A hydrophobic coating of the silica fiber reinforced silica composites(SiO2f/SiO2) was synthesized by sol-gel method using methyltriethoxy-silane(MTES) and boric acid(B(OH)3) as raw materials. The relationship among b...A hydrophobic coating of the silica fiber reinforced silica composites(SiO2f/SiO2) was synthesized by sol-gel method using methyltriethoxy-silane(MTES) and boric acid(B(OH)3) as raw materials. The relationship among boron doping, chemical structure of precursors and durability of hydrophobic coatings was discussed. The Si-O-B and methyl groups were successfully introduced in the gel precursors according to the FT-IR and XPS results. The resins were filled in the internal and surface holes of the SiO2f/SiO2 composites partially or completely, which is beneficial to reduce the physical adsorption of the moisture. In addition, hydroxyl groups of the SiO2f/SiO2 composites reacted with the resins and hydrophobic methyl groups were introduced, leading to the reduction of the chemical adsorption of water. Also, the boron doping was beneficial to enhancing the physical cross-linking between the coating and the SiO2f/SiO2 composites, and improved the adhesion of the coating to the substrate. The results show that the optimal hydrophobic coating with contact angle 130.33°, moisture absorption 0.33% and adhesion level 1 is obtained when the molar ratio of MTES to B(OH)3 is 10:4. The real permittivity of M10B4 is constant in the range of 2.32–2.51 and the dielectric tangent loss is constant in the range of 5.5 × 10-4–8.7 × 10-3. The hydrophobic coating has excellent dielectric properties.展开更多
Hollow B–SiO2@TiO2 composites were prepared by the wet chemical deposition method starting from TiCl4 and hollow B–SiO2 microspheres.TiO2 layers composed of anatase TiO2 nanoparticles were coated on the surfaces of ...Hollow B–SiO2@TiO2 composites were prepared by the wet chemical deposition method starting from TiCl4 and hollow B–SiO2 microspheres.TiO2 layers composed of anatase TiO2 nanoparticles were coated on the surfaces of the hollow B–SiO2 microspheres probably through the formation of Ti—O—Si and Ti—O—B bonds.A great number of—OH groups were also present at the TiO2 coating layers.The presence of Ti—O—Si bonds and Ti—O—B bonds resulted in the formation of defects in the TiO2 coating layers,which decreased the band gap of the TiO2 coating layers to ca.3.0 eV and endowed the TiO2 coating layers with visible light absorption performance.The buoyancy hollow B–SiO2@TiO2 composites exhibited high photocatalytic activities for the degradation of ammonia-nitrogen and green algae.The conversion of ammonia-nitrogen reached 65%when the degradation of ammonia-nitrogen(43 mg·L-1 at pH value of 8)was catalyzed by the B–SiO2@TiO2(100:10)composite under the simulated solar light irradiation at 35°C for 660 min.The green algae(5 mg·L-1)were almost completely degraded over the B–SiO@TiO2(100:20)photocatalyst under the visible light irradiation at 35°C for 510 min.展开更多
Silicon(Si) materials as anode materials for applications in lithium-ion batteries(LIBs) have received increasing attention.Among the Si materials,the electrochemical properties of SiOx-based(0<x≤2)composites are ...Silicon(Si) materials as anode materials for applications in lithium-ion batteries(LIBs) have received increasing attention.Among the Si materials,the electrochemical properties of SiOx-based(0<x≤2)composites are the most prominent.However,due to the cycling stability of SiOx being far from practical,there are some problems,such as Iow initial coulombic efficiency(ICE),obvious volume expansion and poor conductivity.Researchers in various countries have optimized the electrochemical properties of SiOx-based composites by means of pore formation,surface modification,and the choice of constituents.In this review,SiOx-based composites are classified into three categories based on the valency of Si(SiO2 composites,SiO composites and SiOx(0<x<2) composites).The synthesis,morphologies and electrochemical properties of the SiOx-based composites that are applied in LIB are discussed.Finally,the prope rties of several common SiOx-based composites are briefly compared and the challenges faced by SiOx-based composites are highlight.展开更多
Ni-W-P matrix composites containing CeO2 and SiO2 nano-particles were prepared on common carbon steel surface by means of pulse electrodeposition,and the high-temperature oxidation behavior was investigated.The result...Ni-W-P matrix composites containing CeO2 and SiO2 nano-particles were prepared on common carbon steel surface by means of pulse electrodeposition,and the high-temperature oxidation behavior was investigated.The results show that when the oxidation time is controlled in 1 h,oxidation kinetics curve between oxidation mass gain rate and oxidation temperature of CeO2-SiO2/Ni-W-P composites accords with the index increasing law.When the oxidation temperature is controlled at 300℃,the kinetics curve between oxidation mass gain rate and oxidation time accords with the linear increasing law.The composites as-deposited are in the amorphous state and turn into the crystal state at 400℃.The microstructures of oxidation film on the composites will change from the compact state to the loose state with increasing oxidation temperature to 800℃.They are still continuous and compact,and there are no crackle,strip and falling-out.CeO2 and SiO2 nano-particles co-deposited into Ni-W-P alloy can improve the high-temperature oxidation resistance.展开更多
