The expandable graphite(EG)modified TiO_(2) nanocomposites were prepared by the high shearmethod using the TiO_(2) nanoparticles(NPs)and EG as precursors,in which the amount of EG doped in TiO_(2) was 10 wt.%.Followed...The expandable graphite(EG)modified TiO_(2) nanocomposites were prepared by the high shearmethod using the TiO_(2) nanoparticles(NPs)and EG as precursors,in which the amount of EG doped in TiO_(2) was 10 wt.%.Followed by the impregnation method,adjusting the pH of the solution to 10,and using the electrostatic adsorption to achieve spatial confinement,the Pt elementswere mainly distributed on the exposed TiO_(2),thus generating the Pt/10EG-TiO_(2)-10 catalyst.The best CO oxidation activity with the excellent resistance to H_(2)O and SO_(2) was obtained over the Pt/10EG-TiO_(2)-10 catalyst:CO conversion after 36 hr of the reaction was ca.85%under the harsh condition of 10 vol.%H_(2)O and 100 ppm SO_(2) at a high gaseous hourly space velocity(GHSV)of 400,000 hr−1.Physicochemical properties of the catalystswere characterized by various techniques.The results showed that the electrostatic adsorption,which riveted the Pt elements mainly on the exposed TiO_(2) of the support surface,reduced the dispersion of Pt NPs on EG and achieved the effective dispersion of Pt NPs,hence significantly improving CO oxidation activity over the Pt/10EG-TiO_(2)-10 catalyst.The 10 wt.%EG doped in TiO_(2) caused the TiO_(2) support to form a more hydrophobic surface,which reduced the adsorption of H_(2)O and SO_(2) on the catalyst,greatly inhibited deposition of the TiOSO_(4) and formation of the PtSO4 species as well as suppressed the oxidation of SO_(2),thus resulting in an improvement in the resistance to H_(2)O and SO_(2) of the Pt/10EG-TiO_(2)-10 catalyst.展开更多
In this study, Ni/YZrOcatalysts prepared with impregnation method and treated by dielectric barrier discharge plasma(DBD) in different atmospheres have been investigated for methane dry reforming. It is revealed by H-...In this study, Ni/YZrOcatalysts prepared with impregnation method and treated by dielectric barrier discharge plasma(DBD) in different atmospheres have been investigated for methane dry reforming. It is revealed by H-TPR that plasma treatment can enhance the interaction between Ni O/Ni particles and the YZrOpyrochlore support. Therefore, catalysts with smaller Ni O and Ni grains sizes, higher metallic Ni active surface areas can be achieved, as evidenced by XRD, TEM and Hadsorption-desorption measurements. As a consequence, the plasma-treated catalysts show significantly improved activity, stability and coke resistance, as testified by the TEM and TGA-DSC results. Plasma treatment in H/Ar gas mixture is found to be the best condition to prepare Ni/YZrO, which can be used to obtain a catalyst with the highest activity, stability and most potent coke resistance. It is believed that the smaller Ni grain size and higher metallic Ni active surface area induced by plasma treatment are the inherent reasons accounting for the promoted reaction performance of the Ni/YZrOpyrochlore catalysts.展开更多
A comparative study on the corrosion resistance of 17Ni/（NiFe2O4-10NiO） cermet inert anode prepared in differentsintering atmospheres was conducted in Na3AlF6-Al2O3 melt. The results indicate that the corrosion rate...A comparative study on the corrosion resistance of 17Ni/（NiFe2O4-10NiO） cermet inert anode prepared in differentsintering atmospheres was conducted in Na3AlF6-Al2O3 melt. The results indicate that the corrosion rates of NiFe2O4-based cermetanodes prepared in the vacuum and the atmosphere with oxygen content of 2×10^-3 （volume fraction） are 6.46 and 2.71 cm/a,respectively. Though there is a transition layer with lots of holes or pores, a densified layer is formed on the surface of anode due tosome reactions producing aluminates. For the anode prepared in the atmosphere with oxygen content of 2×10^-3, the thickness of thedensification layer （about 50 μm） is thicker than that （about 30 μm） formed on the surface of anode prepared in the vacuum. Thecontents of NiO and Fe（II） in NiFe2xO4-y-z increase with the decrease of oxygen content in sintering atmosphere, which reduces thecorrosion resistance of the material.展开更多
Al2O3/Au nano-laminated composite coatings were prepared by means of magnetron sputtering. The coating was compact and comprised of nano-laminated Al2O3 and Au layers. High temperature cyclic oxidation test was employ...Al2O3/Au nano-laminated composite coatings were prepared by means of magnetron sputtering. The coating was compact and comprised of nano-laminated Al2O3 and Au layers. High temperature cyclic oxidation test was employed to investigate the oxidation resistance of the composite coatings. The results revealed that the applied Al2O3/Au nano-laminated composite coatings improved the oxidation and spallation resistance of the stainless steel substrate significantly. The mechanism accounting for oxidation resistance was related with the suppression of inward oxygen diffusion and selective oxidation of Cr in the substrate. The mechanism accounting for spallation resistance was attributed to the relaxation of thermal stress by the nano-laminated structure.展开更多
基金supported by the National Key R&D Program of China (No.2017YFC0210303).
