为改善SnO_2-Fe_2O_3的电化学性能,通过一步水热法合成SnO_2-Fe_2O_3/rGO纳米复合材料,采用XRD、SEM、电化学工作站和蓝电电池测试系统,研究rGO加入量对SnO_2-Fe_2O_3/rGO复合材料的结构和电化学性能的影响.结果表明:rGO的掺入能很好地...为改善SnO_2-Fe_2O_3的电化学性能,通过一步水热法合成SnO_2-Fe_2O_3/rGO纳米复合材料,采用XRD、SEM、电化学工作站和蓝电电池测试系统,研究rGO加入量对SnO_2-Fe_2O_3/rGO复合材料的结构和电化学性能的影响.结果表明:rGO的掺入能很好地提高SnO_2-Fe_2O_3循环稳定性和倍率性能;对于SnO_2-Fe_2O_3/rGO50复合材料,在160 m A/g的电流密度下,100次循环后,放电比容量仍然保持596.9 m Ah/g,库仑效率为98%;即使在1 A/g的电流密度下,依然有366.6 m Ah/g的平均放电比容量.展开更多
A new SnO2-Fe2O3/SWCNTs（single-walled carbon nanotubes） ternary nanocomposite was first synthesized by a facile hydrothermal approach.SnO2 and Fe2O3 nanoparticles（NPs） were homogeneously located on the surface of ...A new SnO2-Fe2O3/SWCNTs（single-walled carbon nanotubes） ternary nanocomposite was first synthesized by a facile hydrothermal approach.SnO2 and Fe2O3 nanoparticles（NPs） were homogeneously located on the surface of SWCNTs,as confirmed by X-ray diffraction（XRD）,transmission electron microscope（TEM） and energy dispersive X-ray spectroscopy（EDX）.Due to the synergistic effect of different components,the as synthesized SnO2-Fe2O3/SWCNTs composite as an anode material for lithium-ion batteries exhibited excellent electrochemical performance with a high capacity of 692 mAh·g-1 which could be maintained after 50 cycles at 200 mA·g-1.Even at a high rate of2000 mA·g-1,the capacity was still remained at 656 mAh·g-1.展开更多
High-purity(99%)carbon nanocoils(CNCs)have been synthesized by using porousα-Fe2O3/SnO2 catalyst.The yield of CNCs reaches 9,098%after a 6 h growth.This value is much higher than the previously reported data,indicati...High-purity(99%)carbon nanocoils(CNCs)have been synthesized by using porousα-Fe2O3/SnO2 catalyst.The yield of CNCs reaches 9,098%after a 6 h growth.This value is much higher than the previously reported data,indicating that this method is promising to synthesize high-purity CNCs on a large scale.It is considered that an appropriate proportion of Fe and Sn,proper particle size distribution,and a loose-porous aggregate structure of the catalyst are the key points to the high-purity growth of CNCs.Benefiting from the high-purity preparation,a CNC Buckypaper was successfully prepared and the electrical,mechanical,and electrochemical properties were investigated comprehensively.Furthermore,as one of the practical applications,the CNC Buckypaper was successfully utilized as an efficient adsorbent for the removal of methylene blue dye from wastewater with an adsorption efficiency of 90.9%.This study provides a facile and economical route for preparing high-purity CNCs,which is suitable for large-quantity production.Furthermore,the fabrication of macroscopic CNC Buckypaper provides promising alternative of adsorbent or other practical applications.展开更多
文摘为改善SnO_2-Fe_2O_3的电化学性能,通过一步水热法合成SnO_2-Fe_2O_3/rGO纳米复合材料,采用XRD、SEM、电化学工作站和蓝电电池测试系统,研究rGO加入量对SnO_2-Fe_2O_3/rGO复合材料的结构和电化学性能的影响.结果表明:rGO的掺入能很好地提高SnO_2-Fe_2O_3循环稳定性和倍率性能;对于SnO_2-Fe_2O_3/rGO50复合材料,在160 m A/g的电流密度下,100次循环后,放电比容量仍然保持596.9 m Ah/g,库仑效率为98%;即使在1 A/g的电流密度下,依然有366.6 m Ah/g的平均放电比容量.
基金The project was supported by the National Natural Science Foundation of China(21163016,21174114)Gansu Provincial Natural Science Foundation,China(1010RJZA024)Scientific Research Fund of Northwest Normal University,China(NWNU-KJCXGC-03-63)~~
基金supported by the National Key Project on Basic Research(Grant No.2011CB935904)the National Natural Science Foundation of China(Grant No.21171163,91127020)NSF for Distinguished Young Scholars of Fujian Province(Grant No.2013J06006)
文摘A new SnO2-Fe2O3/SWCNTs（single-walled carbon nanotubes） ternary nanocomposite was first synthesized by a facile hydrothermal approach.SnO2 and Fe2O3 nanoparticles（NPs） were homogeneously located on the surface of SWCNTs,as confirmed by X-ray diffraction（XRD）,transmission electron microscope（TEM） and energy dispersive X-ray spectroscopy（EDX）.Due to the synergistic effect of different components,the as synthesized SnO2-Fe2O3/SWCNTs composite as an anode material for lithium-ion batteries exhibited excellent electrochemical performance with a high capacity of 692 mAh·g-1 which could be maintained after 50 cycles at 200 mA·g-1.Even at a high rate of2000 mA·g-1,the capacity was still remained at 656 mAh·g-1.
基金financially supported by the National Natural Science Foundation of China(Nos.51661145025,51972039,and 51803018)
文摘High-purity(99%)carbon nanocoils(CNCs)have been synthesized by using porousα-Fe2O3/SnO2 catalyst.The yield of CNCs reaches 9,098%after a 6 h growth.This value is much higher than the previously reported data,indicating that this method is promising to synthesize high-purity CNCs on a large scale.It is considered that an appropriate proportion of Fe and Sn,proper particle size distribution,and a loose-porous aggregate structure of the catalyst are the key points to the high-purity growth of CNCs.Benefiting from the high-purity preparation,a CNC Buckypaper was successfully prepared and the electrical,mechanical,and electrochemical properties were investigated comprehensively.Furthermore,as one of the practical applications,the CNC Buckypaper was successfully utilized as an efficient adsorbent for the removal of methylene blue dye from wastewater with an adsorption efficiency of 90.9%.This study provides a facile and economical route for preparing high-purity CNCs,which is suitable for large-quantity production.Furthermore,the fabrication of macroscopic CNC Buckypaper provides promising alternative of adsorbent or other practical applications.