SiO2–BN ceramic and Ti plate were joined by active brazing in vacuum with Ag–Cu–Ti＋BN composite filler.The effect of BN content,brazing temperature and time on the microstructure and mechanical properties of the b...SiO2–BN ceramic and Ti plate were joined by active brazing in vacuum with Ag–Cu–Ti＋BN composite filler.The effect of BN content,brazing temperature and time on the microstructure and mechanical properties of the brazed joints was investigated.The results showed that a continuous Ti N–Ti B2reaction layer formed adjacent to the SiO2–BN ceramic,whose thickness played a key role in the bonding properties.Four Ti–Cu compound layers,Ti2Cu,Ti3Cu4,Ti Cu2and Ti Cu4,were observed to border Ti substrate due to the strong affinity of Ti and Cu compared with Ag.The central part of the joint was composed of Ag matrix,over which some fine-grains distributed.The added BN particles reacted with Ti in the liquid filler to form fine Ti B whiskers and Ti N particles with low coefficients of thermal expansion（CTE）,leading to the reduction of detrimental residual stress in the joint,and thus improving the joint strength.The maximum shear strength of 31 MPa was obtained when 3 wt%BN was added in the composite filler,which was 158%higher than that brazed with single Ag–Cu–Ti filler metal.The morphology and thickness of the reaction layer adjacent to the parent materials changed correspondingly with the increase of BN content,brazing temperature and holding time.Based on the correlation between the microstructural evolution and brazing parameters,the bonding mechanism of SiO2–BN and Ti was discussed.展开更多
The precursor infiltration and pyrolysis（PIP） method for preparation of BN/SiO2 composites was used to improve mechanical properties, dielectric properties and feasibility of high temperature dielectric parts with l...The precursor infiltration and pyrolysis（PIP） method for preparation of BN/SiO2 composites was used to improve mechanical properties, dielectric properties and feasibility of high temperature dielectric parts with large dimensions and complex shapes. In the processing procedure, the porous BN ceramic matrix was first successfully prepared by compacting the mixed powders of B and BN and then sintering them at a certain temperature under normal pressure of N2.The polycarbosilane（PCS） solution was vacuum infiltrated into porous BN ceramics at the room temperature and then at 800℃ in the air to depolimerize out amorphous SiO2, and sintered further at 1300℃ in N2 to get BN/SiO2 composites. The microstructure of materials was studied by means of X-ray diffraction and electron probe micro （analysis.） The thermo-decomposition mechanism of PCS was investigated by a TG-DTA and infrared （IR） spectrum analysis. The flexural strengths were measured by the three-point bending method. The dielectric constant and the loss tangent were measured by the wave-guide method. The results show BN/SiO2 composites were fabricated. The obtained composites posses a flexural strength of 61.96-93.31MPa, the dielectric constant in the range of 3.50-3.78 and the order of magnitude of the loss tangent at 10-3, which are good for the high temperature dielectric parts with large size and complex shapes.展开更多
基金supported by the National Natural Science Foundation of China (No. 51405332)
文摘SiO2–BN ceramic and Ti plate were joined by active brazing in vacuum with Ag–Cu–Ti＋BN composite filler.The effect of BN content,brazing temperature and time on the microstructure and mechanical properties of the brazed joints was investigated.The results showed that a continuous Ti N–Ti B2reaction layer formed adjacent to the SiO2–BN ceramic,whose thickness played a key role in the bonding properties.Four Ti–Cu compound layers,Ti2Cu,Ti3Cu4,Ti Cu2and Ti Cu4,were observed to border Ti substrate due to the strong affinity of Ti and Cu compared with Ag.The central part of the joint was composed of Ag matrix,over which some fine-grains distributed.The added BN particles reacted with Ti in the liquid filler to form fine Ti B whiskers and Ti N particles with low coefficients of thermal expansion（CTE）,leading to the reduction of detrimental residual stress in the joint,and thus improving the joint strength.The maximum shear strength of 31 MPa was obtained when 3 wt%BN was added in the composite filler,which was 158%higher than that brazed with single Ag–Cu–Ti filler metal.The morphology and thickness of the reaction layer adjacent to the parent materials changed correspondingly with the increase of BN content,brazing temperature and holding time.Based on the correlation between the microstructural evolution and brazing parameters,the bonding mechanism of SiO2–BN and Ti was discussed.
文摘The precursor infiltration and pyrolysis（PIP） method for preparation of BN/SiO2 composites was used to improve mechanical properties, dielectric properties and feasibility of high temperature dielectric parts with large dimensions and complex shapes. In the processing procedure, the porous BN ceramic matrix was first successfully prepared by compacting the mixed powders of B and BN and then sintering them at a certain temperature under normal pressure of N2.The polycarbosilane（PCS） solution was vacuum infiltrated into porous BN ceramics at the room temperature and then at 800℃ in the air to depolimerize out amorphous SiO2, and sintered further at 1300℃ in N2 to get BN/SiO2 composites. The microstructure of materials was studied by means of X-ray diffraction and electron probe micro （analysis.） The thermo-decomposition mechanism of PCS was investigated by a TG-DTA and infrared （IR） spectrum analysis. The flexural strengths were measured by the three-point bending method. The dielectric constant and the loss tangent were measured by the wave-guide method. The results show BN/SiO2 composites were fabricated. The obtained composites posses a flexural strength of 61.96-93.31MPa, the dielectric constant in the range of 3.50-3.78 and the order of magnitude of the loss tangent at 10-3, which are good for the high temperature dielectric parts with large size and complex shapes.