Sr2Al2SiO7：Ce^3＋, Tb^3＋ white emitting phosphors were fabricated using the sol-gel method. X-Ray Powder Diffraction （XRD） analysis confirmed the formation of Sr2Al2SiO7：Ce^3＋, Tb^3＋. Scanning Electron Microsco...Sr2Al2SiO7：Ce^3＋, Tb^3＋ white emitting phosphors were fabricated using the sol-gel method. X-Ray Powder Diffraction （XRD） analysis confirmed the formation of Sr2Al2SiO7：Ce^3＋, Tb^3＋. Scanning Electron Microscopy （SEM） observation indicated that the microstructure of the phosphor consisted of regular fine grains with an average size of about 0.5-1 μm. Luminescence properties were analyzed by measuring the photoluminescence spectra. The Ce^3＋, Tb^3＋-codoped Sr2Al2SiO7 phosphors showed four main emission peaks： one at 414 nm for Ce^3＋ and three at 482, 543, and 588 nm for Tb^3＋. The emission spectra of the samples with different doping concentrations showed that the Tb^3＋ emission was dominant because of the persistent energy transfer from Ce^3＋. The decay characteristic was better than that prepared by the solid-state process in the comparable condition. The codoped phosphor displayed long persistent white phosphorescence.展开更多
基金the National Natural Science Foundation of China (20376009)the Liaoning Natural Science Foundation (20032129) of China
文摘Sr2Al2SiO7：Ce^3＋, Tb^3＋ white emitting phosphors were fabricated using the sol-gel method. X-Ray Powder Diffraction （XRD） analysis confirmed the formation of Sr2Al2SiO7：Ce^3＋, Tb^3＋. Scanning Electron Microscopy （SEM） observation indicated that the microstructure of the phosphor consisted of regular fine grains with an average size of about 0.5-1 μm. Luminescence properties were analyzed by measuring the photoluminescence spectra. The Ce^3＋, Tb^3＋-codoped Sr2Al2SiO7 phosphors showed four main emission peaks： one at 414 nm for Ce^3＋ and three at 482, 543, and 588 nm for Tb^3＋. The emission spectra of the samples with different doping concentrations showed that the Tb^3＋ emission was dominant because of the persistent energy transfer from Ce^3＋. The decay characteristic was better than that prepared by the solid-state process in the comparable condition. The codoped phosphor displayed long persistent white phosphorescence.