Preparation of high acidity coefficient slag wool fiber with molten slag and modifying agents is considered to be a positive approach for value-added utilization of blast furnace slag. In order to achieve the multi-pu...Preparation of high acidity coefficient slag wool fiber with molten slag and modifying agents is considered to be a positive approach for value-added utilization of blast furnace slag. In order to achieve the multi-purposes of fiber-forming, energy saving, and waste heat recovery, the modifying agents that can improve the acidity coefficient of slag effectively, economically, and environmentally were investigated. Three agents with different acidity coefficients were adopted to modify slag and manufacture wool fibers. The effect of agent and slag proportion on the melting temperature and viscosity of molten slag was studied at a fixed acidity coefficient of 1.8 and 2.0. The results indicate that the sample modified with high acidity coefficient agent and high slag proportion has lower melting temperature and viscosity. The effect of agent and slag temperature on the fiber diameter was also investigated when the acidity coefficient of slag is 2.0. At a fixed slag proportion of 50 wt.%, the mean diameter decreases with increasing temperature and decreasing viscosity coefficient. Besides, the temperature drops caused by the addition of agents and energy consumption of samples for heating the slag were also analyzed.展开更多
This study describes the characteristics of mineral wool and its applications,and also introduces the traditional process of mineral wool made from molten blast furnace （BF） slag. Compared with high energy consumpti...This study describes the characteristics of mineral wool and its applications,and also introduces the traditional process of mineral wool made from molten blast furnace （BF） slag. Compared with high energy consumption of the traditional process,the production of mineral wool by using molten BF slag will be able to take full advantage of the sensible heat of molten slag, and also reduce production costs. However, there are also further issues to resolve such as how to obtain the required amount of molten BF slag and how to make it homogeneous. Based on the physical and chemical properties of the molten BF slag,the investigation into the relationship between temperature and viscosity under different acidity coefficients of the slag and silicon mixture was conducted. Combined with the crystallization and phase diagram of slag wool, its heat resistance, water resistance, durability and corrosion resistance were analyzed. Finally, trends of the technology development are proposed.展开更多
The present paper is aimed at recycling of coal ash and blast furnace slag to produce mineral wool. Considering the mineralogical constitutions of coal ash and blast furnace slag, the primary quaternary slag compositi...The present paper is aimed at recycling of coal ash and blast furnace slag to produce mineral wool. Considering the mineralogical constitutions of coal ash and blast furnace slag, the primary quaternary slag compositions of CaO-SiO2-MgO-Al2O3 with basicity （mass ratio of CaO to SiO2 ） ranging from 0.5 to 0.9 and alumina ranging from 5% to 20% were investigated through a rotating cylinder method. The experimental results indicated that the viscosities decreased with increasing basicity above the liquidus temperature, and increased with increasing alumina content, and the maximum values were reached and as the alumina content was 20%, followed by the decrease with further increasing alumina content due to its amphoteric behavior. The amphoteric behavior of Al2O3 also performed in the relationship between viscosity and non-bridging oxygen per tetrahedrally-eoordinated atom （NBO/T）, and the viscosities decreased with increasing the NBO/T except the slag with a basicity 0.5 and Al2O3 20 % which have a low NBO/T value and a low viscosity than others.展开更多
基金the National Natural Science Foundation of China(Grant No.51974054)Scientific and Technological Research Program of Chongqing Municipal Education Commission(No.KJQN202201537)+2 种基金Research Foundation of Chongqing University of Science and Technology(No.ckrc2020017)Natural Science Foundation Project of Chongqing(No.cstc2021jcyj-msxmX0911)Chongqing Science and Technology Commission(No.sl202100000144).
文摘Preparation of high acidity coefficient slag wool fiber with molten slag and modifying agents is considered to be a positive approach for value-added utilization of blast furnace slag. In order to achieve the multi-purposes of fiber-forming, energy saving, and waste heat recovery, the modifying agents that can improve the acidity coefficient of slag effectively, economically, and environmentally were investigated. Three agents with different acidity coefficients were adopted to modify slag and manufacture wool fibers. The effect of agent and slag proportion on the melting temperature and viscosity of molten slag was studied at a fixed acidity coefficient of 1.8 and 2.0. The results indicate that the sample modified with high acidity coefficient agent and high slag proportion has lower melting temperature and viscosity. The effect of agent and slag temperature on the fiber diameter was also investigated when the acidity coefficient of slag is 2.0. At a fixed slag proportion of 50 wt.%, the mean diameter decreases with increasing temperature and decreasing viscosity coefficient. Besides, the temperature drops caused by the addition of agents and energy consumption of samples for heating the slag were also analyzed.
文摘This study describes the characteristics of mineral wool and its applications,and also introduces the traditional process of mineral wool made from molten blast furnace （BF） slag. Compared with high energy consumption of the traditional process,the production of mineral wool by using molten BF slag will be able to take full advantage of the sensible heat of molten slag, and also reduce production costs. However, there are also further issues to resolve such as how to obtain the required amount of molten BF slag and how to make it homogeneous. Based on the physical and chemical properties of the molten BF slag,the investigation into the relationship between temperature and viscosity under different acidity coefficients of the slag and silicon mixture was conducted. Combined with the crystallization and phase diagram of slag wool, its heat resistance, water resistance, durability and corrosion resistance were analyzed. Finally, trends of the technology development are proposed.
基金Item Sponsored by National Natural Science Foundation of China (50874013)National Key Technology Research and Development Programof China (2007BAB15B04)Program for New Century Excellent Talents in University of China(NCET-07-0071, NCET-08-0723)
文摘The present paper is aimed at recycling of coal ash and blast furnace slag to produce mineral wool. Considering the mineralogical constitutions of coal ash and blast furnace slag, the primary quaternary slag compositions of CaO-SiO2-MgO-Al2O3 with basicity （mass ratio of CaO to SiO2 ） ranging from 0.5 to 0.9 and alumina ranging from 5% to 20% were investigated through a rotating cylinder method. The experimental results indicated that the viscosities decreased with increasing basicity above the liquidus temperature, and increased with increasing alumina content, and the maximum values were reached and as the alumina content was 20%, followed by the decrease with further increasing alumina content due to its amphoteric behavior. The amphoteric behavior of Al2O3 also performed in the relationship between viscosity and non-bridging oxygen per tetrahedrally-eoordinated atom （NBO/T）, and the viscosities decreased with increasing the NBO/T except the slag with a basicity 0.5 and Al2O3 20 % which have a low NBO/T value and a low viscosity than others.