A novel chemical technique combined with unique plasma activated sintering（PAS） was utilized to prepare consolidated copper matrix composites（CMCs） by adding Cu-SnO2-rGO layered micro powders as reinforced fillers...A novel chemical technique combined with unique plasma activated sintering（PAS） was utilized to prepare consolidated copper matrix composites（CMCs） by adding Cu-SnO2-rGO layered micro powders as reinforced fillers into Cu matrix. The repeating Cu-SnO2-rGO structure was composed of inner dispersed reduced graphene oxide（r GO）, SnO2 as intermedia and outer Cu coating. SnO2 was introduced to the surface of rGO sheets in order to prevent the graphene aggregation with SnO2 serving as spacer and to provide enough active sites for subsequent Cu deposition. This process can guarantee rGO sheets to suffi ciently disperse and Cu nanoparticles to tightly and uniformly anchor on each layer of rGO by means of the SnO2 active sites as well as strictly control the reduction speed of Cu^2＋. The complete cover of Cu nanoparticles on rGO sheets thoroughly avoids direct contact among rGO layers. Hence, the repeating structure can simultaneously solve the wettability problem between rGO and Cu matrix as well as improve the bonding strength between rGO and Cu matrix at the well-bonded Cu-SnO2-rGO interface. The isolated rGO can effectively hinder the glide of dislocation at Cu-rGO interface and support the applied loads. Finally, the compressive strength of CMCs was enhanced when the strengthening effi ciency reached up to 41.展开更多
SnO2-reduced graphene oxide （SnO2-rGO） composites were prepared via a hydro-thermal reaction of graphene oxide （GO） and SnCI2·2H2O in the mixed solvent of ethylene glycol and water. During the redox reaction,...SnO2-reduced graphene oxide （SnO2-rGO） composites were prepared via a hydro-thermal reaction of graphene oxide （GO） and SnCI2·2H2O in the mixed solvent of ethylene glycol and water. During the redox reaction, GO was reduced to rGO while Sn2＋ was oxidized to Sn02, uniformly depositing on the surface of rGO sheets. The composites were characterized by X-ray diffraction （XRD）, scanning electron microscopy （SEM）, thermogravimetric analysis （TGA）, infrared spectra analysis （IR） and transmission electron microscopy （TEM）, respectively, and their gas sensing properties were further investigated. Compared with pure SnO2 nanoparticles, the as-prepared SnO2-rGO gas sensor and response-recovery time to ethanol and H2S at responding and low cost SnO2-rGO gas sensor could showed much better gas sensing behavior in sensitivity ow concentrations. Overall, the highly sensitive, quick- be potentially applied in environmental monitoring area.展开更多
为改善SnO_2-Fe_2O_3的电化学性能,通过一步水热法合成SnO_2-Fe_2O_3/rGO纳米复合材料,采用XRD、SEM、电化学工作站和蓝电电池测试系统,研究rGO加入量对SnO_2-Fe_2O_3/rGO复合材料的结构和电化学性能的影响.结果表明:rGO的掺入能很好地...为改善SnO_2-Fe_2O_3的电化学性能,通过一步水热法合成SnO_2-Fe_2O_3/rGO纳米复合材料,采用XRD、SEM、电化学工作站和蓝电电池测试系统,研究rGO加入量对SnO_2-Fe_2O_3/rGO复合材料的结构和电化学性能的影响.结果表明:rGO的掺入能很好地提高SnO_2-Fe_2O_3循环稳定性和倍率性能;对于SnO_2-Fe_2O_3/rGO50复合材料,在160 m A/g的电流密度下,100次循环后,放电比容量仍然保持596.9 m Ah/g,库仑效率为98%;即使在1 A/g的电流密度下,依然有366.6 m Ah/g的平均放电比容量.展开更多
基金Funded by the National Natural Science Foundation of China(51572208)the 111 Project(B13035)+1 种基金the National Natural Science Foundation of Hubei Province(2014CFB257 and 2014CFB258)the Fundamental Research Funds for the Central Universities(WUT:2015-III-059)
文摘A novel chemical technique combined with unique plasma activated sintering（PAS） was utilized to prepare consolidated copper matrix composites（CMCs） by adding Cu-SnO2-rGO layered micro powders as reinforced fillers into Cu matrix. The repeating Cu-SnO2-rGO structure was composed of inner dispersed reduced graphene oxide（r GO）, SnO2 as intermedia and outer Cu coating. SnO2 was introduced to the surface of rGO sheets in order to prevent the graphene aggregation with SnO2 serving as spacer and to provide enough active sites for subsequent Cu deposition. This process can guarantee rGO sheets to suffi ciently disperse and Cu nanoparticles to tightly and uniformly anchor on each layer of rGO by means of the SnO2 active sites as well as strictly control the reduction speed of Cu^2＋. The complete cover of Cu nanoparticles on rGO sheets thoroughly avoids direct contact among rGO layers. Hence, the repeating structure can simultaneously solve the wettability problem between rGO and Cu matrix as well as improve the bonding strength between rGO and Cu matrix at the well-bonded Cu-SnO2-rGO interface. The isolated rGO can effectively hinder the glide of dislocation at Cu-rGO interface and support the applied loads. Finally, the compressive strength of CMCs was enhanced when the strengthening effi ciency reached up to 41.
基金supported by the University of Science and Technology BeijingNational Center for Nanoscience and Technology Beijingthe National Basic Research Program of China (No.2007CB714304)
文摘SnO2-reduced graphene oxide （SnO2-rGO） composites were prepared via a hydro-thermal reaction of graphene oxide （GO） and SnCI2·2H2O in the mixed solvent of ethylene glycol and water. During the redox reaction, GO was reduced to rGO while Sn2＋ was oxidized to Sn02, uniformly depositing on the surface of rGO sheets. The composites were characterized by X-ray diffraction （XRD）, scanning electron microscopy （SEM）, thermogravimetric analysis （TGA）, infrared spectra analysis （IR） and transmission electron microscopy （TEM）, respectively, and their gas sensing properties were further investigated. Compared with pure SnO2 nanoparticles, the as-prepared SnO2-rGO gas sensor and response-recovery time to ethanol and H2S at responding and low cost SnO2-rGO gas sensor could showed much better gas sensing behavior in sensitivity ow concentrations. Overall, the highly sensitive, quick- be potentially applied in environmental monitoring area.
文摘为改善SnO_2-Fe_2O_3的电化学性能,通过一步水热法合成SnO_2-Fe_2O_3/rGO纳米复合材料,采用XRD、SEM、电化学工作站和蓝电电池测试系统,研究rGO加入量对SnO_2-Fe_2O_3/rGO复合材料的结构和电化学性能的影响.结果表明:rGO的掺入能很好地提高SnO_2-Fe_2O_3循环稳定性和倍率性能;对于SnO_2-Fe_2O_3/rGO50复合材料,在160 m A/g的电流密度下,100次循环后,放电比容量仍然保持596.9 m Ah/g,库仑效率为98%;即使在1 A/g的电流密度下,依然有366.6 m Ah/g的平均放电比容量.