Silicon-carbide-fiber-reinforced silicon-carbide-ceramic-based matrix(SiC/SiC)composites possess excellent properties such as low density,high strength and high temperature resistance,showing a potential application f...Silicon-carbide-fiber-reinforced silicon-carbide-ceramic-based matrix(SiC/SiC)composites possess excellent properties such as low density,high strength and high temperature resistance,showing a potential application for structural components in the aerospace field,but their oxidation behavior remains largely unknown.In this study,Yb_(2)Si_(2)O_(7)modified SiC/SiC(SiC/SiC-Yb_(2)Si_(2)O_(7))mini-composites were prepared by introducing Yb_(2)Si_(2)O_(7)as anti-oxidation phase into SiC fiber bundles via Sol-Gel and depositing SiC matrix by chemical vapor deposition(CVD).Influence of Yb_(2)Si_(2)O_(7)on microstructure,mechanical property and oxidation behavior of SiC/SiC mini-composites was investigated.The results showed that after oxidation in air at 1200 and 1400℃for 50 h,the tensile strength retentions of SiC/SiC mini-composites were 77%and 69%,respectively,and the fracture morphology exhibited flat.The Yb_(2)Si_(2)O_(7)introduced by Sol-Gel partially distributed in layers,contributing to the toughening of the material.On the fracture surface,there was interlayer debonding,which extended energy dissipation mechanism of SiC/SiC mini-composites.Tensile strength of SiC/SiC-Yb_(2)Si_(2)O_(7)mini-composites at room temperature was 484 MPa.After oxidation in air at 1200 and 1400℃for 50 h,the tensile strengths decreased to 425 and 374 MPa,resulting in retention rates of 88%and 77%,respectively.It displayed typical non-brittle fracture characteristics.The interface oxygen content of SiC/SiC mini-composites at the fracture surface was higher than that of SiC/SiC-Yb_(2)Si_(2)O_(7)mini-composites,indicating that introduction of Yb_(2)Si_(2)O_(7)could alleviate oxygen diffusion towards the interface,and therefore improve the oxidation resistance of SiC/SiC-Yb_(2)Si_(2)O_(7)mini-composites.展开更多
基金National Natural Science Foundation of China(52222202)National Key R&D Program of China(2022YFB3707700)+2 种基金Project of Shanghai Science and Technology Innovation Action Plan(21511104800)Shanghai Pilot Program for Basic Research-Chinese Academy of Science,Shanghai Branch(JCYJ-SHFY-2021-001)Science Center for Gas Turbine Project(P2022-B-Ⅳ-001-001)。
文摘Silicon-carbide-fiber-reinforced silicon-carbide-ceramic-based matrix(SiC/SiC)composites possess excellent properties such as low density,high strength and high temperature resistance,showing a potential application for structural components in the aerospace field,but their oxidation behavior remains largely unknown.In this study,Yb_(2)Si_(2)O_(7)modified SiC/SiC(SiC/SiC-Yb_(2)Si_(2)O_(7))mini-composites were prepared by introducing Yb_(2)Si_(2)O_(7)as anti-oxidation phase into SiC fiber bundles via Sol-Gel and depositing SiC matrix by chemical vapor deposition(CVD).Influence of Yb_(2)Si_(2)O_(7)on microstructure,mechanical property and oxidation behavior of SiC/SiC mini-composites was investigated.The results showed that after oxidation in air at 1200 and 1400℃for 50 h,the tensile strength retentions of SiC/SiC mini-composites were 77%and 69%,respectively,and the fracture morphology exhibited flat.The Yb_(2)Si_(2)O_(7)introduced by Sol-Gel partially distributed in layers,contributing to the toughening of the material.On the fracture surface,there was interlayer debonding,which extended energy dissipation mechanism of SiC/SiC mini-composites.Tensile strength of SiC/SiC-Yb_(2)Si_(2)O_(7)mini-composites at room temperature was 484 MPa.After oxidation in air at 1200 and 1400℃for 50 h,the tensile strengths decreased to 425 and 374 MPa,resulting in retention rates of 88%and 77%,respectively.It displayed typical non-brittle fracture characteristics.The interface oxygen content of SiC/SiC mini-composites at the fracture surface was higher than that of SiC/SiC-Yb_(2)Si_(2)O_(7)mini-composites,indicating that introduction of Yb_(2)Si_(2)O_(7)could alleviate oxygen diffusion towards the interface,and therefore improve the oxidation resistance of SiC/SiC-Yb_(2)Si_(2)O_(7)mini-composites.
