoretical plates per meter of RJB,lower than that of RZB,increased with increasing rotational speed,and increased firstly and then decreased with increasing gas superficial F-factor.The maximum number of theoretical plates per meter is 40.7 for RJB with rotor of mesh baffles and 40.0 for RJB with rotor of shutter baffles.The specific pressure drop of RJB was far less than that of RZB.The gas phase film volumetric mass-transfer coefficients of RJB with rotor of mess baffles and shutter baffles were correlated with the Reynolds number,Grashof number and Schmidt number.The calculated value agreed well with the experimental value,and the average deviation was less than 15%.