A silicon dioxide fiber-reinforced silicon nitride matrix （SiOJSi3N4） composite used for radomes was prepared by chemical vapor infiltration （CVI） process using the SiCl4-NH3-H2 system. The effects of the process ...A silicon dioxide fiber-reinforced silicon nitride matrix （SiOJSi3N4） composite used for radomes was prepared by chemical vapor infiltration （CVI） process using the SiCl4-NH3-H2 system. The effects of the process conditions, including infiltration temperature, infiltration time, and gas flux were investigated. The energy dispersion spectra （EDS） result showed that the main elements of this composite contained Si, N, and O. The X-ray diffraction （XRD） results indicated that phases of the composite before and after treatment at 1350℃ were all amorphous. A little fiber pull-out was observed on the cross section of the composite by scan electron microscope （SEM）. As a result, the composite exhibited good thermal stability, but an appropriate interface was necessary between the fiber and the matrix.展开更多
Geopolymers,such as phosphate-based geopolymer,are promising materials that have drawn extensive attentions as wave-transparent candidates with low dielectric loss factor.In this paper,multilayer SiO2fibers are introd...Geopolymers,such as phosphate-based geopolymer,are promising materials that have drawn extensive attentions as wave-transparent candidates with low dielectric loss factor.In this paper,multilayer SiO2fibers are introduced into phosphate-based geopolymer matrix to prepare composites.Crack generation and fracture behaviors during the three-point bending tests in as-prepared SiO2f/phosphate geopolymer composites are clarified by in situ observation Before high-temperature treatment,composite with 17 vol%fiber content exhibits the best mechanical properties.A decreasing mechanical strength is observed after being treated at higher temperature,which is attributed to the stronger interface binging between fibers and phosphatebased geopolymer matrix.Most importantly,the presence of SiO2fibers can strengthen mechanical properties of phosphate-based geopolymer matrix but shows negligible impact on its dielectric properties,achieving dielectric loss factor as low as 3.53910-3after being treated at 700°C.展开更多
Thioglycolic acid（TGA）-stabilized CdTe nanocrystals（NCs） were prepared with sodium tellurite as tellurium source,which avoids the cumbersome processes associated with H2Te or NaHTe sources.Fluorescent CdTe/SiO2 co...Thioglycolic acid（TGA）-stabilized CdTe nanocrystals（NCs） were prepared with sodium tellurite as tellurium source,which avoids the cumbersome processes associated with H2Te or NaHTe sources.Fluorescent CdTe/SiO2 composites were synthesized by a sol-gel method without the exchange of surface ligands.The phase structure of CdTe NCs was investigated by X-ray diffractometry.For comparison,some characterizations were done for both the CdTe NCs and the composites.CdTe NCs and CdTe/SiO2 composites were characterized with TEM,digital camera and fluorescence spectrophotometer.The stability of CdTe NCs and the composites were investigated in phosphate-buffered saline（PBS） buffer and the fluorescent properties of the composites were discussed in detail.展开更多
High surface area Nafion/SiO2 nanocomposites with nano-sized Nafion resin particles entrapped and dispersed within the highly porous silica matrix exhibited significantly enhanced activity, high selectivity and long-t...High surface area Nafion/SiO2 nanocomposites with nano-sized Nafion resin particles entrapped and dispersed within the highly porous silica matrix exhibited significantly enhanced activity, high selectivity and long-term stability for the alkylation of benzene with linear C9-C13 alkenes owing to the increased accessibility of Nafion resin-based acid sites to reactants.展开更多
The micro/nano-scale indentation tests were performed to explore the performance of bisphenol-α-glycidyl methacrylate (Bis-GMA)/triethylene glycol dimethacrylate (TEGDMA) dental resin composites. The effect of the fi...The micro/nano-scale indentation tests were performed to explore the performance of bisphenol-α-glycidyl methacrylate (Bis-GMA)/triethylene glycol dimethacrylate (TEGDMA) dental resin composites. The effect of the filling content of nano-SiO2 particles on the mechanical properties of the dental composites was studied as well. The experimental results showed that the incorporation of the nano-SiO2 particles at low concentrations (up to 10 wt.%) can apparently increase the hardness and elastic modulus of the dental rein composites. The plasticity index indicates a best elastic recovery capability at a proper amount (4 wt.%) of the nanoparticles. Combined with the infrared spectrum, the mechanical enhancement mechanisms of the dental resin composites were analyzed.展开更多
