We investigate the properties of light emission from amorphous-Si：H/SiO2 and nc-Si/SiO2 multilayers （MLs）. The size dependence of light emission is well exhibited when the a-Si：H sublayer thickness is thinner than...We investigate the properties of light emission from amorphous-Si：H/SiO2 and nc-Si/SiO2 multilayers （MLs）. The size dependence of light emission is well exhibited when the a-Si：H sublayer thickness is thinner than 4 nm and the interface states are well passlvated by hydrogen. For the nc-Si/Si02 MLs, the oxygen modified interface states and nanocrystalline silicon play a predominant role in the properties of light emission. It is found that the light emission from nc-Si/SiO2 is in agreement with the model of interface state combining with quantum confinement when the size of nc-Si is smaller than 4 nm. The role of hydrogen and oxygen is discussed in detail.展开更多
The one-dimensional photonic crystals of Ag/SiO_(2) system are studied to investigate the photonic band gaps (PBG). The samples were prepared by the ultra-high vacuum electron beam evaporation. The clear band gaps wer...The one-dimensional photonic crystals of Ag/SiO_(2) system are studied to investigate the photonic band gaps (PBG). The samples were prepared by the ultra-high vacuum electron beam evaporation. The clear band gaps were observed. Satisfactory agreement between experimental and calculated results was obtained without fitting. The thickness of SiO_(2 )film has influence on the photonic band gap, as well as it awfully affects the transmittance of Ag. More layers can get clearer PBG.展开更多
We investigated the effects of Si-layer-thickness ratios on ultraviolet (UV) peak intensities of Si/ SiO2 multilayered films produced by alternately stacking several-nanometer-thick Si and SiO2 layers using radio-freq...We investigated the effects of Si-layer-thickness ratios on ultraviolet (UV) peak intensities of Si/ SiO2 multilayered films produced by alternately stacking several-nanometer-thick Si and SiO2 layers using radio-frequency sputtering for the first time. The Si-layer-thickness ratio of the Si/SiO2 film is a very important parameter for enhancing the peak intensity because the ratio is concerned with the size of Si nanocrystals in the film, which might affect the intensity of the UV light emission from the film. We prepared seven samples with various estimated Si-layer-thickness ratios, and measured the photoluminescence spectra of the samples after annealing at 1150°C, 1200°C, or 1250°C for 25 min. From our experiments, we estimate that the proper Si-layer-thickness ratio to obtain the strongest UV peaks from the Si/SiO2 multilayered films is around 0.29. Such a UV-lightemitting thin film is expected to be used in future higher-density optical-disk systems.展开更多
采用全矢量交替方向隐含迭代方法系统分析了高折射率 Si ON薄膜对 Si基 Si O2 阵列波导光栅中波导应力双折射的影响 .分析结果表明在芯区上或下表面沉积 Si ON薄膜可以明显减小 Si基 Si O2 阵列波导光栅 (AWG)中波导的应力双折射 ,但这...采用全矢量交替方向隐含迭代方法系统分析了高折射率 Si ON薄膜对 Si基 Si O2 阵列波导光栅中波导应力双折射的影响 .分析结果表明在芯区上或下表面沉积 Si ON薄膜可以明显减小 Si基 Si O2 阵列波导光栅 (AWG)中波导的应力双折射 ,但这两种补偿方法容易使模场偏移中心位置 ,不利于波导与光纤的耦合 .理想的补偿方法是在芯区上下同时补偿 ,可减小模场偏移 ,并用该方法设计了偏振无关的 1 6通道 AWG.展开更多
基金Supported by the National Natural Science Foundation of China under Grant Nos 60508009, 90301009, 60471021, 50472066, and 10574069, and the State Key Basic Research Programme of China under Grant No 2006CB932202.
文摘We investigate the properties of light emission from amorphous-Si：H/SiO2 and nc-Si/SiO2 multilayers （MLs）. The size dependence of light emission is well exhibited when the a-Si：H sublayer thickness is thinner than 4 nm and the interface states are well passlvated by hydrogen. For the nc-Si/Si02 MLs, the oxygen modified interface states and nanocrystalline silicon play a predominant role in the properties of light emission. It is found that the light emission from nc-Si/SiO2 is in agreement with the model of interface state combining with quantum confinement when the size of nc-Si is smaller than 4 nm. The role of hydrogen and oxygen is discussed in detail.
基金Supported by the National High Technology Development Program of China(Grant No.2003AA32720)Shanghai Nanotechnology Promotion Center(0352nm016, 0359nm204,0252nm084)+2 种基金Science and Technology Council of Shanghai(03dz11009)Fore-research of basic research project(2001CCA02800)the special Foundation for State Major Basic Research Programmeof China(Grant No.001CB610408)
文摘The one-dimensional photonic crystals of Ag/SiO_(2) system are studied to investigate the photonic band gaps (PBG). The samples were prepared by the ultra-high vacuum electron beam evaporation. The clear band gaps were observed. Satisfactory agreement between experimental and calculated results was obtained without fitting. The thickness of SiO_(2 )film has influence on the photonic band gap, as well as it awfully affects the transmittance of Ag. More layers can get clearer PBG.
文摘We investigated the effects of Si-layer-thickness ratios on ultraviolet (UV) peak intensities of Si/ SiO2 multilayered films produced by alternately stacking several-nanometer-thick Si and SiO2 layers using radio-frequency sputtering for the first time. The Si-layer-thickness ratio of the Si/SiO2 film is a very important parameter for enhancing the peak intensity because the ratio is concerned with the size of Si nanocrystals in the film, which might affect the intensity of the UV light emission from the film. We prepared seven samples with various estimated Si-layer-thickness ratios, and measured the photoluminescence spectra of the samples after annealing at 1150°C, 1200°C, or 1250°C for 25 min. From our experiments, we estimate that the proper Si-layer-thickness ratio to obtain the strongest UV peaks from the Si/SiO2 multilayered films is around 0.29. Such a UV-lightemitting thin film is expected to be used in future higher-density optical-disk systems.