文摘The expandable graphite(EG)modified TiO_(2) nanocomposites were prepared by the high shearmethod using the TiO_(2) nanoparticles(NPs)and EG as precursors,in which the amount of EG doped in TiO_(2) was 10 wt.%.Followed by the impregnation method,adjusting the pH of the solution to 10,and using the electrostatic adsorption to achieve spatial confinement,the Pt elementswere mainly distributed on the exposed TiO_(2),thus generating the Pt/10EG-TiO_(2)-10 catalyst.The best CO oxidation activity with the excellent resistance to H_(2)O and SO_(2) was obtained over the Pt/10EG-TiO_(2)-10 catalyst:CO conversion after 36 hr of the reaction was ca.85%under the harsh condition of 10 vol.%H_(2)O and 100 ppm SO_(2) at a high gaseous hourly space velocity(GHSV)of 400,000 hr−1.Physicochemical properties of the catalystswere characterized by various techniques.The results showed that the electrostatic adsorption,which riveted the Pt elements mainly on the exposed TiO_(2) of the support surface,reduced the dispersion of Pt NPs on EG and achieved the effective dispersion of Pt NPs,hence significantly improving CO oxidation activity over the Pt/10EG-TiO_(2)-10 catalyst.The 10 wt.%EG doped in TiO_(2) caused the TiO_(2) support to form a more hydrophobic surface,which reduced the adsorption of H_(2)O and SO_(2) on the catalyst,greatly inhibited deposition of the TiOSO_(4) and formation of the PtSO4 species as well as suppressed the oxidation of SO_(2),thus resulting in an improvement in the resistance to H_(2)O and SO_(2) of the Pt/10EG-TiO_(2)-10 catalyst.
基金supported by the National Natural Science Foundation of China (21567016, 21566022, 21263015)the Natural Science Foundation of Jiangxi Province (20151BBE50006, 20151BAB203024)the Education Department of Jiangxi Province (KJLD14005, GJJ150016)
文摘In this study, Ni/YZrOcatalysts prepared with impregnation method and treated by dielectric barrier discharge plasma(DBD) in different atmospheres have been investigated for methane dry reforming. It is revealed by H-TPR that plasma treatment can enhance the interaction between Ni O/Ni particles and the YZrOpyrochlore support. Therefore, catalysts with smaller Ni O and Ni grains sizes, higher metallic Ni active surface areas can be achieved, as evidenced by XRD, TEM and Hadsorption-desorption measurements. As a consequence, the plasma-treated catalysts show significantly improved activity, stability and coke resistance, as testified by the TEM and TGA-DSC results. Plasma treatment in H/Ar gas mixture is found to be the best condition to prepare Ni/YZrO, which can be used to obtain a catalyst with the highest activity, stability and most potent coke resistance. It is believed that the smaller Ni grain size and higher metallic Ni active surface area induced by plasma treatment are the inherent reasons accounting for the promoted reaction performance of the Ni/YZrOpyrochlore catalysts.
基金Project(51474238)supported by the National Natural Science Foundation of China
文摘A comparative study on the corrosion resistance of 17Ni/（NiFe2O4-10NiO） cermet inert anode prepared in differentsintering atmospheres was conducted in Na3AlF6-Al2O3 melt. The results indicate that the corrosion rates of NiFe2O4-based cermetanodes prepared in the vacuum and the atmosphere with oxygen content of 2×10^-3 （volume fraction） are 6.46 and 2.71 cm/a,respectively. Though there is a transition layer with lots of holes or pores, a densified layer is formed on the surface of anode due tosome reactions producing aluminates. For the anode prepared in the atmosphere with oxygen content of 2×10^-3, the thickness of thedensification layer （about 50 μm） is thicker than that （about 30 μm） formed on the surface of anode prepared in the vacuum. Thecontents of NiO and Fe（II） in NiFe2xO4-y-z increase with the decrease of oxygen content in sintering atmosphere, which reduces thecorrosion resistance of the material.
基金Project (50771021) supported by the National Natural Science Foundation of China
文摘Al2O3/Au nano-laminated composite coatings were prepared by means of magnetron sputtering. The coating was compact and comprised of nano-laminated Al2O3 and Au layers. High temperature cyclic oxidation test was employed to investigate the oxidation resistance of the composite coatings. The results revealed that the applied Al2O3/Au nano-laminated composite coatings improved the oxidation and spallation resistance of the stainless steel substrate significantly. The mechanism accounting for oxidation resistance was related with the suppression of inward oxygen diffusion and selective oxidation of Cr in the substrate. The mechanism accounting for spallation resistance was attributed to the relaxation of thermal stress by the nano-laminated structure.