An ambient pressure synthesis of SiO2/TiO2 binary aerogel was prepared through the low-cost precursors of titanium tetrachloride（TiCl4） and sodium silicate（Na2O·nSiO2）.After gelation,solvent exchange and surf...An ambient pressure synthesis of SiO2/TiO2 binary aerogel was prepared through the low-cost precursors of titanium tetrachloride（TiCl4） and sodium silicate（Na2O·nSiO2）.After gelation,solvent exchange and surface modification were performed simultaneously and the modified gel was finally dried under ambient pressure.Microstructural analyses by transmission electron microscope（TEM） indicate that fabricated SiO2/TiO2 aerogel composite shows similar sponge-like nanostructure as silica aerogel,and the Brunauer-EmmettTeller（BET） analysis shows that the specific surface area of the composite reaches 605 m^2/g,and the average pore size is 9.7 nm.Such binary aerogel exhibits significant photocatalytic performance in this paper for treating model pollutant of methyl orange（MO）,and the decolorizing efficiency of MO is detected as 84.9%after 210 mins exposure to UV light irradiation.Degraded gel suspends in the water so as to separate from solution for reuse,and after 4 times recycling,70%degradation efficiency can be easily reached when composite catalyzed system is exposed for 210 mins under UV irradiation.展开更多
In the present work, structure changes during （SiO2） composites have been investigated systematically stretching of isotactic polypropylene （iPP） and iPP/silicon dioxide The or-form crystal structure of both iPP a...In the present work, structure changes during （SiO2） composites have been investigated systematically stretching of isotactic polypropylene （iPP） and iPP/silicon dioxide The or-form crystal structure of both iPP and iPP/SiO2 composites is destroyed and transforms into the mesophase as the samples are stretched at a low temperature （35℃）, while stretching at high temperatures （90℃ and 120℃） can restrain the appearance of defects and keep the perfection of crystal structure. FTIR results reveal that the stretching temperatures show no obvious difference of the effect on the orientation of pure iPP, however, the orientation of iPP/SiO2 composites is greatly changed by the tensile temperature. In the case of micron-sized SiO2 particles （average particle diameter d 〉 1 μm）, the orientation of the composites is lower than that of pure iPP at all stretching temperatures. The above results suggest that the stretching temperature and the SiO2 particle size have great influence on the structure variation and orientation behavior of iPP/SiO2 composites.展开更多
Three-dimensional （3D） five-directional braided （SiO2）/SiO2 composites were prepared by silicasol-infiltration-sintering （SIS） method. The flexural properties and microstructures were studied. The flexural stren...Three-dimensional （3D） five-directional braided （SiO2）/SiO2 composites were prepared by silicasol-infiltration-sintering （SIS） method. The flexural properties and microstructures were studied. The flexural strength and flexural elastic modulus were found to be 73 MPa and 12 GPa, respectively. The results of stress vs deflection curve and SEM examinations revealed that the fracture mechanism of 3D, five-directional braided （SiO2）/SiO2 composite was a mixture mode of ductile and brittle. The ductile mode was attributed to the weak bonding strength of fiber/matrix at low temperature. The brittle fracture might be caused by the propagation of micro defect or crack, which existed in the as-prepared composites for the ten-cycle process.展开更多
Ablation under oxyacetylene torch with heat flux of 4186.8（10%kW/m2 for 20 s was performed to evaluate the ablation resistance of C/C-SiC composites fabricated by chemical vapor infiltration（CVI） combined with liqu...Ablation under oxyacetylene torch with heat flux of 4186.8（10%kW/m2 for 20 s was performed to evaluate the ablation resistance of C/C-SiC composites fabricated by chemical vapor infiltration（CVI） combined with liquid silicon infiltration（LSI） process.The results indicated that C/C-SiC composites present a better ablation resistance than C/C composites without doped SiC.The doped SiC and the ablation products SiO2 derived from it play key roles in ablation process.Bulk quantities of SiO2 nanowires with diameter of 80 nm-150 nm and length of tens microns were observed on the surface of specimens after ablation.The growth mechanism of the SiO_2 nanowires was interpreted with a developed vapor-liquid-solid（VLS） driven by the temperature gradient.展开更多
Silica( SiO_2) based aerogel/xerogel materials have been received ever-growing attentions for versatile applications. However,the widespread applications are narrowed by the inert properties,fragile and brittle nature...Silica( SiO_2) based aerogel/xerogel materials have been received ever-growing attentions for versatile applications. However,the widespread applications are narrowed by the inert properties,fragile and brittle natureof silica materials and cumbersome preparation processes. In this paper,titania( TiO_2) was introduced into SiO_2 matrix to form photocatalytic hybrid gels. The TiO_2/SiO_2 composites were then reinforced by the impregnation of various fibrillary reinforcements,such as glass,mullite mineral and ceramic fibers. The properties of the composites were studied systematically in terms of fiberstability,microstructure,chemical interaction and thermal conductivity. The final xerogel composites displayed improved monolithic geometry,satisfied thermal conductivity(0. 09-0. 25 W·m^(-1)·K^(-1)) and optimized photocatalytic performance(85% removal of model pollutant of methyl orange( Mo)),which could be expected to be a feasible route to multi-functional building facades in the future.展开更多
