Split sleeve cold expansion(SSCX)can efiectively enhance fatigue life of holes by improving the field of residual stress.Numerical simulations were conducted to investigate the parameter influence mechanism and obtain...Split sleeve cold expansion(SSCX)can efiectively enhance fatigue life of holes by improving the field of residual stress.Numerical simulations were conducted to investigate the parameter influence mechanism and obtain higher compressive residual stress(CRS).Expansion method,degree of cold expansion(DCE),friction coefficient between laminations and depth-diameter ratio were analyzed.For Ti-Al stacked joint holes,two expansion methods are proposed,namely aluminum alloy first followed titanium alloy(Al first)and titanium alloy first followed aluminum alloy(Ti first).The results show that expansion method and DCE have significant efiects on the field of circumferential residual stress,and the friction has a negligible influence.A higher value of CRS and a wider layer of plastic deformation are induced with Ti first.Optimal DCE of TiAl stacked structure is 5.2%-5.6%.As the depth-diameter ratio is in the range of 0.5-1.25,a positive linear correlation between the maximum compressive residual stress(CRS_(max))and depth-diameter ratio is shown.展开更多
基金Funded by National Natural Science Foundation of China(No.51175257)。
文摘Split sleeve cold expansion(SSCX)can efiectively enhance fatigue life of holes by improving the field of residual stress.Numerical simulations were conducted to investigate the parameter influence mechanism and obtain higher compressive residual stress(CRS).Expansion method,degree of cold expansion(DCE),friction coefficient between laminations and depth-diameter ratio were analyzed.For Ti-Al stacked joint holes,two expansion methods are proposed,namely aluminum alloy first followed titanium alloy(Al first)and titanium alloy first followed aluminum alloy(Ti first).The results show that expansion method and DCE have significant efiects on the field of circumferential residual stress,and the friction has a negligible influence.A higher value of CRS and a wider layer of plastic deformation are induced with Ti first.Optimal DCE of TiAl stacked structure is 5.2%-5.6%.As the depth-diameter ratio is in the range of 0.5-1.25,a positive linear correlation between the maximum compressive residual stress(CRS_(max))and depth-diameter ratio is shown.