A new process to synthesize polycrystalline samples of Sr14Cu24O41 was presented. Firstly, dry gel powder of Sr14Cu24O41 was synthesized by the citrates sol-gel method, using Sr（NO3）2, Cu（NO3）2, ethylene glycol an...A new process to synthesize polycrystalline samples of Sr14Cu24O41 was presented. Firstly, dry gel powder of Sr14Cu24O41 was synthesized by the citrates sol-gel method, using Sr（NO3）2, Cu（NO3）2, ethylene glycol and citrate acid as raw materials. Then, polycrystalline samples of Sr14Cu24O41 were prepared by solid-state reaction. Thermal Gravimetric and Differential Thermal Analysis（TG-DTA） showed that the temperature for solid-state reaction is at 942 ℃. The samples are identified to be single phase by X-ray Diffraction（XRD） and Scanning Electron Microscopy（SEM）. The SEM pictures showed that the first-step particles were at even size of about 100 nm by this technique. The electronic transport measurements showed that the doping compound were semiconductor with a crossover temperature T in the Arrhenius plot of the resistivity versus temprature.展开更多
基金the National Natural Science Foundation of China(No.10474074)State Key Laboratory of Advanced Technology for Materials Synthesis and Processing(Wuhan University of Technology)(No.WUT 2004 M03)
文摘A new process to synthesize polycrystalline samples of Sr14Cu24O41 was presented. Firstly, dry gel powder of Sr14Cu24O41 was synthesized by the citrates sol-gel method, using Sr（NO3）2, Cu（NO3）2, ethylene glycol and citrate acid as raw materials. Then, polycrystalline samples of Sr14Cu24O41 were prepared by solid-state reaction. Thermal Gravimetric and Differential Thermal Analysis（TG-DTA） showed that the temperature for solid-state reaction is at 942 ℃. The samples are identified to be single phase by X-ray Diffraction（XRD） and Scanning Electron Microscopy（SEM）. The SEM pictures showed that the first-step particles were at even size of about 100 nm by this technique. The electronic transport measurements showed that the doping compound were semiconductor with a crossover temperature T in the Arrhenius plot of the resistivity versus temprature.
基金Special Foundation for Basic Scientific Research of Central Colleges,China University of Geosciences(Wuhan)(CUGL110236)National Natural Science Foundation of China(41104054,61008054)