An improved sol-gel method was employed to prepare Eu3+ ions doped SiO2-Y2O3 nanocomposites.Systematic study was carried out on the effect of post-annealing treatment on photoluminescence(PL) properties of the samples...An improved sol-gel method was employed to prepare Eu3+ ions doped SiO2-Y2O3 nanocomposites.Systematic study was carried out on the effect of post-annealing treatment on photoluminescence(PL) properties of the samples under various europium ions doping concentrations.X-ray diffraction(XRD) patterns indicated that the samples showed an amorphous matrix structure,and the scanning electron microscopy(SEM) pictures showed that the samples presented a nano size(from 21 to 42 nm) granular-stack structure after hi...展开更多
The present study involves the preparation of TiO 2/ SiO 2nanocrystals and their application in self-cleaning wool-polyester fabrics.The TiO 2/ SiO 2nanocrystals were successfully synthesized and deposited onto wool-p...The present study involves the preparation of TiO 2/ SiO 2nanocrystals and their application in self-cleaning wool-polyester fabrics.The TiO 2/ SiO 2nanocrystals were successfully synthesized and deposited onto wool-polyester fabrics using the low-temperature sol-gel technique.The as-prepared nanocomposites and the nanocomposites coated samples were characterized by X-ray diffraction( XRD) and scanning electron microscopy( SEM),respectively.The XRD and SEM results showed that the single-phase anatase nanocrystallites were formed and loaded on the fabric surface successfully.The photocatalytic activities of TiO 2-coated and TiO 2/ SiO 2-coated wool-polyester fabrics were measured by studying photodegradation of methylene blue dye.Comparison of the photocatalytic activity of the coated samples reveals superiority of TiO 2/ SiO 2modified sample with respect to that of pure TiO 2modified sample.Our observations indicate that by applying this technique to the fabrics,self-cleaning materials can be designed for practical application.展开更多
Al2O3/SiO2 ceramic core nano-composites were prepared and their microstructure was investigated by transmission electron microscope（TEM）. The results show that intergranular nano-composites are achieved. The bonding...Al2O3/SiO2 ceramic core nano-composites were prepared and their microstructure was investigated by transmission electron microscope（TEM）. The results show that intergranular nano-composites are achieved. The bonding between Al2O3 and SiO2 particles is well and the interface is even. Amorphous phases and nano crystals appear in the Al2O3/SiO2 ceramic core nano-composites, which both come into being during the cooling process after sintering. Glass phase does not appear between the Al2O3 and SiO2 particles and only appears among the Al2O3 particles, which can be explained with stress model. The quantity of the glass phase is not much and its influence on the high-temperature deformation of the ceramic core nano-composites is little.展开更多
LaF^3＋ Yb^3＋ , Er^3＋ nanoparticles were successfully synthesized using solvothermal treatment, and LaF^3＋ Yb^3＋ , Er^3＋/SiO2 core/shell nanoparticles were also prepared with reverse microemulsion technique. The ...LaF^3＋ Yb^3＋ , Er^3＋ nanoparticles were successfully synthesized using solvothermal treatment, and LaF^3＋ Yb^3＋ , Er^3＋/SiO2 core/shell nanoparticles were also prepared with reverse microemulsion technique. The crystal structure, morphology and photoluminescence properties of as-prepared core/shell nanoparticles were in- vestigated by X-ray diffraction, transmission electron microscopy and fluorescence spectrophotometer. The re- sults showed thatLaF^3＋ Yb^3＋ , Er^3＋ nanoparticles are of hexagonal structure and SiO2 shell is amorphous. The size ofLaF^3＋ Yb^3＋ , Er^3＋. nanoparticles is 13 nm and the LaF^3＋ Yb^3＋ , Er^3＋/SiO2 nanoparticles present clearly a core/shell structure with 12 nm shell thickness. The solubility of LaF^3＋ Yb^3＋ , Er^3＋ nanocrystals in water and the biocompatibility are both improved by the SiO2 shell. The upconversion luminescence spectra suggested that the SiO~ shell has small effect on the upconversion luminescence properties of the LaF^3＋ Yb^3＋ , Er^3＋ nanocrys- tals. The core/shell structure LaF^3＋ Yb^3＋ , Er^3＋ /SiO2. nanopartlcles are expected to be used in biological appli- cations.展开更多
