Activities of FeO in CaO-SiO2-Al2O3-MgO-FeO slags were determined at 1673 K by electrochemical of the solid electrolyte cell： Mo [Mo＋MoOu[ZrO2（MgO）[Fe＋（CaO-SiO2-Al2O3-MgO-FeO）＋Ag[Fe. The influences of slag com...Activities of FeO in CaO-SiO2-Al2O3-MgO-FeO slags were determined at 1673 K by electrochemical of the solid electrolyte cell： Mo [Mo＋MoOu[ZrO2（MgO）[Fe＋（CaO-SiO2-Al2O3-MgO-FeO）＋Ag[Fe. The influences of slag compositions and basicity on FeO activities were analyzed. The results reveal that, for slags of fixed （%CaO）/（%SiO2） ratio, MgO and Al2O3 content, there was an increase of FeO activities with increase of FeO content. For slags with constant {（%CaO）＋ （%MgO）}/（%SiO2） ratio, fixed FeO and A1203 content, FeO activities decreased when MgO content increased from 5% to 10%, and increased with the increase of MgO content when it was over 10%. The FeO activities increased when （%CaO）/（%SiO2） ratio changed from 1.03 to 1.30 in the slags of constant MgO, FeO and Al2O3 content.展开更多
A multi-phase slag containing Na2O is potential to efficiently dephosphorize high-P hot metal.After dephosphorization,the generated slag with high P2O5 content is regarded as a P resource.Because P2O5 was mainly conce...A multi-phase slag containing Na2O is potential to efficiently dephosphorize high-P hot metal.After dephosphorization,the generated slag with high P2O5 content is regarded as a P resource.Because P2O5 was mainly concentrated in the 2CaO SiO2-3CaO P2O5 solid solution,the recovery of P from dephosphorization slag primarily depends on the separation of the solid solution from other phases.The distribution ratios of P2O5 between solid solution and liquid phase in the CaOSiO2-FeO-P2O5-Nslag system were investigated.The results indicated that the addition of Na2O facilitated the enrichment of P2O5 in the solid solution because it increased not only the distribution ratio of P2O5 but also the mass fraction of the solid solution.The distribution ratio of P2O5 was independent of the P2O5 content in slag.A higher P2O5 content in slag resulted in higher P2O5 and Na2O contents in the solid solution.The distribution ratio of P2O5 increased with the total Fe content in the liquid phase,regardless of the valence of Fe.An increase in the FeO content in slag brought a higher P2O5 content in the solid solution.As slag basicity increased,the distribution ratio of P2O5 increased,but the P2O5 content in the solid solution decreased.展开更多
基金Project supported by the National Natural Science Foundation of China （Grant No.50574036）
文摘Activities of FeO in CaO-SiO2-Al2O3-MgO-FeO slags were determined at 1673 K by electrochemical of the solid electrolyte cell： Mo [Mo＋MoOu[ZrO2（MgO）[Fe＋（CaO-SiO2-Al2O3-MgO-FeO）＋Ag[Fe. The influences of slag compositions and basicity on FeO activities were analyzed. The results reveal that, for slags of fixed （%CaO）/（%SiO2） ratio, MgO and Al2O3 content, there was an increase of FeO activities with increase of FeO content. For slags with constant {（%CaO）＋ （%MgO）}/（%SiO2） ratio, fixed FeO and A1203 content, FeO activities decreased when MgO content increased from 5% to 10%, and increased with the increase of MgO content when it was over 10%. The FeO activities increased when （%CaO）/（%SiO2） ratio changed from 1.03 to 1.30 in the slags of constant MgO, FeO and Al2O3 content.
基金This work was financially supported by the National Natural Science Foundation of China(Nos.51704010,51604003,U1760117)Key Laboratory Open Project Fund of Metallurgical Emission Reduction and Resources Recycling(Anhui University of Technology)Ministry of Education(JKF18-02).
文摘A multi-phase slag containing Na2O is potential to efficiently dephosphorize high-P hot metal.After dephosphorization,the generated slag with high P2O5 content is regarded as a P resource.Because P2O5 was mainly concentrated in the 2CaO SiO2-3CaO P2O5 solid solution,the recovery of P from dephosphorization slag primarily depends on the separation of the solid solution from other phases.The distribution ratios of P2O5 between solid solution and liquid phase in the CaOSiO2-FeO-P2O5-Nslag system were investigated.The results indicated that the addition of Na2O facilitated the enrichment of P2O5 in the solid solution because it increased not only the distribution ratio of P2O5 but also the mass fraction of the solid solution.The distribution ratio of P2O5 was independent of the P2O5 content in slag.A higher P2O5 content in slag resulted in higher P2O5 and Na2O contents in the solid solution.The distribution ratio of P2O5 increased with the total Fe content in the liquid phase,regardless of the valence of Fe.An increase in the FeO content in slag brought a higher P2O5 content in the solid solution.As slag basicity increased,the distribution ratio of P2O5 increased,but the P2O5 content in the solid solution decreased.