SiO2 coated Ce2S3 red pigment was prepared in ethanol/H2O system via sol-gel method and TEOS were used as silica sources. X-ray diffraction （XRD）, scanning electron microscopy （SEM）, energy dispersive spectroscopy...SiO2 coated Ce2S3 red pigment was prepared in ethanol/H2O system via sol-gel method and TEOS were used as silica sources. X-ray diffraction （XRD）, scanning electron microscopy （SEM）, energy dispersive spectroscopy （EDX）, UV-visible spectro-photometer and automatic colorimeter were used to investigate the properties of the samples. The results showed that the compact SiO2 film formed on the surface of Ce2S3 pigment at a cerium silicon molar ratio of 2. The thermal stability temperature of Ce2S3 pigment was improved to 450 oC after SiO2 coating. In addition, the color of Ce2S3 pigment was not affected significantly through coating colorless and transparent SiO2 and it could be used as safe red pigment in higher temperature fields.展开更多
The effects of MgO/Al2 O3 ratio on the viscous behaviors of MgO-Al2 O3-TiO2-CaO-SiO2 systems were investigated by the rotating cylinder method.Raman spectroscopy was used to analyze the structural characteristics of s...The effects of MgO/Al2 O3 ratio on the viscous behaviors of MgO-Al2 O3-TiO2-CaO-SiO2 systems were investigated by the rotating cylinder method.Raman spectroscopy was used to analyze the structural characteristics of slag and Factsage 7.0 was adopted to demonstrate the liquidus temperature of slag.The results show that the viscosity and activation energy for viscous flow decrease when the MgO/Al2O3 ratio increases from 0.82 to 1.36.The break point temperature and liquidus temperature of slag initially decrease and subsequently increase.The complex viscous structures are gradually depolymerized to simple structural units.In conclusion,with the increase of MgO/Al2O3 ratio,the degree of polymerization of slag decreases,which improves the fluidity of slag.The variations of liquidus temperature of slag lead to the same changes of break point temperature.展开更多
基金Project supported by National Science and Technology Support Program(2011BAE30B03)Special Fund from Shaanxi Provincial Department of Education(12JK0467the Graduate Innovation Fund of Shaanxi Universityof Science and Technology for the financial support
文摘SiO2 coated Ce2S3 red pigment was prepared in ethanol/H2O system via sol-gel method and TEOS were used as silica sources. X-ray diffraction （XRD）, scanning electron microscopy （SEM）, energy dispersive spectroscopy （EDX）, UV-visible spectro-photometer and automatic colorimeter were used to investigate the properties of the samples. The results showed that the compact SiO2 film formed on the surface of Ce2S3 pigment at a cerium silicon molar ratio of 2. The thermal stability temperature of Ce2S3 pigment was improved to 450 oC after SiO2 coating. In addition, the color of Ce2S3 pigment was not affected significantly through coating colorless and transparent SiO2 and it could be used as safe red pigment in higher temperature fields.
基金Projects(51574067,51904063)supported by the National Natural Science Foundation of ChinaProjects(N172503016,N172502005,N172506011)supported by Fundamental Research Funds for the Central Universities,ChinaProject(2018M640259)supported by China Postdoctoral Science Foundation
文摘The effects of MgO/Al2 O3 ratio on the viscous behaviors of MgO-Al2 O3-TiO2-CaO-SiO2 systems were investigated by the rotating cylinder method.Raman spectroscopy was used to analyze the structural characteristics of slag and Factsage 7.0 was adopted to demonstrate the liquidus temperature of slag.The results show that the viscosity and activation energy for viscous flow decrease when the MgO/Al2O3 ratio increases from 0.82 to 1.36.The break point temperature and liquidus temperature of slag initially decrease and subsequently increase.The complex viscous structures are gradually depolymerized to simple structural units.In conclusion,with the increase of MgO/Al2O3 ratio,the degree of polymerization of slag decreases,which improves the fluidity of slag.The variations of liquidus temperature of slag lead to the same changes of break point temperature.
基金supported by the National Natural Science Foundation of China(21703194)the Natural Science Foundation of Jiangsu Province(BK20171168,BK20171169)+2 种基金Natural Science Foundation of Jiangsu Higher Education Institutions of China(17KJB530010,17KJB150038 and18KJA430015)Key Research Project of Social Development of Xuzhou(KC17154)Research Project of Xuzhou University of Technology(XKY2017217)