Gold nanorods (AuNRs/GNR) have unique, controllable and anisotropic local surface plasmon resonance (SPR) properties, which have been widely used in biochemistry, electronics and catalysis.<span style="font-fa...Gold nanorods (AuNRs/GNR) have unique, controllable and anisotropic local surface plasmon resonance (SPR) properties, which have been widely used in biochemistry, electronics and catalysis.<span style="font-family:Verdana;"> </span><span style="font-family:Verdana;">It is of great value and significance to study the synthesis, properties, surface modification and structural regulation of AuNRs.</span><span style="font-family:Verdana;"> </span><span style="font-family:;" "=""><span style="font-family:Verdana;">This paper introduces AuNRs and AuNRs@SiO</span><sub><span style="font-size:12px;font-family:Verdana;">2</span></sub><span style="font-family:Verdana;">. The synthesis of AuNRs@SiO</span><sub><span style="font-size:12px;font-family:Verdana;">2</span></sub><span style="font-family:Verdana;"> composite nanomaterials with quantum dots, graphene, rare earth materials and magnetic materials is described.</span></span><span style="font-family:Verdana;"> </span><span style="font-family:Verdana;">The applications of nanocomposites in optics, biomedicine and biosensors are also discussed. The future development of nanocomposites is proposed.</span>展开更多
基金supported by the Taishan Scholar Project(No.ts201511080)the National Natural Science Foundation of China(Nos.51672059,51172050,51102060 and 51302050)the Natural Scientific Research Innovation Foundation in Harbin Institute of Technology(No.HIT.NSRIF.2014129)
文摘A hydrophobic coating of the silica fiber reinforced silica composites(SiO2f/SiO2) was synthesized by sol-gel method using methyltriethoxy-silane(MTES) and boric acid(B(OH)3) as raw materials. The relationship among boron doping, chemical structure of precursors and durability of hydrophobic coatings was discussed. The Si-O-B and methyl groups were successfully introduced in the gel precursors according to the FT-IR and XPS results. The resins were filled in the internal and surface holes of the SiO2f/SiO2 composites partially or completely, which is beneficial to reduce the physical adsorption of the moisture. In addition, hydroxyl groups of the SiO2f/SiO2 composites reacted with the resins and hydrophobic methyl groups were introduced, leading to the reduction of the chemical adsorption of water. Also, the boron doping was beneficial to enhancing the physical cross-linking between the coating and the SiO2f/SiO2 composites, and improved the adhesion of the coating to the substrate. The results show that the optimal hydrophobic coating with contact angle 130.33°, moisture absorption 0.33% and adhesion level 1 is obtained when the molar ratio of MTES to B(OH)3 is 10:4. The real permittivity of M10B4 is constant in the range of 2.32–2.51 and the dielectric tangent loss is constant in the range of 5.5 × 10-4–8.7 × 10-3. The hydrophobic coating has excellent dielectric properties.
基金Supported by the National Natural Science Foundation of China(21506078).
文摘Hollow B–SiO2@TiO2 composites were prepared by the wet chemical deposition method starting from TiCl4 and hollow B–SiO2 microspheres.TiO2 layers composed of anatase TiO2 nanoparticles were coated on the surfaces of the hollow B–SiO2 microspheres probably through the formation of Ti—O—Si and Ti—O—B bonds.A great number of—OH groups were also present at the TiO2 coating layers.The presence of Ti—O—Si bonds and Ti—O—B bonds resulted in the formation of defects in the TiO2 coating layers,which decreased the band gap of the TiO2 coating layers to ca.3.0 eV and endowed the TiO2 coating layers with visible light absorption performance.The buoyancy hollow B–SiO2@TiO2 composites exhibited high photocatalytic activities for the degradation of ammonia-nitrogen and green algae.The conversion of ammonia-nitrogen reached 65%when the degradation of ammonia-nitrogen(43 mg·L-1 at pH value of 8)was catalyzed by the B–SiO2@TiO2(100:10)composite under the simulated solar light irradiation at 35°C for 660 min.The green algae(5 mg·L-1)were almost completely degraded over the B–SiO@TiO2(100:20)photocatalyst under the visible light irradiation at 35°C for 510 min.
基金supported by the National Natural Science Foundation of China(NSFC,Nos.21671170,21673203, 21201010)the Top-notch Academic Programs Project of Jiangsu Higher Education Institutions(TAPP)+2 种基金Program for New Century Excellent Talents of the University in China(NCET,No.13-0645)Postgraduate Research&Practice Innovation Program of Jiangsu Province(No.XSJCX17-015)the Priority Academic Program Development of Jiangsu Higher Education Institutions.
文摘Silicon(Si) materials as anode materials for applications in lithium-ion batteries(LIBs) have received increasing attention.Among the Si materials,the electrochemical properties of SiOx-based(0<x≤2)composites are the most prominent.However,due to the cycling stability of SiOx being far from practical,there are some problems,such as Iow initial coulombic efficiency(ICE),obvious volume expansion and poor conductivity.Researchers in various countries have optimized the electrochemical properties of SiOx-based composites by means of pore formation,surface modification,and the choice of constituents.In this review,SiOx-based composites are classified into three categories based on the valency of Si(SiO2 composites,SiO composites and SiOx(0<x<2) composites).The synthesis,morphologies and electrochemical properties of the SiOx-based composites that are applied in LIB are discussed.Finally,the prope rties of several common SiOx-based composites are briefly compared and the challenges faced by SiOx-based composites are highlight.
基金Project(20806035)supported by the National Natural Science Foundation of ChinaProject(2007E187M)supported by the Applied Basic Research Plans Program of Yunnan Province,China+2 种基金Project supported by the Foundation for Leaders of Disciplines in Science and Technology of Yunnan Province,ChinaProject(08C0025)supported by the Scientific Research Fund of Yunnan Provincial Education Department,ChinaProject supported by the Training Foundation for Talents of Kunming University of Science and Technology,China
文摘Ni-W-P matrix composites containing CeO2 and SiO2 nano-particles were prepared on common carbon steel surface by means of pulse electrodeposition,and the high-temperature oxidation behavior was investigated.The results show that when the oxidation time is controlled in 1 h,oxidation kinetics curve between oxidation mass gain rate and oxidation temperature of CeO2-SiO2/Ni-W-P composites accords with the index increasing law.When the oxidation temperature is controlled at 300℃,the kinetics curve between oxidation mass gain rate and oxidation time accords with the linear increasing law.The composites as-deposited are in the amorphous state and turn into the crystal state at 400℃.The microstructures of oxidation film on the composites will change from the compact state to the loose state with increasing oxidation temperature to 800℃.They are still continuous and compact,and there are no crackle,strip and falling-out.CeO2 and SiO2 nano-particles co-deposited into Ni-W-P alloy can improve the high-temperature oxidation resistance.
基金This study was financially supported by the Key Foundation of National Science in China (No. 90405015), the National Elitist Youth Foundation of China (No. 50425208the Doctorate Foundation of Northwestern Polytechnical University (CX200505).
文摘A silicon dioxide fiber-reinforced silicon nitride matrix （SiOJSi3N4） composite used for radomes was prepared by chemical vapor infiltration （CVI） process using the SiCl4-NH3-H2 system. The effects of the process conditions, including infiltration temperature, infiltration time, and gas flux were investigated. The energy dispersion spectra （EDS） result showed that the main elements of this composite contained Si, N, and O. The X-ray diffraction （XRD） results indicated that phases of the composite before and after treatment at 1350℃ were all amorphous. A little fiber pull-out was observed on the cross section of the composite by scan electron microscope （SEM）. As a result, the composite exhibited good thermal stability, but an appropriate interface was necessary between the fiber and the matrix.
基金financially supported by the National Natural Science Foundation of China(Nos.518720635150205251832002 and 51621091)。
文摘Geopolymers,such as phosphate-based geopolymer,are promising materials that have drawn extensive attentions as wave-transparent candidates with low dielectric loss factor.In this paper,multilayer SiO2fibers are introduced into phosphate-based geopolymer matrix to prepare composites.Crack generation and fracture behaviors during the three-point bending tests in as-prepared SiO2f/phosphate geopolymer composites are clarified by in situ observation Before high-temperature treatment,composite with 17 vol%fiber content exhibits the best mechanical properties.A decreasing mechanical strength is observed after being treated at higher temperature,which is attributed to the stronger interface binging between fibers and phosphatebased geopolymer matrix.Most importantly,the presence of SiO2fibers can strengthen mechanical properties of phosphate-based geopolymer matrix but shows negligible impact on its dielectric properties,achieving dielectric loss factor as low as 3.53910-3after being treated at 700°C.
文摘Thioglycolic acid（TGA）-stabilized CdTe nanocrystals（NCs） were prepared with sodium tellurite as tellurium source,which avoids the cumbersome processes associated with H2Te or NaHTe sources.Fluorescent CdTe/SiO2 composites were synthesized by a sol-gel method without the exchange of surface ligands.The phase structure of CdTe NCs was investigated by X-ray diffractometry.For comparison,some characterizations were done for both the CdTe NCs and the composites.CdTe NCs and CdTe/SiO2 composites were characterized with TEM,digital camera and fluorescence spectrophotometer.The stability of CdTe NCs and the composites were investigated in phosphate-buffered saline（PBS） buffer and the fluorescent properties of the composites were discussed in detail.
文摘High surface area Nafion/SiO2 nanocomposites with nano-sized Nafion resin particles entrapped and dispersed within the highly porous silica matrix exhibited significantly enhanced activity, high selectivity and long-term stability for the alkylation of benzene with linear C9-C13 alkenes owing to the increased accessibility of Nafion resin-based acid sites to reactants.
文摘The micro/nano-scale indentation tests were performed to explore the performance of bisphenol-α-glycidyl methacrylate (Bis-GMA)/triethylene glycol dimethacrylate (TEGDMA) dental resin composites. The effect of the filling content of nano-SiO2 particles on the mechanical properties of the dental composites was studied as well. The experimental results showed that the incorporation of the nano-SiO2 particles at low concentrations (up to 10 wt.%) can apparently increase the hardness and elastic modulus of the dental rein composites. The plasticity index indicates a best elastic recovery capability at a proper amount (4 wt.%) of the nanoparticles. Combined with the infrared spectrum, the mechanical enhancement mechanisms of the dental resin composites were analyzed.
基金Funded by the National Natural Science Foundation of China(NSFC)(Nos.51278073,51308079 and 51408073)
文摘An ambient pressure synthesis of SiO2/TiO2 binary aerogel was prepared through the low-cost precursors of titanium tetrachloride（TiCl4） and sodium silicate（Na2O·nSiO2）.After gelation,solvent exchange and surface modification were performed simultaneously and the modified gel was finally dried under ambient pressure.Microstructural analyses by transmission electron microscope（TEM） indicate that fabricated SiO2/TiO2 aerogel composite shows similar sponge-like nanostructure as silica aerogel,and the Brunauer-EmmettTeller（BET） analysis shows that the specific surface area of the composite reaches 605 m^2/g,and the average pore size is 9.7 nm.Such binary aerogel exhibits significant photocatalytic performance in this paper for treating model pollutant of methyl orange（MO）,and the decolorizing efficiency of MO is detected as 84.9%after 210 mins exposure to UV light irradiation.Degraded gel suspends in the water so as to separate from solution for reuse,and after 4 times recycling,70%degradation efficiency can be easily reached when composite catalyzed system is exposed for 210 mins under UV irradiation.
基金financially supported by the National Natural Science Foundation of China (Nos. 51073004 and 21074141)the China National Funds for Distinguished Young Scientists (No. 50925313)
文摘In the present work, structure changes during （SiO2） composites have been investigated systematically stretching of isotactic polypropylene （iPP） and iPP/silicon dioxide The or-form crystal structure of both iPP and iPP/SiO2 composites is destroyed and transforms into the mesophase as the samples are stretched at a low temperature （35℃）, while stretching at high temperatures （90℃ and 120℃） can restrain the appearance of defects and keep the perfection of crystal structure. FTIR results reveal that the stretching temperatures show no obvious difference of the effect on the orientation of pure iPP, however, the orientation of iPP/SiO2 composites is greatly changed by the tensile temperature. In the case of micron-sized SiO2 particles （average particle diameter d 〉 1 μm）, the orientation of the composites is lower than that of pure iPP at all stretching temperatures. The above results suggest that the stretching temperature and the SiO2 particle size have great influence on the structure variation and orientation behavior of iPP/SiO2 composites.
基金Funded by the Basic Research Project of Science and Technology of Jiangsu Province(No.BK2009002)the National Natural ScienceFoundation of China(No.61176062)the Fundamental Research Funds for the Central Universities(No.NS2013061)
文摘Three-dimensional （3D） five-directional braided （SiO2）/SiO2 composites were prepared by silicasol-infiltration-sintering （SIS） method. The flexural properties and microstructures were studied. The flexural strength and flexural elastic modulus were found to be 73 MPa and 12 GPa, respectively. The results of stress vs deflection curve and SEM examinations revealed that the fracture mechanism of 3D, five-directional braided （SiO2）/SiO2 composite was a mixture mode of ductile and brittle. The ductile mode was attributed to the weak bonding strength of fiber/matrix at low temperature. The brittle fracture might be caused by the propagation of micro defect or crack, which existed in the as-prepared composites for the ten-cycle process.
基金supported by the Specialized Research Fund for the Doctoral Program of Higher Education of China(Grant No.20110006110025)the National Natural Science Foundation of China(Grant No.U1134102)
文摘Ablation under oxyacetylene torch with heat flux of 4186.8（10%kW/m2 for 20 s was performed to evaluate the ablation resistance of C/C-SiC composites fabricated by chemical vapor infiltration（CVI） combined with liquid silicon infiltration（LSI） process.The results indicated that C/C-SiC composites present a better ablation resistance than C/C composites without doped SiC.The doped SiC and the ablation products SiO2 derived from it play key roles in ablation process.Bulk quantities of SiO2 nanowires with diameter of 80 nm-150 nm and length of tens microns were observed on the surface of specimens after ablation.The growth mechanism of the SiO_2 nanowires was interpreted with a developed vapor-liquid-solid（VLS） driven by the temperature gradient.
基金National Natural Science Foundations of China(Nos.51308079,51408073,51678080,51678081)
文摘Silica( SiO_2) based aerogel/xerogel materials have been received ever-growing attentions for versatile applications. However,the widespread applications are narrowed by the inert properties,fragile and brittle natureof silica materials and cumbersome preparation processes. In this paper,titania( TiO_2) was introduced into SiO_2 matrix to form photocatalytic hybrid gels. The TiO_2/SiO_2 composites were then reinforced by the impregnation of various fibrillary reinforcements,such as glass,mullite mineral and ceramic fibers. The properties of the composites were studied systematically in terms of fiberstability,microstructure,chemical interaction and thermal conductivity. The final xerogel composites displayed improved monolithic geometry,satisfied thermal conductivity(0. 09-0. 25 W·m^(-1)·K^(-1)) and optimized photocatalytic performance(85% removal of model pollutant of methyl orange( Mo)),which could be expected to be a feasible route to multi-functional building facades in the future.
基金supported by the Guangdong Province (2007-173)Jiangmen City (2009-217)
文摘An improved sol-gel method was employed to prepare Eu3+ ions doped SiO2-Y2O3 nanocomposites.Systematic study was carried out on the effect of post-annealing treatment on photoluminescence(PL) properties of the samples under various europium ions doping concentrations.X-ray diffraction(XRD) patterns indicated that the samples showed an amorphous matrix structure,and the scanning electron microscopy(SEM) pictures showed that the samples presented a nano size(from 21 to 42 nm) granular-stack structure after hi...
基金the Fundamental Research Funds for the Central Universities,China，China Postdoctoral Science
文摘The present study involves the preparation of TiO 2/ SiO 2nanocrystals and their application in self-cleaning wool-polyester fabrics.The TiO 2/ SiO 2nanocrystals were successfully synthesized and deposited onto wool-polyester fabrics using the low-temperature sol-gel technique.The as-prepared nanocomposites and the nanocomposites coated samples were characterized by X-ray diffraction( XRD) and scanning electron microscopy( SEM),respectively.The XRD and SEM results showed that the single-phase anatase nanocrystallites were formed and loaded on the fabric surface successfully.The photocatalytic activities of TiO 2-coated and TiO 2/ SiO 2-coated wool-polyester fabrics were measured by studying photodegradation of methylene blue dye.Comparison of the photocatalytic activity of the coated samples reveals superiority of TiO 2/ SiO 2modified sample with respect to that of pure TiO 2modified sample.Our observations indicate that by applying this technique to the fabrics,self-cleaning materials can be designed for practical application.
文摘Al2O3/SiO2 ceramic core nano-composites were prepared and their microstructure was investigated by transmission electron microscope（TEM）. The results show that intergranular nano-composites are achieved. The bonding between Al2O3 and SiO2 particles is well and the interface is even. Amorphous phases and nano crystals appear in the Al2O3/SiO2 ceramic core nano-composites, which both come into being during the cooling process after sintering. Glass phase does not appear between the Al2O3 and SiO2 particles and only appears among the Al2O3 particles, which can be explained with stress model. The quantity of the glass phase is not much and its influence on the high-temperature deformation of the ceramic core nano-composites is little.
文摘LaF^3＋ Yb^3＋ , Er^3＋ nanoparticles were successfully synthesized using solvothermal treatment, and LaF^3＋ Yb^3＋ , Er^3＋/SiO2 core/shell nanoparticles were also prepared with reverse microemulsion technique. The crystal structure, morphology and photoluminescence properties of as-prepared core/shell nanoparticles were in- vestigated by X-ray diffraction, transmission electron microscopy and fluorescence spectrophotometer. The re- sults showed thatLaF^3＋ Yb^3＋ , Er^3＋ nanoparticles are of hexagonal structure and SiO2 shell is amorphous. The size ofLaF^3＋ Yb^3＋ , Er^3＋. nanoparticles is 13 nm and the LaF^3＋ Yb^3＋ , Er^3＋/SiO2 nanoparticles present clearly a core/shell structure with 12 nm shell thickness. The solubility of LaF^3＋ Yb^3＋ , Er^3＋ nanocrystals in water and the biocompatibility are both improved by the SiO2 shell. The upconversion luminescence spectra suggested that the SiO~ shell has small effect on the upconversion luminescence properties of the LaF^3＋ Yb^3＋ , Er^3＋ nanocrys- tals. The core/shell structure LaF^3＋ Yb^3＋ , Er^3＋ /SiO2. nanopartlcles are expected to be used in biological appli- cations.
文摘Gold nanorods (AuNRs/GNR) have unique, controllable and anisotropic local surface plasmon resonance (SPR) properties, which have been widely used in biochemistry, electronics and catalysis.<span style="font-family:Verdana;"> </span><span style="font-family:Verdana;">It is of great value and significance to study the synthesis, properties, surface modification and structural regulation of AuNRs.</span><span style="font-family:Verdana;"> </span><span style="font-family:;" "=""><span style="font-family:Verdana;">This paper introduces AuNRs and AuNRs@SiO</span><sub><span style="font-size:12px;font-family:Verdana;">2</span></sub><span style="font-family:Verdana;">. The synthesis of AuNRs@SiO</span><sub><span style="font-size:12px;font-family:Verdana;">2</span></sub><span style="font-family:Verdana;"> composite nanomaterials with quantum dots, graphene, rare earth materials and magnetic materials is described.</span></span><span style="font-family:Verdana;"> </span><span style="font-family:Verdana;">The applications of nanocomposites in optics, biomedicine and biosensors are also discussed. The future development of nanocomposites is proposed.</span>